Tie lines and activities in the system NiO-MgO-SiO2 at 1373 K

The isothermal section of the phase diagram for the system NiO-MgO-SiO2 at 1373 K is established, The tie lines between (NiXMg1-X)O solid solution with rock salt structure and orthosilicate solid solution (NiYMg1-Y)Si0.5O2 and between orthosilicate and metasilicate (NiZMg1-Z)SiO3 crystalline solutions are determined using electron probe microanalysis (EPMA) and lattice parameter measurement on equilibrated samples, Although the monoxides and orthosilicates of Ni and Mg form a continuous range of solid solutions, the metasilicate phase exists only for 0 < Z < 0.096, The activity of NiO in the rock salt solid solution is determined as a function of composition and temperature in the range of 1023 to 1377 K using a solid state galvanic cell, The Gibbs energy of mixing of the monoxide solid solution can be expressed by a pseudo-subregular solution model: Delta G(ex) = X(1 - X)[(-2430 + 0.925T)X + (-5390 + 1.758T)(1 - X)] J/mol, The thermodynamic data for the rock salt phase are combined with information on interphase partitioning of Ni and Mg to generate the mixing properties for the orthosilicate and the metasilicate solid solutions, The regular solution model describes the orthosilicate and the metasilicate solid solutions at 1373 K within experimental uncertainties, The regular solution parameter Delta G(ex)/Y(1 - Y) is -820 (+/-70) J/mol for the orthosilicate solid solution, The corresponding value for the metasilicate solid solution is -220 (+/-150) J/mol, The derived activities for the orthosilicate solid solution are discussed in relation to the intracrystalline ion exchange equilibrium between M1 and M2 sites. The tie line information, in conjunction with the activity data for orthosilicate and metasilicate solid solutions, is used to calculate the Gibbs energy changes for the intercrystalline ion exchange reactions, Combining this with the known data for NiSi0.5O2, Gibbs energies of formation of MgSi0.5O2, MgSiO3, and metastable NiSiO3 are calculated, The Gibbs energy of formation of NiSiO3, from its component oxides, is equal to 7.67 (+/-0.6) kJ/mol at 1373 K.

Graphical User Interface (GUI) for the representation of GM surfaces (using the NRTL model) and curves, including tie-lines and Hessian matrix

A single and very easy to use Graphical User Interface (GUI- MATLAB) based on the topological information contained in the Gibbs energy of mixing function has been developed as a friendly tool to check the coherence of NRTL parameters obtained in a correlation data procedure. Thus, the analysis of the GM/RT surface, the GM/RT for the binaries and the GM/RT in planes containing the tie lines should be necessary to validate the obtained parameters for the different models for correlating phase equlibrium data.

On feasibility of regional frequency-based emergency control plans

Decentralized and regional load-frequency control of power systems operating in normal and near-normal conditions has been well studied; and several analysis/synthesis approaches have been developed during the last few decades. However in contingency and off-normal conditions, the existing emergency control plans, such as under-frequency load shedding, are usually applied in a centralized structure using a different analysis model. This paper discusses the feasibility of using frequency-based emergency control schemes based on tie-line measurements and local information available within a control area. The conventional load-frequency control model is generalized by considering the dynamics of emergency control/protection schemes and an analytic approach to analyze the regional frequency response under normal and emergency conditions is presented.

Comments on the phase diagrams and crystallisation paths of Y-Ba-Cu-O materials

Our micro structural characterisation of Y-Ba-Cu-O quenched partial melts shows that the BaCuO2 (BC1) phase is crystalline at temperatures as high as 1100°C, and that the partial melt self-establishes a micro structural gradient from the surface towards the interior of the samples, which can be associated with a gradient in an equivalent partial pressure of O2 (pO2). The extension of the Y2BaCuO5-YBa2Cu3O7-x (Y211-Y123) tie-line intersects the primary crystallisation field of BC1 first. The actual peritectic reaction that takes place is Y2BaCuO5(s) + BaCuO2(s) + 2BaCu2O2(L) + 1/2O2 → 2YBa2Cu3O6(s). Two schematic representations which allow an analysis of the pO2 dependence are given. The gradient in micro structure self-established by the sample acts as a driving force for texturing. With this new perspective gained about the actual peritectic reaction and mechanisms of melt-texturing of Y123, it is possible to explain most of the aspects about partial melt-texturing. In addition, it seems possible to devise heat treatments that may allow for the production of well-oriented single domains with very large diameters. © 1999 Elsevier Science B.V.

