The structural, morphological and magnetic characteristics of Mn-implanted nonpolar a-plane GaN films

Dilute magnetic nonpolar GaN films have been fabricated by implanting Mn into unintentionally doped nonpolar a-plane GaN films at room temperature, and a subsequent rapid thermal annealing. The X-ray diffraction analysis shows that after rapid thermal annealing the peak of the GaN X-ray diffraction curve shifts to a lower angle, indicating a slight expansion of the GaN crystal lattice. Atomic force microscopy analysis shows that the annealing process does not change the morphology of the sample greatly. Magnetic property analysis indicates that the as-annealed sample shows obvious ferromagnetic properties. (C) 2009 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim

Influence of implantation energy on the characteristics of Mn-implanted nonpolar a-plane GaN films

Nonpolar GaN Mn films have been fabricated by implanting Mn-ion into nonpolar a-plane (MO) GaN films at room temperature. The influence of implantation energy on the Structural, morphological and magnetic characteristics of samples have been investigated by means of stopping and range of ions in matter (SRIM) Simulation software, high-resolution X-ray diffraction (HRXRD), atomic force microscopy (AFM), and superconducting quantum interference device (SQUID). According to the SQUID analysis, obvious room temperature ferromagnetic properties of samples were detected. Moreover, the implantation energy has little impact on the ferromagnetic properties of samples. The XRD and AFM analyses show that the structural and morphological characteristics of samples were severely deteriorated with the increase of implantation energy. (C) 2008 Elsevier B.V. All rights reserved.

Shape stability of InAs self-assembled islands on vicinal GaAs(001) substrates

We have grown InAs self-assembled islands on vicinal GaAs( 001) substrates. Atomic force microscopy and photoluminescence studies show that the islands have a clear bimodal size distribution. While most of the small islands whose growth is limited by the width of one multi-atomic step have compact symmetric shapes, a large fraction of the large islands limited by the width of one step plus one terrace have asymmetric shapes which are elongated along the multi-atomic step lines. These results can be attributed to the shape-related energy of the islands at different states of their growth. (C) 2008 Elsevier B. V. All rights reserved.

Influence of AlN buffer layer thickness on the properties of GaN epilayer on Si(111) by MOCVD

The effect of thickness of the high-temperature (HT) AlN buffer layer on the properties of GaN grown on Si(111) has been investigated. Optical microscopy (OM), atomic force microscopy (AFM) and X-ray diffraction (XRD) are employed to characterize these samples grown by metal-organic chemical vapor deposition (MOCVD). The results demonstrate that the morphology and crystalline properties of the GaN epilayer strongly depend on the thickness of HT AlN buffer layer, and the optimized thickness of the HT AlN buffer layer is about 110 nm. Together with the low-temperature (LT) AlN interlayer, high-quality GaN epilayer with low crack density can be obtained. (C) 2008 Elsevier Ltd. All rights reserved.

Structural, morphological, and magnetic characteristics of Cu-implanted nonpolar GaN films

Diluted magnetic nonpolar GaN:Cu films have been fabricated by implanting Cu ions into unintentionally doped nonpolar a-plane(1 1 (2) over bar 0) GaN films and a subsequent thermal annealing process. The structural, morphological and magnetic characteristics of the samples have been investigated by means of high-resolution X-ray diffraction (HRXRD), atomic force microscopy (AFM), and superconducting quantum interference device (SQUID). The sample shows a clear ferromagnetism behavior at room temperature. It is significantly shown that with a Cu concentration as low as 0.75% the sample exhibits a saturation magnetization about 0.65 mu(B)/Cu atom. Moreover, the possible origin of the ferromagnetism for the sample was also discussed briefly. (C) 2009 Elsevier B. V. All rights reserved.

