Comments on "micro-scale abrasive wear testing of PVD coatings on curved substrates"

Previously published expressions for the wear volume in the micro-scale abrasion test for curved specimen surfaces (K.L. Rutherford and I.M. Hutchings, Tribology Letters 2 (1996) 1-11) were based upon erroneous assumptions about the wear-scar geometry. Accurate volumes have now been computed, and the errors in the use of the original analytical equations are shown to be negligibly small (<0.5% error) for all practical cases. © J.C. Baltzer AG, Science Publishers.

A study of microstructure and wear behaviour of TiB2/Al metal matrix composites

The present paper deals with the study of microstructure and wear characteristics of TiB2 reinforced aluminium metal matrix composites (MMCs). Matrix alloys with 5, 10 and 15% of TiB2 were made using stir casting technique. Effect of sliding velocity on the wear behaviour and tribo-chemistry of the worn surfaces of both matrix and composites sliding against a EN24 steel disc has been investigated under dry conditions. A pin-on-disc wear testing machine was used to find the wear rate, in which EN24 steel disc was used as the counter face, loads of 10-60N in steps of 10N and speeds of 100, 200, 300, 400 and 500 rpm were employed. The results showed that the wear rate was increased with an increase in load and sliding speed for both the materials. However, a lower wear rate was obtained for MMCs when compared to the matrix alloys. The wear transition from slight to severe was presented at the critical applied loads. The transition loads for the MMCs were much higher than that of the matrix alloy. The transition loads were increased with increase in TiB2 and the same was decreased with the increase of sliding speeds. The SEM and EDS analyses were undertaken to demonstrate the effect of TiB2 particles on the wear mechanism for each conditions.

Micro-scale wear characteristics of electroless Ni-P/SiC composite coating under two different sliding conditions

The electroless nickel composite (ENC) with various silicon carbide contents was deposited onto aluminium alloy (LM24) substrate. The wear behaviour and the microhardness of the composite coating samples were investigated and compared with particles free and aluminium substrate samples using micro-scale abrasion tester and microhardness tester respectively. The wear scar marks and wear volume were analysed by optical microscope. The wear tracks were further studied using scanning electron microscopy (SEM). The embedded particles were found to get pressed into the matrix which helps resisting further wearing process for composite samples. However, random orientation of microcuts and microfallow were seen for ENC sample but more uniform wearing was observed for EN sample. The composite coating with low content of SiC was worn minimum. Early penetration into the substrate was seen for samples with higher SiC content. Microhardness was improved after heat treatment for all the samples containing various SiC content. Under dry sliding condition, inclusion of particles in the matrix did not improve the wearing resistance performance in as-deposited state. The wearing worsened as the content of the particles increased generally. However, on heat treatment, the composite coatings exhibited improved wear resistance and the best result was obtained from the one with low particle contents.

Pin on disc wear investigation of nitrocarburised H13 tool steel

Nitrocarburised H13 disks were tested in dry, sliding wear against a stationary ruby ball (pin). Three different 4 h nitrocarburising treatments were compared, using N2/NH3/CO2, N2/NH3/natural gas and N2/NH3 gas mixtures, resulting in compound layers of varying thickness, hardness, porosity and oxide morphology. During mild, oxidative wear, with the formation of abrasive wear debris, the most brittle and oxidised surfaces performed poorly. Polishing to a bright, reflective finish greatly reduced wear. However, the N2/NH3/CO2 sample also frequently maintained a 'very mild' wear regime, owing to the formation of a protective film between the wear surfaces, and resulting in a lowering of the friction coefficient. This treated surface was porous and covered in a complex layer of coarse oxide+epsi-carbonitride. Nitrocarburised samples and wear tracks were characterised by optical microscopy, SEM, atomic force microscopy and stylus profilometry.

Contact pressure and wear in sheet metal forming - an FEM analysis

Wear is the principal cause of tool failure in most sheet metal forming processes. It is well known that the contact pressure between the blank and the tool has a large influence on the wear of the tool, and hence the tool life. This investigation utilises the finite element method to analyse the contact pressure distribution over the die radius for a particular deep drawing process. Furthermore, the evolution of the predicted contact pressure distribution throughout the entire stroke of the punch is also examined. It was found that the majority of the process shows a steady state pressure distribution, with two characteristic peaks over the die radius, at the beginning and end of the sheet contact area. Interestingly, the initial transient contact pressure response showed extremely high localised peak pressures; more than twice that of the steady state peaks. Results are compared to wear reported in the literature, during similar experimental deep drawing processes. Finally, the significance and effect of the results on wear and wear-testing techniques are discussed.

Wear resistance of experimental titanium alloys for dental applications

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

A rolling-gliding wear simulator for the investigation of tribological material pairings for application in total knee arthroplasty

Background: Material wear testing is an important technique in the development and evaluation of materials for use in implant for total knee arthroplasty. Since a knee joint induces a complex rolling-gliding movement, standardised material wear testing devices such as Pin-on-Disc or Ring-on-Disc testers are suitable to only a limited extent because they generate pure gliding motion only.Methods: A rolling-gliding wear simulator was thus designed, constructed and implemented, which simulates and reproduces the rolling-gliding movement and loading of the knee joint on specimens of simplified geometry. The technical concept was to run a base-plate, representing the tibia plateau, against a pivoted cylindrical counter-body, representing one femur condyle under an axial load. A rolling movement occurs as a result of the friction and pure gliding is induced by limiting the rotation of the cylindrical counter-body. The set up also enables simplified specimens handling and removal for gravimetrical wear measurements. Long-term wear tests and gravimetrical wear measurements were carried out on the well known material pairings: cobalt chrome-polyethylene, ceramic-polyethylene and ceramic-ceramic, over three million motion cycles to allow material comparisons to be made.Results: The observed differences in wear rates between cobalt-chrome on polyethylene and ceramic on polyethylene pairings were similar to the differences of published data for existing material-pairings. Test results on ceramic-ceramic pairings of different frontal-plane geometry and surface roughness displayed low wear rates and no fracture failures.Conclusions: The presented set up is able to simulate the rolling-gliding movement of the knee joint, is easy to use, and requires a minimum of user intervention or monitoring. It is suitable for long-term testing, and therefore a useful tool for the investigation of new and promising materials which are of interest for application in knee joint replacement implants. © 2010 Richter et al; licensee BioMed Central Ltd.

Effect of retained austenite on wear resistance of nanostructured dual phase steels

Nanostructured super bainitic and quenching-partitioning (Q&P) martensitic steels with a significant amount of retained austenite obtained by low temperature bainitic transformation and Q&P respectively were studied to explore the effect of retained austenite on stirring wear resistance. The results suggest that the Q&P martensitic steel significantly enhanced the hardness of the worn surface (from 674 to 762 HV1) and increased the thickness of the deformed layer (,3.3 mm), compared to the nanostructured bainitic steel. The underlying reason is that the Q&P martensitic steel has a higher stability of retained austenite thereby providing a superior transformation induced plasticity effect to increase surface hardness and reduce wear rate during the wear process.

Performance comparison of Stellite 6® deposited on steel using supersonic laser deposition and laser cladding

Stellite 6® powders were deposited on carbon steel using Supersonic Laser Deposition. The microstructure and performance of the coatings were examined using SEM, optical microscopy, EDS, XRD, microhardness testing and pin-on-disc wear testing. The results showed that the microstructure and wear behaviour of the most successful SLD deposition conditions with N2 at a pressure of 30bar, a temperature of 450°C and a deposition power of 1.5kW were compared with that of optimised laser cladding. © 2012 Elsevier B.V.