Simultaneous determination of Cr, Fe, Ni and V in crude oil by emulsion sampling graphite furnace atomic absorption spectrometry

In this work a simple and reliable method for the simultaneous determination of Cr, Fe, Ni and V in crude oil, using emulsion sampling graphite furnace atomic absorption spectrometry is proposed. Under the best conditions, sample masses around 50 mg were weighed in polypropylene tubes and emulsified in a mixture of 0.5% (v v(-1)) hexane + 6% (m v(-1)) Triton X-100 (R). Considering the compromised conditions, the pyrolysis an atomization temperatures for the simultaneous determination of Cr, Fe, Ni and V were 1400 degrees C and 2500 degrees C, respectively. Aliquots of 20 mu L of reference solution and sample emulsion were co-injected into the graphite tube with 10 mu L of 1.0 g L(-1) Mg(NO(3))(2) as chemical modifier. The detection limits (n = 10, 3 sigma) and characteristic masses were, respectively: 0.07 mu g g(-1) and 19 pg for Cr; 2.15 mu g g(-1) and 31 pg for Fe; 1.25 mu g g(-1) and 44 pg for Ni; and 1.15 mu g g(-1) and 149 pg for V. The reliability of the proposed method was checked by fuel oil Standard Reference Material (SRMTriton X-100 (R) 1634c - NIST) analysis. The concentrations found presented no statistical differences compared to the certified values at 95% confidence level.

Compatible Ternary Blends of Chitosan/poly(vinyl alcohol)/poly(lactic acid) Produced by Oil-in-Water Emulsion Processing

Ternary compatible blends of chitosan, poly(vinyl alcohol), and poly(lactic acid) were prepared by an oil-in-water (O/W) emulsion process. Solutions of chitosan in aqueous acetic acid, poly(vinyl alcohol) (PVA) in water, and poly(lactic acid) (PLA) in chloroform were blended with a high shear mixer. PVA was used as an emulsifier to stabilize the emulsion and to reduce the interfacial tension between the solid polymers in the blends-produced. It proved to work very well because the emulsions were stable for periods of days or weeks and compatible blends were obtained When PVA was added. This effect was attributed to a synergistic effect of PVA and chitosan because the binary blends PVA/PLA and chitosan/PLA were completely incompatible; The blends were characterized by scanning electron microscopy (SEM), differential scanning calorimetry (DSC), thermal mechanical analysis (TMA), stress strain tests, and Fourier transform infrared spectroscopy (FTIR). The results indicated that despite the fact that the system contained distinct phases some degree of molecular miscibility occurred when the three components were present in the blend.

In-Line Monitoring of Particle Size during Emulsion Polymerization under Different Operational Conditions using NIR Spectroscopy

In the present work, the sensitivity of NIR spectroscopy toward the evolution of particle size was studied during emulsion homopolymerization of styrene (Sty) and emulsion copolymerization of vinyl acetate-butyl acrylate conducted in a semibatch stirred tank and a tubular pulsed sieve plate reactor, respectively. All NIR spectra were collected online with a transflectance probe immersed into the reaction medium. The spectral range used for the NIR monitoring was from 9 500 to 13 000 cm(-1), where the absorbance of the chemical components present is minimal and the changes in the NIR spectrum can be ascribed to the effects of light scattering by the polymer particles. Off-line measurements of the average diameter of the polymer particles by DLS were used as reference values for the development of the multi-variate NIR calibration models based on partial least squares. Results indicated that, in the spectral range studied, it is possible to monitor the evolution of the average size of the polymer particles during emulsion polymerization reactions. The inclusion of an additional spectral range, from 5 701 to 6 447 cm(-1), containing information on absorbances (""chemical information"") in the calibration models was also evaluated.

Development of a Continuous Emulsion Copolymerization Process in a Tubular Reactor

This contribution describes the development of a continuous emulsion copolymerization processs for vinyl acetate and n-butyl acrylate in a tubular reactor. Special features of this reactor include the use of oscillatory (pulsed) flow and internals (sieve plates) to prevent polymer fouling and promote good radial mixing, along with a controlled amount of axial mixing. The copolymer system studied (vinyl acetate and butyl acrylate) is strongly prone to composition drift due to very different reactivity ratios. An axially dispersed plug flow model, based on classical free radical copolymerization kinetics, was developed for this process and used successfully to optimize the lateral feeding profile to reduce compositional drift. An energy balance was included in the model equations to predict the effect of temperature variations on the process. The model predictions were validated with experimental data for monomer conversion, copolymer composition, average particle size, and temperature measured along the reactor length.

Modeling Vinyl Acetate and n-Butyl Acrylate Emulsion Copolymerization Process

This work presents a mathematical model for the vinyl acetate and n-butyl acrylate emulsion copolymerization process in batch reactors. The model is able to explain the effects of simultaneous changes in emulsifier concentration, initiator concentration, monomer-to-water ratio, and monomer feed composition on monomer conversion, copolymer composition and, to lesser extent, average particle size evolution histories. The main features of the system, such as the increase in the rate of polymerization as temperature, emulsifier, and initiator concentrations increase are correctly represented by the model. The model accounts for the basic features of the process and may be useful for practical applications, despite its simplicity and a reduced number of adjustable parameters.

