Fire protection durability of intumescent coatings after accelerated aging

The most common method of achieve the required fire resistance is by the use of passive fire protection systems, being intumescent coatings the fire protection material frequently used. These are usually considered thin film coatings as they are applied with a dry film thickness (DFT) between 0.3-3 [mm]. The required DFT is obtained by experimental fire resistance tests performed to assess the contribution of this reactive fire protection material to the steel member fire resistance. This tests are done after dry coating and a short time period of atmospheric conditioning, at constant temperature and humidity. As the coatings formulation is mainly made from polymeric basis compounds, it is expected that the environmental factors, such temperature, humidity and UV radiation (UVA and UVB) significantly affect the intumescent coating fire protection performance and its durability. This work presents a research study about the effects of aging on the fire protection performance of intumescent coatings. A commercial water based coating is submitted to an accelerated aging cycle, using a QUV Accelerated Weathering Tester. This tests aim to simulate 10 years of the coating natural aging. The coating durability is tested comparing the fire protection of small steel samples submitted to a radiant heat flux exposure from a cone calorimeter. In total, 28 tests were performed on intumescent coating protected steel specimens, of which 14 specimens were tested before the hydrothermal aging test and other 14 after accelerated aging. The experimental tests results of the steel temperature evolution shows that increasing the intumescent dry coating film thickness, the fire resistance time increases. After the accelerated aging cycles, the coating lose their ability to expand, resulting in an increase of the steel temperature of approximately 200 [ºC], compared to the samples without aging.

Caratterizzazione delle Prestazioni di Protezione al Fuoco di Vernici Intumescenti

Le pitture intumescenti sono utilizzate come protettivi passivi antincendio nel settore delle costruzioni. In particolare sono utilizzate per aumentare la resistenza al fuoco di elementi in acciaio. Le proprietà termiche di questi rivestimenti sono spesso sconosciute o difficili da stimare per via del fatto che variano notevolmente durante il processo di espansione che subisce l’intumescente quando esposto al calore di un incendio. Per questa ragione la validazione della resistenza al fuoco di un rivestimento presente in commercio si basa su metodi costosi economicamente e come tempi di esecuzione nel quale ciascuna trave e colonna rivestita di protettivo deve essere testata una alla volta attraverso il test di resistenza al fuoco della curva cellulosica. In questo lavoro di tesi adottando invece un approccio basato sulla modellazione termica del rivestimento intumescente si ottiene un aiuto nella semplificazione della procedura di test ed un supporto nella progettazione della resistenza al fuoco delle strutture. Il tratto di unione nei vari passaggi della presente tesi è stata la metodologia di stima del comportamento termico sconosciuto, tale metodologia di stima è la “Inverse Parameter Estimation”. Nella prima fase vi è stata la caratterizzazione chimico fisica della vernice per mezzo di differenti apparecchiature come la DSC, la TGA e l’FT-IR che ci hanno permesso di ottenere la composizione qualitativa e le temperature a cui avvengono i principali processi chimici e fisici che subisce la pittura come anche le entalpie legate a questi eventi. Nella seconda fase si è proceduto alla caratterizzazione termica delle pitture al fine di ottenerne il valore di conduttività termica equivalente. A tale scopo si sono prima utilizzate le temperature dell’acciaio di prove termiche alla fornace con riscaldamento secondo lo standard ISO-834 e successivamente per meglio definire le condizioni al contorno si è presa come fonte di calore un cono calorimetrico in cui la misura della temperatura avveniva direttamente nello spessore del’intumescente. I valori di conduttività ottenuti sono risultati congruenti con la letteratura scientifica e hanno mostrato la dipendenza della stessa dalla temperatura, mentre si è mostrata poco variante rispetto allo spessore di vernice deposto ed alla geometria di campione utilizzato.

