InAs/ln(0.52)Al(0.48)As quantum wire structure with the specific layer-ordering orientation on InP(001)

Quantum wires were formed in the 6-period InAs/In0.52Al0.48As structure on InP(0 0 1) grown by molecular beam epitaxy. The structure was characterized with transmission electron microscopy. It was found that the lateral periodic compositional modulation in the QWR array was in the [1 (1) over bar 0] direction and layer-ordered along the specific orientation deviating from the [0 0 1] growth direction by about 30 degrees. This deviating angle is consistent with the calculation of the distribution of elastic distortion around quantum wires in the structure using the finite element technique. (C) 1999 Elsevier Science B.V. All rights reserved.

Origin of the vertical-anticorrelation arrays of InAs/InAlAs nanowires with a fixed layer-ordering orientation

InAs/In0.52Al0.48As nanowire multilayer arrays were grown on (001) InP substrate by molecular-beam epitaxy. The structural property of the arrays was investigated by transmission electron microscopy. The results clearly showed the formation of InAs nanowires, evolution of InAs/InAlAs interface, and composition and thickness modulations in the InAlAs spacer layer. A fixed spatial ordering of InAs/InAlAs nanowires was revealed for all the samples. Regardless of the change in InAlAs spacer thickness of different samples, (i) the nanowires of one InAs layer are positioned above the nanowire spacing in the previous InAs layer and (ii) the layer-ordering orientation angle of nanowires is fixed. The results were explained from the viewpoint of the growth kinetics. The effect of InAlAs spacers is suggested to play an important role on the spatial ordering of the nanowire arrays. (C) 2002 American Institute of Physics.

Orientation and alignment of reagent molecules by two-photon excitation

The expressions used for describing the angular distribution of oriented and aligned reagent molecules are derived. The algebraic forms of orientation and alignment parameters of molecules in the excited states are obtained for two-photon excitation. The reagent molecules after absorbing two-photon may produce the higher order orientation and alignment than doing one-photon. (C) 2002 Elsevier Science B.V. All rights reserved.

TEM study of the AlN grain orientation grown on NCD diamond substrate

Piezoelectric AlN layer grain orientation, grown by room temperature reactive sputtering, is analyzed by transmission electron microscopy (TEM).Two types of samples are studied: (i) AlN grown on well-polished NCD (nano-crystalline diamond) diamond, (ii) AlN grown on an up-side down NCD layer previously grown on a Si substrate, i.e. diamond surface as smooth as that of Si substrates. The second set of sample show a faster lignment of their AlN grain caxis attributed to it smoother diamond free surface. No grain orientation relationship between diamond substrate grain and the AlN ones is evidenced, which seems to indicate the preponderance role of the surface substrate state.

Uniformity in Bias Tilt for Nematics Oriented by Polyvinyl Alcohol Surface Layers

Uniformity in bias tilt, for the polyvinyl alcohol(PVA)surface layer induced orientation of nematic liquid crystals, could be achieved for large area display panels, if one of the transparent electrodes is first directionally rubbed with fine abrasive; then both the electrodes coated with PVA, followed by directionally buffing the chemisorbed layers in the same direction. Uniformity may be due to increased 'train' configuration of the adsorbed macromolecule by falling on to microgrooves and maintaining the same sense of asymmetry for the looped segments.

Edge dislocation of b=[001]/2 in the InAs nanostructure on InP(001)

The self-organized InAs/In0.52Al0.48As nanostructure were grown on InP (001) using molecular beam epitaxy (MBE). The nanostructure has been studied using transmission electron microscopy (TEM) and high resolution transmission electron microscopy (HRTEM). The edge dislocations with the Burgers vector b = ([001]/2) and extending along the [$(110) over bar $] direction are observed. The results show that in the region near an edge dislocation, no InAs wires were formed, while in the regions free of dislocation, wire-like nanostructures were formed. The mechanisms for the formation of the [001]/2 edge dislocations were discussed.

Kaposi's sarcoma-associated herpesvirus latency-associated nuclear antigen 1 mimics Epstein-Barr virus EBNA1 immune evasion through central repeat domain effects on protein processing

