Caracterização textural e estrutural de V 2O 5/TiO 2 obtidos via sol-gel: Comparação entre secagem convencional e supercrítica

This work describes a modified sol-gel method for the preparation of V 2O 5/TiO 2 catalysts. The samples have been characterized by N 2 adsorption at 77K, x-ray diffractometry (XRD) and Fourier Transform Infrared (FT-IR). The surface area increases with the vanadia loading from 24 m 2 g -1, for pure TiO 2, to 87 m 2 g -1 for 9wt.% of V 2O 5. The rutile form is predominant for pure TiO 2 but became enriched with anatase phase when vanadia loading is increased. No crystalline V 2O 5 phase was observed in the catalysts diffractograms. Two species of surface vanadium observed by FT-IR spectroscopy a monomeric vanadyl and polymeric vanadates, the vanadyl/vanadate ratio remains practically constant.

Photodegradation of soluble and emulsive cutting fluids using TiO 2 as catalyst

This paper describes results of the photo-degradation of three types of soluble and emulsive cutting fluids in an aqueous medium, using TiO2 as catalyst in suspension and UV radiation. The TiO2 proved to be an effective catalyst for the degradation of the cutting fluids investigated. The degradation rate depends on pH and nature of the fluids. The best performance of catalyst was observed at pH 8.0 for all the fluids when most of 70% of the organic load was decomposed. ©2006 Sociedade Brasileira de Química.

Structural refinement and photoluminescence properties of cube-like (Ca 1-xCu x)TiO 3 crystals synthesized by the microwave-hydrothermal method

In this work, (Ca 1-xCu x)TiO 3 crystals with (x = 0, 0.01 and 0.02), labeled as CTO, CCTO1 and CCTO2, were synthesized by the microwave-hydrothermal method at 140°C for 32 min. XRD patterns (Fig. 1), Rietveld refinement and FT-Raman spectroscopy indicated that these crystals present orthorhombic structure Pbnm. Micro-Raman and XANES spectra suggested that the substitution of Ca by Cu in A-site promoted a displacement of the [TiO6]-[TiO6] clusters adjacent from its symmetric center, which leads distortions on the [CaO 12] clusters neighboring and consequently cause the strains into the CaTiO3 lattice. FE-SEM images showed that these crystals have an irregular shape as cube like probably indicating an Ostwald-ripening and self-assemble as dominant mechanisms to crystals growth. The powders presented an intense PL blue-emission.

Estudo da correlação entre propriedades não-ôhmicas, processos de relaxação dielétrica e microestrutura de cerâmicas policristalinas do tipo (Ca IND. 1/4 Cu IND. 3/4)TiO IND. 3

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Preparação e caracterização estrutural e elétrica de células solares sensibilizadas por corantes empregando anodos nanoestruturados à base de 'TiO IND. 2'

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Meu tio Atahualpa de Paulo de Carvalho Neto: o enigma mulher no universo feminino do romance malandro

Pós-graduação em Letras - FCLAS

Avaliação da performance de eletrodos de filmes finos de Ti/TiO 2 com diferentes tamanhos de nanopartículas na oxidação fotoeletrocatalítica de Índigo Carmim

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Preparação de espumas cerâmicas de 'TIO IND. 2' a partir do processo sol-emulsão-gel

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Preparação, caracterização e aplicação de eletrodos bicomponentes de 'W' / 'WO IND. 3' / 'TIO IND 2' na oxidação fotoeletrocatalítica e fotocatalítica de corantes de cabelos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação de processos de degradação de corantes dispersos por técnicas eletroquímica e fotoeletroquímica usando eletrodos de Pt, filmes finos e nanotubos de 'TI'/'TIO IND. 2' e bicomponentes 'W'/'WO IND. 3'/'TIO IND. 2'

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

All sol-gel electrochromic smart windows: CeO2-TiO 2/Ormolyte/WO3

A solid state system having the configuration WO 3/Ormolyte/CeO2-TiO2 has been assembled. Syntheses routes for tungsten oxide WO3, and cerium-titanium CeO 2-TiO2 oxide sols, were developed. A novel solid electrolyte - Ormolyte is reported, which were obtained by the sol-gel process, they have a chemical stability due to the covalent bonds between the inorganic and organic phase, and were prepared with different [O]/[L] ratios, being the best for [O]/[L]=15. The variation of transmittance of the electrochromic device using the ormolyte [O]/[L]=15 was 35% (colored state) and 77% (bleached state).

Nanostructured TiO2-based composites for light absorption

Metal oxide nanocomposites were prepared by two different routes: polyol and sol-gel. Characterization by X ray diffraction showed that the first process produces directly a two-phase material, while the sol-gel powder never showed second phase below 600°C. Light spectroscopy of the treated powders indicated similarities for the processed materials. Although the overall material compositions are about the same, different structural characteristics are found for each processing. With the exception of Ti-Zn materials, all the double metal oxide powders showed higher absorbance than either TiO2 powder.

