Yb：Y2O3陶瓷薄片激光器获得10．5W连续激光输出

室温下采用中心波长约970nm准直输出的大功率激光二极管模块作为抽运源，端面抽运双程吸收的腔型结构，抽运原子数分数为8％的Yb：Y2O3多晶透明陶瓷片获得连续激光输出。抽运阈值功率为7W，当抽运功率达到35W时，获得优化连续激光输出功率为10．5W，光光转换效率为30％，斜率效率为37．5％。激光输出功率随抽运功率基本呈线性增长。采用更高功率抽运源、优化谐振腔结构和减小热效应的影响，Yb：Y2O3陶瓷激光器的输出功率和效率将会得到进一步提高。

Yb：Y2O3透明陶瓷的光学性能研究

介绍了一种基于纳米粉末真空烧结技术的新型固体激光材料——Yb：Y2O3多晶陶瓷的制备工艺、物理化学特性、能级结构和光谱特性，并与Yb：YAG单晶进行了对比．采用紧凑型有源镜激光器（CAMIL）的抽运方式，验证了Yb：Y2O3透明陶瓷的激光输出性能．在35W的最大抽运功率下，得到波长1078nm，功率10．5w的连续激光输出，斜率效率达到37．5％．实验中还观察到激光输出波长随抽运功率增加而红移以及随输出耦合镜变化而漂移的现象．Yb：Y2O3多晶陶瓷是一种理想的激光材料，不仅具有与Yb：YAG单晶同样优秀的

Diode-pumped Yb : YAG ceramic laser

Transparent polycrystalline Yb:YAG ceramics were fabricated by solid-state reactive sintering a mixture of commercial Al2O3, Y2O3, and Yb2O3 powders. The powders were mixed in ethanol and doped with 0.5 wt% tetraethoxysilane, dried, and pressed. Pressed samples were sintered at 1730 degrees C in vacuum. Transparent fully dense samples with grain sizes of several micrometers were obtained. The phase from 1500 degrees to 1700 degrees C was important for the grain growth, in which the grains grew quickly and a mass of pores were eliminated from the body of the sample. Annealing was an important step to remove the vacancies of oxygen and transform Yb2+ to Yb3+. The 1 at.% Yb:YAG ceramic sample was pumped by a diode laser to study the laser properties. The maximum output power of 1.02 W was obtained with a slope efficiency of 25% at 1030 nm. The size of the lasering sample was 4 mm x 4 mm x 3 mm.

5.5W CWYb3+ : Y2O3 ceramic laser pumped with 970 nm laser diode

CW laser output has been demonstrated for polycrystalline transparent 10 at.% Yb3+-doped Y2O3 ceramics. End-pumped with 970 nm laser diode, a maximum output power of 5.5 W has been obtained with absorbed pump power of 31.1 W. The slope efficiency is 25% while the threshold pump power is 5.6 W. Saturation is not observed in our experiments, indicating higher laser output can be expected with higher pump power. (C) 2004 Elsevier B.V. All rights reserved.

La2O3对Yb：Y2O3透明陶瓷光谱性能的影响

研究了La2O3对Yb：Y2O3透明陶瓷光谱性能的影响，添加适量La2O3以后，Yb：Y2O3透明陶瓷的吸收峰和发射峰的位置不变，但由于La^3＋的离子半径大于Y^3＋的离子半径，在Y2O3中引入La^3＋离子后，导致Y2O3晶格常数变大，晶场强度变弱，同时降低了Y2O3晶体的有序度，致使发射峰强度有所下降，发射截面变小．过量的№La2O3（x=0．16）造成yb^3＋激活离子发射强度明显下降；其荧光寿命在添加La2O3后总体增大45％-60％.

Theoretical study on longitudinally pumped Yb3+:Y2O3 lasers

To optimize the performance of longitudinally pumped Yb^(3+):Y2O3 ceramic lasers, cavity parameters such as material length and output coupler transmission at a certain laser output power are calculated numerically using quasi-three-level laser model. The results show great potential of Yb^(3+):Y2O3 ceramics for highly efficient diode-pumped solid-state lasers.

Investigation of the spectroscopic properties of Yb3+-doped yttrium lanthanum oxide transparent ceramic

Spectroscopic properties of (Y0.9-xLa0.1Ybx)(2)O-3 transparent ceramic were studied. Two main absorption peaks of the specimen are centered at 940 and 970 nm, which are suitable for InGaAs laser diode pumping. The main emission peaks were located at 1032 and 1075 nm with larger emission cross-section and longer fluorescence lifetime than those of Yb:Y2O3. These properties of (Y0.9-xLa0.1Ybx)(2)O-3 transparent ceramic are favorable to achieve high efficiency and high power laser output. (c) 2007 Elsevier B.V. All rights reserved.

激光二极管抽运的国产Yb:YAG陶瓷激光器

研究了国产Yb:YAG陶瓷的激光输出特性。激光器采用激光二极管(LD)纵向同轴抽运Yb:YAG陶瓷样品,样品的掺杂原子数分数为1%,一端面镀940 nm和1030 nm双增透膜,另一端面镀1030 nm增透膜,激光器在1031 nm处获得了近红外激光输出。实验中分别测试了Yb:YAG陶瓷在不同输出透射率(T=4%,8%,10%)条件下的激光输出特性。整个实验过程中,激光器维持基横模运转。当输出透射率为10%,吸收的抽运功率为9 W时,激光器获得最大的激光输出功率为1.63 W,相应的斜率效率为23.2%。

Yb：YAG透明陶瓷的制备和激光输出

制备了高质量的Yb：YAG透明陶瓷．Yb：YAG透明陶瓷的晶粒尺寸为10μm左右且分布均匀，晶界处和晶粒中没有杂质、气孔的存在．Yb：YAG样品中所有元素分布均匀，不同的晶粒间，晶粒和晶界间成分是一致的，没有出现成分的偏析．4mm厚样品的透过率为80％．LD泵浦获得了波长为1030nm，最大功率为268mW的连续激光输出．