Czochralski growth and crystal structure of cerium-doped Lu2Si2O7 scintillator

Cerium-doped lutetium pyrosilicate crystal, Ce:Lu2Si2O7 (Ce:LPS), was grown by the Czochralski method. The segregation coefficient of Ce3+ ion was studied by the ICP-AES method. X-ray diffraction analysis showed that the structure of Ce:LPS crystal was monoclinic symmetry with space group of C2/m. Perfect cleavage planes (110) and imperfect cleavage planes (001) were observed by optical microscope. The reasons why it is difficult to grow crack-free crystals were studied. After optimized growth parameters, a Ce:LPS crystal with dimension of Phi 25 x 30 mm was grown, which is colorless, high optical quality, cracking-free and no inclusions. The transmittance of Ce:LPS crystal from 380 to 800 nm is over 82% and there is no observable absorption. (c) 2005 Elsevier B.V. All rights reserved.

Ce：Lu2Si2O7闪烁晶体的结构和光谱特性

采用中频感应提拉法生长出Ce：Lu：Si2O7(Ce：LPS)晶体．通过x射线粉末衍射分析，晶体结构属单斜晶系的C21m空间群·光学显微镜下可观测到晶体的(110)解理．在室温下测试了Ce：LPS晶体的吸收光谱、激发光谱和发射光谱。结果表明，Ce：LPS晶体的吸收峰只有两个，分别位于302和349nm，且与激发峰的位置一致，归因于Ce^3+的4f^1→5d^1跃迁的特征吸收所致．发射光谱具有Ce^3+典型的双峰特征，经Gaussian多峰值拟合，带状谱是由384和407nm两个发射峰叠加而成，且后者的强度

Yb:YAP与Yb:YAG晶体光谱性能比较

应用中频感应提拉法生长出掺杂浓度为10 at.-%的Yb:YAG与Yb:YAP晶体，对比了室温下两种晶体的吸收和发射光谱特性。结果表明，Yb:YAG晶体比Yb:YAP晶体有更好的激光性能和低的阈值；同时对比发现，Yb:YAP晶体的吸收截面是Yb:YAG晶体的2.16倍，它容易实现LD泵；由于Yb:YAP晶体的各向异性，它有轴向效应明显，它可以产生偏振激光。

铝酸钇晶体中的生长小面

采用提拉法生长了掺Ce、掺Yb和掺Mn的铝酸钇(YAlO3,YAP)晶体,晶体均完整透明,无肉眼可见的气泡、散射和包裹物等宏观缺陷。通过化学腐蚀和同步辐射白光形貌实验检测了YAP晶体中的生长小面缺陷。结果表明:晶体生长过程中,由于凸向熔体的固-液界面,造成了小面生长现象。沿[101]方向生长的YAP晶体中出现的小面为(102),(201),(121)和(121)奇异面。X射线摇摆曲线表征的结果表明:生长小面的存在严重破坏了晶体的微观结构完整性和均匀性,并导致了小角度晶界缺陷的产生。

Comparison of space- and ground-grown Ce: Bi12SiO20 single crystals

Ce doped Bi12SiO20 single crystals were grown either on board of the Chinese Spacecraft-Shenzhou No.3 (SZ-3) or on the ground at the same conditions with the exception of microgravity. The surface morphology of crystals clearly showed significant differences between the space- and ground-grown portions. The space- and ground-grown crystals have been measured by X-ray rocking curve, Cc concentration distribution in growth direction, dislocation density, absorption spectrums. These results show that the compositional homogeneity and structural perfection of Ce doped crystal grown in space are obviously improved.

Yb掺杂的YAlO<3/sub>单晶体的温梯法生长和光谱性能

The dark-brown colored 5 at% Yb-doped YAlO3 (Yb:YAP) single crystal was grown successfully by temperature gradient technique (TGT) for the first time. The TGT-grown Yb:YAP crystal with the perovskite structure and excellent crystallization perfection were confirmed by the X-ray diffractions techniques. The dark-brown color of TGT-Yb:YAP crystal turned into the colorless after annealing in the air at 1200 degrees C for 10h. The absorption spectra, LD-excited infrared emission and X-ray excited luminescence spectra of the air-annealed Yb:YAP single crystal were investigated at the room temperature. The results indicate that the TGT-Yb:YAP single crystals can be used for the laser and scintillation applications. (c) 2005 Elsevier B.V. All rights reserved.

Effects of gamma irradiation and air annealing on Yb-doped YAlO3 single crystals

The effects of gamma irradiation on as-grown 5 at% Yb:YAlO3 (YAP) and air annealing on gamma-irradiated 5 at% Yb: YAP have been studied by the difference in the absorption spectra before and after treatment. The gamma irradiation and air annealing led to opposite changes of the absorption properties of the Yb: YAP crystal. After air annealing, the gamma-irradiation effects were totally removed over the wavelength range 390-800 nm and the concentrations of Fe3+ and Yb3+ were slightly increased. For the first time, the gamma-irradiation-induced valence changes between Yb3+ and Yb2+ ions in Yb: YAP crystals have been observed. (c) 2005 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Comparison of spectroscopic parameters of 15 at% Yb : YAlO3 and 15 at% Yb : Y3Al5O12

Yb: YAlO3 (YAP) (15 at %) and Yb: Y3Al5O12 (YAG)(15 at %) have been grown using the Czochralski method. Their absorption and fluorescence spectra were measured at room temperature and important spectroscopic parameters were calculated. Through the comparison of spectroscopic parameters of Yb:YAP and Yb: YAG, all results indicate that 15 at % Yb:YAP crystal is a potential candidate used for compact, efficient thin chip lasers when the laser output wavelength is 1012 or 103 8 nm. (C) 2004 Elsevier B.V. All rights reserved.

Cooperative and charge transfer luminescence in Yb3+ -doped yttrium aluminum perovskite (YAlO3)

YAlO3 (YAP) crystals with different Yb3+ concentration have been grown by Czochralski method and cooperative fluorescence of Yb3+ ions in YAP crystal was studied under 940-nm infrared (IR) LD excitation at room temperature. The Yb concentration dependence of absorption intensity of IR and charge transfer bands exhibit different features. The green emission band in the region of 480-520nm was assigned to the cooperative deexcitation of two Yb3+ ions. The remaining upconverted emission bands containing various sharp peaks associated with impurity ions were observed and discussed. Charge transfer luminescence of heavily doped 20at% Yb:YAP is strongly temperature dependent and no concentration quenching of the charge transfer luminescence was found through the investigation of different Yb levels samples. (c) 2006 Elsevier B.V. All rights reserved.

Growth of CeO2 : Bi12SiO20 crystals in multi-position furnace(II) - Space growth experiment

Ce-doped Bi12SiO20 single crystal with size of phi10mm x 40mm was successfully grown in space on board of the spacecraft Shenzhou No.3. The surface morphology of space-grown crystal is different from that of ground-grown crystal The space- and ground-grown crystals were measured by X-ray rocking curves, absorption spectra and micro-Raman spectra. The results show that the quality of Ce-deped crystal grown in space is better than that of the ground-grown one. The effect of doping on optical properties of BSO grown in space is evident in comparison with the ground-grown crystal.