Effect of cement type and water storage time on the push-out bond strength of a glass fiber post

This study investigated the effects of the cement type and the water storage time on the push-out bond strength of a glass fiber post. Glass fiber posts (Fibrekor, Jeneric Pentron) were luted to post spaces using a self-cured resin cement (C&B Cement [CB]), a glass ionomer cement (Ketac Cem [KC]) or a resin-modified glass ionomer cement (GC FujiCEM [FC]) according to the manufacturers’ instructions. For each luting agent, the specimens were exposed to one of the following water storage times (n=5): 1 day (T1), 7 days (T7), 90 days (T90) and 180 days (T180). Push-out tests were performed after the storage times. Control specimens were not exposed to water storage, but subjected to the push-out test 10 min after post cementation. Data (in MPa) were analyzed by Kruskal-Wallis and Dunn`s test (α=0.05). Cement type and water storage time had a significant effect (p<0.05) on the push-out bond strength. CB showed significantly higher values of retention (p<0.05) than KC and FC, irrespective of the water storage time. Water storage increased significantly the push-out bond strength in T7 and T90, regardless of the cement type (p<0.05). The results showed that fiber posts luted to post spaces with the self-cured resin cement exhibited the best bonding performance throughout the 180-day water storage period. All cements exhibited a tendency to increase the bond strength after 7 and 90 days of water storage, decreasing thereafter.

Adhesion of an endodontic sealer to dentin and gutta-percha: shear and push-out bond strength measurements and SEM analysis

The use of an adequate method for evaluation of the adhesion of root canal filling materials provides more reliable results to allow comparison of the materials and substantiate their clinical choice. The aims of this study were to compare the shear bond strength (SBS) test and push-out test for evaluation of the adhesion of an epoxy-based endodontic sealer (AH Plus) to dentin and gutta-percha, and to assess the failure modes on the debonded surfaces by means of scanning electron microscopy (SEM). Three groups were established (n=7): in group 1, root cylinders obtained from human canines were embedded in acrylic resin and had their canals prepared and filled with sealer; in group 2, longitudinal sections of dentin cylinders were embedded in resin with the canal surface smoothed and turned upwards; in group 3, gutta-percha cylinders were embedded in resin. Polyethylene tubes filled with sealer were positioned on the polished surface of the specimens (groups 2 and 3). The push-out test (group 1) and the SBS test (groups 2 and 3) were performed in an Instron universal testing machine running at crosshead speed of 1 mm/min. Means (±SD) in MPa were: G1 (8.8±1.13), G2 (5.9±1.05) and G3 (3.8±0.55). Statistical analysis by ANOVA and Student's t-test (a=0.05) revealed statistically significant differences (p<0.01) among the groups. SEM analysis showed a predominance of adhesive and mixed failures of AH Plus sealer. The tested surface affected significantly the results with the sealer reaching higher bond strength to dentin than to gutta-percha with the SBS test. The comparison of the employed methodologies showed that the SBS test produced significantly lower bond strength values than the push-out test, was skilful in determining the adhesion of AH Plus sealer to dentin and gutta-percha, and required specimens that could be easily prepared for SEM, presenting as a viable alternative for further experiments.

Push-out Bond Strength of Fiber Posts Luted with Unfilled Resin Cement

Purpose: The study evaluates the behavior of different adhesive systems and resin cements in fiber post placement, with the intent to clarify the possible role of unfilled resin as a luting material for fiber posts. Materials and Methods: Two luting agents (Dual-Link and Unfilled Resin) for cementing fiber posts into root canals were applied either with All-Bond 2 or One-Step Plus, or without an adhesive system, and challenged with the push-out test. Slices of roots restored with posts were loaded until post segment extrusion in the apical-coronal direction. Failure modes were analyzed under SEM. Results: Push-out strength was significantly influenced by the luting agent (p < 0.05), but not by the bonding strategy (p > 0.05). The best results were obtained in combination with Unfilled Resin with One-Step Plus. Dual-Link groups failed mainly cohesively within the cement, while Unfilled Resin demonstrated more adhesive fracture at the post interface. Conclusion: The results of this study support the hypothesis that adhesive unfilled resin application is essential for achieving high bond strength to radicular dentin.

