Low-energy exciton states in a ZnO cylindrical nanodisk

We consider the electron-hole pair confined in a simplified infinite potential. The low-lying excition states in a ZnO cylindrical nanodisk are calculated based on effective-mass theory. To further understand the optical properties, we calculate the linear optical susceptibilities chi(w) and the radiative recombination lifetime tau of excitons in a ZnO nanodisk. The exciton radiative lifetime in a cylindrical nanodisk is of the order of tens of picoseconds, which is small compared with the lifetime of bulk ZnO material. (C) 2008 American Institute of Physics. [DOI: 10.1063/1.3006134]

Fiber Bragg grating hydrophone with high sensitivity

A fiber Bragg grating (FBG) hydrophone with high sensitivity was demonstrated. This hydrophone used a rubber diaphragm and a copper hard core as the sensing element. To compensate the hydrostatic pressure, a capillary tube was fixed at the end of the hydrophone. Theoretical analysis of the acoustic pressure sensitivity was given in this letter. Experiments were carried out to test the frequency response of the hydrophone. The result shows that when the Young's modulus of the diaphragm is higher, a flatter frequency response will be obtained.

Transmission properties through a double quantum dot with a wave packet

The transmiss on time and tunneling probability of an electron through a double quantum dot are studied using the transfer matrix technique. The time-dependent Schrodinger equation is applied for a Gaussian wave packet passing through the double quantum clot. The numerical calculations are carried out for a double quantum clot consisting of GaAs/InAs material. We find that the electron tunneling resonance peaks split when the electron transmits through the double quantum dot. The splitting energy increases as the distance between the two quantum dots decreases. The transmission time can be elicited from the temporal evolution of the Gaussian wave packet in the double quantum dot. The transmission time increases quickly as the thickness of tire barrier increases. The lifetime of the resonance state is calculated tram the temporal evolution of the Gaussian-state at the centers of quantum dots.

Study of valence intersubband absorption in tensile strained Si/SiGe quantum wells

The hole subband structures and effective masses of tensile strained Si/Si1-yGey quantum wells are calculated by using the 6x6 k.p method. The results show that when the tensile strain is induced in the quantum well, the light-hole state becomes the ground state, and the light hole effective masses in the growth direction are strongly reduced while the in-plane effective masses are considerable. Quantitative calculation of the valence intersubband transition between two light hole states in a 7nm tensile strained Si/Si0.55Ge0.45 quantum well grown on a relaxed Si0.5Ge0.5 (100) substrates shows a large absorption coefficient of 8400 cm(-1).

Growth and fabrication of AlGaN/GaN HEMT based on Si(111) substrates by MOCVD

AlGaN/GaN high electron mobility transistor (HEMT) hetero-structures were grown on the 2-in Si (1 1 1) substrate using metal-organic chemical vapor deposition (MOCVD). Low-temperature (LT) AlN layers were inserted to relieve the tension stress during the growth of GaN epilayers. The grown AlGaN/GaN HEMT samples exhibited a maximum crack-free area of 8 mm x 5 mm, XRD GaN (0 0 0 2) full-width at half-maximum (FWHM) of 661 arcsec and surface roughness of 0.377 nm. The device with a gate length of 1.4 mu m and a gate width of 60 mu m demonstrated maximum drain current density of 304 mA/mm, transconductance of 124 mS/mm and reverse gate leakage current of 0.76 mu A/mm at the gate voltage of -10 V. (C) 2008 Published by Elsevier Ltd.

Improved light extraction of GaN-based LEDs with nano-roughened p-GaN surfaces

p-GaN surfaces are nano-roughened by plasma etching to improve the optical performance of GaN-based light emitting diodes (LEDs). The nano-roughened GaN present a relaxation of stress. The light extraction of the LEDs with nano-roughened surfaces is greatly improved when compared with that of the conventional LEDs without nano-roughening. PL-mapping intensities of the nano-roughened LED epi-wafers for different roughening times present two to ten orders of enhancement. The light output powers are also higher for the nano-roughened LED devices. This improvement is attributed to that nano-roughened surfaces can provide photons multiple chances to escape from the LED surfaces.

Influence of electron irradiation on hydrothermally grown zinc oxide single crystals

The resistivity of hydrothermally grown ZnO single crystals increased from similar to 10(3) Omega cm to similar to 10(6) Omega cm after 1.8 MeV electron irradiation with a fluence of similar to 10(16) cm(-2), and to similar to 10(9) Omega cm as the fluence increased to similar to 10(18) cm(-2). Defects in samples were studied by thermally stimulated current (TSC) spectroscopy and positron lifetime spectroscopy (PLS). After the electron irradiation with a fluence of 10(18) cm(-2), the normalized TSC signal increased by a factor of similar to 100. A Zn vacancy was also introduced by the electron irradiation, though with a concentration lower than expected. After annealing in air at 400 degrees C, the resistivity and the deep traps concentrations recovered to the levels of the as-grown sample, and the Zn vacancy was removed.

The performance enhancement in organic light-emitting diode using a semicrystalline composite for hole injection

A semicrystalline composite, 3, 4, 9, 10 perylenetetracarboxylic dianhydride (PTCDA) doped N,N'-di(1-naphthyl)-N,N'-diphenylbenzidine (NPB), has been fabricated and characterized. An organic light-emitting diode using such a composite in hole injection exhibits the improved performance as compared with the reference device using neat NPB in hole injection. For example, at a luminance of 2000 cd/m(2), the former device gives a current efficiency of 2.0cd/A, higher than 1.6cd/A obtained from the latter device. Furthermore, the semicrystalline composite has been shown thermally to be more stable than the neat NPB thin film, which is useful for making organic light emitting diodes with a prolonged lifetime.

