离子束辅助反应制备的氧化铪薄膜特性

采用电子束直接蒸发氧化铪、无辅助电子束反应蒸发和离子束辅助反应蒸发金属铪3种沉积方式制备了单层HfO2薄膜,对样品的光学性能、结构特性以及激光损伤特性进行了研究。实验结果表明:通过反应沉积的方法可以有效减少缺陷产生并改善均匀性,施加离子辅助可以提高薄膜的折射率,在一定条件下还可以有效地降低吸收,但激光损伤阈值仍未达到直接采用氧化铪制备的水平;晶体结构方面,离子辅助条件下可以获得单斜相氧化铪薄膜,并且随着轰击能量的提高由(002)面的择优取向向(-111)面转变。

A nitrocarburising and low-temperature chromising duplex surface treatment

A duplex surface treatment has been developed involving the pre-treatment of hardened and tempered AISI H13 chromium hot-work tool steel by a ferritic nitrocarburising process, and a subsequent treatment of the nitrocarburised surface by a low-temperature chromium thermo-reactive deposition process.  The process formed a thin and hard chromium carbonitride surface layer above a hardened diffusion zone, and the low processing temperature allowed the properties of the core material to be retained. It is expected this surface treatment will find application in the treatment  of tooling used for aluminium forming operations.

Microstructure and mechanical properties of nitrided and chromized short steel fiber reinforced aluminum based P/M composites

The present investigation is on the microstructure evolution and hardness of powder metallurgically processed Al- 0.5 wt.%Mg base 10 wt.% short steel fiber reinforced composites. The 0.38 wt.% C short steel fibers of average diameter 50µm and 500-800µm length were nitrided and chromized in a fluid bed furnace. Nitriding was carried out at 525°C for 90, 30 and 5 min durations. Chromizing was performed at 950°C for 53 and 7 min durations, using thermal reactive deposition (TRD) and diffusion technique. The treated fibers and resulting reaction interfaces were characterized using metallographic, microhardness and XRD techniques.

Electrostatically confined plasma in segmented hollow cathode geometries for surface engineering

A segmented hollow cathode (SHC) geometry was used for electrostatic confinement of plasma, and surface engineering treatments were conducted in this arrangement. The assessed processes included plasma nitriding, reactive deposition of sputtered material, and deposition of carbonaceous films by plasma-enhanced chemical vapor deposition with a bipolar pulsed-dc power supply on steel substrates. The treated specimens exhibited uniform surface morphology and deposition layers. Characterization techniques included optical microscopy, scanning electron microscopy with energy dispersive X-ray capability, and X-ray diffraction. The advantages and potential applications of the SHC arrangement are discussed in view of these results.

Nanocrystalline vanadium oxide films synthesized by plasma-assisted reactive rf sputtering deposition

Plasma-assisted reactive rf magnetron sputtering deposition is used to fabricate vanadium oxide films on glass, silica and silicon substrates. The process conditions are optimized to synthesize phase-pure vanadium pentoxide (V2O5) featuring a nanocrystalline structure with the predominant (0 0 1) crystallographic orientation, surface morphology with rod-like nanosized grains and very uniform (the non-uniformity does not exceed 4%) coating thickness over large surface areas. The V2O5 films also show excellent and temperature-independent optical transmittance in a broad temperature range (20-95 °C). The results are relevant to the development of smart functional coatings with temperature-tunable properties. © 2007 IOP Publishing Ltd.

Reactive plasma-aided RF sputtering deposition of hydroxyapatite bio-implant coatings

The plasma-assisted RF sputtering deposition of a biocompatible, functionally graded calcium phosphate bioceramic on a Ti6A14 V orthopedic alloy is reported. The chemical composition and presence of hydroxyapatite (HA), CaTiO3, and CaO mineral phases can be effectively controlled by the process parameters. At higher DC biases, the ratio [Ca]/[P] and the amount of CaO increase, whereas the HA content decreases. Optical emission spectroscopy suggests that CaO+ is the dominant species that responds to negative DC bias and controls calcium content. Biocompatibility tests in simulated body fluid confirm a positive biomimetic response evidenced by in-growth of an apatite layer after 24 h of immersion.

