Fracture load and marginal fit of shrinkage-free ZrSiO4 all-ceramic crowns after chewing simulation

The aim of this in vitro study was to evaluate the fracture load and marginal accuracy of crowns made from a shrinkage-free ZrSiO4 ceramic cemented with glass-ionomer or composite cement after chewing simulation. Thirty-two human mandibular molars were randomly divided into two groups. All teeth were prepared for and restored with shrinkage-free ZrSiO4 ceramic crowns (Everest HPC (R), KaVo). The crowns of group A (N = 16) were luted to the teeth using KetacCem (R) and group B (N = 16) were adhesively cemented using Panavia (R) 21EX. Measurements of the marginal accuracy before and after cementation were made using replicas and an image analysis system. All specimens were exposed to 1.2 million cycles of thermo-mechanical fatigue in a chewing simulator. Surviving specimens were subsequently loaded until fracture in a static testing device. Fracture loads (N) were recorded. All specimens survived chewing simulation. The mean fracture loads (+/- s.d.) were Group A, 1622 N (+/- 433); group B, 1957 N (+/- 806). There was no significant difference between the two groups (P > 0.05). The marginal gap values before cementation were (mean +/- s.d.): Group A, 32.7 mu m (+/- 6.8); group B, 33.0 mu m (+/- 6.7).The mean marginal gap values after cementation were (+/- s.d.): Group A, 44.6 mu m (+/- 6.7); group B, 46.6 mu m (+/- 7.7). The marginal openings were significantly higher after cementation for both groups (P < 0.05). All test groups demonstrated fracture load and marginal accuracy values within the range of clinical acceptability.

Preparation, characterization and in vitro angiogenic capacity of cobalt substituted β-tricalcium phosphate ceramics

Divalent cobalt ions (Co2+) have been shown to possess the capacity to induce angiogenesis by activating hypoxia inducible factor-1α (HIF-1α) and subsequently inducing the production of vascular endothelial growth factor (VEGF). However, there are few reports about Co-containing biomaterials for inducing in vitro angiogenesis. The aim of the present work was to prepare Co-containing β-tricalcium phosphate (Co-TCP) ceramics with different contents of calcium substituted by cobalt (0, 2, 5 mol%) and to investigate the effect of Co substitution on their physicochemical and biological properties. Co-TCP powders were synthesized by a chemistry precipitation method and Co-TCP ceramics were prepared by sintering the powder compacts. The effect of Co substitution on phase transition and the sintering property of the β-TCP ceramics was investigated. The proliferation and VEGF expression of human bone marrow mesenchymal stem cells (HBMSCs) cultured with both powder extracts and ceramic discs of Co-TCP was further evaluated. The in vitro angiogenesis was evaluated by the tube-like structure formation of human umbilical vein endothelial cells (HUVECs) cultured on ECMatrix™ in the presence of powder extracts. The results showed that Co substitution suppressed the phase transition from β- to α-TCP. Both the powder extracts and ceramic discs of Co-TCP had generally good cytocompatibility to support HBMSC growth. Importantly, the incorporation of Co into β-TCP greatly stimulated VEGF expression of HBMSCs and Co-TCP showed a significant enhancement of network structure formation of HUVECs compared with pure TCP. Our results suggested that the incorporation of Co into bioceramics is a potential viable way to enhance angiogenic properties of biomaterials. Co-TCP bioceramics may be used for bone tissue regeneration with improved angiogenic capacity.

Investigation of ternary zirconia ceramics

Transformation toughening ceramics (TTCs) are engineering materials which combine ceramic properties such as hardness, corrosion resistance and low thermal conductivity with good toughness and mechanical strength. At elevated temperatures their use is limited due to destabilisation of the transformation toughening microstructure (partially stabilised zirconia or PSZ) or creep and hydrothermal degradation (tetragonal zirconia polycrystals or TZPs). Despite these limitations, the use of TTCs, particularly zirconia based, has become widespread. To date, most commercial TTCs are based on combinations of zirconia and one stabilising oxide. This work investigates a zirconia ceramic containing two stabilisers, namely yttria and titania in roughly equal proportions.