Activities in the $FeTiO_{3}-NiTiO_{3}$ Solid Solution from Alloy-Oxide Equilibria at 1273 K

Nine tie-lines between Fe-Ni alloys and FeTiO3-NiTiO3 solid solutions were determined at 1273 K. Samples were equilibrated in evacuated quartz ampoules for periods up to 10 days. Compositions of the alloy and oxide phases at equilibrium were determined by energy-dispersive x-ray spectroscopy. X-ray powder diffraction was used to confirm the results. Attainment of equilibrium was verified by the conventional tie-line rotation technique and by thermodynamic analysis of the results. The tie-lines are skewed toward the FeTiO3 corner. From the tie-line data and activities in the Fe-Ni alloy phase available in the literature, activities of FeTiO3 and NiTiO3 in the ilmenite solid solution were derived using the modified Gibbs-Duhem technique of Jacob and Jeffes [K.T. Jacob and J.H.E. Jeffes, An Improved Method for Calculating Activities from Distribution Equilibria, High Temp. High Press., 1972, 4, p 177-182]. The components of the oxide solid solution exhibit moderate positive deviations from Raoult's law. Within experimental error, excess Gibbs energy of mixing for the FeTiO3-NiTiO3 solid solution at 1273 K is a symmetric function of composition and can be represented as: Delta G(E) = 8590 (+/- 200) X-FeTiO3 X-NiTiO3 J/mol Full spectrum of tie-lines and oxygen potentials for the three-phase equilibrium involving Fe-Ni alloys, FeTiO3-NiTiO3 solid solutions, and TiO2 at 1273 K were computed using results obtained in this study and data available in the literature.

Phase relations between Al2O3---Cr2O3 and FeAl2O4---FeCr2O4 solid solutions at 1823 K

Tie-lines between the corundum and spinel solid solutions have been determined experimentally at 1823 K. Next, activities of FeCr2O4 and FeAl2O4 in the spinel solid solution were determined by combining the tie-line data with literature values for the activities of Cr2O3 and Al2O3 in the corundum phase. Activities and the Gibbs energy of mixing for the spinel solid solution were also obtained from a model based on cation distribution between nonequivalent crystallographic sites in the oxide lattice. The difference between the Gibbs energy of mixing obtained experimentally and from the model has been attributed to a strain enthalpy term which is relatively unchanged in magnitude from the reported at 1373 K. The integral enthalpy of mixing obtained from experimental data at 1373 and 1823 K using the second law is compared with the model result.

Evidence for a thermally reversing window in bulk Ge-Te-Si glasses revealed by alternating differential scanning calorimetry

Experiments on Ge15Tc85-xSix glasses (2 <= x <= 12) using alternating differential scanning calorimetry (ADSC) indicate that these glasses exhibit one glass transition and two crystallization reactions upon heating. The glass transition temperature has been found to increase almost linearly with silicon content, in the entire composition tie-line. The first crystallization temperature (T-cl) exhibits an increase with silicon content for x<5; T-cl remains almost a constant in the composition range 5 < x <= 10 and it increases comparatively more sharply with silicon content thereafter. The specific heat change (Delta C-p) is found to decrease with an increase in silicon content, exhibiting a minimum at x=5 (average coordination number, (r) = 2.4); a continuous increase is seen in Delta C-p with silicon concentration above x = 5. The effects seen in the variation with composition of T-cl and Delta C-p at x=5, are the specific signatures of the mean-field stiffness threshold at (r) = 2.4. Furthermore, a broad trough is seen in the enthalpy change (Delta H-NR), which is indicative of a thermally reversing window in Ge15Te85-xSix glasses in the composition range 2 <= x <= 6 (2.34 <= (r) <= 2.42).

