Estudo da influência da temperatura de brasagem nas uniões zircônia/aço inox 304 utilizando metalização mecânica

Metal-Ceramic (M/C) Zirconia-stainless steel interfaces have been processed through brazing techniques due to the excellent combination of properties such as high temperature stability, high corrosion resistance and good mechanical properties. However, some M/C interfaces show some defects, like porosity and cracks results in the degradation of the interfaces, leading even to its total rupture. Most of time, those defects are associated with an improper brazing parameters selection to the M/C system. In this work, ZrO2 Y-TZP and ZrO2 Mg - PSZ were joint with the stainless steel grade 304 by brazing using a eutectic silver-copper (Ag28Cu) interlayer alloy with different thermal cycles. Ceramic surfaces were previous mechanically metallized with titanium to improve adhesion of the system. The effect of temperature on the M/C interface was studied. SEM-EDS and 3 point flexural bend test were performed to evaluate morphology, chemical composition and mechanical resistance of the M/C interfaces. Lower thermal cycle temperatures produced better results of mechanical resistance, and more regular/ homogeneous reaction layers between braze alloy and metal-ceramic surfaces. Also was proved the AgCu braze alloy activation in situ by titanium

Estudo da influência da temperatura de brasagem nas uniões zircônia/aço inox 304 utilizando metalização mecânica

Metal-Ceramic (M/C) Zirconia-stainless steel interfaces have been processed through brazing techniques due to the excellent combination of properties such as high temperature stability, high corrosion resistance and good mechanical properties. However, some M/C interfaces show some defects, like porosity and cracks results in the degradation of the interfaces, leading even to its total rupture. Most of time, those defects are associated with an improper brazing parameters selection to the M/C system. In this work, ZrO2 Y-TZP and ZrO2 Mg - PSZ were joint with the stainless steel grade 304 by brazing using a eutectic silver-copper (Ag28Cu) interlayer alloy with different thermal cycles. Ceramic surfaces were previous mechanically metallized with titanium to improve adhesion of the system. The effect of temperature on the M/C interface was studied. SEM-EDS and 3 point flexural bend test were performed to evaluate morphology, chemical composition and mechanical resistance of the M/C interfaces. Lower thermal cycle temperatures produced better results of mechanical resistance, and more regular/ homogeneous reaction layers between braze alloy and metal-ceramic surfaces. Also was proved the AgCu braze alloy activation in situ by titanium

The adherence of Pseudomonas fluorescens to marble, granite, synthetic polymers, and stainless steel

The adherence of Pseudomonas fluorescens cells to nine food-processing contact surfaces was evaluated using the plate-count method. The surfaces include marble, granite, stainless steel, polyvinyl chloride, polyurethane, and silicone-coated cloth, which have been used only in a few studies concerning bacterial adherence. The number of cells adhered to the surfaces increased with contact time reaching 5.0-6.1 log CDM.cm-2 after 10 hours, which can be considered a well established adherence process. The number of adhered cells doubled in 29.5 minutes and 23.5 minutes on stainless steel and thin polyvinyl chloride-coated cloth, respectively. For the other surfaces, this value was 9.8 minutes on average. Marble, granite, thick polyvinyl-coated cloth, double-faced rugous polyurethane, and silicone-coated cloth were not different (p < 0.05) in their ability to adhere cells (CFU/cm²) after 2 and 10 hours. The surfaces that had higher percentage of similarity in the adhesion level and higher log CFU/cm² of adhered cells were double-faced rugous polyurethane, silicone-coated cloth, and granite. The surfaces showed very different microtopography characteristics when viewed using scanning electron microscopy. This experiment showed the importance of using appropriate materials for food contact during processing, which will affect the cleaning and sanitation procedures.

A comparative study to evaluate surface microbial contamination associated with copper-containing and stainless steel pens used by nurses in the critical care unit

A clinical study was undertaken to compare the surface microbial contamination associated with pens constructed of either a copper alloy or stainless steel used by nurses on intensive care units. A significantly lower level of microbial contamination was found on the copper alloy pens. Copyright © 2011 by the Association for Professionals in Infection Control and Epidemiology, Inc. Published by Elsevier Inc. All rights reserved.

Does the casting mode influence microstructure, fracture and properties of different metal ceramic alloys?

