Wear of two artificial tooth materials in vivo: a 12-month pilot study.

STATEMENT OF PROBLEM: Wear of methacrylate artificial teeth resulting in vertical loss is a problem for both dentists and patients. PURPOSE: The purpose of this study was to quantify wear of artificial teeth in vivo and to relate it to subject and tooth variables. MATERIAL AND METHODS: Twenty-eight subjects treated with complete dentures received 2 artificial tooth materials (polymethyl methacrylate (PMMA)/double-cross linked PMMA fillers; 35%/59% (SR Antaris DCL, SR Postaris DCL); experimental 48%/46%). At baseline and after 12 months, impressions of the dentures were poured with improved stone. After laser scanning, the casts were superimposed and matched. Maximal vertical loss (mm) and volumetric loss (mm(3)) were calculated for each tooth and log-transformed to reduce variability. Volumetric loss was related to the occlusally active surface area. Linear mixed models were used to study the influence of the factors jaw, tooth, and material on adjusted (residual) wear values (alpha=.05). RESULTS: Due to drop outs (n=5) and unmatchable casts (n=3), 69% of all teeth were analyzed. Volumetric loss had a strong linear relationship to surface area (P<.001); this was less pronounced for vertical loss (P=.004). The factor showing the highest influence was the subject. Wear was tooth dependent (increasing from incisors to molars). However, these differences diminished once the wear rates were adjusted for occlusal area, and only a few remained significant (anterior versus posterior maxillary teeth). Another influencing factor was the age of the subject. CONCLUSIONS: Clinical wear of artificial teeth is higher than previously measured or expected. The presented method of analyzing wear of artificial teeth using a laser-scanning device seemed suitable.

Effect of Flasking and Polymerization Techniques on Tooth Movement in Complete Denture Processing

Purpose: The purpose of this study was to compare the artificial tooth positional changes following the flasking and polymerization of complete dentures by a combination of two flasking methods and two polymerization techniques using computer graphic measurements.Materials and Methods: Four groups of waxed complete dentures (n = 10) were invested and polymerized using the following techniques: (1) adding a second investment layer of gypsum and conventional water bath polymerization (Control), (2) adding a second investment layer of gypsum and polymerization with microwave energy (Gyp-micro), (3) adding a second investment layer of silicone (Zetalabor) and conventional polymerization (Silwater), and (4) adding a second investment layer of silicone and polymerization with microwave energy (Silmicro). For each specimen, six segments of interdental distances (A to F) were measured to determine the artificial tooth positions in the waxed and polymerized stages using software program AutoCad R14. The mean values of the changes were statistically compared by univariate ANOVA with Tukey post-hoc test at 5% significance.Results: There were no significant differences among the four groups, except for segment D of the Silmicro group (-0.004 +/- 0.032 cm) in relation to the Gypwater group (0.044 +/- 0.031 cm) (p < 0.05), which presented, repectively, expansion and shrinkage after polymerization.Conclusions: Within the limitations of this study, it was concluded that although the differences were not statistically significant, the use of a silicone investment layer when flasking complete dentures resulted in the least positional changes of the artificial teeth regardless of the polymerization technique.

Influence of Different Base Thicknesses on Maxillary Complete Denture Processing: Linear and Angular Graphic Analysis on the Movement of Artificial Teeth

Objective: The purpose of this study was to compare the dental movement that occurs during the processing of maxillary complete dentures with 3 different base thicknesses, using 2 investment methods, and microwave polymerization.Methods: A sample of 42 denture models was randomly divided into 6 groups (n = 7), with base thicknesses of 1.25, 2.50, and 3.75 mm and gypsum or silicone flask investment. Points were demarcated on the distal surface of the second molars and on the back of the gypsum cast at the alveolar ridge level to allow linear and angular measurement using AutoCAD software. The data were subjected to analysis of variance with double factor, Tukey test and Fisher (post hoc).Results: Angular analysis of the varying methods and their interactions generated a statistical difference (P = 0.023) when the magnitudes of molar inclination were compared. Tooth movement was greater for thin-based prostheses, 1.25 mm (-0.234), versus thick 3.75 mm (0.2395), with antagonistic behavior. Prosthesis investment with silicone (0.053) showed greater vertical change compared with the gypsum investment (0.032). There was a difference between the point of analysis, demonstrating that the changes were not symmetric.Conclusions: All groups evaluated showed change in the position of artificial teeth after processing. The complete denture with a thin base (1.25 mm) and silicone investment showed the worst results, whereas intermediate thickness (2.50 mm) was demonstrated to be ideal for the denture base.

