Early stage assessment of the inspectability of welded components : A case from the aerospace industry

This paper proposes a method to indicate potential problems when planning dye penetrant and x-ray inspection of welded components. Inspection has been found to be an important part of the manufacturability evaluation made in a large CAD-based parametric environment for making multidisciplinary design simulations in early stages of design at an aircraft component manufacturer. The paper explains how the proposed method is to be included in the design platform at the company. It predicts the expected probability of detection of cracks (POD) in situations where the geometry of the parts is unfavourable for inspection so that potential problems can be discovered and solved in early stages. It is based on automatically extracting information from CAD-models and making a rule-based evaluation. It also provides a scale for how favourable the geometry is for inspection. In the paper it is also shown that the manufacturability evaluation need to take into consideration the expected stresses in the structures, highlighting the importance of multi-disciplinary simulations.

Väsymismitoitusperusteiden ja kuormitusten määrittäminen hitsatuille sekoitinakseleille

Työssä selvitettiin vastusvenymäliuskamittausten avulla sekoitinakselin kuormitukset sekä perehdyttiin väsymisilmiöön ja hitsattujen rakenteiden väsymismitoitukseen. Kuormitusten mittauksessa rekisteröitiin akselin kriittisen kohdan taivutus- ja vääntövenymät. Mittaustulosten avulla tutkittiin kuormituksia ja kuormitusten luonnetta sekä johdettiin väsymismitoitusperusteet sekoitinakseleille. Väsymismitoitus perustuu kahteen eri menetelmään. Vakioamplitudiseen väsymisrajaan perustuvassa menetelmässä vaihtuva-amplitudisella jännityksellä suurinkin jännitysheilahdus jää väsymisrajan alle. Kokonaisväsymisvaurioon perustuvassa mitoituksessa puolestaan sallitaan vakioamplitudisen väsymisrajan ylitys. Kestoikä on käytetty loppuun, kun väsymisvaurio saavuttaa väsymiskestävyyden arvon. Menetelmän valinta riippuu käytettävästä sekoitinelintyypistä ja käytön aikana ilmenevistä väsymisen kannalta vaarallisista tilanteista.

Hitsatun rakenteen lujuustarkastelu kokeellisesti määritetyn kuormitushistorian perusteella

Työssä tutkittiin jätteen murskauksesta murskaimeen aiheutuvia kuormituksia vastusvenymäliuskamittauksilla. Eri jätetyyppien aiheuttamia kuormituksia tutkittiin erillisinä tapauksina ja näistä tyyppikuormituksista johdettiin rakenteen normaalia käyttöä vastaava kuormitushistoria käyttäen painokertoimia eri tyyppikuormien kesken. Murskaimen runkorakennetta tutkittiin FE-analyysillä käyttäen kuormituksena kenttämittauksilla saatua todellista kuormitusta. FE-menetelmällä tutkittiin väsymisen kannalta kriittisiä kohtia rakenteesta. Tulosten perusteella kriittisiin yksityiskohtiin laadittiin parannusehdotuksia, joiden perusteella yhteistyössä työn teettäjän kanssa laadittiin uudet rakenneratkaisut. Rakenteen kestoikä määritettiin väsymisvaurion kannalta kriittisimmän yksityiskohdan mukaan. Kestoiän määrittämiseen käytettiin Palmgren-Miner menetelmää ja Palmgren-Miner menetelmästä johdettua ekvivalentin jännitysvaihtelun menetelmää. Muutosten jälkeen rakenne täyttää sille asetetun suunnittelukestoiän käytettyjen menetelmien perusteella.

Fatigue crack growth assessments in welded components including crack closure effects: Experiments and 3-D numerical modeling

This work provides a numerical and experimental investigation of fatigue crack growth behavior in steel weldments including crack closure effects and their coupled interaction with weld strength mismatch. A central objective of this study is to extend previously developed frameworks for evaluation of crack clo- sure effects on FCGR to steel weldments while, at the same time, gaining additional understanding of commonly adopted criteria for crack closure loads and their influence on fatigue life of structural welds. Very detailed non-linear finite element analyses using 3-D models of compact tension C ( T ) fracture spec- imens with center cracked, square groove welds provide the evolution of crack growth with cyclic stress intensity factor which is required for the estimation of the closure loads. Fatigue crack growth tests con- ducted on plane-sided, shallow-cracked C ( T ) specimens provide the necessary data against which crack closure effects on fatigue crack growth behavior can be assessed. Overall, the present investigation pro- vides additional support for estimation procedures of plasticity-induced crack closure loads in fatigue analyses of structural steels and their weldments

