Effect of different polishing systems on the surface roughness of microhybrid composites

The use of composite resins in dentistry is well accepted for restoring anterior and posterior teeth. Many polishing protocols have been evaluated for their effect on the surface roughness of restorative materials. This study compared the effect of different polishing systems on the surface roughness of microhybrid composites. Thirty-six specimens were prepared for each composite $#91;Charisma® (Heraeus Kulzer), Fill Magic® (Vigodent), TPH Spectrum® (Dentsply), Z100® (3M/ESPE) and Z250® (3M/ESPE)] and submitted to surface treatment with Enhance® and PoGo® (Dentsply) points, sequential Sof-Lex XT® aluminum oxide disks (3M/ESPE), and felt disks (TDV) combined with Excel® diamond polishing paste (TDV). Average surface roughness (Ra) was measured with a mechanical roughness tester. The data were analyzed by two-way ANOVA with repetition of the factorial design and the Tukey-Kramer test (p<0.01). The F-test result for treatments and resins was high (p<0.0001 for both), indicating that the effect of the treatment applied to the specimen surface and the effect of the type of resin on surface roughness was highly significant. Regarding the interaction between polishing system and type of resin used, a p value of 0.0002 was obtained, indicating a statistically significant difference. A Ra of 1.3663 was obtained for the Sof-Lex/TPH Spectrum interaction. In contrast, the Ra for the felt disk+paste/Z250 interactions was 0.1846. In conclusion, Sof-Lex polishing system produced a higher surface roughness on TPH Spectrum resin when compared to the other interactions.

Effect of experimental heat treatment on mechanical properties of resin composites

The aim of this study was to verify the influence of an experimental heat treatment (170ºC/10 min) using a casting furnace on the mechanical properties (hardness and flexural strength) of 2 commercial direct resin composites (TPH Spectrum and Filtek P60) compared to a commercial indirect resin system (BelleGlass). Heat treatment temperature was determined after thermal characterization by thermogravimetry (TG) and differential scanning calorimetry (DSC). Data was analyzed by ANOVA and Tukey's test at 5% significance level. There was statistical significance for the main factor heat treatment (p=0.03) and composite (p=0.02), for flexural strength. For Knoop hardness, only the main factor composite was statistically significant (p=0.00). P60 presented higher hardness than TPH. No statistically significant correlation between mechanical properties tested was detected. Based on these results, it was possible to conclude that heat treatment influenced flexural strength of direct composites, while it was not observed for hardness. The association of direct composites with a simple post-cure heat treatment may be an alternative for current indirect composite systems, although more studies are needed to verify other properties of the composites for this application.

Thermal and structural properties of commercial dental resins light-cured with blue emitting diodes (LEDs)

We have investigated the thermal and structural properties of different commercial dental resins: Filtek(TM) Z-350, Grandio(A (R)), Tetric Ceram(A (R)), and TPH Spectrum(A (R)). The purpose of the present study was to evaluate quantitatively the photo-polymerization behavior and the effect of filler contents on the kinetic cures of the dental resins by using Differential Scanning Calorimetry (DSC) and Fourier Transform Infrared Spectroscopy (FT-IR) techniques. We have successfully obtained the low and high glass transition T (g) values of the dental composite resins from DSC curves. It was also observed a good agreement between the both T (g) values, activation energies from thermal degradation, and the degree of conversion obtained for all samples. The results have shown that Tetric Ceram(A (R)) dental resin presented the higher T (g) values, activation energy of 215 +/- A 6 KJ mol(-1), and the higher degree of conversion (63%) when compared to the other resins studied herein.

Clinical assessment of postoperative sensitivity in posterior composite restorations

This incidence of postoperative sensitivity was evaluated in resin-based posterior restorations. Two hundred and ninety-two direct restorations were evaluated in premolars and molars. A total of 143 Class I and 149 Class 11 restorations (MO/OD and MOD) were placed in patients ranging in age from 30 to 50 years. After the cavity preparations were completed, a rubber dam was placed, and the preparations were restored using a total-etch system (Prime & Bond NT) and a resin-based restorative material (TPH Spectrum). The patients were contacted after 24 hours and 7, 30 and 90 days postoperatively and questioned regarding the presence of sensitivity and the stimuli that triggered that sensitivity. The Chi-square and Fisher's Exact Test were used for statistical analysis. Evaluation at 24 hours after restorative treatment revealed statistically significant differences among the types of cavity preparations restored and the occurrence of postoperative sensitivity (p=0.0003), with a higher frequency of sensitivity in Class H MOD restorations (26%), followed by Class II MO/DO (15%) and Class I restorations (5%). At 7, 30 and 90 days after restorative treatment, there was a decrease in the occurrence of sensitivity for all groups. The percentage of sensitivity among the groups was not significantly different. This study shows that the occurrence of sensitivity is correlated with the complexity of the restoration.

