Proton irradiation-induced defects in undoped GaSb studied by positron lifetime spectroscopy and photoluminescence

Undoped GaSb was irradiated by 2.6 MeV protons. The irradiation-induced defects were studied by positron lifetime spectroscopy (PLS) and photoluminescence (PL). Positron lifetime measurements showed that vacancy-type defects were introduced after irradiation, and divacancies were formed at higher irradiation dose. Annealing experiments revealed there were different annealing steps between the as grown and proton-irradiated samples, the reason for which was tentatively attributed to the formation of divacancies in the proton-irradiated samples during annealing. All the vacancy defects could be annealed out at around 500 degrees C. The PL intensity quickly fell down after proton irradiation and decreased with increasing irradiation dose, indicating that irradiation induced non-irradiative recombination centers, whose candidates were assigned to the vacancy defects induced by proton irradiation.

Role of edge dislocation and Si impurity in linking the blue luminescence and yellow luminescence in n-type GaN films

A close relationship is found between the blue and yellow luminescence bands in n-type GaN films, which are grown without intentional acceptor doping. The intensity ratio of blue luminescence to yellow luminescence (I-BL/I-YL) decreases with the increase in edge dislocation densities as demonstrated by the (102) full width at half maximum of x-ray diffraction. In addition, the I-BL/I-YL ratio decreases with the increase in Si doping. It is suggested that the edge dislocation and Si impurity play important roles in linking the blue and yellow luminescence.

Determination of wurtzite InN/cubic In2O3 heterojunction band offset by x-ray photoelectron spectroscopy

In2O3 is a promising partner of InN to form InN/In2O3 heterosystems. The valence band offset (VBO) of wurtzite InN/cubic In2O3 heterojunction is determined by x-ray photoemission spectroscopy. The valence band of In2O3 is found to be 1.47 +/- 0.11 eV below that of InN, and a type-I heterojunction with a conduction band offset (CBO) of 0.49-0.99 eV is found. The accurate determination of the VBO and CBO is important for use of InN/In2O3 based electronic devices.

Measuring spin diffusion of electrons in bulk n-GaAs using circularly dichromatic absorption difference spectroscopy of spin gratings

Circular dichromatic absorption difference spectroscopy is developed to measure the spin diffusion dynamics of electrons in bulk n-GaAs. This spectroscopy has higher detection sensitivity over homodyne detection of spin-grating-diffracted signal. A model to describe circular dichromatic absorption difference signal is derived and used to fit experimental signal to retrieve decaying rate of spin gratings. A spin diffusion constant of D-s=201 +/- 25 cm(2)/s for bulk n-GaAs has been measured at room temperature using this technique and is close to electron diffusion constant (D-c), which is much different from the case in GaAs quantum wells where D-s is markedly less than D-c.