A general route to transform normal hydrophilic cloths into superhydrophobic surfaces

Herein, we describe a simple and inexpensive method for forming superhydrophobic cloths with the highest water contact angle of close to 180 degrees, in which normal commercial cloths serving as pristine materials are modified with suitable gold micro/nanostructures.

Nano-Tribological Study on a Super-Hydrophobic Film Formed on Rough Aluminum

A novel super-hydrophobic stearic acid (STA) film with a water contact angle of 166° was prepared by chemical adsorption on aluminum wafer coated with polyethyleneimine (PEI) film. The micro-tribological behavior of the super-hydrophobic STA monolayer was compared with that of the polished and PEI-coated Al surfaces. The effect of relative humidity on the adhesion and friction was investigated as well. It was found that the STA monolayer showed decreased friction, while the adhesive force was greatly decreased by increasing the surface roughness of the Al wafer to reduce the contact area between the atomic force microscope (AFM) tip and the sample surface to be tested. Thus the friction and adhesion of the Al wafer was effectively decreased by generating the STA monolayer, which indicated that it could be feasible and rational to prepare a surface with good adhesion resistance and lubricity by properly controlling the surface morphology and the chemical composition. Both the adhesion and friction decreased as the relative humidity was lowered from 65% to 10%, though the decrease extent became insignificant for the STA monolayer.

Analysis of super compact finite difference method and application to simulation of vortex-shock interaction

Turbulence and aeroacoustic noise high-order accurate schemes are required, and preferred, for solving complex flow fields with multi-scale structures. In this paper a super compact finite difference method (SCFDM) is presented, the accuracy is analysed and the method is compared with a sixth-order traditional and compact finite difference approximation. The comparison shows that the sixth-order accurate super compact method has higher resolving efficiency. The sixth-order super compact method, with a three-stage Runge-Kutta method for approximation of the compressible Navier-Stokes equations, is used to solve the complex flow structures induced by vortex-shock interactions. The basic nature of the near-field sound generated by interaction is studied.

SUPER CE/SE的新算法及其在爆炸力学中的应用

研究了SUPER CE/SE的新算法及其在爆炸力学中的应用. 算法和模型方面, 主要包括改进CE/SE算法、快速杂交粒子水平集方法、常用化学反应模型和两流体模型. 使用上述算法和模型, 对激波楔面反射、爆炸焊接、爆轰波胞格结构和气液两相爆轰问题进行了数值模拟. 数值结果表明, 该文采用的算法具有计算精度高、应用范围广和兼容性强等优点, 可广泛应用于爆炸力学的数值研究.

New Numerical Algorithms in SUPER CE/SE and Their Applications in Explosion Mechanics

The new numerical algorithms in SUPER/CESE and their applications in explosion mechanics are studied. The researched algorithms and models include an improved CE/SE (space-time Conservation Element and Solution Element) method, a local hybrid particle level set method, three chemical reaction models and a two-fluid model. Problems of shock wave reflection over wedges, explosive welding, cellular structure of gaseous detonations and two-phase detonations in the gas-droplet system are simulated by using the above-mentioned algorithms and models. The numerical results reveal that the adopted algorithms have many advantages such as high numerical accuracy, wide application field and good compatibility. The numerical algorithms presented in this paper may be applied to the numerical research of explosion mechanics.

Super-resolution with annular binary phase filter in the 4Pi-confocal system

In order to realize super-resolution in the 4Pi-confocal systems, the annular binary pure phase filter is designed with the vector diffraction theory. The relations between the super-resolved parameters, such as S, G(T), G(A), and the radial position theta(i) of each zone, are obtained. For simple illumination of the design procedure, three-zone binary pure phase filters are studied, and several numerical simulation results show that in the 4Pi-confocal system with the properly designed binary pure phase filter the super-resolution can be realized with low sidelobes.

Pure-phase plates for super-Gaussian focal-plane irradiance profile generations of extremely high order

A set of recursive formulas for diffractive optical plates design is described. The pure-phase plates simulated by this method homogeneously concentrate more than 96% of the incident laser energy in the desired focal-plane region. The intensity focal-plane profile fits a lath-order super-Gaussian function and has a nearly perfect flat top. Its fit to the required profile measured in the mean square error is 3.576 x 10(-3). (C) 1996 Optical Society of America

Novel approach to super-resolution pits readout

We proposed a novel method to realize the readout of super-resolution pits by using a super-resolution reflective film to replace the reflective layer of the conventional ROM. At the same time, by using Sb as the super-resolution reflective layer and SiN as a dielectric layer, the super-resolution pits with diameters of 380 nm were read out by a setup whose laser wavelength is 632.8 nm and numerical aperture is 0.40. In addition, the influence of the Sb thin film thickness on the readout signal was investigated, the results showed that the optimum Sb thin film thickness is 28 to 30 nm, and the maximum CNR is 38 to 40 dB. (C) 2002 Society of Photo-Optical Instrumentation Engineers.

