用高速阴影技术研究K9玻璃中的失效波=Investigations of Failure Waves in K9 Glass Using Shadowgraph

用高速阴影摄影技术研究了爆轰加载下K9 玻璃样品中波的传播和压缩区内损伤破坏的物理图象 和规律。实验中观测到冲击波阵面后有一个移动速度为2. 1～2. 2 mm/μs 的黑色阴影区边界,即失效波(Failure wave) ;实验发现只有当冲击载荷接近材料的HEL 时,在冲击波和失效波之间的区域才有少量的微裂纹成 核和长大,而在冲击载荷较低时却没有观察到;同时实验中观测到失效波萌生于被撞击面,并在两块玻璃的交 界面上观测到失效波的再生。这些结果表明失效波的产生基本与冲击相变无关,主要与玻璃样品表面的初始 损伤有关,换言之,失效波是玻璃样品表面微裂纹在冲击波作用下失稳扩展造成的。

K9玻璃薄膜对离子交换磷酸盐玻璃波导表面保护的优化研究

采用镀K9玻璃薄膜方法来解决离子交换掺铒磷酸盐玻璃波导表面的侵蚀问题,对K9玻璃薄膜的厚度进行了优化研究。测量分析了样品的荧光光谱和荧光寿命,采用光学显微镜和棱镜耦合技术对不同K9玻璃薄膜厚度下制备波导的表面形貌和导光特性进行了表征和测试。结果表明,与掺铒磷酸盐玻璃原材料相比,镀K9玻璃薄膜后荧光光谱保持不变,荧光寿命稍有下降(约0.2 ms);K9玻璃薄膜的厚度在60~80 nm的范围内保护效果最佳。为下一步制备掺铒有源玻璃光波导器件奠定了良好的实验基础。

掺铒磷酸盐玻璃离子交换波导表面保护的研究

对离子交换波导制备过程中掺铒磷酸盐玻璃表面的侵蚀问题进行了研究，分析了产生侵蚀的原因，提出镀K9玻璃薄膜的方法，对掺铒磷酸盐玻璃表面进行保护．采用光学显微镜和原子力显微镜对波导表面特性进行了表征。同时对平板波导的光学特性进行了测试．研究表明K9玻璃薄膜不仅能够对掺铒磷酸盐玻璃起到保护作用，同时允许交换离子透过进入磷酸盐玻璃形成波导层．

Wideband antireflection film fabricated by glancing angle deposition

Graded-index ZrO2 films has been fabricated on K9 glass by glancing angle deposition. Because the index mismatch at the interface has been reduced, the film results in wideband high-transmission antireflection. From 400nm to 1200nm, the film reflection is lower than 0.8% and the lowest value is 0.2% at 432nm.

Optical properties and structure of Sb-rich AgInSbTe phase change thin films

A new composition content quaternary-alloy-based phase change thin film, Sb-rich AgInSbTe, has been prepared by DC-magnetron sputtering on a K9 glass substrate. After the film has been subsequently annealed at 200degreesC for 30 min, it becomes a crystalline thin film. The diffraction peak of antimony (Sb) are observed by shallow (0.5 degree) x-ray diffraction in the quaternary alloy thin film. The analyses of the measurement from differential scanning calorimetry (DSC) show that the crystallization temperature of the phase change thin film is about 190degreesC and increases with the heating rate. By Kissinger plot, the activation energy for crystallization is determined to be 3.05eV. The reflectivity, refractive index and extinction coefficient of the crystalline and amorphous phase change thin films are presented. The optical absorption coefficient of the phase change thin films as a function of photon energy is obtained from the extinction coefficient. The optical band gaps of the amorphous and crystallization phase change thin films are 0.265eV and 1.127eV, respectively.

Synthesis of nickel(II) complexes of alpha-isoxazolylazo-beta-diketones and their absorption of spin-coating films and thermal properties for HD-DVD-R

Three kinds of new nickel(II) complexes of alpha-isoxazolylazo-beta-diketones with blue-violet light absorption were synthesized. Their structures were postulated based on elemental analysis, MS and FT-IR spectra. Smooth films on K9 glass substrates were prepared using the spin-coating method. The absorption properties and thermal stability of these complexes were discussed. The static optical recording test for high density digital versatile disc-recordable (HD-DVD-R) system was also studied. (c) 2005 Elsevier B.V. All rights reserved.

Optical properties of nickel(II)-azo complexes thin films for potential application as high-density recordable optical recording media

Smooth thin films of three kinds of nickel(II)-azo complexes were prepared by the spin-coating method. Absorption spectra of the thin films on K9 glass substrate in the 300-600 nn wavelength region were measured. Optical constants (complex refractive index N = n + ik) and thickness of the thin films prepared on single-crystal silicon substrate in the 300-600 nm wavelength region were investigated on rotating analyzer-polarizer type of scanning ellipsometer, and dielectric constants epsilon (epsilon = epsilon(1) + i epsilon(2)), absorption coefficients a as well as reflectance R of thin films were then calculated at 405 nm. In addition, in order to examine the possible use of nickel(II)-azo complex thin film as an optical recording medium, one of the nickel(II)-azo complex thin film prepared on K9 glass substrate with an Ag reflective layer was also studied by atomic force microscopy and static optical recording. The results show that the nickel(II)-azo complex thin film is smooth and has a root mean square surface roughness of 2.25 nm, and the recording marks on the nickel(II)-azo complex thin film are very clear and circular, and their size can reach 200 nn or less. (c) 2006 Elsevier Ltd. All rights reserved.

