Application of a hybrid blocking layer in dye-sensitized solar cells

In dye-sensitized solar cells a blocking layer between the transparent electrode and the mesoporous titanium dioxide film is used to prevent short-circuits between the hole-conductor and the front electrode. The conventional approach is to use a compact layer of titanium dioxide prepared by spin coating or spray pyrolysis. The thickness of the blocking layer is critical. On one hand, the layer has to be thick enough to cover the rough substrate completely. On the other hand, the serial resistance increases with increasing film thickness, because the layer acts as an ohmic resistance itself. In this thesis an amphiphilic diblock copolymer is used as a functional template to produce an alternative, hybrid blocking layer. The hybrid blocking layer is thinner than the conventional, compact titanium dioxide film and thereby possesses a higher conductivity. Still, this type of blocking layer covers the rough electrode material completely and avoids current loss through charge recombination. The novel blocking layer is prepared using a tailored, amphiphilic block copolymer in combination with sol-gel chemistry. While the hydrophilic poly(ethylene oxide) part of the polymer coordinates a titanium dioxide precursor to form a percolating network of titania particles, the hydrophobic poly(dimethylsiloxane) part turns into an insulating ceramic layer. With this technique, crack-free films with a thickness down to 24 nm are obtained. The presence of a conductive titanium dioxide network for current flow, which is embedded in an insulating ceramic material, is validated by conductive scanning force microscopy. This is the first time that such a hybrid blocking layer is implemented in a solar cell. With this approach the efficiency could be increased up to 27 % compared to the conventional blocking layer. Thus, it is demonstrated that the hybrid blocking layer represents a competitive alternative to the classical approach.

Electrical scanning probe microscopy on organic optoelectronic structures

In the field of organic optoelectronics, the nanoscale structure of the materials has huge im-pact on the device performance. Here, scanning force microscopy (SFM) techniques become increasingly important. In addition to topographic information, various surface properties can be recorded on a nanometer length scale, such as electrical conductivity (conductive scanning force microscopy, C-SFM) and surface potential (Kelvin probe force microscopy, KPFM).rnrnIn the context of this work, the electrical SFM modes were applied to study the interplay be-tween morphology and electrical properties in hybrid optoelectronic structures, developed in the group of Prof. J. Gutmann (MPI-P Mainz). In particular, I investigated the working prin-ciple of a novel integrated electron blocking layer system. A structure of electrically conduct-ing pathways along crystalline TiO2 particles in an insulating matrix of a polymer derived ceramic was found and insulating defect structures could be identified. In order to get insights into the internal structure of a device I investigated a working hybrid solar cell by preparing a cross cut with focused ion beam polishing. With C-SFM, the functional layers could be identified and the charge transport properties of the novel active layer composite material could be studied. rnrnIn C-SFM, soft surfaces can be permanently damaged by (i) tip induced forces, (ii) high elec-tric fields and (iii) high current densities close to the SFM-tip. Thus, an alternative operation based on torsion mode topography imaging in combination with current mapping was intro-duced. In torsion mode, the SFM-tip vibrates laterally and in close proximity to the sample surface. Thus, an electrical contact between tip and sample can be established. In a series of reference experiments on standard surfaces, the working mechanism of scanning conductive torsion mode microscopy (SCTMM) was investigated. Moreover, I studied samples covered with free standing semiconducting polymer nano-pillars that were developed in the group of Dr. P. Theato (University Mainz). The application of SCTMM allowed non-destructive imag-ing of the flexible surface at high resolution while measuring the conductance on individual pillarsrnrnIn order to study light induced electrical effects on the level of single nanostructures, a new SFM setup was built. It is equipped with a laser sample illumination and placed in inert at-mosphere. With this photoelectric SFM, I investigated the light induced response in function-alized nanorods that were developed in the group of Prof. R. Zentel (University Mainz). A block-copolymer containing an anchor block and dye moiety and a semiconducting conju-gated polymer moiety was synthesized and covalently bound to ZnO nanorods. This system forms an electron donor/acceptor interface and can thus be seen as a model system of a solar cell on the nanoscale. With a KPFM study on the illuminated samples, the light induced charge separation between the nanorod and the polymeric corona could not only be visualized, but also quantified.rnrnThe results demonstrate that electrical scanning force microscopy can study fundamental processes in nanostructures and give invaluable feedback to the synthetic chemists for the optimization of functional nanomaterials.rn

