Stabilization of metastable tetragonal phase in a rhombohedral magnetoelectric multiferroic BiFeO3-PbTiO3

The phase formation behaviour of the magnetoelectric multiferroic 0.8BiFeO(3)-0.2PbTiO(3) was studied as a function of heat treatment at different temperatures of a sol-gel derived powder. While under ordinary synthesis conditions this composition exhibits antiferromagnetic ordering and a rhombohedral structure; the sol-gel-enabled low-temperature synthesis could stabilize a tetragonal metastable phase along with the stable rhombohedral phase, mimicking a morphotropic phase boundary state. The phase coexistence state exhibits relatively enhanced ferromagnetic correlation. The same system with a relatively higher PbTiO3 concentration, 0.65BiFeO(3)-0.35PbTiO(3), on the other hand, exhibits a rhombohedral metastable phase. These results suggest that the occurrence of metastable phases is a very common feature in the BiFeO3-PbTiO3 magnetoelectric ferroelectric system and that it affects the ferroelectric and magnetic properties of system quite remarkably.

Structural phase transition study of the morphotropic phase boundary compositions of Na0.5Bi0.5TiO3-PbTiO3

Neutron, synchrotron x-ray powder diffraction and dielectric studies have been performed for morphotropic phase boundary (MPB) compositions of the (1 - x )Na1/2Bi1/2TiO3-xPbTiO(3) system. At room temperature, the MPB compositions (0.10 < x <= 0.15) consist of a mixture of rhombohedral (space group R3c) and tetragonal ( space group P4mm) structures with the fraction of tetragonal phase increasing with increasing PbTiO3 content. On heating, while the rhombohedral phase just outside the MPB region, i.e. x = 0.10, transforms directly to a cubic phase, the rhombohedral phase of the MPB compositions transforms gradually to a tetragonal phase, until interrupted by a rhombohedral-cubic phase transition. The correspondence of the dielectric anomalies with the structural transitions of the different compositions has been examined and compared with earlier reports.

Ab initio electronic structures of rhombohedral and cubic HgXO3 (X = Ti, Pb)

First-principles calculations were performed for orthorhombic HgO, rhombohedral and cubic phases of HgTiO3 (HTO) and HgPbO3 (HPO). The calculations show that in the rhombohedral phase HTO is a direct gap insulator with a gap of ~1.6 eV. The rhombohedral phase of HPO, on the other hand, shows a weak metallic character. The results provide an explanation for the electrical properties of these compounds. The cubic phases of HTO and HPO are invariably metallic in nature, thereby suggesting that for HTO the rhombohedral–cubic transition must also be accompanied by a change in the electrical state. Examination of the electronic density of states of these systems revealed no significant on-site mixing of Hg 5d and Hg 6s states in any of these materials.

Competing structural phase transition scenarios in the giant tetragonality ferroelectric BiFeO3-PbTiO3: Isostructural vs multiphase transition

A systematic x-ray and neutron powder diffraction study of the giant tetragonality multiferroic (1-x) BiFeO3-(x) PbTiO3 have revealed that the compositions close to the morphotropic phase boundary present two different structural phase transition scenarios on cooling from the cubic phase: (i) cubic -> tetragonal (T-2) + tetragonal (T-1) -> tetragonal (T-1) and (ii) cubic -> tetragonal (T-2) + tetragonal (T-1) + rhombohedral (R3c) -> tetragonal (T-1) + rhombohedral (R3c). The comparatively larger tetragonality (c/a - 1) of the T-1 phase as compared to the coexisting isostructural T-2 phase is shown to be a result of significantly greater degree of overlap of the Pb/Bi-6s and Ti/Fe-3d with the O-2p orbitals as compared to that in the T-2 phase. The formation/suppression of the minor metastable rhombohedral phase seems to be governed by subtle play of local kinetic factors. In the scenario when the minor rhombohedral (R) phase is formed along with the tetragonal phases it is able to accommodate the large transformation stress in the system due to formation of the tetragonal phases, and prevent the solid from disintegration into powder after sintering. When the metastable rhombohedral phase is not formed, the large transformation strain ruptures the grain boundaries leading to fragmentation of the dense solid to powder. (C) 2013 American Institute of Physics. http://dx.doi.org/10.1063/1.4792215]

Anomalous polarization in the antiferroelectric-ferroelectric phase coexistence state in PbZrO3-Bi(Mg1/2Ti1/2)O-3

The ferroelectric system (1-x)PbZrO3-(x)Bi(Mg1/2Ti1/2)O-3 has been investigated as a function of composition, temperature, and electric field by x-ray powder diffraction, dielectric, and ferroelectric measurements. Within the solubility limit (x similar to 0.25), the system evolves from an orthorhombic-antiferroelectric to rhombohedral-ferroelectric state through a phase coexistence region. The highest polarization was found not for the composition exhibiting a pure ferroelectric state, but for a composition x = 0.15 exhibiting ferroelectric + antiferroelectric phase coexistence close to the rhombohedral phase boundary. Electric poling of the equilibrium two-phase state led to irreversible enhancement in the rhombohedral phase fraction suggesting that the enhanced polarization is related to the enhanced polarizability of the lattice due to first order criticality as in ferroelectric-ferroelectric morphotropic phase boundary systems. (C) 2013 AIP Publishing LLC.