Comparative in vitro study of the shear bond strength of brackets bonded with restorative and orthodontic resins

The aim of this study was to evaluate the shear bond strength of brackets bonded with different restorative systems and compare it with that afforded by an established orthodontic bonding system. Seventy human bicuspids were used, divided into five different groups with 14 teeth each. Whereas a specific orthodontic bonding resin (Transbond (TM) XT) was used in the control group, the restorative systems Charisma, Tetric Ceram, TPH Spectrum and Z100 were used in the other four groups. Seven days after bonding the brackets to the samples, shear forces were applied under pressure in a universal testing machine. The data collected was evaluated using the ANOVA test and, when a difference was identified, the Tukey test was applied. A 5% level of significance was adopted. The mean results of the shear bond strength tests were as follows: Group 1 (Charisma), 14.98 MPa; Group 2 (Tetric Ceram), 15.16 MPa; Group 3 (TPH), 17.70 MPa; Group 4 (Z100), 13.91 MPa; and Group 5 or control group (Transbond (TM) XT), 17.15 MPa. No statistically significant difference was found among the groups. It was concluded that all tested resins have sufficient bond strength to be recommended for bonding orthodontic brackets.

Clinical and radiographic evaluation of pulpotomies employing calcium hydroxide and trioxide mineral aggregate

This study utilized clinical and radiographic examinations to compare the effectiveness of calcium hydroxide paste and mineral trioxide aggregate (MTA) for pulpotomies of primary molars in children. Ninety primary molars that showed clinical and radiographic indications for pulpotomy treatment were selected. The pulpotomies were performed in two sessions, using a corticosteroid/ antibiotic solution as therapeutic dressing. The sample was divided into two groups of 45 teeth, in which the pulpal remains were protected with either calcium hydroxide paste (Group 1) or MTA (Group 2). Radiographs were taken immediately and at 3-, 6-, and 12-month follow-up appointments. Three teeth in Group 1 failed after three months, while two cases failed after six months and one more failed at one year. Two failures were found in Group 2 at the 12-month follow-up. These results indicate that both materials may be utilized for pulpotomies in primary teeth.

Análise quantitativa de espectros de absorção no infravermelho de compósitos odontológicos fotoativados

Pós-graduação em Ciência dos Materiais - FEIS

Estudo de propriedades físico-químicas de resinas odontológicas: grau de conversão, dureza e expansão térmica

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo do grau de conversão e dureza em compósitos odontológicos fotopolimerizáveis

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Adhesion of substrate-adherent combinations for early composite repairs: Effect of intermediate adhesive resin application

This study evaluated the effect of intermediate adhesive resin application (IAR) on tensile bond strength (TBS) for early composite repairs in situations where substrate and repair composite bonded together were once of the same kind with the substrate (similar) and once other than the substrate material (dissimilar). Specimens from three types of composites (TPH Spectrum (TPH), Charisma (CHA) and Filtek Z250 (Z250)) were fabricated. The specimens in each composite group (n=72) were randomly divided into six subgroups (n=12). In each composite group, the similar and two dissimilar composites were bonded onto the substrates once using an IAR (Adper Single Bond Plus) and once without. After water storage for I week at 37 degrees C, substrate-adherent combinations were submitted to tensile test. Data were analyzed with three-way ANOVA and Tukey's tests (alpha=0.05). The substrate-adherent combination (p=0.0001), adherent (repair) composite (p=0.0001), and application of IAR (p=0.0001) significantly affected the results. Utilization of IAR improved the repair bond strength for all composite combinations. (C) 2013 Elsevier Ltd. All rights reserved.