Read-only memory disk with AgOx super-resolution mask layer

A novel read-only memory (ROM) disk with an AgOx mask layer was proposed and studied in this letter. The AgOx films sputtered on the premastered substrates, with pits depth of 50 nm and pits length of 380 nm, were studied by an atomic force microscopy. The transmittances of these AgOx films were also measured by a spectrophotometer. Disk measurement was carried out by a dynamic setup with a laser wavelength of 632.8 nm and a lens numerical aperture (NA) of 0.40. The readout resolution limit of this setup was λ/(4NA) (400 nm). Results showed that the super-resolution readout happened only when the oxygen flow ratios were at suitable values for these disks. The best super-resolution performance was achieved at the oxygen flow ratio of 0.5 with the smoothest film surface. The super-resolution readout mechanism of these ROM disks was analyzed as well.

Optical recording properties of metal-azo dye as recording medium with super-resolution near-field structure

A novel metallized azo dye has been synthesized. The absorption spectra of the thin film and thermal characteristic are measured. Static optical recording properties with and without the Bi mask layer super-resolution near-field structure (Super-RENS) of the metal-azo dye are investigated. The results show that the metal-azo dye film has a broad absorbance band in the region of 450-650 nm and the maximum absorbance wavelength is located at 603 nm. It is also found that the new metallized azo dye occupies excellent thermal stability, initiatory decomposition temperature is at 270 degrees C and the mass loss is about 48% in a narrow temperature region (15 degrees C). The complex refractive index N (N = n + ik) is measured. High refractive index (n = 2.45) and low extinction coefficient (k = 0.2) at the recording wavelength 650nm are attained. Static optical recording tests with and without Super-RENS are carried out using a 650nm semiconductor diode laser with recording power of 7mW and laser pulse duration of 200ns. The AFM images show that the diameter of recording mark on the dye film with the Bi mask layer is reduced about 42%, compared to that of recorded mark on the dye film without Super-RENS. It is indicated that Bi can well performed as a mask layer of the dye recording layer and the metallized azo dye can be a promising candidate for recording media with the super-resolution near-field structure.

Super-resolution with a nonlinear thin film: Beam reshaping via internal multi-interference

In laser applications, the size of the focus spot can be reduced beyond the diffraction limit with a thin film of strong nonlinear optical Kerr effect. We present a concise theoretical simulation of the device. The origin of the super-resolution is found to be mainly from the reshaping effect due to the strongly nonlinear refraction mediated multi-interference inside the thin film. In addition, both diffraction and self-focusing effects have been explored and found negligible for highly refractive and ultrathin films in comparison with the reshaping effect. Finally, the theoretic model has been verified in experiments with single Ge2Sb2Te5 film and SiN/Si/SiN/Ge2Sb2Te2 multilayer structures. (c) 2006 American Institute of Physics.

Investigation on the static recording characteristic of super-resolution near-field structure with antimony mask layer

Static recording characteristic of super-resolution near-field structure with antimony (Sb) is investigated in this paper. The recording marks are observed by a scanning electron microscopy (SEM), a high-resolution optical microscopy with a CCD camera and an atomic force microscopy (AFM). The super-resolution mechanism is also analyzed based on these static recording marks. Results show that the light reaching on recording layer is composed of two parts, one is the linear transmissive light (propagating field) and the other is the nonlinear evanescent light in the optical near field. The evanescent light may be greatly enhanced in the center of the spot because Sb will transit from a semiconductor to a metal when it is melted under the high laser power irradiation. This local melted area in the spot center may be like a metal tip in the optical near field that can collect and enhance the information that is far beyond the diffraction limit, which leads to the super-resolution recording and readout. (c) 2005 Elsevier Ltd. All rights reserved.

Numerical analysis and comparison of three metal-oxide-type super-resolution near field structures

Based on the Fresnel-Kirchkoff diffraction theory, we build up a Gaussian diffraction model of metal-oxide-type super-resolution near field structure (super-RENS), which can describe far field optical properties. The spectral contrast induced by refractive index and the structural changes in AgOx, PtOx and PdOx thin films, which are the key functional layers in super-RENS, are studied by using this model. Comparison results indicate that the spectral contrast intensively on laser-induced distribution and change of the refractive index in the metal-oxide films. The readout mechanism of the metal-oxide-type super-RENS optical disc is further clarified. This Gaussian diffraction model can be used as a simple and effective method for choosing proper active materials in super-RENS.

Structure-change-dependent transmittance of PtOx thin film in super-resolution near-field structure: Diffraction effect analysis

To study working mechanism of super-resolution near-field structure (super-RENS) optical disk from a far-field optics view is very necessary because of the actual far-field writing/readout process in the optical disk system. A Gaussian diffraction model based on Fresnel-Kirchhoff diffraction theory of PtOx-type super-RENS has been set up in this Letter. The relationship between micro-structural deformation (change of bubble structure and refractive index profile) with far-field optical response of PtOx thin film has been studied with it in detail. The simulation results are in good agreement with the experimental results reported in literatures with a designed configuration. These results may provide more quantitative information for better understanding of the working mechanism of metal-oxide-type super-RENS. (c) 2007 Elsevier B.V. All rights reserved.