Effect of Resin Cement System and Root Region on the Push-out Bond Strength of a Translucent Fiber Post

Objectives: This study evaluated the bond strength of luting systems for bonding glass fiber posts to root canal dentin. The hypothesis tested was that there are no differences in bond strength of glass fiber posts luted with different cement systems.Methods: Forty bovine incisors were randomly assigned to five different resin cement groups (n=8). After endodontic treatment and crown removal, translucent glass fiber posts were bonded into the root canal using five different luting protocols (self-cured cement and etch-and-rinse adhesive system; dual-cured cement and etch-and-rinse adhesive system; self-cured cement and self-etch adhesive system; dual-cured cement and self-etch adhesive system; and dual-cured self-adhesive cement). Push-out bond strength was evaluated at three different radicular levels: cervical, middle, and apical. The interface between resinous cement and the post was observed using a stereoscopic microscope.Results: Analysis of variance showed a statistically significant difference among the cements (p<0.05) and the root canal thirds (p<0.05). The self-adhesive resinous cement had lower values of retention.Conclusions: The resin cements used with etch-and-rinse and self-etch adhesive systems seem to be adequate for glass fiber post cementation.

The Disk-Specimen Thickness Does Not Influence the Push-Out Bond Strength Results Between Fiber Post and Root Dentin

This study evaluated the effect of different thickness of disk-shaped specimens on the push-out bond strength test. Eighteen lower bovine teeth were sectioned (20mm) and prepared (15mm) with the same post system drill (Light Post (R) #1, Schaumburg, IL, Bisco, USA). The apical third of each specimen was embedded in a plastic matrix filled with an acrylic resin (Dencrilay (TM), Dencril, São Paulo, Brazil). The posts were cleaned with alcohol, silanated (ProSil (R), FGM, Joenville, SC, Brazil) and cemented with the RelyX (TM) U100 (3M ESPE, St. Paul, MN, USA). Each specimen was sectioned into three pieces of differing thicknesses (1, 2, and 4 mm). These disk-samples were allocated into 3 groups (n=18) and subjected to push-out testing. One-way ANOVA showed no influence of the specimen thickness on the results (p=0.842). No correlation was observed between thickness and push-out bond strength (Pearson Correlation, r(2)=0.0688; P=0.6209). The push-out bond strength test was not affected by the thickness of the disk-specimens.

Effect of mechanical cycling on the push-out bond strength of fiber posts adhesively bonded to human root dentin

This study evaluated the effect of mechanical cycling on the bond strength of fiber posts bonded to root dentin. The hypotheses examined were that bond strength is not changed after fatigue testing and bond strength does not present vast variations according to the type of fiber post. Sixty crownless, single-rooted human teeth were endodontically treated, with the space prepared at 12 mm. Thirty specimens received a quartz fiber post (Q-FRC (DT Light-Post), and the remaining 30 specimens received a glass fiber post (G-FRC) (FRC Postec Plus). All the posts were resin luted (All Bond+Duolink), and each specimen was embedded in a cylinder with epoxy resin. The specimens were divided into six groups: G1-Q-FRC+no cycling, G2- Q-FRC+20,000 cycles (load: 50N, angle of 45 degrees; frequency: 8Hz); G3- Q-FRC+2,000,000 cycles; G4- G-FRC+no cycling; G5- G-FRC+20,000 cycles; G6- GFRC+2,000,000 cycles. The specimens were cut perpendicular to their long axis, forming 2-mm thick disc-samples, which were submitted to the push-out test. ANOVA (alpha=.05) revealed that: (a) QFRC (7.1 +/- 2.2MPa) and G-FRC (6.9 +/- 2.1MPa) were statistically similar (p=0.665); (b) the no cycling groups (7.0 +/- 2.4MPa), 20,000 cycles groups (7.0 +/- 2.1MPa) and 2,000,000 cycles groups (7.0 +/- 2.0MPa) were statistically similar (p=0.996). It concluded that mechanical cycling did not affect the bond strength of two fiber posts bonded to dentin.

Fiber Post Cementation Strategies: Effect of Mechanical Cycling on Push-out Bond Strength and Cement Polymerization Stress

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Evaluation of the Interaction Between Sodium Hypochlorite and Several Formulations Containing Chlorhexidine and its Effect on the Radicular Dentin-SEM and Push-Out Bond Strength Analysis