Synthesis, spectral, and thermal characterizations of Ni(II) and Cu(II) beta-diketone complexes with thenoyltrifluoroacetone ligand

Two kinds of nickel(II) and copper(II) P-diketone complexes derived from thenoyltrifluoroacetone ligand with blue-violet light absorption were synthesized by reacting free ligand and different metal(II) ions in sodium methoxide solution. Their structures were postulated based on elemental analysis, ESI-MS, FT-IR spectra and UV-vis electronic absorption spectra. Smooth films on K9 glass substrates were prepared using the spin-coating method. Their solubility in organic solvents, absorption properties of thin film and thermal stability of these complexes were evaluated. (c) 2006 Elsevier B.V. All rights reserved.

Spectroscopic, and thermal studies of some new binuclear transition metal(II) complexes with hydrazone ligands containing acetoacetanilide and isoxazole

A new chelating ligand, 2-(2-(5-tert-butylisoxazol-3-yl)hydrazono)-N-(2,4-dimethylphenyl)-3-oxobutanamide (HL), and its four binuclear transition metal complexes, M-2(L)(2) (mu-OCH3)(2) [M = Ni(II), Co(II), Cu(II), Zn(II)], were synthesized using the procedure of diazotization, coupling and metallization. Their structures were postulated based on elemental analysis, H-1 NMR, MALDI-MS, FT-IR spectra and UV-vis electronic absorption spectra. Smooth films of these complexes on K9 glass substrates were prepared using the spin-coating method and their absorption properties were evaluated. The thermal properties of the metal(II) complexes were investigated by thermogravimetry (TG) and differential scanning calorimetry (DSC. Different thermodynamic and kinetic parameters namely activation energy (E

Rare earth dibenzoylmethane complexes for potential application as high-density recordable optical recording materials

Three kinds of rare earth complexes derived from dibenzoylmethane (DBM) ligand were synthesized by reacting free ligand and different rare earth ions(La (3+), Sm3+ and Gd3+). Their contents and structures were postulated based on elemental analysis, LDI-TOF-MS, FT-IR spectra and UV-Vis spectra. Smooth films on K9 glass substrates were prepared using the spin-coating method. Their solubility in organic solvents, absorption and reflection properties of thin film and thermal stability of these complexes were evaluated. These complexes would be a promising recording material for high-density digital versatile disc-recordable (HD-DVD-R) system. (c) 2007 Elsevier B.V. All rights reserved.

Nickel(II) and copper(II) complexes containing 2-(2-(5-substitued isoxazol-3-yl)hydrazono)-5,5-dimethylcyclohexane-1,3-dione ligands: Synthesis, spectral and thermal characterizations

Two new hydrazone chelating ligands, 2-(2-(5-methylisoxazol-3-yl)hydrazono)-5,5-dimethylcyclohexane-1,3-dione (HL1) and 2-(2-(5-tert-butylisoxazol-3-yl)hydrazono)-5,5-dimethylcyclohexane- 1,3-dione (HL2), and their nickel(II) and copper(II) complexes were synthesized using the procedure of diazotization, coupling and metallization. Their structures were postulated based on elemental analysis, H-1 NMR, ESI-MS, FT-IR spectra and UV-vis electronic absorption spectra. Smooth films of these complexes on K9 glass substrates were prepared using spin-coating and their absorption properties were evaluated. The thermal properties of the metal(II) complexes were investigated by thermogravimetry (TG) and differential thermogravimetry (DTG). Different thermodynamic and kinetic parameters namely activation energy (E

飞秒激光辐照K9玻璃引起的暗化和折射率变化

对不同辐照条件下近红外飞秒激光在K9玻璃内部诱导产生的暗化现象和永久性折射率改变进行了实验研究。通过辐照前后的显微镜图片、吸收光谱、电子自旋共振谱(ESR)以及激光衍射实验，分析了K9玻璃中暗化现象产生的微观过程，发现暗化是由诱导产生的空穴型色心引起的。暗化程度和折射率改变随激光强度、扫描速度、扫描行间距变化而变化。光致色心的形成与非线性电离有关。对折射率永久性改变进行了简单说明，其机理仍在探索中。

应用离子后处理技术提高薄膜激光损伤阈值

利用电子束热蒸发方法在K9玻璃基底上沉积氧化锆薄膜,并对其中一些样品用低能O2^+进行了后处理.采用表面热透镜技术测量薄膜样品表面弱吸收,采用显微镜观察样品离子后处理前后的显微缺陷密度.测试结果表明:经离子后处理样品表面的缺陷密度从18.6/mm^2降低到6.2/mm^2,且其激光损伤阈值从15.9 J/cm^2提高到23.1 J/cm^2,样品的平均吸收率从处理前的1.147×10^-4降低到处理后的9.56×10^-5.通过对处理前后样品的表面微缺陷密度、吸收率及损伤形貌等的分析发现:离子后处理可以降