Structure and photoluminescence of InGaAs self-assembled quantum dots grown on InP(001)

Molecular beam epitaxy has been used for growing InGaAs self-assembled quantum dots (QDs) in InAlAs on an InP(001) substrate. Nominal deposition of 9.6 monolayers of In0.9Ga0.1As results in QDs of similar to 6.5 nm high with an areal density of 3.3 X 10(11) cm(-2). Conspicuous bimodal size distribution is identified, and is responsible for the observed QDs photoluminescence (PL) emission with two peaks at 0.627 and 0.657 eV. Good agreement is achieved between the observed PL peak energies and calculated results. (C) 1999 American Institute of Physics. [S00218979(99)00101-2].

Threshold reduction in strained-layer InGaAs/GaAs quantum well lasers by liquid phase epitaxy regrowth

When liquid phase epitaxy regrowth at 780 degrees C for 2 h is applied to the samples after molecular beam epitaxy, a decrease of the threshold current density in strained InGaAs/GaAs quantum well lasers by a factor of 3 to 4 is obtained. We suggest that this improvement is attributed to the reduction of nonradiative centers associated with deep levels at the three regions of the active region, the graded layer and the cladding layer. Indeed, a significant reduction of deep center densities has been observed by using minority and majority carrier injection deep level transient spectroscopy measurements. (C) 1998 Elsevier Science B.V. All rights reserved.

Conduction-band offset in a pseudomorphic GaAs/In0.2Ga0.8As quantum well determined by capacitance-voltage profiling and deep-level transient spectroscopy techniques

The conduction-band offset Delta E-C has been determined for a molecular beam epitaxy grown GaAs/In0.2Ga0.8As single quantum-well structure, by measuring the capacitance-voltage (C - V) profiling, taking into account a correction for the interface charge density, and the capacitance transient resulting from thermal emission of carriers from the quantum well, respectively. We found that Delta E-C = 0.227 eV, corresponding to about 89% Delta E-g, from the C - V profiling; and Delta E-C = 0.229eV, corresponding to about 89.9% Delta E-g, from the deep-level transient spectroscopy (DLTS) technique. The results suggest that the conduction-band discontinuity Delta E-C obtained from the C-V profiling is in good agreement with that obtained from the DLTS technique. (C) 1998 American Institute of Physics.

Stability improvement of selective oxidation during the fabrication of InGaAs/GaAs vertical cavity surface emitting laser

The effects of the carrier gas flow and water temperature on the oxidation rate for different reaction temperatures were investigated. The optimum conditions for stable oxidation were obtained. Two mechanisms of the oxidation process are revealed. One is the flow-controlling process, which is unstable. The other is the temperature-controlling process, which is stable. The stable region decreases for higher reaction temperatures. The simulation results for the stable oxidation region are also given. With optimum oxidation conditions, the stability and precision of the oxidation can be dramatically improved.

980nm InGaAs/InGaAsP quantum well lasers with AlGaAs cladding grown by metal organic chemical vapour deposition

The authors report on the fabrication of 980 nm InGaAs strained quantum well lasers with hybrid materials of InGaAsP as waveguide and AlGaAs as cladding grown by metal organic chemical vapour deposition. The InGaAs/InGaAsP/AlGaAs diode lasers (100 x 800 mu m) with broadened waveguide structure exhibit a threshold current of 180 mA, a slope efficiency of 1.0 W/A, and a high characteristic temperature coefficient (T-0) of 230 K.

Observation of the third subband population in modulation-doped InGaAs/InAlAs heterostructure

The population of the third (n = 3) two-dimensional electron subband of InGaAs/InAlAs modulation-doped structures has been observed by means of Fourier transform photoluminescence (PL). Three well resolved PL peaks centred at 0.737, 0.908, and 0.980eV are observed, which are attributed to the transitions from the lowest three electron subbands to the n = 1 heavy-hole subband. The subband separations clearly exhibiting the features of the stepped quantum well with triangle and square potentials are consistent with numerical calculation. Thanks to the presence of Fermi cutoff, the population ratio of these three subbands can be estimated. Temperature- and excitation-dependent luminescences are also analyzed.