Comparação da infiltração marginal de restaurações adesivas empregando instrumento rotativo ou um sistema químico-mecânico na remoção do tecido cariado

Pós-graduação em Odontologia Restauradora - ICT

Thermal and structural properties of commercial dental resins light-cured with blue emitting diodes (LEDs)

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Properties of dental resins submitted to pH catalysed hydrolysis

Objectives: This study evaluated the surface microhardness (SM) and roughness (SR) alterations of dental resins submitted to pH catalysed degradation regimens. Methods: Thirty discs of each TPH Spectrum (Dentsply), Z100 (3M-ESPE), or an unfilled experimental bis-GMA/TEGDMA resin were fabricated, totaling 90 specimens. Each specimen was polymerized for 40 s, finished, polished, and individually stored in deionized water at 37 degrees C for 7 days. Specimens were randomly assigned to the following pH solutions: 1.0, 6.9 or 13, and for SM or SR evaluations (n = 5). Baseline Knoop-hardness of each specimen was obtained by the arithmetic mean of five random micro-indentations. For SR, mean baseline values were obtained by five random surface tracings (R-a). Specimens were then soaked in one of the following storage media at 37 degrees C: (1) 0.1 M, pH 1.0 HCl, (2) 0.1 N, pH 13.0 NaOCl, and (3) deionized water (pH 6.9). Solutions were replaced daily. Repeated SM and SR measurements were performed at the 3-, 7- and 14-day storage time intervals. For each test and resin, data were analysed by two-way ANOVA followed by Tukey's test (alpha = 0.05). Results: There was significant decrease in SM and increase in SR values of composites after storage in alkaline medium. TPH and Z100 presented similar behaviour for SM and SR after immersion in the different media, whereas unfilled resin values showed no significant change. Conclusion: Hydrolytic degradation of resin composites seems to begin with the silanized inorganic particles and therefore depend on their composition. Significance: To accelerate composite hydrolysis and produce quick in vitro microstructural damage, alkaline medium appears to be more suitable than acidic medium. Contemporary resin composite properties seem to withstand neutral and acidic oral environments tolerably well. (C) 2012 Elsevier Ltd. All rights reserved.

Evaluation Of Characteristic-to-total Spectrum Ratio: Comparison Between Experimental And A Semi-empirical Model.

Primary X-ray spectra were measured in the range of 80-150kV in order to validate a computer program based on a semiempirical model. The ratio between the characteristic and total air Kerma was considered to compare computed results and experimental data. Results show that the experimental spectra have higher first HVL and mean energy than the calculated ones. The ratios between the characteristic and total air Kerma for calculated spectra are in good agreement with experimental results for all filtrations used.

Validity and reliability of the Structured Clinical Interview for Mood Spectrum: Brazilian version (SCIMOODS-VB)

OBJECTIVE: The aim of this study was to translate the Structured Clinical Interview for Mood Spectrum into Brazilian Portuguese, measuring its reliability, validity, and defining scores for bipolar disorders. METHOD: Questionnaire was translated (into Brazilian Portuguese) and back-translated into English. Sample consisted of 47 subjects with bipolar disorder, 47 with major depressive disorder, 18 with schizophrenia and 22 controls. Inter-rater reliability was tested in 20 subjects with bipolar disorder and MDD. Internal consistency was measured using the Kuder Richardson formula. Forward stepwise discriminant analysis was performed. Scores were compared between groups; manic (M), depressive (D) and total (T) threshold scores were calculated through receiver operating characteristic (ROC) curves. RESULTS: Kuder Richardson coefficients were between 0.86 and 0.94. Intraclass correlation coefficient was 0.96 (CI 95 % 0.93-0.97). Subjects with bipolar disorder had higher M and T, and similar D scores, when compared to major depressive disorder (ANOVA, p < 0.001). The sub-domains that best discriminated unipolar and bipolar subjects were manic energy and manic mood. M had the best area under the curve (0.909), and values of M equal to or greater than 30 yielded 91.5% sensitivity and 74.5% specificity. CONCLUSION: Structured Clinical Interview for Mood Spectrum has good reliability and validity. Cut-off of 30 best differentiates subjects with bipolar disorder vs. unipolar depression. A cutoff score of 30 or higher in the mania sub-domain is appropriate to help make a distinction between subjects with bipolar disorder and those with unipolar depression.