Infrared and Mössbauer spectroscopic study of the metal-insulator transition in some oxides of perovskite structure

The IR spectra of some LaNi1−xBxO3 (B = Cr, Fe, and Co) compounds having perovskite structure have been studied in the range 1000−300 cm−1. An investigation of the changes in the metal-oxygen stretching frequency as x → xc from the insulating side has been carried out. An important feature is that as x → xc the vibrational features in the infrared spectra disappear when the resistivity is not, vert, similar10−1 Ω cm which is of two orders of magnitude more than the value of varrho0 at which the temperature coefficient of resistance changes sign. Mössbauer studies on Fe-containing samples with various conductivities show that the isomer shift decreases as conductivity increases which is indicative of larger Fe---O overlap.

Synthesis of Cuprates of Perovskite Structure in the Ba-Pb-Cu-O, Ba-Bi-Cu-O, and Ba-Pb-Tl-Cu-O Systems: Possible High Tc Superconductivity in a Perovskite-like Phase in the Ba-Pb-Tl-Cu-O System

Cubic cuprates (a not, vert, similar 18.6 Å) with a BaCuO2-type structure were obtained in the Ba-Pb-Cu-O and Ba-Bi-Cu-O systems by the reaction of the component oxides at a high temperature (1370-1420 K), followed by quenching. By annealing these phases in oxygen at 1070-1120 K, perovskite-like phase (a not, vert, similar 4.3 Å) of the formulae BaPb1-xCuxO3-y and BaBi1-xCuxO3-y (0 < x ? 0.5) were obtained. A perovskite of nominal composition BaPb0.25Tl0.25 Cu0.5O3-y, prepared by a similar procedure, was found to be superconducting with a Tc of not, vert, similar 70 K.

ChemInform Abstract: Slicing the Perovskite Structure into Layers: Synthesis of Novel Three- Dimensional and Layered Perovskite Oxides, ALaSrNb2M(II)O9 (A: Na, Cs)

ChemInform is a weekly Abstracting Service, delivering concise information at a glance that was extracted from about 100 leading journals. To access a ChemInform Abstract of an article which was published elsewhere, please select a “Full Text” option. The original article is trackable via the “References” option.

LiSr1.65 square 0.35B1.3B ' O-1.7(9) (B = Ti, Zr; B ' = Nb, Ta): New lithium ion conductors based on the perovskite structure

We describe the design and synthesis of new lithium ion conductors with the formula, LiSr(1.65)rectangle(0.35)B(1.3)B'O-1.7(9) (rectangle = vacancy; B = Ti, Zr; B' = Nb, Ta), on the basis of a systematic consideration of the composition-structure-property correlations in the well-known lithium-ion conductor, La-(2/3-x)Li(3x)rectangle((1/3)-2x)TiO3 (I), as well as the perovskite oxides in Li-A-B,B'-O (A = Ca, Sr, Ba; B = Ti, Zr; B' = Nb, Ta) systems. A high lithium-ion conductivity of ca. 0.12 S/cm at 360 degrees C is exhibited by LiSr(1.65)rectangle(0.35)Ti(1.3)Ta(1.7)O(9) (III) and LiSr(1.65)rectangle(0.35)Zr(1.3)Ta(1.7)O(9) (IV), of which the latter containing stable Zr(IV) and Ta(V) oxidation states is likely to be a candidate electrolyte material for all-solid-state lithium battery application. More importantly, we believe the approach described here could be extended to synthesize newer, possibly better, lithium ion conductors.

Neutron powder diffraction study of Ba3ZnRu2-xIrxO9 (x=0, 1, 2) with 6H-type perovskite structure

The triple perovskites Ba3ZnRu2-xIrxO9 with x = 0, 1, and 2 are insulating compounds in which Ru(Ir) cations form a dimer state. Polycrystalline samples of these materials were studied using neutron powder diffraction (NPD) at 10 and 295 K. No structural transition nor evidence of long range magnetic order was observed within the investigated temperature range. The results from structural refinements of the NPD data and its polyhedral analysis are presented, and discussed as a function of Ru/Ir content. (C) 2015 Elsevier Masson SAS. All rights reserved.