Measurement of Interfacial Porosity at the Acrylic Resin/Denture Tooth Interface

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Bond strength of artificial teeth attached to a microwave-polymerized denture base resin after immersion in disinfectant solutions

To evaluate the bond strength between two types of acrylic resin teeth and a microwave denture base resin after immersion in disinfectant solutions for 180 days. Eighty specimens made of acrylic resin teeth (Biotone and Biotone IPN) attached to a microwave polymerized denture base resin (Nature-Cryl MC) were divided into eight groups (n = 10) according to the treatment (distilled water-control, 2% chlorhexidine digluconate, 1% sodium hypochlorite and sodium perborate solution-Corega Tabs). The shear strength tests (MPa) were carried out using a universal testing machine with a 0.5 mm/min speed. Data analysis was performed using ANOVA and multiple comparison Student-Newman-Keuls post hoc test (α = 0.05). Biotone IPN showed similar results among the groups (distilled water, 8.25 ± 1.81 MPa; chlorhexidine, 7.81 ± 3.34 MPa; hypochlorite, 7.75 ± 3.72 MPa; and Corega Tabs, 7.58 ± 2.27 MPa, whereas Biotone showed significantly lower shear bond strength values for the groups immersed in Corega Tabs (5.25 ± 3.27 MPa) and chlorhexidine (6.08 ± 2.35 MPa). Soaking the dentures in 1% sodium hypochlorite could be recommended as a disinfectant solution for dentures fabricated with conventional acrylic resin denture teeth and microwave denture base resin. For dentures fabricated with IPN teeth and microwave denture base resin, all the soaking solutions evaluated in this study could be suggested to denture wearers.

Color stability and surface roughness of artificial teeth brushed with an experimental Ricinus communis toothpaste

Aim: To evaluate, in vitro, the effect of brushing with a Ricinus communis -based experimental toothpaste on color stability and surface roughness of artificial teeth. Methods: Ninety artificial teeth (maxillary central incisors) in different shades, light and dark (NatusDent Triple Pressing, Dentbras) were used. Initial color (Spectrophotometer Easyshade, VITA) and surface roughness (Rugosimeter Surfcorder SE 1700, Kosakalab) readouts were performed. After baseline measurements, samples were assigned to 10 groups (n=9) according to the artificial tooth shade and type of toothpaste used during the mechanical brushing test (Pepsodent, MAVTEC): Sorriso Dentes Brancos – SDB, Colgate Luminous White - CLW (Colgate-Palmolive), Close up White Now - CWN (Unilever), Trihydral - THL (Perland Pharmacos) and Ricinus communis - RCE (Experimental). After 29,200 cycles of brushing, corresponding to 2 years of brushing by a healthy individual, new color and roughness readouts of the specimens were performed. Data (before and after the tests) were statistically analyzed (2-way repeated measures ANOVA, Tukey, p<0.05). Results: RCE toothpaste produced the greatest color stability for dark tooth shade and the second best color stability for light tooth shade. For surface roughness alteration, there was no difference (p>0.05) for any tested toothpaste regardless of tooth shade. Conclusions: The experimental Ricinus communis toothpaste did not cause color and surface roughness alteration in the artificial teeth, and it may be considered a suitable option for denture cleaning.