Melamine phosphate as a component of intumescent coatings

Melamine orthophosphate has been shown to exhibit variations in its chemical constitution, and crystal shape and size, dependent upon the method of production. These crystal types have been incorporated with epoxy resin to produce intumescent coatings, which have been tested on a small scale fire testing device, designed and calibrated within this project. The factors influencing performance in three fire test regimes are the percentage loading of melamine phosphate, its chemical constitution, crystal size and shape, thermal degradation, and state of agglomeration . and dispersion in the coating, determined by the method of incorporation into the coating. When melamine phosphate is heat treated at 210ºC, a process designed to reduce its solubility, the performance of coatings produced with such material is profoundly affected, depending mainly on crystal size and shape alone. Consideration of heat transfer across the chars produced has allowed a quantitative evaluation of the thermal resistance of chars throughout a test. An optimum production route for melamine phosphate has been suggested, taking into account the requirements for weatherability of coatings as well as performance in a fire.

Metal oxide nanofibres membranes assembled by spin-coating method

Ceramic membranes are of particular interest in many industrial processes due to their ability to function under extreme conditions while maintaining their chemical and thermal stability. Major structural deficiencies under conventional fabrication approach are pin-holes and cracks, and the dramatic losses of flux when pore sizes are reduced to enhance selectivity. We overcome these structural deficiencies by constructing hierarchically structured separation layer on a porous substrate using larger titanate nanofibres and smaller boehmite nanofibres. This yields a radical change in membrane texture. The differences in the porous supports have no substantial influences on the texture of resulting membranes. The membranes with top layer of nanofibres coated on different porous supports by spin-coating method have similar size of the filtration pores, which is in a range of 10–100 nm. These membranes are able to effectively filter out species larger than 60 nm at flow rates orders of magnitude greater than conventional membranes. The retention can attain more than 95%, while maintaining a high flux rate about 900 L m-2 h. The calcination after spin-coating creates solid linkages between the fibres and between fibres and substrate, in addition to convert boehmite into -alumina nanofibres. This reveals a new direction in membrane fabrication.

Corrosion studies on the plasma-sprayed nanostructured titanium dioxide coating

Purpose: The purpose of this paper is to report the resistance of plasma-sprayed titanium dioxide (TiO2) nanostructured coatings in a corrosive environment.----- Design/methodology/approach: Weight loss studies are performed according to ASTM G31 specifications in 3.5?wt% NaCl. Electrochemical polarization resistance measurements are made according to ASTM G59-91 specifications. Corrosion resistance in a humid and corrosive environment is determined by exposing the samples in a salt spray chamber for 100?h. Microstructural studies are carried out using an atomic force microscope and scanning electron microscope.----- Findings: The nanostructured TiO2 coatings offer good resistance to corrosion, as shown by the results of immersion, electrochemical and salt spray studies. The corrosion resistance of the coating is dictated primarily by the geometry of splat lamellae, density of unmelted nanoparticles, magnitude of porosity and surface homogeneity.----- Practical implications: The TiO2 nanostructured coatings show promising potential for use as abrasion, wear-resistant and thermal barrier coatings for service in harsh environments.----- Originality/value: The paper relates the corrosion resistance of nanostructured TiO2 coatings to their structure and surface morphology.

Determination of elastic modulus of thin coating materials using nanoindentation and finite element analysis

A deconvolution method that combines nanoindentation and finite element analysis was developed to determine elastic modulus of thin coating layer in a coating-substrate bilayer system. In this method, the nanoindentation experiments were conducted to obtain the modulus of both the bilayer system and the substrate. The finite element analysis was then applied to deconvolve the elastic modulus of the coating. The results demonstrated that the elastic modulus obtained using the developed method was in good agreement with that reported in literature.

Coating of biomaterial scaffolds with the collagen-mimetic peptide GFOGER for bone defect repair