Charge generation and recombination in hybrid organic,inorganic solar cells

This thesis deals with the investigation of exciton and charge dynamics in hybrid solar cells by time-resolved optical spectroscopy. Quasi-steady-state and transient absorption spectroscopy, as well as time-resolved photoluminescence spectroscopy, were employed to study charge generation and recombination in solid-state organic dye-sensitized solar cells, where the commonly used liquid electrolyte is replaced by an organic solid hole transporter, namely 2,2′7,7′-tetrakis-(N,N-di-p-methoxyphenyl-amine)-9,9′-spirobifluorene (spiro-MeOTAD), and polymer-metal oxide bulk heterojunction solar cells, where the commonly used fullerene acceptor [6,6]-phenyl C61 butyric acid methyl ester (PCBM) is replaced by zinc oxide (ZnO) nanoparticles. By correlating the spectroscopic results with the photovoltaic performance, efficiency-limiting processes and processes leading to photocurrent generation in the investigated systems are revealed. rnIt is shown that the charge generation from several all-organic donor-π-bridge-acceptor dyes, specifically perylene monoimide derivatives, employed in solid-state dye-sensitized solar cells, is strongly dependent on the presence of a commonly used additive lithium bis(trifluoromethanesulphonyl)imide salt (Li-TFSI) at the interface. rnMoreover, it is shown that charges can not only be generated by electron injection from the excited dye into the TiO2 acceptor and subsequent regeneration of the dye cation by the hole transporter, but also by an alternative mechanism, called preceding hole transfer (or reductive quenching). Here, the excited dye is first reduced by the hole transporter and the thereby formed anion subsequently injects an electron into the titania. This additional charge generation process, which is only possible for solid hole transporters, helps to overcome injection problems. rnHowever, a severe disadvantage of solid-state dye-sensitized solar cells is re-vealed by monitoring the transient Stark effect on dye molecules at the inter-face induced by the electric field between electrons and holes. The attraction between the negative image charge present in TiO2, which is induced by the positive charge carrier in the hole transporter due to the dielectric contrast between the organic spiro-MeOTAD and inorganic titania, is sufficient to at-tract the hole back to the interface, thereby increasing recombination and suppressing the extraction of free charges.rnBy investigating the effect of different dye structures and physical properties on charge generation and recombination, design rules and guidelines for the further advancement of solid-state dye-sensitized solar cells are proposed.rnFinally, a spectroscopic study on polymer:ZnO bulk heterojunction hybrid solar cells, employing different surfactants attached to the metal oxide nanoparticles, was performed to understand the effect of surfactants upon photovoltaic behavior. By applying a parallel pool analysis on the transient absorption data, it is shown that suppressing fast recombination while simultaneously maintaining the exciton splitting efficiency by the right choice of surfactants leads to better photovoltaic performances. Suppressing the fast recombination completely, whilst maintaining the exciton splitting, could lead to a doubling of the power conversion efficiency of this type of solar cell.

Synergistischer photoinduzierter Schadstoffabbau mittels eines Porphyrazin-Titandioxid-Hybrids