The aim of the current study was to evaluate the presence of debris and smear layer after endodontic irrigation with different formulations of 2% chlorhexidine gluconate (CHX) and its effects on the push-out bond strength of an epoxy-based sealer on the radicular dentin. One hundred extracted human canines were prepared to F5 instrument and irrigated with 2.5% sodium hypochlorite and 17% ethylenediaminetetraacetic acid. Fifty teeth were divided into five groups (n=10), according to the final irrigation protocol with different 2% CHX formulations: G1 (control, no final rinse irrigation), G2 (CHX solution), G3 (CHX gel), G4 (Concepsis), and G5 (CHX Plus). In sequence, the specimens were submitted to scanning electron microscopy (SEM) analysis, in the cervical-medium and medium-apical segments, to evaluate the presence of debris and smear layer. The other 50 teeth were treated equally to a SEM study, but with the root canals filled with an epoxy-based endodontic sealer and submitted to a push-out bond strength test, in the cervical, middle, and apical thirds. G2, G3, G4, and G5 provided higher precipitation of the debris and smear layer than G1 (P<0.05), but these groups were similar to each other (P>0.05), in both segments. The values obtained in the push out test did not differ between groups, independent of the radicular third (P>0.05). The CHXs formulations caused precipitation of the debris and smear layer on the radicular dentin, but these residues did not interfere in the push-out bond strength of the epoxy-based sealer. Microsc. Res. Tech. 77:17-22, 2014. (c) 2013 Wiley Periodicals, Inc.

Evaluation of the physicochemical properties and push-out bond strength of mta-based root canal cement

Aim: This study investigated the flowability, setting time, pH, calcium release and bond strength of a MTA-based cement (MTA Fillapex®) compared to AH Plus and Sealapex. Materials and methods: For the flowability test, the ISO 6876:2001 specification was utilized and for the setting time test, the ASTM C266-03 specification was utilized. For the pH and calcium release measurements, 10 samples were prepared for each group and analyzed for several different periods. For the push-out test, dentin disks were distributed into three groups, according to the cement utilized and into three subgroups, according to the root third (n = 10). After obturation, the specimens underwent push-out testing. The data were compared statistically using a significance level of 5%. Results: The flowability of all materials was found to be similar (p > 0.05). The setting times were different among the groups tested (MTA Fillapex < Sealapex < AH Plus) (p < 0.05). At days 7 and 28, the MTA Fillapex presented the higher pH values (p < 0.05). At 24 hours and at 14 days, the calcium release of the MTA Fillapex was similar to that of Sealapex (p > 0.05). AH Plus presented the lowest pH and calcium release values (p < 0.05). In all root thirds, the adhesion to the dentin of the MTA Fillapex and Sealapex were significantly lower than that of AH Plus (p < 0.05). Conclusion: MTA Fillapex and Sealapex presented several similar properties and both were found to be different than AH Plus. Clinical significance: This study evaluated the physicochemical and mechanical properties of new MTA-based root canal cement, in order to use this scaler in root canal fillings. MTA Fillapex showed satisfactory properties for clinical use.

Push-out bond strength of calcium hydroxide and mineral trioxide aggregate based sealers

The adhesiveness of six root canal sealers: Acroseal, Endo CPM, Epiphany, White MTA, Sealapex and Sealer 26 to dentin, was evaluated in a push-out test design. Methods: Twenty eight roots of freshly extracted teeth were gauged with a size 5 Largo drill. With a cutting machine slices of 2 mm were prepared, rinsed with 5.25% NaOCl and a final rinse with 17% EDTA, dried and filled with one of the sealers. After setting their bond strength was measured in a mechanical testing machine. The data were statistically analyzed by using a One Way ANOVA and post hoc Tukey test. Results: The mean and standard deviation from values of bond strength was: Sealapex 2.2±0.4; Endo CPM 3.8±1.3; White MTA 6.0±1.4; Epiphany 10.9±2.6; Sealer 26 12.3±2.3; and Acroseal 12.2±1.4. Acroseal, Sealer 26 and Epiphany presented a significantly (P<0.01) greater bond strength compared with the other sealers. Also White MTA showed higher adhesiveness compared with Endo CPM and Sealapex (P<0.01). Conclusion: The bond strength between endodontic sealers and root dentin was maximal when Acroseal, Sealer 26 and Epiphany were used; Sealapex e Endo CPM, in turn, presented the lowest bond strength mean values.

Effect of calcium hydroxide dressing on push-out bond strength of endodontic sealers to root canal dentin

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Push-out bond strength of fiber posts to root dentin using glass ionomer and resin modified glass ionomer cements

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Multi-step adhesive cementation versus one-step adhesive cementation: push-out bond strength between fiber post and root dentin before and after mechanical cycling

This study evaluated the effects of mechanical cycling on resin push-out bond strength to root dentin, using two strategies for fiber post cementation. Forty bovine roots were embedded in acrylic resin after root canal preparation using a custom drill of the fiber post system. The fiber posts were cemented into root canals using two different strategies (N = 20): a conventional adhesive approach using a three-step etch-and-rinse adhesive system combined with a conventional resin cement (ScotchBond Multi Purpose Plus + RelyX ARC ), or a simplified adhesive approach using a self-adhesive resin cement (RelyX U100). The core was built up with composite resin and half of the specimens from each cementation strategy were submitted to mechanical cycling (45 degree angle; 37 degrees C; 88 N; 4 Hz; 700,000 cycles). Each specimen was cross-sectioned and the disk specimens were pushed-out. The means from every group (n = 10) were statistically analyzed using a two-way ANOVA and a Tukey test (P = 0.05). The cementation strategy affected the push-out results (P < 0.001), while mechanical cycling did not (P = 0.3716). The simplified approach (a self-adhesive resin cement) had better bond performance despite the conditioning. The self-adhesive resin cement appears to be a good option for post cementation. Further trials are needed to confirm these results.