Fatigue Analysis of Welded Cruciform Joints with Cold Laps

Työssä on tutkittu vetojännityskuormituksen alaisena olevien hitsattujen kuormaa kantamattomien X-liitosten hitsin paikallisen geometrian variaation vaikutusta väsymislujuuteen. Muuttujina olivat reunan pyöristyssäde, kylmäjuoksun suuruus ja kylkikulma. Geometristen muuttujien parametrinen riippuvuussuhde on analysoitu usealla elementtimallilla. Väsymistarkastelu on suoritettu käyttämällä lineaaris-elastista murtumismekaniikkaa (LEFM) tasovenymätilassa ja materiaalina terästä. Särönkasvun suunnan ennustamisessaon käytetty maksimipääjännityskriteeriä sekä jännitysintensiteettikertoimet on määritetty J-integraalilla. Särön ydintymisvaihetta ei ole otettu huomioon. Rakenteen on oletettu olevan hitsatussa tilassa ja jännitysheilahdus on kokonaan tehollinen. Särön kasvunopeuden ennustamiseen on käytetty Paris'n lakia. Väsymislujuustulokset on esitetty karakteristisina väsymisluokkina (FAT) ja sovitettu parametriseksi yhtälöksi. Lopuksi väsymisanalyysin ennustamia tuloksia on verrattu saatavilla oleviin väsytystestituloksiin.

Multivariable regression analysis and hot-spot stress approach into fatigue life estimations of welded joints

Kolmen eri hitsausliitoksen väsymisikä arvio on analysoitu monimuuttuja regressio analyysin avulla. Regression perustana on laaja S-N tietokanta joka on kerätty kirjallisuudesta. Tarkastellut liitokset ovat tasalevy liitos, krusiformi liitos ja pitkittäisripa levyssä. Muuttujina ovat jännitysvaihtelu, kuormitetun levyn paksuus ja kuormitus tapa. Paksuus effekti on käsitelty uudelleen kaikkia kolmea liitosta ajatellen. Uudelleen käsittelyn avulla on varmistettu paksuus effektin olemassa olo ennen monimuuttuja regressioon siirtymistä. Lineaariset väsymisikä yhtalöt on ajettu kolmelle hitsausliitokselle ottaen huomioon kuormitetun levyn paksuus sekä kuormitus tapa. Väsymisikä yhtalöitä on verrattu ja keskusteltu testitulosten valossa, jotka on kerätty kirjallisuudesta. Neljä tutkimustaon tehty kerättyjen väsymistestien joukosta ja erilaisia väsymisikä arvio metodeja on käytetty väsymisiän arviointiin. Tuloksia on tarkasteltu ja niistä keskusteltu oikeiden testien valossa. Tutkimuksissa on katsottu 2mm ja 6mm symmetristäpitkittäisripaa levyssä, 12.7mm epäsymmetristä pitkittäisripaa, 38mm symmetristä pitkittäisripaa vääntökuormituksessa ja 25mm/38mm kuorman kantavaa krusiformi liitosta vääntökuormituksessa. Mallinnus on tehty niin lähelle testi liitosta kuin mahdollista. Väsymisikä arviointi metodit sisältävät hot-spot metodin jossa hot-spot jännitys on laskettu kahta lineaarista ja epälineaarista ekstrapolointiakäyttäen sekä paksuuden läpi integrointia käyttäen. Lovijännitys ja murtumismekaniikka metodeja on käytetty krusiformi liitosta laskiessa.

A novel approachfor assessing the fatigue strength of ultrasonic impact treated welded structures.

It is commonly observed that complex fabricated structures subject tofatigue loading fail at the welded joints. Some problems can be corrected by proper detail design but fatigue performance can also be improved using post-weld improvement methods. In general, improvement methods can be divided into two main groups: weld geometry modification methods and residual stress modification methods. The former remove weld toe defects and/or reduce the stress concentrationwhile the latter introduce compressive stress fields in the area where fatigue cracks are likely to initiate. Ultrasonic impact treatment (UIT) is a novel post-weld treatment method that influences both the residual stress distribution andimproves the local geometry of the weld. The structural fatigue strength of non-load carrying attachments in the as-welded condition has been experimentally compared to the structural fatigue strength of ultrasonic impact treated welds. Longitudinal attachment specimens made of two thicknesses of steel S355 J0 have been tested for determining the efficiency of ultrasonic impacttreatment. Treated welds were found to have about 50% greater structural fatigue strength, when the slope of the S-N-curve is three. High mean stress fatigue testing based on the Ohta-method decreased the degree of weld improvement only 19%. This indicated that the method could be also applied for large fabricated structures operating under high reactive residual stresses equilibrated within the volume of the structure. The thickness of specimens has no significant effect tothe structural fatigue strength. The fatigue class difference between 5 mm and 8 mm specimen was only 8%. It was hypothesized that the UIT method added a significant crack initiation period to the total fatigue life of the welded joints. Crack initiation life was estimated by a local strain approach. Material parameters were defined using a modified Uniform Material Law developed in Germany. Finite element analysis and X-ray diffraction were used to define, respectively, the stress concentration and mean stress. The theoretical fatigue life was found to have good accuracy comparing to experimental fatigue tests.The predictive behaviour of the local strain approach combined with the uniformmaterial law was excellent for the joint types and conditions studied in this work.