Reactive species in RF plasma sputtering deposition of nanocrystalline calcium phosphate bio-active films

Optical emission of reactive plasma species during the synthesis of functionally graded calcium phosphate-based bioactive films has been investigated. The coatings have been deposited on Ti-6Al-4V orthopedic alloy by co-sputtering of hydroxyapatite (HA) and titanium targets in reactive plasmas of Ar + H2O gas mixtures. The species, responsible for the Ca-P-Ti film growth have been non-intrusively monitored in situ by a high-resolution optical emission spectroscopy (OES). It is revealed that the optical emission originating from CaO species dominates throughout the deposition process. The intensities of CaO, PO and CaPO species are strongly affected by variations of the operating pressure, applied RF power, and DC substrate bias. The optical emission intensity (OEI) of reaction species can efficiently be controlled by addition of H2O reactant.

Reactive Pulsed Laser Deposition of titanium nitride thin film: Optimization of process parameters using Secondary Ion Mass Spectrometry

Reactive Pulsed Laser Deposition is a single step process wherein the ablated elemental metal reacts with a low pressure ambient gas to form a compound. We report here a Secondary Ion Mass Spectrometry based analytical methodology to conduct minimum number of experiments to arrive at optimal process parameters to obtain high quality TiN thin film. Quality of these films was confirmed by electron microscopic analysis. This methodology can be extended for optimization of other process parameters and materials. (C) 2009 Elsevier B.V. All rights reserved.

Reactive pulsed laser deposition and characterization of niobium nitride thin films

We present a systematic study to explore the effect of important process variables on the composition and structure of niobium nitride thin films synthesized by Reactive Pulsed Laser Deposition (RPLD) technique through ablation of high purity niobium target in the presence of low pressure nitrogen gas. Secondary Ion Mass Spectrometry has been used in a unique way to study and fix gas pressure, substrate temperature and laser fluence, in order to obtain optimized conditions for one variable in single experimental run. The x-ray diffraction and electron microscopic characterization have been complemented by proton elastic backscattering spectroscopy and x-ray photoelectron spectroscopy to understand the incorporation of oxygen and associated non-stoichiometry in the metal to nitrogen ratio. The present study demonstrates that RPLD can be used for obtaining thin film architectures using non-equilibrium processing. Finally the optimized NbN thin films were characterized for their hardness using nano-indentation technique and found to be similar to 30 GPa at the deposition pressure of 8 Pa. (C) 2011 Elsevier B.V. All rights reserved.

Effect of post-deposition annealing on composition and electrical properties of dc reactive magnetron sputtered Al2O3 thin films

We have investigated the effect of post- deposition annealing on the composition and electrical properties of alumina (Al2O3) thin films. Al2O3 were deposited on n-type Si < 100 >. substrates by dc reactive magnetron sputtering. The films were subjected to post- deposition annealing at 623, 823 and 1023 K in vacuum. X-ray photoelectron spectroscopy results revealed that the composition improved with post- deposition annealing, and the film annealed at 1023 K became stoichiometric with an O/Al atomic ratio of 1.49. Al/Al2O3/Si metal-oxide-semiconductor (MOS) structures were then fabricated, and a correlation between the dielectric constant epsilon(r) and interface charge density Q(i) with annealing conditions were studied. The dielectric constant of the Al2O3 thin films increased to 9.8 with post- deposition annealing matching the bulk value, whereas the oxide charge density decreased to 3.11 x 10(11) cm(-2.) Studies on current-voltage IV characteristics indicated ohmic and Schottky type of conduction at lower electric fields (<0.16 MV cm(-1)) and space charge limited conduction at higher electric fields.

Deposition of c-axis orientation aluminum nitride films on flexible polymer substrates by reactive direct-current magnetron sputtering

Aluminum nitride (AlN) piezoelectric thin films with c-axis crystal orientation on polymer substrates can potentially be used for development of flexible electronics and lab-on-chip systems. In this study, we investigated the effects of deposition parameters on the crystal structure of AlN thin films on polymer substrates deposited by reactive direct-current magnetron sputtering. The results show that low sputtering pressure as well as optimized N 2/Ar flow ratio and sputtering power is beneficial for AlN (002) orientation and can produce a highly (002) oriented columnar structure on polymer substrates. High sputtering power and low N 2/Ar flow ratio increase the deposition rate. In addition, the thickness of Al underlayer also has a strong influence on the film crystallography. The optimal deposition parameters in our experiments are: deposition pressure 0.38 Pa, N 2/Ar flow ratio 2:3, sputtering power 414 W, and thickness of Al underlayer less than 100 nm. © 2012 Elsevier B.V. All rights reserved.