Dielectric properties of barium magnesiotitanate ceramics, BaMg6Ti6O19

Phase-pure samples of barium magnesiotitanate, BaMg6Ti6O19 (BMT) are prepared by the wet chemical `gel-carbonate' method wherein the formation of BMT is complete below 950 degrees C as a result of the reaction between nanoparticles of BaCO3, MgO and TiO2. BMT powders are sintered at 1350-1450 C to dense ceramics. Extensive melting is noticed when the bulk composition falls between 0.4MgTiO(3)+0.6BaTiO(3)) and (0.6MgTiO(3)+0.4BaTiO(3)) along the MgTiO3-BaTiO3 tie-line in BaO-MgO-TiO2, phase diagram. Dielectric properties of sintered (BMT) ceramics have been investigated which showed epsilon similar or equal to 39 at 2 GHz, quality factor Q >= 10,000 and positive temperature coefficient of dielectric constant around 370 ppm degrees C-1.

A reinforcement learning approach to automatic generation control

This paper formulates the automatic generation control (AGC) problem as a stochastic multistage decision problem. A strategy for solving this new AGC problem formulation is presented by using a reinforcement learning (RL) approach This method of obtaining an AGC controller does not depend on any knowledge of the system model and more importantly it admits considerable flexibility in defining the control objective. Two specific RL based AGC algorithms are presented. The first algorithm uses the traditional control objective of limiting area control error (ACE) excursions, where as, in the second algorithm, the controller can restore the load-generation balance by only monitoring deviation in tie line flows and system frequency and it does not need to know or estimate the composite ACE signal as is done by all current approaches. The effectiveness and versatility of the approaches has been demonstrated using a two area AGC model. (C) 2002 Elsevier Science B.V. All rights reserved.

Evaluation and improvement of total transfer capability - A case study

With deregulation, the total transfer capability (TTC) calculation, which is the basis for evaluating available transfer capability (ATC), has become very significant. TTC is an important index in power markets with large volume of inter-area power exchanges and wheeling transactions taking place on an hourly basis. Its computation helps to achieve a viable technical and commercial transmission operation. The aim of the paper is to evaluate TTC in the interconnections and also to improve it using reactive optimization technique and UPFC devices. Computations are carried out for normal and contingency cases such as single line, tie line and generator outages. Base and optimized results are presented, and the results show how reactive optimization and unified power flow controller help to improve the system conditions. In this paper repeated power flow method is used to calculate TTC due to its ease of implementation. A case study is carried out on a 205 bus equivalent system, a part of Indian Southern grid. Parameters like voltage magnitude, L-index, minimum singular value and MW losses are computed to analyze the system performance.

Inter and intra crystalline ion exchange equilibria in the system Fe Cr Al O

The tie lines delineating ion-exchange equilibria between FeCr2O4FeAl2O4 spinel solid solution and Cr2O3Al2O3 solid solution with corundum structure have been determined at 1373 K by electron microprobe and EDAX point count analysis of oxide phases equilibrated with metallic iron. Activities in the spinel solid solution are derived from the tie lines and the thermodynamic data on Cr2O3Al2O3 solid solution available in the literature. The oxygen potentials corresponding to the tie-line composition of oxide phases in equilibrium with metallic iron were measured using solid oxide galvanic cells with CaOZrO2 and Y2O3ThO2 electrolytes. These electrochemical measurements also yield activities in the spinel solid solution, in good agreement with those obtained from tie lines. The activity-composition relationship in the spinel solid solution is analysed in terms of the intra-crystalline ion exchange between the tetrahedral and octahedral sites of the spinel structures. The ion exchange is governed by site-preference energies of the cations and the entropy of cations mixing on each site.