Photoelastic Study of the Support Structures of Distal-Extension Removable Partial Dentures

Purpose: The double system of support, in which the distal-extension removable partial denture adapts, causes inadequate stress around abutment teeth, increasing the possibility of unequal bone resorption. Several ways to reduce or more adequately distribute the stress between abutment teeth and residual ridges have been reported; however, there are no definitive answers to the problem. The purpose of this study was to analyze, by means of photoelasticity, the most favorable stress distribution using three retainers: T bar, rest, proximal plate, I bar (RPI), and circumferential with mesialized rest. Materials and Methods: Three photoelastic models were made simulating a Kennedy Class II inferior arch. Fifteen dentures with long saddles, five of each design, were adjusted to the photoelastic patterns and submitted first to uniformly distributed load, and then to a load localized on the last artificial tooth. The saddles were then shortened and the tests repeated. The quantitative and qualitative analyses of stress intensity were done manually and by photography, respectively. For intragroup analyses the Wilcoxon test for paired samples was used, while for intergroup analyses Friedman and Wilcoxon tests were used to better identify the differences (p < 0.05). Results: The RPI retainer, followed by the T bar, demonstrated the best distribution of load between teeth and residual ridge. The circumferential retainer caused greater concentration of stress between dental apexes. Stress distribution was influenced by the type of retainer, the length of the saddle, and the manner of load application. Conclusions: The long saddles and the uniformly distributed loads demonstrated better distribution of stress on support structures.

Evaluation of the Bond Strength of Denture Base Resins to Acrylic Resin Teeth: Effect of Thermocycling

Purpose: The purpose of this study was to evaluate the thermocycling effects and shear bond strength of acrylic resin teeth to denture base resins. Materials and Methods: Three acrylic teeth (Biotone, Trilux, Ivoclar) were chosen for bonding to four denture base resins: microwave-polymerized (Acron MC), heat-polymerized (Lucitone 550 and QC-20), and light-polymerized (Versyo. bond). Twenty specimens were produced for each denture base/acrylic tooth combination and were divided into two groups (n = 10): without thermocycling (control groups) and thermocycled groups submitted to 5000 cycles between 4 and 60 degrees C. Shear strength tests (MPa) were performed with a universal testing machine at a crosshead speed of 1 mm/min. Statistical analysis of the results was carried out with three-way ANOVA and Bonferroni`s multiple comparisons post hoc analysis for test groups (alpha = 0.05). Results: The shear bond strengths of Lucitone/Biotone, Lucitone/Trilux, and Versyo/Ivoclar specimens were significantly decreased by thermocycling, compared with the corresponding control groups (p < 0.05). The means of Acron/Ivoclar and Lucitone/Ivoclar specimens increased after thermocycling (p < 0.05). The highest mean shear bond strength value was observed with Lucitone/Biotone in the control group (14.54 MPa) and the lowest with QC-20/Trilux in the thermocycled group (3.69 MPa). Conclusion: Some acrylic tooth/denture base resin combinations can be more affected by thermocycling; effects vary based upon the materials used.

Evaluation of the Bond Strength of Denture Base Resins to Acrylic Resin Teeth: Effect of Thermocycling

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Resistência de união entre dentes artificiais e resinas acrílicas para base protética

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Nasal width as a guide for the selection of maxillary complete denture anterior teeth in four racial groups

Purpose: Selecting artificial teeth for edentulous patients is difficult when pre-extraction records are not available. Various guidelines have been suggested for determining the width of the maxillary anterior denture teeth. This study was undertaken to evaluate the use of the nasal width as a guide for the selection of proper width maxillary anterior denture teeth in four racial groups of the Brazilian population. Materials and Methods: One hundred and sixty subjects (40 Whites, 40 Mulattos, 40 Blacks, and 40 Asians) were selected. Using a sliding caliper, the nasal width and the intercanine distance were measured. The Pearson product-moment correlation coefficient was used to determine the relationship between the above measurements. A prediction was made of the percentage of subjects of the White, Mulatto, Black, and Asian populations in which the selection error due to the clinical application of the method of the nasal width would be within 0 to 2 mm, within 2 to 4 mm, and greater than 4 mm. Results: The four racial groups showed a weak correlation between the intercanine distance and the nasal width. In 39.7% of the White, 55.7% of the Mulatto, 81.9% of the Black, and 48.2% of the Asian populations, errors greater than 4 mm would be present with the use of the nasal width. Conclusions: The correlation found between the intercanine distance and the nasal width was not high enough to be used as a predictive factor. The relationship between natural tooth width and artificial tooth width as predicted by the nasal width showed that the nasal width method is not accurate for all the studied groups. Copyright © 2006 by The American College of Prosthodontists.