Photocatalytic decomposition of rhodamine-b using scandium and silver-modified TiO2 powders

Semiconductor-mediated photocatalytic oxidation is an interesting method for water decontamination and a specially modified TiO2 is said to be a promising material. This study verified that the synthesis of 1wt%Ag modified-Sc0.01Ti0.99O1.995 powder samples prepared by Polymeric Precursor Method is capable of forming a mixture of anatase-rutile phase with high photocatalytic performance. This kind of material is found to have a lower bandgap compared to the TiO2-anatase commercial powders, which can be associated to an innovative hybrid modification. The simultaneous insertion of scandium in order to generate a p-type semiconductor and a metallic silver nanophase acting as an electron trapper demonstrated being capable of enhancing the degradation of rhodamine B compared to the commercial TiO2. In spite of the different thermal treatments or phase amounts, the hybrid modified powder samples showed higher photocatalytic activity than the commercial ones.

Synthesis and characterization of nanostructured TiO2-SnO2 composite

Nanostructured composites based on titanium dioxide have been studied in order to improve optical and photo-catalytic properties, as well as their performance in gas sensors. In this work, titanium and tin dioxides were simultaneously synthesized by the polyol method resulting in TiO2 platelet coated with SnO2 nanoparticles as was observed by scanning electron microscopy. The thermal analysis showed that the combined synthesis promotes more easily the crystallization of the TiO2 rutile phase. The composite obtained after heat treatment at 500 °C showed to be formed of almost only rutile phases of both oxides. The optical properties analyzed by UV-Vis spectroscopy showed that the combined oxides have higher absorbance, which reinforces a model found in the literature based on the flow of photo-generated electrons to the conduction band of SnO2 delaying the recombination of charges.

Untersuchungen zur Löslichkeit von Kobalt und Eisen in TiO 2-Bulk sowie in TiO 2-Nanoproben und deren Einfluss auf die magnetischen Eigenschaften

Co- und Fe-dotierte Rutil- und Anatas-Bulkproben wurden über einen Sol-Gel Prozess und anschließende thermische Behandlung dargestellt und auf ihre Zugehörigkeit zu der Gruppe der verdünnten magnetischen Oxide untersucht. Die Untersuchungen der dotierten Rutil-Proben mittels Röntgenbeugung, Elektronenmikroskopie und magnetischen Methoden zeigen, dass die Löslichkeit von Co und Fe in der TiO2-Modifikation Rutil sehr gering ist. Oberhalb von 1at% Co bzw. Fe wird neben Rutil die Bildung der Oxide CoTiO3 bzw. Fe2TiO5 beobachtet. Weitere thermische Behandlung im Argon-H2-Strom führte aufgrund der Bildung von metallischem Co bzw. Fe zu einem ferromagnetischen Verhalten. Die TiO2-Modifikation Anatas besitzt eine höhere Löslichkeit, so dass erst oberhalb von 4at% Co bzw. 10at% Fe die Phasen Co3O4 bzw. FeTiO3 neben Anatas auftreten. Entsprechende Proben zeigen ein paramagnetisches Verhalten. Oberhalb der Löslichkeitsgrenze führt die Reduktion im Argon-H2-Strom zu einem ferromagnetischen Verhalten, welches auf metallisches Co bzw. Fe zurückzuführen ist. Analog zu den Bulkproben wurden Co- und Fe-dotierte TiO2-Nanodrähte hergestellt. Das magnetische Verhalten der Fe-dotierten TiO2-Nanodrähte entspricht dem der Fe-dotierten Anatas-Bulkproben. Dagegen führt die Co-Dotierung nicht zu einem Einbau in die TiO2-Nanodrähte, sondern zur Bildung von CoOx-Nanopartikeln. Die entsprechenden Proben zeigen ein schwach ferromagnetisches Verhalten. Dies ist jedoch nicht auf eine ferromagnetische Dotierung der TiO2-Nanodrähte zurückzuführen, sondern auf nicht kompensierte Momente an den Oberflächen der als Verunreinigungen auftretenden CoOx-Nanopartikel. Zusammenfassend wird festgestellt, dass die Löslichkeit von Co und Fe in TiO2 für die Ausbildung eines ferromagnetischen Verhaltens zu gering ist. Der beobachtete Ferromagnetismus lässt sich eindeutig auf magnetische Verunreinigungen zurückführen. Somit können die dotierten TiO2 Proben nicht den verdünnten magnetischen Oxiden zugeordnet werden.