Fiber Post Cementation Strategies: Effect of Mechanical Cycling on Push-out Bond Strength and Cement Polymerization Stress

Purpose: To evaluate the effect of mechanical cycling and cementation strategies on the push-out bond strength between fiber posts and root dentin and the polymerization stresses produced using three resin cements. Materials and Methods: Eighty bovine mandibular teeth were sectioned to a length of 16 mm, prepared to 12 mm, and embedded in self-curing acrylic resin. The specimens were then distributed into 8 groups (n = 10): Gr1 - Scotchbond Multi Purpose + RelyX ARC; Gr2 - Scotchbond Multi Purpose + RelyX ARC + mechanical cycling; Gr3 - AdheSE + Multilink Automix; Gr4 - AdheSE + Multilink Automix + mechanical cycling; Gr5 - phosphoric acid + RelyX U100 (self-adhesive cement); Gr6 - phosphoric acid+ RelyX U100 + mechanical cycling; Gr7 - RelyX U100; Gr8 - RelyX U100 + mechanical cycling. The values obtained from the push-out bond strength test were submitted to two-way ANOVA and Tukey's test (p = 0.05), while the values obtained from the polymerization stress test were subjected to one-way ANOVA and Tukey's test (alpha = 0.05). Results: Mechanical cycling did not affect the bond strength values (p = 0.236), while cementation strategies affected the push-out bond strength (p < 0.001). Luting with RelyX U100 and Scotch Bond Multi Purpose + RelyX ARC yielded higher push-out bond strength values. The polymerization stress results were affected by the factor "cement" (p = 0.0104): the self-adhesive cement RelyX U100 exhibited the lowest values, RelyX ARC resulted in the highest values, while Multi link Automix presented values statistically similar to the other two cements. Conclusion: The self-adhesive cement appears to be a good alternative for luting fiber posts due to the high push-out bond strengths and lower polymerization stress values.

Push-out bond strength and SEM evaluation of a new bonding approach into the root canal

Objective: This study evaluated the performance of different adhesive systems in fiber post placement aiming to clarify the influence of different hydrophobic experimental blend adhesives, and of one commercially available adhesive on the frictional retention during a luting procedure. Material and Methods: One luting agent (70 Wt% BisGMA, 28.5% TEGDMA; 1.5% p-tolyldiethanolamine) to cement fiber posts into root canals was applied with 4 different adhesive combinations: Group 1: The etched roots were rinsed with water for 30 s to remove the phosphoric acid, then rinsed with 99.6% ethanol for 30 s, and blot-dried. A trial adhesive (base to catalyst on a 1: 1 ratio) was used with an experimental luting agent (35% Bis-GMA, 14.37% TEGDMA, 0.5% EDMAB, 0.13% CQ); Group 2: A trial adhesive (base to catalyst on a 1: 2 ratio) was luted as in Group 1; Group 3: One-Step Plus (OSP, Bisco Inc.) following the ethanol bonding technique in combination with the luting agent as in Group 1; Group 4: OSP strictly following the manufacturer's instructions using the luting agent as in Group 1. The groups were challenged with push-out tests. Posted root slices were loaded until post segment extrusion in the apical-coronal direction. Failure modes were analyzed under scanning electron microscopy. Results: Push-out strength was not significantly influenced by the luting agent (p>0.05). No statistically significant differences among the tested groups were found as Group 1 (Exp 1 - ethanol-wet bonding technique)=Group 2 (Exp 2 - ethanol-wet bonding technique)= Group 3 (OSP - ethanol-wet bonding technique)= Group 4 (control, OSP - water-wet bonding technique) (p>0.05). The dominating failure modes in all the groups were cohesive/adhesive failures, which were predominantly observed on the post/luting agent interface. Conclusions: The results of this study support the hypothesis that the proposal to replace water with ethanol to bond fiber posts to the root canal using highly hydrophobic resin is plausible, but this seems to be more the proof of a concept than a clinically applicable procedure.