Damage analysis of tetragonal perovskite structure ceramics implicated by asymptotic field solutions and boundary conditions

Cracking of ceramics with tetragonal perovskite grain structure is known to appear at different sites and scale level. The multiscale character of damage depends on the combined effects of electromechanical coupling, prevailing physical parameters and boundary conditions. These detail features are exhibited by application of the energy density criterion with judicious use of the mode I asymptotic and full field solution in the range of r/a = 10(-4) to 10(-2) where r and a are, respectively, the distance to the crack tip and half crack length. Very close to the stationary crack tip, bifurcation is predicted resembling the dislocation emission behavior invoked in the molecular dynamics model. At the macroscopic scale, crack growth is predicted to occur straight ahead with two yield zones to the sides. A multiscale feature of crack tip damage is provided for the first time. Numerical values of the relative distances and bifurcation angles are reported for the PZT-4 ceramic subjected to different electric field to applied stress ratio and boundary conditions that consist of the specification of electric field/mechanical stress, electric displacement/mechanical strain, and mixed conditions. To be emphasized is that the multiscale character of damage in piezoceramics does not appear in general. It occurs only for specific combinations of the external and internal field parameters, elastic/piezoelectric/dielectric constants and specified boundary conditions. (C) 2002 Published by Elsevier Science Ltd.

Phase behavior of BaLn(2)Mn(2)O(7) (Ln = rare earth) with a layered perovskite structure

Many phases appear in BaLn(2)Mn(2)O(7) family (Ln = rare earth) belonging to one of the Ruddlesden-Popper type compounds, depending upon the experimental conditions such as heating conditions when prepared and composition. Some of these phases were characterized by powder X-ray diffraction method using Rietveld analysis. These phases have only a little difference in crystal structure which has fundamentally K2NiF4 type structure, although the X-ray diffraction patterns are clearly different: a little deformation or tilting of the oxygen octahedron surrounding a central manganese ion composing the main frame of this structure induce these different diffraction patterns. Phase behavior of these compounds, mainly the detailed relation between various phases in BaTb2Mn2O7, was refined including the data of high temperature X-ray diffractometry.

Synthesis, structural and electrical characterizations of Sr2Fe1-xMxNbO6 (M = Zn and Cu) with double perovskite structure

Sr2Fe1-xZnxNbO6-x/2 (0 <= x <= 0.5) and Sr2Fe1-xCuxNbO6-x/2 (0.01 <= x <= 0.05) with the double perovskite structure have been synthesized. The crystal structures at room temperature were determined from Rietveld refinements of X-ray powder diffraction data. The plots of the imaginary parts of the impedance spectrum, Z '', and the electric modulus, M '', versus log (frequency), possess maxima for both curves separated by less than a half decade in frequency with associated capacities of 2 nF. The enhancement of the overall conductivity Of Sr2Fe1-xMxNbO6-x/2 (M = Cu and Zn) is observed, as increases from 2.48 (3) x 10(-4) S/cm for Sr2FeNbO6 to 3.82 (5) x 10(-3) S/cm for Sr2Fe0.8Zn0.2NbO5.9 at 673 K. Sr2Fe0.8Zn0.2NbO5.9 is chemically stable under the oxygen partial pressure from 1 atm to 10(-22) atm at 873 K. The p and n-type electronic conductions are dominant under oxidizing and reducing conditions, respectively, suggesting a small-polaron hopping mechanism of electronic conduction.

Organic template-directed crystallization of the complex fluoride NH4MnF3 with perovskite structure

(100)-oriented NH4MnF3 perovskite with different morphologies have been obtained in situ via an organic template; experimental results can be rationalized in terms of electrostatic interactions and lattice matching between the organic template and the ions undergoing nucleation.

Layered La-Ba-Cu mixed oxides with perovskite structure as catalyst for NO reduction by CO

The mixed oxides, including LaBa2Cu3O7, LaBaCu2O5, La4BaCu5O12 with perovskite structure, were prepared. The catalysts were characterized by means of chemical analysis, XRD, H-2-TPR. It was found that their structures were layered ABO(3) perovskite structure and they were the active catalysts for the NO reduction by CO. The existence of Cu3+ is an important factor to give the catalysts a high activity for the NO reduction by CO.