A modified structural stress method for fatigue assessment of welded structures

Fatigue life assessment of weldedstructures is commonly based on the nominal stress method, but more flexible and accurate methods have been introduced. In general, the assessment accuracy is improved as more localized information about the weld is incorporated. The structural hot spot stress method includes the influence of macro geometric effects and structural discontinuities on the design stress but excludes the local features of the weld. In this thesis, the limitations of the structural hot spot stress method are discussed and a modified structural stress method with improved accuracy is developed and verified for selected welded details. The fatigue life of structures in the as-welded state consists mainly of crack growth from pre-existing cracks or defects. Crack growth rate depends on crack geometry and the stress state on the crack face plane. This means that the stress level and shape of the stress distribution in the assumed crack path governs thetotal fatigue life. In many structural details the stress distribution is similar and adequate fatigue life estimates can be obtained just by adjusting the stress level based on a single stress value, i.e., the structural hot spot stress. There are, however, cases for which the structural stress approach is less appropriate because the stress distribution differs significantly from the more common cases. Plate edge attachments and plates on elastic foundations are some examples of structures with this type of stress distribution. The importance of fillet weld size and weld load variation on the stress distribution is another central topic in this thesis. Structural hot spot stress determination is generally based on a procedure that involves extrapolation of plate surface stresses. Other possibilities for determining the structural hot spot stress is to extrapolate stresses through the thickness at the weld toe or to use Dong's method which includes through-thickness extrapolation at some distance from the weld toe. Both of these latter methods are less sensitive to the FE mesh used. Structural stress based on surface extrapolation is sensitive to the extrapolation points selected and to the FE mesh used near these points. Rules for proper meshing, however, are well defined and not difficult to apply. To improve the accuracy of the traditional structural hot spot stress, a multi-linear stress distribution is introduced. The magnitude of the weld toe stress after linearization is dependent on the weld size, weld load and plate thickness. Simple equations have been derived by comparing assessment results based on the local linear stress distribution and LEFM based calculations. The proposed method is called the modified structural stress method (MSHS) since the structural hot spot stress (SHS) value is corrected using information on weld size andweld load. The correction procedure is verified using fatigue test results found in the literature. Also, a test case was conducted comparing the proposed method with other local fatigue assessment methods.

Effect of Mechanical and Geometric Mismatching on Fatigue and Damage of Welded Joints

The future of high technology welded constructions will be characterised by higher strength materials and improved weld quality with respect to fatigue resistance. The expected implementation of high quality high strength steel welds will require that more attention be given to the issues of crack initiation and mechanical mismatching. Experiments and finite element analyses were performed within the framework of continuum damage mechanics to investigate the effect of mismatching of welded joints on void nucleation and coalescence during monotonic loading. It was found that the damage of undermatched joints mainly occurred in the sandwich layer and the damageresistance of the joints decreases with the decrease of the sandwich layer width. The damage of over-matched joints mainly occurred in the base metal adjacent to the sandwich layer and the damage resistance of the joints increases with thedecrease of the sandwich layer width. The mechanisms of the initiation of the micro voids/cracks were found to be cracking of the inclusions or the embrittled second phase, and the debonding of the inclusions from the matrix. Experimental fatigue crack growth rate testing showed that the fatigue life of under-matched central crack panel specimens is longer than that of over-matched and even-matched specimens. Further investigation by the elastic-plastic finite element analysis indicated that fatigue crack closure, which originated from the inhomogeneousyielding adjacent to the crack tip, played an important role in the fatigue crack propagation. The applicability of the J integral concept to the mismatched specimens with crack extension under cyclic loading was assessed. The concept of fatigue class used by the International Institute of Welding was introduced in the parametric numerical analysis of several welded joints. The effect of weld geometry and load condition on fatigue strength of ferrite-pearlite steel joints was systematically evaluated based on linear elastic fracture mechanics. Joint types included lap joints, angle joints and butt joints. Various combinations of the tensile and bending loads were considered during the evaluation with the emphasis focused on the existence of both root and toe cracks. For a lap joint with asmall lack-of-penetration, a reasonably large weld leg and smaller flank angle were recommended for engineering practice in order to achieve higher fatigue strength. It was found that the fatigue strength of the angle joint depended strongly on the location and orientation of the preexisting crack-like welding defects, even if the joint was welded with full penetration. It is commonly believed that the double sided butt welds can have significantly higher fatigue strength than that of a single sided welds, but fatigue crack initiation and propagation can originate from the weld root if the welding procedure results in a partial penetration. It is clearly shown that the fatigue strength of the butt joint could be improved remarkably by ensuring full penetration. Nevertheless, increasing the fatigue strength of a butt joint by increasing the size of the weld is an uneconomical alternative.