The aim of the present study was to evaluate the tensile strength, elongation, microhardness, microstructure and fracture pattern of various metal ceramic alloys cast under different casting conditions. Two Ni-Cr alloys, Co-Cr and Pd-Ag were used. The casting conditions were as follows: electromagnetic induction under argon atmosphere, vacuum, using blowtorch without atmosphere control. For each condition, 16 specimens, each measuring 25 mm long and 2.5 mm in diameter, were obtained. Ultimate tensile strength (UTS) and elongation (EL) tests were performed using a Kratos machine. Vickers Microhardness (VM), fracture mode and microstructure were analyzed by SEM. UTS, EL and VM data were statistically analyzed using ANOVA. For UTS, alloy composition had a direct influence on casting condition of alloys (Wiron 99 and Remanium CD), with higher values shown when cast with Flame/Air (p < 0.05). The factors "alloy" and "casting condition" influenced the EL and VM results, generally presenting opposite results, i.e., alloy with high elongation value had lower hardness (Wiron 99), and casting condition with the lowest EL values had the highest VM values (blowtorch). Both factors had significant influence on the properties evaluated, and prosthetic laboratories should select the appropriate casting method for each alloy composition to obtain the desired property.

Correlation between metal-ceramic bond strength and coefficient of linear thermal expansion difference

The purpose of this study was to evaluate the metal-ceramic bond strength (MCBS) of 6 metal-ceramic pairs (2 Ni-Cr alloys and 1 Pd-Ag alloy with 2 dental ceramics) and correlate the MCBS values with the differences between the coefficients of linear thermal expansion (CTEs) of the metals and ceramics. Verabond (VB) Ni-Cr-Be alloy, Verabond II (VB2), Ni-Cr alloy, Pors-on 4 (P), Pd-Ag alloy, and IPS (I) and Duceram (D) ceramics were used for the MCBS test and dilatometric test. Forty-eight ceramic rings were built around metallic rods (3.0 mm in diameter and 70.0 mm in length) made from the evaluated alloys. The rods were subsequently embedded in gypsum cast in order to perform a tensile load test, which enabled calculating the CMBS. Five specimens (2.0 mm in diameter and 12.0 mm in length) of each material were made for the dilatometric test. The chromel-alumel thermocouple required for the test was welded into the metal test specimens and inserted into the ceramics. ANOVA and Tukey's test revealed significant differences (p=0.01) for the MCBS test results (MPa), with PI showing higher MCBS (67.72) than the other pairs, which did not present any significant differences. The CTE (10-6 oC-1) differences were: VBI (0.54), VBD (1.33), VB2I (-0.14), VB2D (0.63), PI (1.84) and PD (2.62). Pearson's correlation test (r=0.17) was performed to evaluate of correlation between MCBS and CTE differences. Within the limitations of this study and based on the obtained results, there was no correlation between MCBS and CTE differences for the evaluated metal-ceramic pairs.

Joining copper to stainless steel by friction stir diffusion process

Dissertação apresentada na Faculdade de Ciências e Tecnologia da Universidade Nova de Lisboa para obtenção do Grau de Mestre em Engenharia Mecânica

EFFECT OF METAL PRIMERS ON MICROTENSILE BOND STRENGTH BETWEEN ZIRCONIA AND RESIN CEMENTS

Statement of problem. There are no established clinical procedures for bonding zirconia to tooth structure using resin cements. Purpose. The purpose of this study was to evaluate the influence of metal primers, resin cements, and aging on bonding to zirconia. Material and methods. Zirconia was treated with commercial primers developed for bonding to metal alloys (Metaltite, Metal Primer II, Alloy Primer or Totalbond). Non-primed specimens were considered as controls. One-hundred disk-shaped specimens (19 x 4 mm) were cemented to composite resin substrates using Panavia or RelyX Unicem (n=5). Microtensile bond strength specimens were tested after 48 hours and 5 months (150 days), and failure modes were classified as type 1 (between ceramic/cement), 2 (between composite resin/cement) or 3 (mixed). Data were analyzed by 3-way ANOVA and Multiple Comparison Tukey test (alpha=.05). Results. The interactions primer/luting system (P=.016) and luting system/storage time (P=.004) were statistically significant. The use of Alloy Primer significantly improved the bond strength of RelyX Unicem (P<.001), while for Panavia, none of the primers increased the bond strength compared to the control group. At 48 hours, Panavia had statistically higher bond strength (P=.004) than Unicem (13.9 +/- 4.4MPa and 10.2 +/- 6.6MPa, respectively). However, both luting systems presented decreasing, statistically similar; values after aging (Panavia: 3.6 +/- 2.2MPa; Unicem: 6.1 +/- 5.3MPa). At 48 hours, Alloy Primer/Unicem had the lowest incidence of type 1 failure (8%). After aging, all the groups showed a predominance of type 1 failures. Conclusions. The use of Alloy Primer improved bond strength between RelyX Unicem and zirconia. Though the initial values obtained with Panavia were significantly higher than RelyX Unicem, after aging, both luting agents presented statistically similar performances. (J Prosthet Dent 2011;105:296-303)