The impact of implantation dose on the characteristics of diluted-magnetic nonpolar GaN:Cu films

Diluted-magnetic nonpolar GaN:Cu films have been fabricated by implanting Cu ions into p-type nonpolar a-plane (1120) GaN films with a subsequent thermal annealing process. The impact of the implantation dose on the structural. morphological and magnetic characteristics of the samples have been investigated by means of high-resolution X-ray diffraction (HRXRD). atomic force microscopy (AFM), and superconducting quantum interference device (SQUID). The XRD and AFM analyses show that the structural and morphological characteristics of samples deteriorated with the increase of implantation dose. According to the SQUID analysis. obvious room-temperature ferromagnetic properties of samples were detected. Moreover, the saturation magnetization per Cu atom decreased as the implantation dose increased. (C) 2009 Elsevier B.V. All rights reserved.

Surface morphology of AlN buffer layer and its effect on GaN growth by metalorganic chemical vapor deposition

The in situ optical reflectivity measurements are employed to monitor the GaN epilayer growth process above low-temperature AlN buffer layer on c-plane sapphire substrate by metalorganic chemical vapor deposition. It is found that the lateral growth of GaN islands and their coalescence is promoted in the initial growth stage if the AlN buffer layer is treated with a long annealing time and has an optimal thickness: As confirmed by atomic force microscopy observations, the quality of GaN epilayers is closely dependent on the surface morphology of AlN buffer layer, especially the grain size and nuclei density after the annealing treatment. (C) 2004 American Institute of Physics.

Effect of the oxygen concentration on the properties of Gd2O3 thin films

Gd2O3 thin films were deposited on Si (100) substrates at 650degreesC by a magnetron sputtering system under different Ar/O-2 ratios of 6:1, 4:1 and 2:1. The effect of the oxygen concentration on the properties of oxide thin films was investigated by X-ray diffraction, X-ray photoelectron spectroscopy, atomic force microscopy and capacitance-voltage (C-V)measurement. X-ray diffraction shows that the structure of oxide films changed from the monoclinic Gd2O3 phase to cubic Gd2O3 phase when the oxygen concentration increased. According to C-V measurement, the dielectric constant value of the samples deposited at different Ar/O-2 ratios is about 12. (C) 2004 Elsevier B.V. All rights reserved.

Effect of the InAlAs and InGaAs combination strain-reducing layer on 1.3 mu m emission self-assembled InAs/GaAs quantum dots

Self-assembled InAs quantum dots (QDs) with differing deposition thicknesses covered by InxAl1-xAs (x = 0.2, 0.3) and In0.2Ga0.8As combination strain-reducing layers (CSRLs) were grown by molecular beam epitaxy. Their structural and optical properties were investigated by atomic force microscopy and photoluminescence spectroscopy, respectively. The emission peak position of InAs QDs capped by CSRL can reach 1.34 mum at room temperature with a relatively larger energy splitting of 93 meV between the ground and first excited states.

Ordering growth of InAs quantum dots on ultra-thin InGaAs strained layer

InAs quantum dots (QDs) were grown On Ultra-thin In0.15Ga0.85As strained layers by molecular beam epitaxy on GaAs (00 1) substrates. Combining reflection high-energy electron diffraction, atomic force microscopy and transmission electron microscopy, we analyzed the stress field of dislocations in the strained layer/substrate interface. Specially, we revealed the relative position of QDs and dislocations. We found that the difference of the stress field around dislocations is prominent when the strained layer is ultra-thin and the stress field will directly affect the following growth. On the strained layer surface, In0.15Ga0.85As ridges will form at the inclined upside of dislocations. Then, InAs QDs will prefer nucleating on the ridges, there is relatively small stress between InAs and In0.15Ga0.85As. By selecting ultra-thin In0.15Ga0.85As layer (50 nm) and controlling the QD layer at just form QDs, we obtained ordered InAs QDs. (C) 2004 Elsevier B.V. All rights reserved.