Die zunehmende Luftverschmutzung aufgrund des steigenden Energiebedarfs und Mobilitätsanspruchs der Bevölkerung, insbesondere in urbanen Gebieten, erhöht das Gefährdungspotential für die Gesundheit und verschlechtert so die Lebensqualität. Neben der Vermeidung von Emissionen toxischer Gase als mittel- und langfristig optimale Maßnahme zur Verbesserung der Luftqualität, stellt der Abbau emittierter Luftschadstoffe ein geeignetes und kurzfristig wirksames Mittel dar. Ein solcher Abbau kann durch Photokatalyse erzielt werden, allerdings nutzen Photokatalysatoren, die auf dem Halbleiter Titandioxid (TiO2) basieren, das solare Emissionsspektrum nur geringfüfig aus und sind in Innenräumen und anderen UV-schwachen Bereichen nicht wirksam. Um diese Nachteile zu überwinden, wurde ein Photokatalysator entwickelt und hergestellt, der aus TiO2 (P25) als UV-aktiver Photokatalysator und als Trägermaterial sowie einem seinerseits im Vis-Bereich photoaktiven Porphyrazin-Farbstoff als Beschichtung besteht. Die sterisch anspruchsvollen und in der Peripherie mit acht Bindungsmotiven für TiO2 versehenen Farbstoffmoleküle wurden zu diesem Zweck auf der Halbleiteroberfläche immobilisiert. Die so gebildeten Porphyrazin-Titandioxid-Hybride wurde ausführlich charakterisiert. Dabei wurden unter anderem die Bindung der Farbstoffe auf der Titandioxidoberfläche mittels Adsorptionsisothermen und die UV/Vis-spektroskopischen Eigenschaften des Hybridmaterials untersucht. Zur Bestimmung der photokatalytischen Aktivitäten der Einzelkomponenten und des Hybridmaterials wurden diese auf die Fähigkeit zur Bildung von Singulett-Sauerstoff, Wasserstoffperoxid und Hydroxylradikalen hin sowie in einem an die ISO-22197-1 angelehnten Verfahren auf die Fähigkeit zum Abbau von NO hin jeweils bei Bestrahlung in drei Wellenlängenbereichen (UV-Strahlung, blaues Licht und rotes Licht) geprüft. Darüber hinaus konnte die Aktivität des Hybridmaterials bei der Photodynamischen Inaktivierung (PDI) von Bakterien unter UV- und Rotlichtbestrahlung im Vergleich zum reinen Ttandioxid bestimmt werden. Die Charakterisierung des Hybridmaterials ergab, dass die Farbstoffmoleküle in einer neutralen Suspension nahezu irreversibel in einer monomolekularen Schicht mit einer Bindungsenergie von -41.43 kJ/mol an die Oberfläche gebunden sind und das Hybridmaterial mit hohen Extinktionskoeffizienten von bis zu 105 M-1cm-1 in großen Bereichen des UV/Vis-Spektrums Photonen absorbiert. Das Spektrum des Hybridmaterials setzt sich dabei additiv aus den beiden Einzelspektren zusammen. Die Auswirkungen der Charakterisierungsergebnisse auf die Bildung reaktiver Sauerstoffspezies wurden ausführlich diskutiert. Der Vergleich der Aktivitäten in Bezug auf die Bildung der reaktiven Sauerstoffspezies zeigte, dass die Aktivität des Hybridmaterials bis auf die bei der Bildung von Hydroxylradikalen unter UV-Bestrahlung in allen Versuchen deutlich höher war als die Aktivität des reinen Titandioxids. Im Gegensatz zu reinem Titandioxid erzeugte das Hybridmaterial in allen untersuchten Wellenlängenbereichen Mengen an Singulett-Sauerstoff, die photophysikalisch eindeutig detektierbar waren. Zur Erklärung und Deutung dieser Beobachtungen wurde eine differenzierte Diskussion geführt, die die Ergebnisse der Hybridpartikelcharakterisierung aufgreift und implementiert. Der Vergleich der NO-Abbaueffizienzen ergab bei allen Experimenten durchgängig deutlich höhere Werte für das Hybridmaterial. Zudem wurden durch das Hybridmaterial nachgewiesenermaßen wesentlich geringere Mengen des unerwünschten Nebenprodukts des Abbaus (NO2) gebildet. Im Zuge der Diskussion wurden verschiedene mögliche Mechanismen der „sauberen“ Oxidation zu Nitrat durch das Hybridmaterial vorgestellt. Untersuchungen zur Photodynamischen Inaktivierung verschiedener Bakterien ergaben, dass das Hybridmaterial neben einer zu P25 ähnlichen Aktivität unter UV-Bestrahlung, anders als P25, auch eine PDI verschiedener Bakterien unter Rotlichtbestrahlung erreicht.

Determination of preventive maintenance lead time using hybrid analysis

The time for conducting Preventive Maintenance (PM) on an asset is often determined using a predefined alarm limit based on trends of a hazard function. In this paper, the authors propose using both hazard and reliability functions to improve the accuracy of the prediction particularly when the failure characteristic of the asset whole life is modelled using different failure distributions for the different stages of the life of the asset. The proposed method is validated using simulations and case studies.