Microstructure, mechanical properties and chemical degradation of brazed AISI 316 stainless steel/alumina systems

The main aims of the present study are simultaneously to relate the brazing parameters with: (i) the correspondent interfacial microstructure, (ii) the resultant mechanical properties and (iii) the electrochemical degradation behaviour of AISI 316 stainless steel/alumina brazed joints. Filler metals on such as Ag–26.5Cu–3Ti and Ag–34.5Cu–1.5Ti were used to produce the joints. Three different brazing temperatures (850, 900 and 950 °C), keeping a constant holding time of 20 min, were tested. The objective was to understand the influence of the brazing temperature on the final microstructure and properties of the joints. The mechanical properties of the metal/ceramic (M/C) joints were assessed from bond strength tests carried out using a shear solicitation loading scheme. The fracture surfaces were studied both morphologically and structurally using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction analysis (XRD). The degradation behaviour of the M/C joints was assessed by means of electrochemical techniques. It was found that using a Ag–26.5Cu–3Ti brazing alloy and a brazing temperature of 850 °C, produces the best results in terms of bond strength, 234 ± 18 MPa. The mechanical properties obtained could be explained on the basis of the different compounds identified on the fracture surfaces by XRD. On the other hand, the use of the Ag–34.5Cu–1.5Ti brazing alloy and a brazing temperature of 850 °C produces the best results in terms of corrosion rates (lower corrosion current density), 0.76 ± 0.21 μA cm−2. Nevertheless, the joints produced at 850 °C using a Ag–26.5Cu–3Ti brazing alloy present the best compromise between mechanical properties and degradation behaviour, 234 ± 18 MPa and 1.26 ± 0.58 μA cm−2, respectively. The role of Ti diffusion is fundamental in terms of the final value achieved for the M/C bond strength. On the contrary, the Ag and Cu distribution along the brazed interface seem to play the most relevant role in the metal/ceramic joints electrochemical performance.

Survival of zirconia- and metal-supported fixed dental prostheses: a systematic review

Purpose: The aim of this review was to systematically evaluate and compare the frequency of veneer chipping and core fracture of zirconia fixed dental prostheses (FOPS) and porcelain-fused-to-metal (PFM) FDPs and determine possible influencing factors. Materials and Methods: The SCOPUS database and International Association of Dental Research abstracts were searched for clinical studies involving zirconia and PFM FDPs. Furthermore, studies that were integrated into systematic reviews on PFM FDPs were also evaluated. The principle investigators of any clinical studies on zirconia FDPs were contacted to provide additional information. Based on the available information for each FOP, a data file was constructed. Veneer chipping was divided into three grades (grade 1 = polishing, grade 2 = repair, grade 3 = replacement). To assess the frequency of veneer chipping and possible influencing factors, a piecewise exponential model was used to adjust for a study effect. Results: None of the studies on PFM FDPs (reviews and additional searching) sufficiently satisfied the criteria of this review to be included. Thirteen clinical studies on zirconia FDPs and two studies that investigated both zirconia and PFM FDPs were identified. These studies involved 664 zirconia and 134 PFM FDPs at baseline. Follow-up data were available for 595 zirconia and 127 PFM FDPs. The mean observation period was approximately 3 years for both groups. The frequency of core fracture was less than 1% in the zirconia group and 0% in the PFM group. When all studies were included, 142 veneer chippings were recorded for zirconia FDPs (24%) and 43 for PFM FDPs (34%). However, the studies differed extensively with regard to veneer chipping of zirconia: 85% of all chippings occurred in 4 studies, and 43% of all chippings included zirconia FDPs. If only studies that evaluated both types of core materials were included, the frequency of chipping was 54% for the zirconia-supported FDPs and 34% for PFM FDPs. When adjusting the survival rate for the study effect, the difference between zirconia and PFM FDPs was statistically significant for all grades of chippings (P = .001), as well as for chipping grade 3 (P = .02). If all grades of veneer chippings were taken into account, the survival of PFM FDPs was 97%, while the survival rate of the zirconia FDPs was 90% after 3 years for a typical study. For both PFM and zirconia FDPs, the frequency of grades 1 and 2 veneer chippings was considerably higher than grade 3. Veneer chipping was significantly less frequent in pressed materials than in hand-layered materials, both for zirconia and PFM FDPs (P = .04). Conclusions: Since the frequency of veneer chipping was significantly higher in the zirconia FDPs than PFM FDPs, and as refined processing procedures have started to yield better results in the laboratory, new clinical studies with these new procedures must confirm whether the frequency of veneer chipping can be reduced to the level of PFM. Int J Prosthodont 2010;23:493-502