High-performance 2 mm gate width GaNHEMTs on 6H-SiC with output power of 22.4 W @ 8 GHz

Optimized AlGaN/AlN/GaN high electron mobility transistors (HEMTs) structures were grown on 2-in semi-insulating (SI) 6H-SiC substrate by metal-organic chemical vapor deposition (MOCVD). The 2-in. HEMT wafer exhibited a low average sheet resistance of 305.3 Omega/sq with a uniformity of 3.85%. The fabricated large periphery device with a dimension of 0.35 pm x 2 nun demonstrated high performance, with a maximum DC current density of 1360 mA/mm, a transconductance of 460 mS/mm, a breakdown voltage larger than 80 V, a current gain cut-off frequency of 24 GHz and a maximum oscillation frequency of 34 GHz. Under the condition of continuous-wave (CW) at 9 GHz, the device achieved 18.1 W output power with a power density of 9.05 W/mm and power-added-efficiency (PAE) of 36.4%. While the corresponding results of pulse condition at 8 GHz are 22.4 W output power with 11.2 W/mm power density and 45.3% PAE. These are the state-of-the-art power performance ever reported for this physical dimension of GaN HEMTs based on SiC substrate at 8 GHz. (c) 2008 Elsevier Ltd. All rights reserved.

Fabrication of triplexers based on flattop SOI AWG

A triplexer is fabricated based on SOI arrayed waveguide gratings (AWGs). Three wavelengths of the triplexer operate at different diffraction orders of an arrayed waveguide grating. The signals of 1490 nm and 1550 nm, which are input from central input waveguide of an AWG, are demultiplexed and the signal of 1310 nm, which is input from central output waveguide of an AWG, is uploaded. The tested results show that the downloaded and uploaded signals have flat-top response. The insertion loss is 9 dB on chip, the nonadjacent crosstalk is less than -30 dB for 1490 nm and 1301 nm, and is less than -25 dB for 1550 nm, the 3 dB bandwidth equates that of the input light source.

Organic light emitting diodes using magnesium doped organic acceptor as electron injection layer and silver as cathode

Organic light emitting diodes employing magnesium doped electron acceptor 3, 4, 9, 10 perylenetetracarboxylic dianhydride (Mg: PTCDA) as electron injection layer and silver as cathode were demonstrated. As compared to Mg: Ag cathode, the combination of the Mg: PTCDA layer and silver provided enhanced electron injection into tris (8-quinolinolato) aluminium. The device with 1: 2 Mg: PTCDA and Ag showed an increase of about 12% in the maximum current efficiency, mainly due to the improved hole-electron balance, and an increase of about 28% in the maximum power efficiency, as compared to the control device using Mg: Ag cathode. The properties of Mg: PTCDA composites were studied as well.

Fiber Bragg grating pressure sensor with enhanced sensitivity

A novel fiber Bragg grating (FBG) pressure sensor with the enhanced sensitivity has been demonstrated. A piston-like diaphragm with a hard core in the center is used to enhance the sensitivity. Both the theoretical analysis and the experimental result show that the radius of the hard core has significant effect on the pressure sensitivity. When the radius of the hard core is 1.5 mm, a pressure sensitivity of 7.23 nm/MPa has been achieved.

The growth temperatures dependence of optical and electrical properties of InN films

InN films grown on sapphire at different substrate temperatures from 550 degrees C to 700 degrees C by metalorganic chemical vapor deposition were investigated. The low-temperature GaN nucleation layer with high-temperature annealing (1100 degrees C) was used as a buffer for main InN layer growth. X-ray diffraction and Raman scattering measurements reveal that the quality of InN films can be improved by increasing the growth temperature to 600 degrees C. Further high substrate temperatures may promote the thermal decomposition of InN films and result in poor crystallinity and surface morphology. The photoluminescence and Hall measurements were employed to characterize the optical and electrical properties of InN films, which also indicates strong growth temperature dependence. The InN films grown at temperature of 600 degrees C show not only a high mobility with low carrier concentration, but also a strong infrared emission band located around 0.7 eV. For a 600 nm thick InN film grown at 600 degrees C, the Hall mobility achieves up to 938 cm(2)/Vs with electron concentration of 3.9 x 10(18) cm(-3).

Coulomb blockade double-dot Aharonov-Bohm interferometer: Giant fluctuations

Electron transport through two parallel quantum dots is a kind of solid-state realization of double path interference We demonstrate that the inter-clot Coulomb correlation and quantum coherence would result in strong current fluctuations with a divergent Fano factor at zero frequency. We also provide physical interpretation for this surprising result, which displays its generic feature and allows us to recover this phenomenon in more complicated systems. (C) 2009 Elsevier B.V. All rights reserved.

Effect of silver growth temperature on the contacts between Ag and ZnO thin films

Highly c-axis oriented ZnO thin films were deposited on Si substrates by the pulsed laser deposition (PLD) method. At different growth temperatures, 200 nm silver films as the contact metal were deposited on the ZnO thin films. The growth temperatures have great influence on the crystal quality of Ag films. Current-voltage characteristics were measured at room temperature. The Schottky contacts between Ag and ZnO thin films were successfully obtained when silver electrodes were deposited at 150A degrees C and 200A degrees C. Ohmic contacts were formed while the growth temperatures were lower than 150A degrees C or higher than 200A degrees C. After analysis, the forming of Ag/ZnO Schottky contacts was shown to be dependent on the appearance of the p-type inversion layer at the interface between Ag and ZnO layers.