Microcrystalline silicon films and tandem solar cells prepared by triode PECVD

This paper investigates the effects of the diphasic structure on the optoelectronic properties of hydrogenated microcrystalline silicon (mu c-Si:H) films prepared in a triode three-chamber plasma-enhanced chemical vapor deposition (PECVD) system. The influences of boron-compensation doping on the dark-and photo-conductivity of mu c-Si:H films are also described. A tandem solar cell with an entirely mu c-Si:H p-i-n bottom cell and an a-Si:H top cell has been prepared with an initial conversion efficiency of 8.91% (0.126 cm(2), AM1.5, 100 mW/cm(2)).

Photodilatation effect of undoped a-Si:H films

A photodilatation effect of undoped a-Si:H films has been discovered by a differential dilatometric method. The film thickness has been found to increase instantaneously when the sample is exposed to light. The dilatation weakens with illumination time, following a stretched exponential law, and finally reaches a saturation value. The dilatation disappears when light is off. The results unambiguously show that the whole structure of the film becomes less compact and less stable under light exposure. The metastable change (Staebler-Wronski effect) could be a redistribution of different configurations after this photodilatation in the a-Si:H films.

Magnetospectroscopy of bound phonons in high purity GaAs

Far infrared magnetophotoconductivity performed on high purity GaAs reveals the existence of fine structures in the resonant magnetopolaron regions. The fine structures are attributed to the presence of bound phonons due to multiphonon processes. We demonstrate that the magnetopolaron energy spectrum consists of bound phonon branches and magnetopolaron branches. Our results also indicate that different phonons are bound to a single impurity, and that the bound phonon in Si-doped GaAs is a quasilocalized mode.

Improvement of the stability of hydrogenated amorphous silicon films by intermittent illumination treatment at elevated temperature

The intermittent illumination treatment by white light at elevated temperature is proved to be a convenient and efficient method for the improvement of the stability of hydrogenated amorphous silicon (a-Si:H) films. The effect of the treatment on electrical properties, light-induced degradation, and gap states of undoped a-Si:H films has been investigated in detail. With the increase of cycling number, the dark- as well as photo-conductivities in annealed state and light-soaked state approach each other, presenting an unique irreversible effect. The stabilization and ordering processes by the present treatment can not be achieved merely by annealing under the same conditions. It is shown that the treatment proposed here results in a shift to higher values of the energy barriers between defects and their precursors, and hence an improved stability of a-Si:H films. (C) 1996 American Institute of Physics.

A new structure of In-based ohmic contacts to n-type GaAs

Electrical, structural and reaction characteristics of In-based ohmic contacts to n-GaAs were studied. Attempts were made to form a low-band-gap interfacial phase of InGaAs to reduce the barrier height at the metal/semiconductor junction, thus yielding low-resistance, highly reliable contacts. The contacts were fabricated by e-beam sputtering Ni, NiIn and Ge targets on VPE-grown n(+)-GaAs film (approximate to 1 mu m, 2 x 10(18) cm(-3)) in ultrahigh vacuum as the structure of Ni(200 Angstrom)/NiIn(100 Angstrom)/Ge(40 Angstrom)/n(+)-GaAs/SI-GaAs, followed by rapid thermal annealing at various temperatures (500-900 degrees C). In this structure, a very thin layer of Ge was employed to play the role of heavily doping donors and diffusion limiters between In and the GaAs substrate. Indium was deposited by sputtering NiIn alloy instead of pure In in order to ensure In atoms to be distributed uniformly in the substrate; nickel was chosen to consume the excess indium and form a high-temperature alloy of Ni3In. The lowest specific contact resistivity (rho(c)) of (1.5 +/- 0.5)x 10(-6) cm(2) measured by the Transmission Line Method (TLM) was obtained after annealing at 700 degrees C for 10 s. Auger sputtering depth profile and Transmission Electron Microscopy (TEM) were used to analyze the interfacial microstructure. By correlating the interfacial microstructure to the electronical properties, InxGa1-xAs phases with a large fractional area grown epitaxially on GaAs were found to be essential for reduction of the contact resistance.