Effect of Airborne-Particle Abrasion and Mechanico-Thermal Cycling on the Flexural Strength of Glass Ceramic Fused to Gold or Cobalt-Chromium Alloy

Purpose: To evaluate the effect of airborne-particle abrasion and mechanico-thermal cycling on the flexural strength of a ceramic fused to cobalt-chromium alloy or gold alloy.Materials and Methods: Metallic bars (n = 120) were made (25 mm x 3 mm x 0.5 mm): 60 with gold alloy and 60 with Co-Cr. At the central area of the bars (8 mm x 3 mm), a layer of opaque ceramic and then two layers of glass ceramic (Vita VM13, Vita Zahnfabrick) were fired onto it (thickness: 1 mm). Ten specimens from each alloy group were randomly allocated to a surface treatment [(tungsten bur or air-particle abrasion (APA) with Al(2)O(3) at 10 mm or 20 mm away)] and mechanico-thermal cycling (no cycling or mechanically loaded 20,000 cycles; 10 N distilled water at 37 degrees C and then thermocycled 3000 cycles; 5 degrees C to 55 degrees C, dwell time 30 seconds) combination. Those specimens that did not undergo mechanico-thermal cyclingwere stored inwater (37 degrees C) for 24 hours. Bond strength was measured using a three-point bend test, according to ISO 9693. After the flexural strength test, failure types were noted. The data were analyzed using three factor-ANOVA and Tukey's test (alpha = 0.05).Results: There were no significant differences between the flexural bond strength of gold and Co-Cr groups (42.64 +/- 8.25 and 43.39 +/- 10.89 MPa, respectively). APA 10 and 20 mm away surface treatment (45.86 +/- 9.31 and 46.38 +/- 8.89 MPa, respectively) had similar mean flexural strength values, and both had significantly higher bond strength than tungsten bur treatment (36.81 +/- 7.60 MPa). Mechanico-thermal cycling decreased the mean flexural strength values significantly for all six alloy-surface treatment combinations tested when compared to the control groups. The failure type was adhesive in the metal/ceramic interface for specimens surface treated only with the tungsten bur, and mixed for specimens surface treated with APA 10 and 20 mm.Conclusions: Considering the levels adopted in this study, the alloy did not affect the bond strength; APA with Al(2)O(3) at 10 and 20 mm improved the flexural bond strength between ceramics and alloys used, and the mechanico-thermal cycling of metal-ceramic specimens resulted in a decrease of bond strength.

Internal fit of two all-ceramic systems and metal-ceramic crowns

Objectives: The aim of this study was to investigate the internal fit (IF) of glass-infiltrated alumina (ICA - In-Ceram Alumina), yttria-stabilized tetragonal zirconia polycrystals (Y-TZP - IPS e.max ZirCAD), and metal-ceramic (MC - Ni-Cr alloy) crowns. Material and Methods: Sixty standardized resin-tooth replicas of a maxillary first molar were produced for crown placement and divided into 3 groups (n=20 each) according to the core material used (metal, ICA or Y-TZP). The IF of the crowns was measured using the replica technique, which employs a light body polyvinyl siloxane impression material to simulate the cement layer thickness. The data were analyzed according to the surfaces obtained for the occlusal space (OS), axial space (AS) and total mean (TM) using two-way ANOVA with Tukey's multiple comparison test (p<0.05). Results: No differences among the different areas were detected in the MC group. For the Y-TZP and ICA groups, AS was statistically lower than both OS and TM. No differences in AS were observed among the groups. However, OS and TM showed significantly higher values for ICA and Y-TZP groups than MC group. Comparisons of ICA and Y-TZP revealed that OS was significantly lower for Y-TZP group, whereas no differences were observed for TM. Conclusions: The total mean achieved by all groups was within the range of clinical acceptability. However, the metal-ceramic group demonstrated significantly lower values than the all-ceramic groups, especially in OS.