Avaliação da resistência de união entre dentes artificiais e resinas acrílicas para base protética. Efeito de termociclagem

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Análise por computação gráfica da variação da posição relativa dos dentes artificiais antes e após o processamento de próteses totais superiores

Pós-graduação em Odontologia - FOA

Análise das proporções faciais e sua relação com o formato dentário e com a dimensão vertical de repouso e de oclusão entre discentes institucionalizados

Considering the importance of the esthetic and the adequate register of vertical dimension (VD) to the oral rehabilitation, this study had as aims the analysis and comparison of two methods to get VD (Pleasure and Willis), functional space (FE), acquisition and correlation of facial and dental measurements. To do this, rest (RVD) and occlusal vertical dimension (OVD) and FE were achieved from the 30 students of the Federal University of Goias College of Dentistry. Following that, dental measurements of height and of the superior central incisors (SCI) and canine distance were registered. A facial analysis was performed to get the intercomissura, interalar, interpupilar, intercantal distance, besides register parameters as coincidence of dental and facial line, type of smile, face and SCI forms, and mastication type. The collected data were tabulated, compared by medias and standard deviations, and submitted to non-parametrical statistical analysis of Kruskal-Wallis and .Mann-Whitney with 5% of probability. The results doesn’t indicated statistical significant difference between FE of the two techniques. The measures of facial analysis are comparable with literature published data’s, but can’t be used as a parameter to the selection of intercanine distance. In 56.7% of the cases, there were coincidences of face and SCI forms, which could be a viable parameter in the selection of acrylic resin artificial tooth.

Abrasion wear resistance of different artificial teeth opposed to metal and composite antagonists

One of the most important properties of artificial teeth is the abrasion wear resistance, which is determinant in the maintenance of the rehabilitation's occlusal pattern. OBJECTIVES: This in vitro study aims to evaluate the abrasion wear resistance of 7 brands of artificial teeth opposed to two types of antagonists. MATERIAL AND METHODS: Seven groups were prepared with 12 specimens each (BIOLUX & BL, TRILUX & TR, BLUE DENT & BD, BIOCLER & BC, POSTARIS & PO, ORTHOSIT & OR, GNATHOSTAR & GN), opposed to metallic (M & nickel-chromium alloy), and to composite antagonists (C & Solidex indirect composite). A mechanical loading device was used (240 cycles/min, 4 Hz speed, 10 mm antagonist course). Initial and final contours of each specimen were registered with aid of a profile projector (20x magnification). The linear difference between the two profiles was measured and the registered values were subjected to ANOVA and Tukey's test. RESULTS: Regarding the antagonists, only OR (M = 10.45 ± 1.42 µm and C = 2.77 ± 0.69 µm) and BC (M = 6.70 ± 1.37 µm and C = 4.48 ± 0.80 µm) presented statistically significant differences (p < 0.05). Best results were obtained with PO (C = 2.33 ± 0.91 µm and M = 1.78 ± 0.42 µm), followed by BL (C = 3.70 ± 1.32 µm and M = 3.70 ± 0.61 µm), statistically similar for both antagonists (p>0.05). Greater result variance was obtained with OR, which presented the worse results opposed to Ni-Cr (10.45 ± 1.42 µm), and results similar to the best ones against composite (2.77 ± 0.69 µm). CONCLUSIONS: Within the limitations of this study, it may be concluded that the antagonist material is a factor of major importance to be considered in the choice of the artificial teeth to be used in the prosthesis.