Raman scattering of folded acoustic phonons in self-assembled Si/Ge dot superlattices

Self-assembled Si/Ge dot multilayers with small, uncorrelated dots fabricated by molecular beam epitaxy in the Stranski-Krastanov growth mode are studied by Raman scattering of folded longitudinal acoustic (FLA) modes. The FLA Raman spectra are analyzed and modeled with respect to mode frequencies and the spectral envelope of mode intensities. The deduced average superlattice properties are consistent with results from atomic force microscopy. The simple Rytov model used for Si/Ge layer structures reproduces very well the frequencies of the FLA modes up to 150 cm(-1). The nonlinearity of phonon dispersion curves in bulk Si for large momenta, however, becomes important for modeling the higher frequencies of observed FLA modes up to 22nd order. The effective dot layer width and an activation energy for thermal intermixing of 2.1+/-0.2 eV are determined from the spectral envelopes of FLA mode intensities of as-grown and annealed Si/Ge dot multilayers. (C) 2004 American Institute of Physics.

Mn implanted GaAs by low energy ion beam deposition

High dose Mn was implanted into semi-insulating GaAs substrate to fabricate embedded ferromagnetic Mn-Ga binary particles by mass-analyzed dual ion beam deposit system at room temperature. The properties of as-implanted and annealed samples were measured with X-ray diffraction, high-resolution X-ray diffraction to characterize the structural changes. New phase formed after high temperature annealing. Sample surface image was observed with atomic force microscopy. All the samples showed ferromagnetic behaviour at room temperature. There were some differences between the hysteresis loops of as-implanted and annealed samples as well as the cluster size of the latter was much larger than that of the former through the surface morphology. (C) 2004 Elsevier B.V. All rights reserved.

The fabrication of self-aligned InAs nanostructures on GaAs(331)A substrates

Self-aligned InAs quantum wires (QWRs) or three-dimensional (3D) islands are fabricated on GaAs(331)A substrates by molecular beam epitaxy (MBE). InAs QWRs are selectively grown on the step edges formed by GaAs layers. The surface morphology of InAs nanostructures is carefully investigated by atomic force microscopy (AFM) measurements. Different growth conditions, such as substrate temperature, growth approaches, and InAs coverage, exert a great effect on the morphology of InAs islands. Low substrate temperatures favour the formation of wirelike nanostructures, while high substrate temperatures favour 3D islands. The shape transition is attributed to the trade-off between surface energy and strain energy. A qualitative agreement of our experimental data with the theoretical results derived from the model proposed by Tersoff and Tromp is achieved.

The fabrication and properties of InAs/GaAs columnal islands

A columnal islands system, which was composed of three layers of self-assembled InAs/GaAs quantum dots (QDs), has been fabricated by solid-source molecular beam epitaxy (MBE) through S-K mode on a (100) semi-insulating GaAs substrate. The effects of the thickness of GaAs space layer, the growth interruption time and the amount of InAs deposition on the emission wavelength of columnal islands were presented. The image of atomic force microscopy (AFM) indicated the columnal islands with high uniformity in size and shape. At room temperature, the emission wavelength of columnal islands with different effective heights was achieved 1.32 and 1.4 mum; however, the emission wavelength of single-layer QDs with normal height was just 1. l mum. It provides a useful and intuitive approach to artificially control the emission wavelength of a QD material system.

Photoluminescence study of InGaN/GaN quantum dots grown on passivated GaN surface

We have measured photoluminescence (PL) and time-resolve photoluminescence (TRPL) from InGaN/GaN quantum dots (QDs) grown on passivated GaN surfaces by metalorganic chemical vapor deposition (MOCVD). Strong PL emission was observed from the QDs structure even at room temperature. By comparing the PL and TRPL dependence on temperature, a significant difference between the QD and wetting layer emissions was revealed. The QD emission is characterized by a strong exciton localization effect, which leads to a larger thermal activation energy, a nearly constant radiative lifetime independent of temperature and an unusual temperature behavior of the PL peak energy. (C) 2003 Elsevier B.V. All rights reserved.