Kaposi's sarcoma-associated herpesvirus (KSHV/human herpesvirus 8 [HHV8]) and Epstein-Barr virus (EBV/HHV4) are distantly related gammaherpesviruses causing tumors in humans. KSHV latency-associated nuclear antigen 1 (LANA1) is functionally similar to the EBV nuclear antigen-1 (EBNA1) protein expressed during viral latency, although they have no amino acid similarities. EBNA1 escapes cytotoxic lymphocyte (CTL) antigen processing by inhibiting its own proteosomal degradation and retarding its own synthesis to reduce defective ribosomal product processing. We show here that the LANA1 QED-rich central repeat (CR) region, particularly the CR2CR3 subdomain, also retards LANA1 synthesis and markedly enhances LANA1 stability in vitro and in vivo. LANA1 isoforms have half-lives greater than 24 h, and fusion of the LANA1 CR2CR3 domain to a destabilized heterologous protein markedly decreases protein turnover. Unlike EBNA1, the LANA1 CR2CR3 subdomain retards translation regardless of whether it is fused to the 5′ or 3′ end of a heterologous gene construct. Manipulation of sequence order, orientation, and composition of the CR2 and CR3 subdomains suggests that specific peptide sequences rather than RNA structures are responsible for synthesis retardation. Although mechanistic differences exist between LANA1 and EBNA1, the primary structures of both proteins have evolved to minimize provoking CTL immune responses. Simple strategies to eliminate these viral inhibitory regions may markedly improve vaccine effectiveness by maximizing CTL responses. Copyright © 2007, American Society for Microbiology. All Rights Reserved.

Influence of smectite suspension structure on sheet orientation in dry sediments : XRD and AFM applications

The structure-building phenomena within clay aggregates are governed by forces acting between clay particles. Measurements of such forces are important to understand in order to manipulate the aggregate structure for applications such as dewatering of mineral processing tailings. A parallel particle orientation is required when conducting XRD investigation on the oriented samples and conduct force measurements acting between basal planes of clay mineral platelets using at. force microscopy (AFM). To investigate how smectite clay platelets were oriented on silicon wafer substrate when dried from suspension range of methods like SEM, XRD and AFM were employed. From these investigations, we conclude that high clay concns. and larger particle diams. (up to 5 μm) in suspension result in random orientation of platelets in the substrate. The best possible laminar orientation in the clay dry film, represented in the XRD 0 0 1/0 2 0 intensity ratio of 47 was obtained by drying thin layers from 0.02 wt.% clay suspensions of the natural pH. Conducted AFM investigations show that smectite studied in water based electrolytes show very long-range repulsive forces lower in strength than electrostatic forces from double-layer repulsion. It was suggested that these forces may have structural nature. Smectite surface layers rehydrate in water environment forms surface gel with spongy and cellular texture which cushion approaching AFM probe. This structural effect can be measured in distances larger than 1000 nm from substrate surface and when probe penetrate this gel layer, structural linkages are forming between substrate and clay covered probe. These linkages prevent subsequently smooth detachments of AFM probe on way back when retrieval. This effect of tearing new formed structure apart involves larger adhesion-like forces measured in retrieval. It is also suggested that these effect may be enhanced by the nano-clay particles interaction.

Effects of layer orientation of CFRP strengthened steel hollow members

This paper reveals the effects of layer orientation on structural behaviour of three layers configured (LHL, HHL, LLH) CFRP strengthened circular hollow section (CHS) members subjected to bending. The beams were loaded to failure under four-point bending. The structural behaviour of the CFRP strengthened tubular steel beams with various layer orientations were presented in terms of failure load, stiffness, composite beam action and modes of failure. The LHL and LLH layers oriented strengthened beams perform slightly better than HHL layers oriented strengthened beams. The LHL and LLH layers oriented treated beams showed very similar structural behaviour.

Unsteady laminar incompressible second-order boundary-layer flow at a three-dimensional stagnation point

The unsteadely laminar incompressible second-order boundary-layer flow at the stagnation point of a three-dimensional body has been studied for both nodal and saddle point regions. The effects of mass transfer and Prandtl number have been taken into account. The equations governing the flow have been solved numerically using an implicit finite-difference scheme. It has been found that the parameter characterizing the unsteadiness in the velocity of the free stream, the nature of the stagnation point, the mass transfer and Prandtl number strongly affect the second-order skin friction and heat transfer. The overall skin friction becomes less due to second-order effects but the heat transfer has the opposite behaviour. For large injection, the second-order skin-friction and heat-transfer results prevail over the first-order boundary layer results whereas for the case of large suction the behaviour is just the opposite.

Unsteady laminar compressible stagnation-point boundary-layer flow over a three-dimensional body: Higher order effects

The unsteady laminar compressible three-dimensional stagnation-point boundary-layer flow with variable properties has been studied when the velocity of the incident stream, mass transfer and wall temperature vary arbitrarily with time. The second-order unsteady boundary-layer equations for all the effects have been derived by using the method of matched asymptotic expansions. Both nodal and saddle point flows as well as cold and hot wall cases have been considered. The partial differential equations governing the flow have been solved numerically using an implicit finite-difference scheme. Computations have been carried out for an accelerating stream, a decelerating stream and a fluctuating stream. The results indicate that the unsteady free stream velocity distributions, the nature of the stagnation point, the mass transfer, the wall temperature and the variation of the density-viscosity product across the boundary significantly affect the skin friction and heat transfer. The variation of the wall temperature with time strongly affects the heat transfer whereas its effect is comparatively less on skin friction. Suction increases the skin friction and heat transfer but injection does the opposite. The skin friction in the x direction due to the combined effects of first- and second-order boundary layers is less than the skin-friction in the x direction due to the first-order boundary layers for all the parameters. The overall skin friction in the z direction and heat transfer are more or less than the first-order boundary layers depending upon the values of the various parameters.