The third subband population in modulation-doped InGaAs/InAlAs heterostructures

We have observed the population of the third (n=3) two-dimensional electron subband of InGaAs/ InAlAs modulation-doped structures with very dense sheet carrier density by means of Fourier transform photoluminescence (PL). Three well-resolved PL peaks centered at 0.737, 0.908, and 0.980 eV are observed, which are attributed to the recombination transitions from the lowest three electron subbands to the n=1 heavy-hole subband. The subband separations clearly exhibit the features of the stepped quantum well with triangle and square potential, consistent with numerical calculation. Thanks to the presence of the Fermi cutoff, the population ratio of these three subbands can be estimated. Temperature and excitation intensity dependence of the quantum well luminescence intensity is also analyzed. (C) 1997 American Institute of Physics.

长波长InGaAs/InP雪崩光电二极管

于G批量导入至Hzhangdi

长波长InGaAs/InP雪崩光电二极管

于G批量导入至Hzhangdi

长波长InGaAs.APD光接收组件

于G批量导入至Hzhangdi

低阈值1.3um InGaAs/InP 双区共腔双稳激光器

于G批量导入至Hzhangdi

Long-Wavelength Emission InAs Quantum Dots Grown on InGaAs Metamorphic Buffers

In this work, InAs quantum dots (QDs) grown on a linear graded InGaAs metamorphic buffer layer by molecular beam epitaxy have been investigated. The growth of the metamorphic buffer layers was carefully optimized, yielding a smooth surface with a minimum root mean square of roughness of less than 0.98 nm as measured by atomic force microscopy (AFM). InAs QDs were then grown on the buffer layers, and their emission wavelength at room-temperature is 1.49 mu m as measured by photoluminescence (PL). The effects of post-growth rapid thermal annealing (RTA) on the optical properties of the InAs QDs were investigated. After the RTA, the PL peak of the QDs was blue-shifted and the full width at half maximum decreased.

Corrugated surfaces formed on GaAs (331)a substrates: The template for laterally ordered InGaAs nanowires

Morphology evolution of high-index (331)A surfaces during molecular beam epitaxy (MBE) growth have been investigated in order to uncover their unique physic properties and fabricate spatially ordered low dimensional nanostructures. Atomic Force Microscope (AFM) measurements have shown that the step height and terrace width of GaAs layers increase monotonically with increasing substrate temperature in conventional MBE. However, this situation is reversed in atomic hydrogen-assisted MBE, indicating that step bunching is partly suppressed. We attribute this to the reduced surface migration length of Ga adatoms with atomic hydrogen. By using the step arrays formed on GaAs (331)A surfaces as the templates, we fabricated laterally ordered InGaAs self-aligned nanowires.

Influence of Al content on electrical and structural properties of Si-doped AlxGa1-xN/GaN HEMT structures

Improved electrical properties of AlxGa1-xN/GaN high electron mobility transistor (HEMT) structures grown by metalorganic chemical vapor deposition (MOCVD) were achieved through increasing the Al mole fraction in the AlGaN barrier layers. An average sheet resistance of 326.6 Omega/sq and a good resistance uniformity of 98% were obtained for a 2-inch Al0.38Ga0 62N/GaN HEMT structure. The surface morphology of AlxGa1-xN/GaN HEMT structures strongly correlates with the Al content. More defects were formed with increasing Al content due to the increase of tensile strain, which limits further reduction of the sheet resistance. (c) 2006 WILEY-VCH Verlag GmbH & Co KGaA, Weinheim.

Molecular-beam epitaxial growth of position controlled InAs islands on cleaved edge of InGaAs/GaAs superlattice

A promising approach for positioning of InAs islands on (110)GaAs is demonstrated. By combining self-assembly of quantum dots with solid source molecular beam epitaxy (MBE) on cleaved edge of InGaAs/GaAs superlattice (SL), linear alignment of InAs islands on the InGaAs strain layers have been fabricated The cleaved edge of InGaAs/GaAs SL acts as strain nanopattern for InAs selective growth. Indium atoms incident on the surface will preferentially migrate to InGaAs regions where favorable bonding sites are available. The strain nanopattern's effect is studied by the different indium fraction and thickness of InxGa1-xAs/GaAs SL. The ordering of the InAs islands is found to depend on the properties of the underlying InGaAs strain layers.