Investigation of the fatigue performance of welded duplex stainless steel

Diplomityössä tutkitaan hitsatun duplex-teräksen, laatu: EN 1.4462 (Outokumpu laatu 2205) väsymislujuutta. Tutkimusmetodologia noudattaa sekä kokeellisia että laskennallisia menetelmiä. Kokeelliset menetelmät sisältävät hitsatun teräksen väsytystestaukset laboratoriossa, hitsausten jälkikäsittelyt (HiFIT) sekä perusaineelle ja hitseille tehtävät metallurgiset tutkimukset. Väsytyskokeista saatavia tuloksia verrataan kansainvälisen hitsausinstituutin (IIW) vahvistamiin rakennekohtaisiin standardeihin sekä kirjallisuudessa esiintyviin tutkimustuloksiin. Laskennalliset menetelmät sisältävät vertailulaskelmia tehollisen lovijännityksen (ENS) menetelmää hyödyntäen. Tehollisen lovijännityksen menetelmässä liitoksissa vaikuttavat teholliset lovijännitykset selvitetään elementtimenetelmän (FEM) avulla. Tulokset vahvistavat, että hitsauksella ja hitsausten jälkikäsittelyllä on suuri merkitys rakenteen kestoikään. Suurin osa väsytyskokeiden tuloksista osoitti parempia väsymiskestävyyden arvoja kuin rakennekohtaiset standardit, mutta liitosten liitosvirheiden todettiin heikentävän väsytyskestävyyttä. Jälkikäsittelyiden todettiin parantavan liitosten väsymiskestävyyden tuloksia ja todettiin tulosten olevan hyödynnettävissä mitoituksessa.

Residual Stresses and Fatigue Behavior of Welded Structural Members, HR-94, 1967

A research project entitled "Residual Stresses and Fatigue Behavior of Welded Structural Members" was conducted at the Structural Research Laboratory of the Engineering Research Institute at Iowa State University under the sponsorship of the Iowa State Highway Commission. The objective of the project was to study experimentally the fatigue behavior of flange plates in welded beam sections as influenced by different residual stress distributions which are caused by different sizes of welds.

Fatigue of tube-to-plate fillet welds and methods for their improvement /

"July 1997."

Influence of food components on lipid metabolism: scenarios and perspective on the control and prevention of dyslipidemias

Cardiovascular diseases (CVD) are the main causes of death in the Western world. Among the risk factors that are modifiable by diet, for reducing cardiovascular disease risks, the total plasma concentrations of cholesterol, triglycerides, LDL-C, and HDL-C are the most important. Dietary measures can balance these components of the lipid profile thus reducing the risk of cardiovascular diseases. The main food components that affect the lipid profile and can be modified by diet are the saturated and trans fats, unsaturated fats, cholesterol, phytosterols, plant protein, and soluble fiber. A wealth of evidence suggests that saturated and trans fats and cholesterol in the diet raise the total plasma cholesterol and LDL-C. Trans fats also reduce HDL-C, an important lipoprotein for mediating the reverse cholesterol transport. On the other hand, phytosterols, plant proteins, isoflavones, and soluble fiber are protective diet factors against cardiovascular diseases by modulating plasma lipoprotein levels. These food components at certain concentrations are able to reduce the total cholesterol, TG, and LDL-C and raise the plasma levels of HDL-C. Therefore, diet is an important tool for the prevention and control of cardiovascular diseases, and should be taken into account as a whole, i.e., not only the food components that modulate plasma concentrations of lipoproteins, but also the diet content of macro nutrients and micronutrients should be considered.

Erosion-fatigue of steam turbine blades

The premature failure of steam turbine rotor blades, manufactured in forged 12% Cr-NiMoV martensitic stainless steel, was investigated using visual inspection non-destructive testing, macro and microfractography, microstructural characterization, EDS microanalysis, chemical analysis, micro hardness and tensile testing. The blades belonged to the last stage of a thermoelectric plant steam turbine generator (140 MV A). The results indicated that the failure of the blades was promoted by foreign-particle erosion, which attacked preferentially the low-pressure side of the lower trailing edge of the blades. The resulting wear grooves acted as stress raisers and promoted the nucleation of fatigue cracks, which probably grew during the transition events of the steam turbine operation. Finally, water drop erosion was observed on the blade upper leading edge (low-pressure side). (C) 2009 Elsevier Ltd. All rights reserved.