Healing large bone defects and non-unions remains a significant clinical problem. Current treatments, consisting of auto and allografts, are limited by donor supply and morbidity, insufficient bioactivity and risk of infection. Biotherapeutics, including cells, genes and proteins, represent promising alternative therapies, but these strategies are limited by technical roadblocks to biotherapeutic delivery, cell sourcing, high cost, and regulatory hurdles. In the present study, the collagen-mimetic peptide, GFOGER, was used to coat synthetic PCL scaffolds to promote bone formation in critically-sized segmental defects in rats. GFOGER is a synthetic triple helical peptide that binds to the [alpha]2[beta]1 integrin receptor involved in osteogenesis. GFOGER coatings passively adsorbed onto polymeric scaffolds, in the absence of exogenous cells or growth factors, significantly accelerated and increased bone formation in non-healing femoral defects compared to uncoated scaffolds and empty defects. Despite differences in bone volume, no differences in torsional strength were detected after 12 weeks, indicating that bone mass but not bone quality was improved in this model. This work demonstrates a simple, cell/growth factor-free strategy to promote bone formation in challenging, non-healing bone defects. This biomaterial coating strategy represents a cost-effective and facile approach, translatable into a robust clinical therapy for musculoskeletal applications.

Bonding of aluminum alloy by hot-dipping tin coating

This paper presents bonding technology of aluminum alloy by hot-dipping tin. The dissolution curve of copper in molten tin liquid was obtained in the experiment of hot-dipping Sn. Optimal hot-dipping parameter which was suitable for soldering was designed. To elucidate characteristics of interfacial evolution, the microstructure of the coatings, soldered joint were analyzed using optical microscopy, SEM and EDX. The shear strength of soldered joints was tested as high as 39.9Mpa, which is high enough to achieve the requirement of electronic industry.

In vivo performance of melimine as an antimicrobial coating for contact lenses in models of CLARE and CLPU

Purpose: One strategy to minimize bacteria-associated adverse responses such as microbial keratitis, contact lens–induced acute red eye (CLARE), and contact lens induced peripheral ulcers (CLPUs) that occur with contact lens wear is the development of an antimicrobial or antiadhesive contact lens. Cationic peptides represent a novel approach for the development of antimicrobial lenses.---------- Methods: A novel cationic peptide, melimine, was covalently incorporated into silicone hydrogel lenses. Confirmation tests to determine the presence of peptide and anti-microbial activity were performed. Cationic lenses were then tested for their ability to prevent CLPU in the Staphylococcus aureus rabbit model and CLARE in the Pseudomonas aeruginosa guinea pig model. ---------- Results: In the rabbit model of CLPU, melimine-coated lenses resulted in significant reductions in ocular symptom scores and in the extent of corneal infiltration (P < 0.05). Evaluation of the performance of melimine lenses in the CLARE model showed significant improvement in all ocular response parameters measured, including the percentage of eyes with corneal infiltrates, compared with those observed in the eyes fitted with the control lens (P ≤ 0.05). ---------- Conclusions: Cationic coating of contact lenses with the peptide melimine may represent a novel method of prevention of bacterial growth on contact lenses and consequently result in reduction of the incidence and severity of adverse responses due to Gram-positive and -negative bacteria during lens wear.

Porous zirconia scaffold modified with mesoporous bioglass coating

Porous yttria-stabilized zirconia (YSZ) has been regarded as a potential candidate for bone substitute as its high mechanical strength. However, porous YSZ bodies are biologically inert to bone tissue. It is therefore necessary to introduce bioactive coatings onto the walls of the porous structures to enhance the bioactivity. In this study, the porous zirconia scaffolds were prepared by infiltration of Acrylonitrile Butadiene Styrene (ABS) scaffolds with 3 mol% yttria stabilized zirconia slurry. After sintering, a method of sol-gel dip coating was involved to make coating layer of mesoporous bioglass (MBGs). The porous zirconia without the coating had high porosities of 60.1% to 63.8%, and most macropores were interconnected with pore sizes of 0.5-0.8mm. The porous zirconia had compressive strengths of 9.07-9.90MPa. Moreover, the average coating thickness was about 7μm. There is no significant change of compressive strength for the porous zirconia with mesoporous biogalss coating. The bone marrow stromal cell (BMSC) proliferation test showed both uncoated and coated zirconia scaffolds have good biocompatibility. The scanning electron microscope (SEM) micrographs and the compositional analysis graphs demonstrated that after testing in the simulated body fluid (SBF) for 7 days, the apatite formation occurred on the coating surface. Thus, porous zirconia-based ceramics were modified with bioactive coating of mesoporous bioglass for potential biomedical applications.