Semi-similar solutions of the unsteady compressible second-order boundary layer flow at the stagnation point

Semi-similar solutions of the unsteady compressible laminar boundary layer flow over two-dimensional and axisymmetric bodies at the stagnation point with mass transfer are studied for all the second-order boundary layer effects when the free stream velocity varies arbitrarily with time. The set of partial differential equations governing the unsteady compressible second-order boundary layers representing all the effects are derived for the first time. These partial differential equations are solved numerically using an implicit finite-difference scheme. The results are obtained for two particular unsteady free stream velocity distributions: (a) an accelerating stream and (b) a fluctuating stream. It is observed that the total skin friction and heat transfer are strongly affected by the surface mass transfer and wall temperature. However, their variation with time is significant only for large times. The second-order boundary layer effects are found to be more pronounced in the case of no mass transfer or injection as compared to that for suction. Résumé Des solutions semi-similaires d'écoulement variable compressible de couche limite sur des corps bi-dimensionnels thermique, sont étudiées pour tous les effets de couche limite du second ordre, lorsque la vitesse de l'écoulement libre varie arbitrairement avec le temps. Le systéme d'équations aux dérivées partielles représentant tous les effets est écrit pour la premiére fois. On le résout numériquement á l'aide d'un schéma implicite aux différences finies. Les résultats sont obtenus pour deux cas de vitesse variable d'écoulement libre: (a) un écoulement accéléré et (b) un écoulement fluctuant. On observe que le frottement pariétal total et le transfert de chaleur sont fortement affectés par le transfert de masse et la température pariétaux. Néanmoins, leur variation avec le temps est sensible seulement pour des grandes durées. Les effets sont trouvés plus prononcés dans le cas de l'absence du transfert de masse ou de l'injection par rapport au cas de l'aspiration.

Second-order boundary-layer effects for the unsteady laminar incompressible three-dimensional stagnation-point flow

All the second-order boundary-layer effects on the unsteady laminar incompressible flow at the stagnation-point of a three-dimensional body for both nodal and saddle point regions have been studied. It has been assumed that the free-stream velocity, wall temperature and mass transfer vary arbitrarily with time. The effect of the Prandtl number has been taken into account. The partial differential equations governing the flow have been derived for the first time and then solved numerically unsteady free-stream velocity distributions, the nature of the using an implicit finite-difference scheme. It is found that the stagnation point and the mass transfer strongly affect the skin friction and heat transfer whereas the effects of the Prandtl number and the variation of the wall temperature with time are only on the heat transfer. The skin friction due to the combined effects of first- and second-order boundary layers is less than the skin friction due to, the first-order boundary layers whereas the heat transfer has the opposite behaviour. Suction increases the skin friction and heat transfer but injection does the opposite

Influence of seed layer orientation on the growth and physical properties of SnS nanostructures

Stoichiometric tin (II) sulfide (SnS) nano-structures were synthesized on SnS(010)/glass substrates using a simple and low-temperature chemical solution method, and their physical properties were investigated. The as-synthesized SnS nanostructures exhibited orthorhombic crystal structure and most of the nanocrystals are preferentially oriented along the <010> direction. These nanostructures showed p-type electrical conductivity and high electrical resistivity of 93 Omega cm. SnS nanostructures exhibited a direct optical band gap of 1.43 eV. While increasing the surrounding temperature from 20 to 150 degrees C, the electrical resistivity of the structures decreased and exhibited the activation energy of 0.28 eV.

The growth of gamma-LiAlO2 layer with a highly-preferred orientation on (0001) sapphire

Using vapor transport equilibration (VTE) technique we succeeded in the fabrication of single-phase gamma-LiAlO2 layer on (0001) sapphire substrate. X-ray diffraction indicated that the as-fabricated layer was highly textured with [100] orientation at proper VTE treatment temperature range from 1050 degrees C to 1100 degrees C. The main factors affecting the quality of the gamma-LiAlO2 layer were investigated by SEM and transmission spectra. These results reveal the possibility of fabricating gamma-LiAlO2 (100)//sapphire (0001) composite substrate for GaN-based epitaxial film by VTE.