基底微缺陷对介质薄膜光学性能影响的理论研究

基于非均匀膜理论提出一种存在微缺陷的介质基底的折射率分层模型，将基底依次分为表面层、亚表面层和体材料层，其中表面层和亚面层分别等效为折射率服从统计分布的非均匀膜，将它们分别再次细分为N1和N2个子层，每一子层均视为均匀介质膜．应用光学薄膜特征矩阵法对其进行理论分析，并对单层介质膜的光学性能进行数值计算．研究结果表明：基底的表面和亚表面微缺陷改变了薄膜和基底的等效折射率，导致了准Brewster角和组合反射率与理想情形的偏离．同时这些微缺陷也改变了光在薄膜和基底中的传播特性，因此反射相移和相位差均偏离理想情

微缺陷对薄膜滤光片环境稳定性的影响

用热蒸发方法沉积了薄膜滤光片．并将样品分别在去离子水中浸泡10天和30天．通过分光光度计、光学暗场显微镜、及扫描电子显微镜等多种测试手段，对诱导透射滤光片在潮湿环境下的稳定性进行了研究．实验发现，在潮湿环境下滤光片产生的膜层分离都是从薄膜中微缺陷点处开始发生和发展的，微缺陷是影响滤光片环境稳定性的重要原因之一，其中杂质和针孔是滤光片中两种最常见的微缺陷．EDS能谱分析进一步表明，薄膜中杂质缺陷成分即为Al2O3膜料本身，所以不能推测，薄膜沉积中的喷溅可能是微缺陷产生的根本原因，抑制喷溅可以有效提高薄膜滤光

Working pressure dependence of properties of Al2O3 thin films prepared by electron beam evaporation

The effects of working pressure on properties of Al2O3 thin films are investigated. Transmittance of the Al2O3 thin film is measured by a Lambda 900 spectrometer. Laser-induced damage threshold (LIDT) is measured by a Nd:YAG laser at 355nm with a pulse width of 7ns. Microdefects were observed under a Nomarski microscope. The samples are characterized by optical properties and defect, as well as LIDT under the 355 nm Nd: YAG laser radiation. It is found that the working pressure has fundamental effect on the LIDT. It is the absorption rather than the microdefect that plays an important role on the LID T of Al2O3 thin film.

SiO2保护层和退火对Ta2O5薄膜激光损伤阈值影响的对比研究

Ta2O5薄膜采用传统的电子束蒸发方法沉积在BK7基底上。文中对SiO2保护层和退火对Ta2O5薄膜的激光损伤阈值的不同影响进行了研究。结果表明，SiO2保护层不会影响薄膜内的电场分布，薄膜微结构和微缺陷密度，但是会使薄膜的吸收稍微增大；而退火对降低薄膜的微缺陷密度和吸收较有效。SiO2保护层和退火都有利于提高Ta2O5薄膜的抗激光损伤能力，并且退火对提高阈值的影响更为明显。此外，采用SiO2保护层和退火结合的方法，获得了具有最大激光损伤阈值的薄膜。

不同方法制备的Ta_2O_5薄膜光学性能和激光损伤阈值的对比分析

采用电子束蒸发(EBE)和离子束溅射(IBS)制备了不同的Ta_2O_5薄膜,同时对电子束蒸发制备的薄膜进行了退火处理。研究了制备的Ta_2O_5薄膜的光学性能、激光损伤阈值(LIDT)、吸收、散射、粗糙度、微缺陷密度和杂质含量。结果表明,退火可使电子束蒸发制备的薄膜的光学性能得到改善,接近离子束溅射的薄膜的光学性能。电子束蒸发制备的薄膜的损伤阈值较低的主要原因在于吸收大,微缺陷密度和杂质含量高,而与薄膜的散射和粗糙度关系不大。退火后薄膜的吸收和微缺陷密度都明显降低,损伤阈值得到提高。退火后的薄膜损伤阈值仍然低于溅射得到的薄膜损伤阈值是因为退火并不能降低膜内的杂质含量,因此选用高纯度的蒸发膜料和减少电子束蒸发过程中的污染有可能进一步提高薄膜的损伤阈值。

Electrical properties of GaN deposited on nitridated sapphire by molecular beam epitaxy using NH3 cracked on the growing surface

We have found that GaN epilayers grown by NH3-source molecular beam epitaxy (MBE) contain hydrogen. Dependent on the hydrogen concentration, GaN on (0001) sapphire can be either under biaxially compressive strain or under biaxially tensile strain. Furthermore, we notice that background electrons in GaN increase with hydrogen incorporation. X-ray photoelectron spectroscopy (XPS) measurements of the N1s region indicate that hydrogen is bound to nitrogen. So, the microdefect Ga...H-N is an effective nitrogen vacancy in GaN, and it may be a donor partly answering for the background electrons. (C) 1999 Elsevier Science B.V. All rights reserved.

Electrical properties of GaN deposited on nitridated sapphire by molecular beam epitaxy using NH3 cracked on the growing surface

We have found that GaN epilayers grown by NH3-source molecular beam epitaxy (MBE) contain hydrogen. Dependent on the hydrogen concentration, GaN on (0001) sapphire can be either under biaxially compressive strain or under biaxially tensile strain. Furthermore, we notice that background electrons in GaN increase with hydrogen incorporation. X-ray photoelectron spectroscopy (XPS) measurements of the N1s region indicate that hydrogen is bound to nitrogen. So, the microdefect Ga...H-N is an effective nitrogen vacancy in GaN, and it may be a donor partly answering for the background electrons. (C) 1999 Elsevier Science B.V. All rights reserved.