Epitaxial strain stabilization of ferroelectric phase in PbZrO3 thin films

PbZrO3/SrRuO3/SrTiO3 (100) epitaxial heterostructures with different thickness of the PbZrO3 (PZO) layer (d(PZO) similar to 5-160 nm) were fabricated by pulsed laser deposition. The ultrathin PZO films (d(PZO) <= 10 nm) were found to possess a rhombohedral structure. On increasing the PZO film thickness, a bulk like orthorhombic phase started forming in the film with d(PZO) similar to 22 nm and became abundant in the thicker films. Nanobeam electron diffraction and room-temperature micro-Raman measurements revealed that the stabilization of the rhombohedral phase of PZO could be attributed to the epitaxial strain accommodated by the heterostructures. Room-temperature polarization vs electric field measurements performed on different samples showed characteristic double hysteresis loops of antiferroelectric materials accompanied by a small remnant polarization for the thick PZO films (dPZO >= 50 nm). The remnant polarization increased by reducing the PZO layer thickness, and a ferroelectric like hysteresis loop was observed for the sample with d(PZO) similar to 22 nm. Local ferroelectric properties measured by piezoresponse force microscopy also exhibited a similar thickness-dependent antiferroelectric-ferroelectric transition. Room-temperature electrical properties observed in the PZO thin films in correlation to their structural characteristics suggested that a ferroelectric rhombohedral phase could be stabilized in thin epitaxial PZO films experiencing large interfacial compressive stress.

Mechanism of phase formation in Pb(ZrxTi1-x)O3 synthesized by a partial oxalate method

The phase formation mechanism, as well as the morphotropic phase boundary, of lead zirconate titanate (PZT) processed by a partial oxalate method was investigated by simultaneous thermal analysis (TG-DTA) and by qualitative and quantitative X-ray diffraction (XRD). The results show that the ZrxTi1-xO2 (ZT) phase reacts with PbO forming the PZT phase without intermediate phases. XRD analysis showed the coexistence of rhombohedral and tetragonal phases for 0.47 ≤ x ≤ 0.55 with the phase boundary composition for x = 0.51. For low calcination temperatures, preferential formation of the PZT rhombohedral phase was observed. A model for phase formation of PZT by the partial oxalate method is proposed based on the existence of two interfaces of reaction (PbO-PZT and PZT-ZT) and diffusion of cations.

Effect of fuel on the formation structure, transport and magnetic properties of LaMnO3+nanopowders

Single-step low-temperature solution combustion (LCS) synthesis was adopted for the preparation of LaMnO3+ (LM) nanopowders. The powders were well characterized by powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS),surface area and Fourier transform infrared spectroscopy (FTIR). The PXRD of as-formed LM showed a cubic phase but, upon calcination (900degrees C, 6 h), it transformed into a rhombohedral phase. The effect of fuel on the formation of LM was examined, and its structure and magnetoresistance properties were investigated. Magnetoresistance (MR) measurements on LM were carried out at 0, 1, 4 and 7 T between 300 and 10 K. LM (fuel-to-oxidizer ratio; = 1) showed an MR of 17% at 1 T, whereas, for 4 and 7 T, it exhibited an MR of 45 and 55%, respectively, near the TM-I. Metallic resistivity data below TM-I showed that the double exchange interaction played a major role in this compound. It was interesting to observe that the sample calcined at 1200 degrees C for 3 h exhibited insulator behavior.

Multifunctional cryogenic sensors from n-BaTiO3 ceramics having strong negative temperature coefficient of resistance

Donor-doped n-BaTiO3 polycrystalline ceramics show a strong negative temperature coefficient of resistivity below the orthorhombic-rhombohedral phase transition point, from 10(2-3) Omega cm af 190 K to 10(10-13) Omega cm at less than or similar to 50 K, with thermal coefficient of resistance alpha = 20-23% K-1. Stable thermal sensors for low-temperature applications are realized therefrom. The negative temperature coefficient of resistivity region can be modified by substituting isovalent ions in the lattice. Highly nonlinear current-voltage (I-V) curves are observed at low temperatures, with a voltage maximum followed by the negative differential resistance. The I-V curves are sensitive to dissipation so that cryogenic sensors can be fabricated for liquid level control, flow rate monitoring, radiation detection or in-rush voltage limitation.