Phase relations and activities in the Co Ni O system at 1373 K

The tie-lines delineating equilibria between CoO-NiO and Co-Ni solid solutions in the ternary Co-Ni-O system at 1373 K have been determined by electron microprobe andedax point count analysis of the oxide phase equilibrated with the alloy. The oxygen potentials corresponding to the tie-line compositions have been measured using a solid oxide galvanic cell with calcia-stabilized zirconia electrolyte and Ni + NiO reference electrode. Activities in the metallic and oxide solid solution have been derived using a new Gibbs-Duhem integration technique. Both phases exhibit small positive deviations from ideality; the values ofG E/X 1 X 2 are 2640 J mol−1 for the metallic phase and 2870 J mol−1 for the oxide solid solution.

Phase equilibria in the Co Ni F system and activities in (CoxNi1 x)F2 solid solutions at 1373 K

The tie-lines delineating equilibria between CoF2-NiF2 and Co-Ni solid solutions in the ternary Co-Ni-F system at 1373 K have been determined by electron microprobe and EDAX point count analysis of the equilibrated phases. Activities in the fluoride solid solution have been derived from the knowledge of activitycomposition relation in the metallic solid solution and tie-line data,using a modified form of the Gibbs-Duhem integration. The fluorine potentials corresponding to the tie-line compositions have been calculated.The excess Gibbs' energy of mixing for the fluoride solid solution derived from the present data can be represented by the expression

Evidence for a thermally reversing window in bulk Ge–Te–Si glasses revealed by alternating differential scanning calorimetry

Experiments on Ge15Te85− x Si x glasses (2 ≤ x ≤ 12) using alternating differential scanning calorimetry (ADSC) indicate that these glasses exhibit one glass transition and two crystallization reactions upon heating. The glass transition temperature has been found to increase almost linearly with silicon content, in the entire composition tie-line. The first crystallization temperature (T c1) exhibits an increase with silicon content for x < 5; T c1 remains almost a constant in the composition range 5 < x ≤ 10 and it increases comparatively more sharply with silicon content thereafter. The specific heat change (ΔC p) is found to decrease with an increase in silicon content, exhibiting a minimum at x = 5 (average coordination number, r = 2.4); a continuous increase is seen in ΔC p with silicon concentration above x = 5. The effects seen in the variation with composition of T c1 and ΔC p at x = 5, are the specific signatures of the mean-field stiffness threshold at r = 2.4. Furthermore, a broad trough is seen in the enthalpy change (ΔH NR), which is indicative of a thermally reversing window in Ge15Te85− x Si x glasses in the composition range 2 ≤ x ≤ 6 (2.34 ≤ r ≤ 2.42).

A neural network based automatic generation control design through reinforcement learning

This paper presents the design and implementation of a learning controller for the Automatic Generation Control (AGC) in power systems based on a reinforcement learning (RL) framework. In contrast to the recent RL scheme for AGC proposed by us, the present method permits handling of power system variables such as Area Control Error (ACE) and deviations from scheduled frequency and tie-line flows as continuous variables. (In the earlier scheme, these variables have to be quantized into finitely many levels). The optimal control law is arrived at in the RL framework by making use of Q-learning strategy. Since the state variables are continuous, we propose the use of Radial Basis Function (RBF) neural networks to compute the Q-values for a given input state. Since, in this application we cannot provide training data appropriate for the standard supervised learning framework, a reinforcement learning algorithm is employed to train the RBF network. We also employ a novel exploration strategy, based on a Learning Automata algorithm,for generating training samples during Q-learning. The proposed scheme, in addition to being simple to implement, inherits all the attractive features of an RL scheme such as model independent design, flexibility in control objective specification, robustness etc. Two implementations of the proposed approach are presented. Through simulation studies the attractiveness of this approach is demonstrated.