Growth of CeO2 : Bi12SiO20 crystals in multi-position furnace(II) - Space growth experiment

Ce-doped Bi12SiO20 single crystal with size of phi10mm x 40mm was successfully grown in space on board of the spacecraft Shenzhou No.3. The surface morphology of space-grown crystal is different from that of ground-grown crystal The space- and ground-grown crystals were measured by X-ray rocking curves, absorption spectra and micro-Raman spectra. The results show that the quality of Ce-deped crystal grown in space is better than that of the ground-grown one. The effect of doping on optical properties of BSO grown in space is evident in comparison with the ground-grown crystal.

Influence of Fe3+ on perovskite oxides: La2/3Ca1/3Mn1-xFexO3

The structure and magnetoresistance properties in sintered samples of La-2/3 Ca-1/3 Mn1-x FexO3 (0 less than or equal to x less than or equal to 0.84) are studied by using Mossbauer spectroscopy, XRD and magnetic measurement. There are antiferromagnetic interactions between Fe and its nearest neighbors (Fe, Mn) when 0 less than or equal to x less than or equal to 0.67, which are important factors influencing the double-exchange between Mn3+ and Mn4+, Curie temperature, magnetic moment and GMR. It is suggested that the Mn3+(Fe3+)/Mn4+ system also consists of magnetic clusters with different sizes.

A study of the interface of CeO2/Si heterostructure grown by ion beam deposition

Epitaxial cerium dioxide films on single-crystal silicon substrates (CeO2/Si) have been grown by a dual mass-analyzed low-energy ion beam deposition (IBD) system. By double-crystal X-ray diffraction (XRD), Full Width at Half Maximum (FWHM) are 23' and 33' in the rocking curves for (222) and (111) faces of the CeO2 film, respectively, and the lattice-mismatch Delta a/a with the substrate is about - 0.123%. The results show that the CeO2/Si grown by IBD is of high crystalline quality. In this work, the CeO2/Si heterostructure were investigated by X-ray Photoelectron Spectroscopy (XPS) and Auger Electron Spectroscopy (AES) measurements. Especially, XPS and AES depth profiling was used to analyze the compositions and structures in the interface regions of the as-grown and post-annealed CeO2/Si. It was found that there was no silicon oxide in the interface region of the as-grown sample but silicon oxide in the post-annealed sample. The reason for obtaining such high quality heterostructure mainly depends on the absence of silicon oxide in the surface at the beginning of the deposition. (C) 1998 Elsevier Science Ltd. All rights reserved.

Influence of fluorine on radiation-induced charge trapping in the SIMOX buried oxides

Charge trapping in the fluorinated SIMOX buried oxides before and after ionizing radiation has been investigated by means of C-V characteristics. Radiation-induced positive charge trapping which results in negative shift of C-V curves can be restrained by implanting fluorine ions into the SIMOX buried oxides. Pre-radiation charge trapping is suppressed in the fluorinated buried oxides. The fluorine dose and post-implantation anneal time play a very important role in the control of charge trapping.

CERIUM SILICIDE FORMATION IN THIN CE SI MULTILAYER FILMS

Alternating layers of Si(200 angstrom thick) and Ce(200 angstrom thick) up to 26 layers altogether were deposited by electron evaporation under ultrahigh vacuum conditions on Si(100) substrate held at 150-degrees-C. Isothermal, rapid thermal annealing has been used to react these Ce-Si multilayer films. A variety of analytical techniques has been used to study these multilayer films after annealing, and among these are Auger electron spectroscopy, Rutherford backscattering, X-ray diffraction, and high resolution transmission electron microscopy. Intermixing of these thin Ce-Si multilayer films has occurred at temperatures as low as 150-degrees-C for 2 h, when annealed. Increasing the annealing temperature from 150 to 400-degrees-C for 1 h, CeSi2 forms gradually and the completion of reaction occurs at approximately 300-400-degrees-C. During the formation of CeSi2 from 150-400-degrees-C, there is some evidence for small grains in the selected area diffraction patterns, indicating that CeSi2 crystallites were present in some regions. However, we have no conclusive evidence for the formation of epitaxial CeSi2 layers, only polycrystals were formed when reacted in the solid phase even after rapid thermal anneal at 900-degrees-C for 10 s. The formation mechanism has also been discussed in combining the results of the La-Si system.

CHARACTERISTICS OF OXIDES FORMED FROM A SI0.5GE0.5

X-ray photoelectron spectroscopy (XPS) combined with Auger electron spectroscopy (AES) have been used to study the oxides from a Si0.5Ge0.5 alloy grown by molecular beam epitaxy (MBE). The oxidation was performed at 1000 degrees C wet atmosphere. The oxide consists of two layers: a mixed (Si,Ge)O-x layer near the surface and a pure SiOx layer underneath. Ge is rejected from the pure SiOx and piles up at the SiOx/SiGe interface. XPS analysis demonstrates that the chemical shifts of Si 2p and Ge 3d in the oxidized Si0.5Ge0.5 are significantly larger than those in SiO2 and GeO2 formed from pure Si and Ge crystals.

Sensitivity of Total-Dose Radiation Hardness of SIMOX Buried Oxides to Doses of Nitrogen Implantation into Buried Oxides

In order to improve the total-dose radiation hardness of the buried oxides(BOX) in the structure of separa tion-by-implanted-oxygen(SIMOX) silicon-on-insulator(SOI), nitrogen ions are implanted into the buried oxides with two different doses,2 × 1015 and 3 × 1015 cm-2 , respectively. The experimental results show that the radiation hardness of the buried oxides is very sensitive to the doses of nitrogen implantation for a lower dose of irradiation with a Co-60 source. Despite the small difference between the doses of nitrogen implantation, the nitrogen-implanted 2 × 1015 cm-2 BOX has a much higher hardness than the control sample (i. e. the buried oxide without receiving nitrogen implantation) for a total-dose irradiation of 5 × 104rad(Si), whereas the nitrogen-implanted 3 × 1015 cm-2 BOX has a lower hardness than the control sample. However,this sensitivity of radiation hardness to the doses of nitrogen implantation reduces with the increasing total-dose of irradiation (from 5 × 104 to 5 × 105 rad (Si)). The radiation hardness of BOX is characterized by MOS high-frequency (HF) capacitance-voltage (C-V) technique after the top silicon layers are removed. In addition, the abnormal HF C-V curve of the metal-silicon-BOX-silicon(MSOS) structure is observed and explained.