Magnetic ordering in La0.85Pb0.15Mn1-xTixO3 (0 <= x <= 0.15)

Powder-neutron diffraction study has been carried out at 300 and 10 K in La0.85Pb0.15Mn1-xTixO3 (0 less than or equal to x less than or equal to 0.15). The samples crystallize in the rhombohedral phase. The magnetic moment reduces nonlinearly with increase in Ti and correlates well with the reported behavior of T-C. The change in the moment and T-C could not be related to change in the one electron bandwidth, W. The reduction is attributed to the effect of dilution and thereby reducing the double exchange ferromagnetic interaction. (C) 2002 Elsevier Science B.V. All rights reserved.

Magneto-structural study of the multiferroic BiFeo(3)-SrTiO3

The structural and magnetic study of the pseudo-binary multiferroic (1 x)BiFeO3 (x)SrTiO3 has been investigated as a function of composition and temperature. In contrary to the previous studies, detailed examination revealed that the reported anomaly in the magnetization at x-0.30 does not occur at the composition induced rhombohedral-cubic phase boundary, but within the rhombohedral phase itself. The rhombohedral to cubic transition occurs at x > 0.4. Evidence of magneto-elastic coupling near the Neel temperature and nucleation-growth mode of the rhombohedral-cubic transformation, with both the phases coexisting over a range of temperature was found. (C) 2014 Elsevier B.V. All rights reserved.

Equilibrium phases in the multiferroic BiFeO3-PbTiO3 system - a revisit

The(1-x) BiFeO3-(x) PbTiO3 solid solution exhibiting a Morphotropic Phase Boundary (MPB) has attracted considerable attention recently because of its unique features such as multiferroic, high Curie point (T-C similar to 700 degrees C) and giant tetragonality (c/a -1 similar to 0.19). Different research groups have reported different composition range of MPB for this system. In this work we have conclusively proved that the wide composition range of MPB reported in the literature is due to kinetic arrest of the metastable rhombohedral phase and that if sufficient temperature and time is allowed the metastable phase disappears. The genuine MPB was found to be x=0.27 for which the tetragonal and the rhombohedral phases are in thermodynamic equilibrium. In-situ high temperature structural study of x=0.27 revealed the sluggish kinetics associated with the temperature induced structural transformation. Neutron powder diffraction study revealed that themagnetic ordering at room temperature occurs in the rhombohedral phase. The magnetic structure was found to be commensurate G-type antiferromagnetic with magnetic moments parallel to the c-direction (of the hexagonal cell). The present study suggests that the equilibrium properties in this solid solution series should be sought for x=0.27.

PHYSICAL VAPOR TRANSPORT AND CRYSTAL-GROWTH OF GESEXTE1-X SOLID-SOLUTIONS

Physical vapor transport studies of GeSe(x)Te1 - x (x = 0.1, 0.2, 0.3, and 0.4) solid solutions demonstrated, that individual, large single crystals of these materials can be grown in closed ampoules. A compositional analysis of the grown crystals revealed, that the mass transport (crystal growth) process under steady-state conditions is pseudo-congruent and controlled by diffusion processes in the source material. From these experiments, the degree of non-stoichiometry (Ge-vacancy concentrations) of GeSe(x)Te1 - x single crystals could be estimated. The effects of the cubic to rhombohedral phase transformation during cooling on the microstructure and morphology of the grown mixed crystals are observed. This work provides the basis for subsequent defect studies and electrical measurements on these crystals.

Effect of magnesium on structure and properties of LiNbO3 prepared from polymeric precursors

The effect of magnesium addition on the phase formation and electric properties of LiNbO3 powder prepared from polymeric precursor was analyzed. It was shown that the unit-cell volume of the rhombohedral phase decreased with increasing magnesium concentration. Small amounts of secondary phases were observed in LiNbO3 powder doped with 5 and 10 mol% Mg+2. These results indicated that the Mg+2 ion was substituted for niobium ion in the rhombohedral phase. The addition of Mg+2 promotes densification of LiNbO3 ceramics. It was noticed that the increase in additive concentration leads to a decrease of electric properties, K-p and d(33). This is due to formation of LiNb3O8 and MgNb2O6 phases at the grain boundaries. (C) 2002 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Synthesis and sintering of PZT ceramics

Lead zirconate powder, with Zr/Ti ratio of 50/50 was prepared by polymeric precursor method and doped with 3, 5 and 7 mol% of Sr+2 Or Ba+2, as well as by 0.2 to 5 mol% of Nb+5. The powder was calcined at 750 degrees C by 4 hours and milled during 1.5 h in isopropilic alcohol. Powders were characterized by surface area measurements (BET method), by infrared spectroscopy and by X-ray diffraction to characterize the crystal structure. Isostatically pressed samples were sintered in a dilatometer furnace by using a constant heating rate of 10 degrees C/min from ambient to 1200 degrees C. Synthetic air and air with water vapor were used as atmospheres. Both Sr+2 and Ba+2 substitute Pb+2 and favor the formation of rhombohedral phase. Otherwise, Nb+5 substitute preferentially Zr+4 favoring tetragonal phase. The concentration of dopants and the atmosphere influence the densification and the microstructure of the PZT, which alters the dielectric and piezoelectric properties of the ceramics.