Evolution of microstructure, macrotexture and mechanical properties of commercially pure Ti during ECAP-conform processing and drawing

Long-length ultrafine-grained (UFG) Ti rods are produced by equal-channel angular pressing via the conform scheme (ECAP-C) at 200 °C, which is followed by drawing at 200 °C. The evolution of microstructure, macrotexture, and mechanical properties (yield strength, ultimate tensile strength, failure stress, uniform elongation, elongation to failure) of pure Ti during this thermo-mechanical processing is studied. Special attention is also paid to the effect of microstructure on the mechanical behavior of the material after macrolocalization of plastic flow. The number of ECAP-C passes varies in the range of 1–10. The microstructure is more refined with increasing number of ECAP-C passes. Formation of homogeneous microstructure with a grain/subgrain size of 200 nm and its saturation after 6 ECAP-C passes are observed. Strength properties increase with increasing number of ECAP passes and saturate after 6 ECAP-C passes to a yield strength of 973 MPa, an ultimate tensile strength of 1035 MPa, and a true failure stress of 1400 MPa (from 625, 750, and 1150 MPa in the as-received condition). The true strain at failure failure decreases after ECAP-C processing. The reduction of area and true strain to failure values do not decrease after ECAP-C processing. The sample after 6 ECAP-C passes is subjected to drawing at 200¯C resulting in reduction of a grain/subgrain size to 150 nm, formation of (10 1¯0) fiber texture with respect to the rod axis, and further increase of the yield strength up to 1190 MPa, the ultimate tensile strength up to 1230 MPa and the true failure stress up to 1600 MPa. It is demonstrated that UFG CP Ti has low resistance to macrolocalization of plastic deformation and high resistance to crack formation after necking.

Al-doped ZnO ceramic sputtering targets based on nanocrystalline powders produced by emulsion detonation synthesis – deposition and application as a transparent conductive oxide material

Transparent conducting oxides (TCOs) have been largely used in the optoelectronic industry due to their singular combination of low electrical resistivity and high optical transmittance. They are usually deposited by magnetron sputtering systems being applied in several devices, specifically thin film solar cells (TFSCs). Sputtering targets are crucial components of the sputtering process, with many of the sputtered films properties dependent on the targets characteristics. The present thesis focuses on the development of high quality conductive Al-doped ZnO (AZO) ceramic sputtering targets based on nanostructured powders produced by emulsion detonation synthesis method (EDSM), and their application as a TCO. In this sense, the influence of several processing parameters was investigated from the targets raw-materials synthesis to the application of sputtered films in optoelectronic devices. The optimized manufactured AZO targets present a final density above 99 % with controlled grain size, an homogeneous microstructure with a well dispersed ZnAl2O4 spinel phase, and electrical resistivities of ~4 × 10-4 Ωcm independently on the Al-doping level among 0.5 and 2.0 wt. % Al2O3. Sintering conditions proved to have a great influence on the properties of the targets and their performance as a sputtering target. It was demonstrated that both deposition process and final properties of the films are related with the targets characteristics, which in turn depends on the initial powder properties. In parallel, the influence of several deposition parameters in the film´s properties sputtered from these targets was investigated. The sputtered AZO TCOs showed electrical properties at room temperature that are superior to simple oxides and comparable to a reference TCO – indium tin oxide (ITO), namely low electrical resistivity of 5.45 × 10-4 Ωcm, high carrier mobility (29.4 cm2V-1s-1), and high charge carrier concentration (3.97 × 1020 cm-3), and also average transmittance in the visible region > 80 %. These superior properties allowed their successful application in different optoelectronic devices.

Propriedades estruturais e microestruturais de manganitas dopadas com cobre

We report a structural study on polycrystalline La0.86Sr0.14Mn1-y Cu yO3+delta samples (y = 0, 0.05, 0.10, 0.15, 0.20) using refinement of powder X-ray diffraction data and analysis of scanning electron microscopy images. It is found that the structure remains rhombohedral through the whole series, with a decrease in the average Mn-Mn bond distances, slight variations in Mn-O-Mn angle and reduction in the unit cell volume with increasing Cu amounts. The values of Mn-Mn distances suggest compact structures with d within ±1%. Scanning electron microscopy images reveal homogeneous microstructure in all samples, besides a trend for smaller grains and larger porosity with increasing Cu content.

Sinterização de Ce1-XEuXO2-(X/2) para aplicação como eletrólito sólido em células a combustível de temperaturas intermediárias

Given the environmental concern over global warming that occurs mainly by emission of CO2 from the combustion of petroleum, coal and natural gas research focused on alternative and clean energy generation has been intensified. Among these, the highlight the solid oxide fuel cell intermediate temperature (IT-SOFC). For application as electrolyte of the devices doped based CeO2 with rare earth ions (TR+ 3) have been quite promising because they have good ionic conductivity and operate at relatively low temperatures (500-800 ° C). In this work, studied the Ce1-xEuxO2-δ (x = 0,1, 0,2 and 0,3), solid solutions synthesized by the polymeric precursor method to be used as solid electrolyte. It was also studied the processing steps of these powders (milling, compaction and two step sintering) in order to obtain dense sintered pellets with reduced grain size and homogeneous microstructure. For this, the powders were characterized by thermal analysis, X-ray diffraction, particle size distribution and scanning electrons microscopy, since the sintered samples were characterized by dilatometry, scanning electrons microscopy, density and grain size measurements. By x-ray diffraction, it was verified the formation of the solid solution for all compositions. Crystallites in the nanometric scale were found for both sintering routes but the two step sintering presented significant reduction in the average grain size