Physical Stability Assessment and Sensory Optimization of a Dairy-Free Emulsion Using Response Surface Methodology

Desserts made with soy cream, which are oil-in-water emulsions, are widely consumed by lactose-intolerant individuals in Brazil. In this regard, this study aimed at using response surface methodology (RSM) to optimize the sensory attributes of a soy-based emulsion over a range of pink guava juice (GJ: 22% to 32%) and soy protein (SP: 1% to 3%). WHC and backscattering were analyzed after 72 h of storage at 7 degrees C. Furthermore, a rating test was performed to determine the degree of liking of color, taste, creaminess, appearance, and overall acceptability. The data showed that the samples were stable against gravity and storage. The models developed by RSM adequately described the creaminess, taste, and appearance of the emulsions. The response surface of the desirability function was used successfully in the optimization of the sensory properties of dairy-free emulsions, suggesting that a product with 30.35% GJ and 3% SP was the best combination of these components. The optimized sample presented suitable sensory properties, in addition to being a source of dietary fiber, iron, copper, and ascorbic acid.

Stability and in vitro penetration study of rutin incorporated in a cosmetic emulsion through an alternative model biomembrane

Rutin is employed as antioxidant and to prevent the capillary fragility and, when incorporated in cosmetic emulsions, it must target the action site. In vitro cutaneous penetration studies through human skin is the ideal situation, however, there are difficulties to obtain and to maintain this tissue viability. Among the membrane models, shed snake skin presents itself as pure stratum corneum, providing barrier function similar to human and it is obtained without the animal sacrifice. The objectives of this research were the development and stability evaluation of a cosmetic emulsion containing rutin and propylene glycol (penetration enhancer) and the evaluation or rutin in vitro cutaneous penetration and retention from the emulsion, employing an alternative model biomembrane. Emulsion was developed with rutin and propylene glycol, both at 5.0% w/w. Active substance presented on the formulation was quantified by a validated spectrophotometric method at 361.0 nm. Rutin Rutin cutaneous penetration and retention was performed in vertical diffusion cells with shed snake skin of Crotalus durissus, as alternative model biomembrane, and distilled water and ethanol 99.5% (1:1), as receptor fluid. The experiment was conducted for six hours, at 37.0 +/- 0.5 degrees C with constant stirring of 300 rpm. Spectrophotometry at 410.0 nm, previously validated, determined the active substance after cutaneous penetration/ retention. Emulsion did not promote rutin cutaneous penetration through C. durissus skin, retaining 0.931 +/- 0.0391 mu g rutin/mg shed snake skin. The referred formulation was chemically stable for 30 days after stored at 25.0 +/- 2.0 degrees C, 5.0 +/- 0.5 degrees C and 45.0 +/- 0.5 degrees C. In conclusion, it has not been verified the active cutaneous penetration through the model biomembrane, but only its retention on the Crotalus durissus stratum corneum, condition considered stable for 30 days.

Preparation and characterization of D, L-PLA loaded 17-beta-Estradiol valerate by emulsion/evaporation methods

PLA microparticles containing 17-beta-estradiol valerate were prepared by an emulsion/evaporation method in order to sustain drug release. This system was characterized concerning particle size, particle morphology and the influence of formulation and processing parameters on drug encapsulation and in vitro drug release. The biodegradation of the microparticles was observed by tissue histological analysis. Scanning electron microscopy and particle size analysis showed that the microparticles were spherical, presenting non-aggregated homogeneous surface and had diameters in the range of 718-880 nm (inert microparticles) and 3-4 mu m (drug loaded microparticles). The encapsulation efficiency was similar to 80%. Hormone released from microparticles was sustained. An in vivo degradation experiment confirmed that microparticles are biodegradable. The preparation method was shown to be suitable, since the morphological characteristics and efficiency yield were satisfactory. Thus, the method of developed microparticles seems to be a promising system for sustained release of 17-beta-estradiol.

A simple analysis of the changes during evaporation of a commercial emulsion of unknown composition

Optical microscopy and centrifugation were used to observe the Structural changes during evaporation of a commercial skin lotion of unknown composition. The degree of evaporation was determined from the changed weight of a microscope slide with the emulsion on a defined area and thickness, the evaporation loss versus time being measured by a balance under an infrared lamp. The results revealed not only which parts of the emulsion were most prone to evaporation without chemical analysis, but also gave surprising information as to which kind of structures would appear after extensive evaporation. The importance of these changes for the action of a skin lotion is briefly discussed.