Studies on the elimination of NO over the La-Ba-Cu mixed oxide catalysts with perovskite structure

The mixed oxides, including YBa2Cu3O7, LaBa2Cu3O7, LaBaCu2O5, La2BaCu3O7, La4BaCu5O12 with perovskite structure, were prepared. The catalysts were characterized by means of chemical analysis, XRD, TPD and TPR method. It was found that they were the active catalysts for the NO decomposition and NO reduction by CO. The existance of Cu3+ is an important factor to give the catalysts a high activity for the NO reduction by CO.

Luminescence properties of Ce3+ in KMF3(M=Mg, Ca, Sr, Ba) hosts with perovskite structure

KMF3(M = Mg, Ca, Sr, Ba) compounds were synthesized by solid state reaction under argon atmosphere. Their structures were determined by X-ray diffraction. It belongs to cubic system with perovskite structure. The excitation and emission spectra of KMF3:Ce3+ were measured. According to the characteristics of spectral structures, the occupation site of Ce3+ is discussed.

Mechanochemical synthesis of ceramic powders with perovskite structure

The mechanical activation is one of the most effective method for obtaining highly disperse system due to mechanical action stress fields form in solids during milling procedure. This effect results in changes of free energy, leading to release of heat, formation of a new surface, formation of different crystal lattice defects and initiation of solid-state chemical reaction. The accumulated deformation energy determines irreversible changes of crystal structure and consequently microstructure resulting in the change of their properties. Mechanochemical processing route has been developed recently for the production of intermetallic and alloy compounds. The intrinsic advantage of this process is that the solid-state reaction is activated due to mechanical energy instead of the temperature. It was shown that the chemical reactivity of starting materials could be improved significantly after mechanochemical activation and, subsequently, the calcination temperature was reduced. Besides, it was apparent that the mechanochemical treatment could enhance the reactivity of constituent oxides; however, the sintering process could not be avoided to develop the desired ceramics. A novel mechanochemical technique for synthesis of fine-grained perovskite structured powders has shown that it is possible to form perovskite at room temperature. The effect of milling on the formation of perovskite structure of barium titanate (BT), lead titanate (PT), PZT, PZN, magnesium niobate (PMN) and LM ceramic materials was analyzed. The dielectric properties of sintered ceramics are comparable with those prepared by other methods in the literature. (C) 2003 Elsevier B.V. B.V. All rights reserved.

Lanthanum cobaltite black pigments with perovskite structure

In this work La1-xCaxCoO3 (x = 0-0.4) pigments were synthesized by the polymeric precursor method with heat treatments at 700, 800 and 900 C for 4 h. The powders were characterized by colorimetry, UV-vis spectroscopy and powder X-ray diffraction (XRD). The X-ray diffraction patterns showed the presence of a single phase perovskite, changing its structure from rhombohedral to cubic, when calcium was added to the lattice. All of the pigments had a black colour with a strong absorption over the whole of the visible spectrum as a consequence of the different oxidation states of cobalt and the high short-range disorder. The substitution of Ca2+ for La3+ did not influence the pigment colour but decreased its final cost. © 2013 Elsevier Ltd. All rights reserved.

Crystal structure and thermal and electrical properties of the perovskite solid solution Nd1-xSrxFeO3-delta (0 <= x <= 0.4)

The crystal structure, thermal expansion and electrical conductivity of strontium-doped neodymium ferrite (Nd1-xSrxFeO3-delta where 0less than or equal toxless than or equal to0.4) were investigated. All compositions had the GdFeO3-type orthorhombic perovskite structure. The lattice parameters were determined at room temperature by X-ray powder diffraction. The orthorhombic distortion decreases with increasing Sr substitution. The pseudocubic lattice parameter shows a minimum at x=0.3. The thermal expansion curves for x=0.2-0.4 displayed rapid increase in slope at higher temperatures. The electrical conductivity increased with Sr content and temperature. The calculated activation energies for electrical conduction decreased with increasing x. The electrical conductivity can be described by the small polaron hopping mechanism. The charge compensation for divalent ion on the A-site is provided by the formation of Fe4+ ions on the B site and vacancies on the oxygen sublattice. The results indicate two defect domains: for low values of x, the predominant defect is Fe4+ ions, whereas for higher values of x, oxygen vacancies dominate. (C) 2002 Elsevier Science B.V. All rights reserved.