Estudo da sinterização de cavacos de aço ferritico

This research studies the sintering of ferritic steel chips from the machining process. Were sintered metal powder obtained from machining process chips for face milling of a ferritic steel. The chip was produced by machining and characterized by SEM and EDS, and underwent a process of high energy mill powder characterized also by SEM and EDS. Were constructed three types of matrixes for uniaxial compression (relation l / d greater than 2.5). The differences in the design of the matrixes were essentially in the direction of load application, which for cylindrical case axial direction, while for the rectangular arrays, the longer side. Two samples were compressed with different geometries, a cylindrical and rectangular with the same compaction pressure of 700 MPa. The samples were sintered in a vacuum resistive furnace, heating rate 20 °C / min., isotherm 1300 °C for 60 minutes, and cooling rate of 25 °C / min to room temperature. The starting material of the rectangular sample was further annealed up to temperature of 800 ° C for 30 min. Sintered samples were characterized by scanning electron microscopy, optical microscopy and EDS. The sample compressed in the cylindrical matrix did not show a regular density reflecting in the sintered microstructure revealed by the irregular geometry of the pores, characterizing that the sintering was not complete, reaching only the second phase. As for the specimen compacted in the rectangular array, the analysis performed by scanning electron microscopy, optical microscopy and EDS indicate a good densification, and homogeneous microstructure in their full extent. Additionally, the EDS analyzes indicate no significant changes in chemical composition in the process steps. Therefore, it is concluded that recycling of chips, from the processed ferritic steel is feasible by the powder metallurgy. It makes possible rationalize raw material and energy by manufacture of known properties components from chips generated by the machining process, being benefits to the environment

Mechanical properties and dimensional effects of ZnO- and SnO(2)-based varistors

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Nonlinear properties and stability of SnO2 varistors prepared by evaporation and decomposition of suspensions

SnO2 varistors doped with CoO, Cr2O3 and Nb2O5 were prepared by evaporation and decomposition of suspensions. The composition of the varistors was optimized to improve electrical properties, such as nonlinearity, leakage current and electrical stability. The best results were achieved with the following composition: 99.15% SnO2 +0.75% CoO+0.05% Cr2O3 +0.05% Nb2O5. Samples showed high density, reaching 99.5% of the theoretical density, as well as an homogeneous microstructure. The nonlinear coefficient was higher than 30 in the current range from 10(-7) to 10(-2) A/cm(2). The leakage current was 0.86 mu A/cm(2). These samples showed high stability of electrical parameters when they were exposed to high current of 27 mA/cm(2) for different time periods up to 30 min. (c) 2005 Elsevier Ltd. All rights reserved.

PROCESSING AND CHARACTERIZATION OF LOW-VOLTAGE VARISTORS

ZnO seed particles and Cr2O3 were used in this study to control the microstructure of ZnO varistors. The seed particles were prepared by adding 1.0 mol % BaO to ZnO. The powder was then calcined at 800-degrees-C for 2 h, pressed into pellets and sintered at 1400-degrees-C for 8 h. The sintered ZnO was ground and the BaO eliminated by washing in water. The remaining ZnO powder was classified into a size fraction ranging from 38 to 149 mum. The addition of a small amount (1 weight %) ZnO seed grains produces varistors with low breakdown voltages (7.6 V/mm) and an alpha coefficient of approximately 10. The addition of Cr2O3 stabilizes the spinel phase yielding a more homogeneous microstructure, but degraded electrical behaviour of the ZnO varistor.

The effect of heating rate on the sintering of agglomerated NaNbO3 powders

The effect of heating rate on the sintering of agglomerated NaNbO3 powders, processed by the polymeric precursors method, was studied. The results showed that the presence of agglomerated powder leads to a heterogeneous microstructure, with bimodal grain size distribution, after sintering. Using a high heating rate, the sintering of agglomerated particles was inhibits, leading to a homogeneous microstructure, with single grain size distribution. (C) 1998 Kluwer Academic Publishers.

The influence of the sintering system on PMN properties

PMN powder samples with PbO excess of 0, 1,2 and 3% were submitted to the pressing and sintering at 1200°C for 4h with a heating rate of 3°C/min. A new sintering system, developed at our laboratories, was used. It allows obtaining more information on the sintering process. The sintered samples in the new system were compared to sintered samples in the C system. The microstructure, dielectric properties and the effect of the PbO excess in different sintering systems were compared. The N system permitted to obtain a ceramic with better properties, such density, dielectric constant and very homogeneous microstructure.

High-density nanoparticle ceramic bodies: A study of heating rates in the sinterization of Gadolinium-doped Ceria

An investigation on the sinterization of Gd:CeO2 (Ce 0.85Gd0.15O1.9-δ ceramic system) 3-10 nm nanoparticles in pressed bodies was done. The heating rate was taken as a key parameter and two competing sinterization processes were identified, associated with different diffusional mechanisms. Using heating rates of 113 C min -1, a high-final density (98 % of the theoretical) was obtained by superposing the two aforementioned mechanisms, resulting in a homogeneous microstructure at lower temperatures. © 2012 Akadémiai Kiadó, Budapest, Hungary.

Preparação de espuma cerâmica à base de zircônia pelo processo sol-emulsão-gel

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Interface of dentine to root canal sealers

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Fe-doping on the structural, microstructural, optical, and ferroeletric properties of Pb1/2Sr1/2Ti1-xFexO3 oxide prepared by spin coating technique

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Caracterização de uma cerâmica 3Y-TZP e avaliação do efeito de tratamentos de superfície na adesão da cerâmica ao glaze ou cimento resinoso

Pós-graduação em Odontologia Restauradora - ICT