Relationship between Rheological Properties and One-Step W/O/W Multiple Emulsion Formation

Formation of a normal (not temporary) W/O/W multiple emulsion via the one-step method as a result of the simultaneous occurrence of catastrophic and transitional phase inversion processes has been recently reported. Critical features of this process include the emulsification temperature (corresponding to the ultralow surface tension point), the use of a specific nonionic surfactant blend and the surfactant blend/oil phase ratio, and the addition of the surfactant blend to the oil phase. The purpose of this study was to investigate physicochemical properties in an effort to gain a mechanistic understanding of the formation of these emulsions. Bulk, surface, and interfacial theological properties of adsorbed nonionic surfactant (CremophorRH40 and Span80) films were investigated under conditions known to affect W/O/W emulsion formation. Bulk viscosity results demonstrated that CremophorRH40 has a higher mobility in oil compared than in water, explaining the significance of the solvent phase. In addition, the bulk viscosity profile of aqueous solutions containing CremophorRH40 indicated a phase transition at around 78 +/- 2 degrees C, which is in agreement with cubic phase formation in the Winsor III region. The similarity in the interfacial elasticity values of CremophorRH40 and Span80 indicated that canola oil has a major effect on surface activity, showing the significance of vegetable oil. The highest interfacial shear elasticity and viscosity were observed when both surfactants were added to the oil phase, indicating the importance of the microstructural arrangement. CremophorRH40/Span80 complexes tended to desorb from the solution/solution interface with increasing temperature, indicating surfactant phase formation as is theoretically predicted in the Winsor III region. Together these interfacial and bulk rheology data demonstrate that one-step W/O/W emulsions form as a result of the simultaneous occurrence of phase-transition processes in the Winsor III region and explain the critical formulation and processing parameters necessary to achieve the formation of these normal W/O/W emulsions.

A Comparative Analysis of the Changes During Evaporation of Three Different Commercial Emulsion of Unknown Composition

Optical microscope and centrifugation were used to observe the structure change during evaporation of three different commercial emulsions of unknown composition. The degree of evaporation under an infrared lamp at 70 degrees C was determined from the changed weight of a microscope slide with the emulsion on a defined area and thickness. The results revealed information as to which kind of structure would appear after evaporation.

Preparation of protein-loaded-PLGA microspheres by an emulsion/solvent evaporation process employing LTCC micromixers

This study presents the possibilities offered by microfluidic structures for the production of polymeric microspheres, using a process based upon the production of an emulsion. LTCC (Low Temperature Co-fired Ceramics) micromixers have been used for the preparation of polymeric microspheres. The effect of the geometry of the micromixers has been studied, with a specific focus on the size of the microspheres. as well as the control release properties of a model protein loaded within these microspheres. (C) 2008 Published by Elsevier B.V.

Development of a synthetic 7-ketocholesterol- rich emulsion resembling chylomicrons

Lipid emulsions that mimic natural lipoproteins help to understand the metabolism and the constitutional organization of circulating lipids. Chylomicrons synthesised by enterocyte cells usually contain oxysterols such as 7-ketocholesterol (7-KC). Here we describe the development of a 7-KC-containing emulsion as a model for oxisterol-rich chylomicron. Different amounts of 7-KC were used. Emulsion characteristics as effective diameter, lipid saturation with radiolabeled lipids was evaluated. In conclusion, the production of a synthetic 7-KC-rich emulsion resembling hylomicrons was feasible, being a model for in vivo metabolism studies.

Al-doped ZnO ceramic sputtering targets based on nanocrystalline powders produced by emulsion detonation synthesis – deposition and application as a transparent conductive oxide material

Transparent conducting oxides (TCOs) have been largely used in the optoelectronic industry due to their singular combination of low electrical resistivity and high optical transmittance. They are usually deposited by magnetron sputtering systems being applied in several devices, specifically thin film solar cells (TFSCs). Sputtering targets are crucial components of the sputtering process, with many of the sputtered films properties dependent on the targets characteristics. The present thesis focuses on the development of high quality conductive Al-doped ZnO (AZO) ceramic sputtering targets based on nanostructured powders produced by emulsion detonation synthesis method (EDSM), and their application as a TCO. In this sense, the influence of several processing parameters was investigated from the targets raw-materials synthesis to the application of sputtered films in optoelectronic devices. The optimized manufactured AZO targets present a final density above 99 % with controlled grain size, an homogeneous microstructure with a well dispersed ZnAl2O4 spinel phase, and electrical resistivities of ~4 × 10-4 Ωcm independently on the Al-doping level among 0.5 and 2.0 wt. % Al2O3. Sintering conditions proved to have a great influence on the properties of the targets and their performance as a sputtering target. It was demonstrated that both deposition process and final properties of the films are related with the targets characteristics, which in turn depends on the initial powder properties. In parallel, the influence of several deposition parameters in the film´s properties sputtered from these targets was investigated. The sputtered AZO TCOs showed electrical properties at room temperature that are superior to simple oxides and comparable to a reference TCO – indium tin oxide (ITO), namely low electrical resistivity of 5.45 × 10-4 Ωcm, high carrier mobility (29.4 cm2V-1s-1), and high charge carrier concentration (3.97 × 1020 cm-3), and also average transmittance in the visible region > 80 %. These superior properties allowed their successful application in different optoelectronic devices.