Two-dimensional ordering of self-assembled InxGal-xAs quantum dots grown on GaAs(311)B surfaces

Two-dimensional (2D) ordering of self-assembled InxGa1-xAs quantum dots (QDs) fabricated on GaAs(311)B surface by molecular beam epitaxy (MBE) are reported. The QDs are aligned into rows deferring from the direction of the misorientation of the substrate, and strongly dependent on the mole In content x of InxGa1-xAs solid solution. The ordering alignment deteriorates significantly as the In content is increased to above 0.5. The 2D ordering can be described as a centered rectangular unit mesh with the two sides parallel to [01 (1) over bar] and [(2) over bar 33], respectively. Their relative arrangement seems to be determined by a combination of the strongly repulsive elastic interaction between neighbouring islands and the minimization of the strain energy of the whole system. The ordering also helps to improve the size homogeneity of the InGaAs islands. Photoluminescence (PL) result demonstrates that QDs grown on (311)B have the narrowest linewidth and the strongest integrated intensity, compared to those grown on (100) and other high-index planes under the same condition. (C) 1999 Elsevier Science B.V. All rights reserved.

Two-dimensional ordering of self-assembled InxGa1-xAs quantum dots grown on GaAs(311)B surfaces

The two-dimensional (2D) ordering of self-assembled InxGa1-xAs quantum dots (QDs) fabricated on GaAs(3 1 1)B surface by molecular beam epitaxy (MBE) are reported. The QDs are aligned into rows differing from the direction of the misorientation of the substrate, and strongly dependent on the mole In content x of InxGa1-As-x solid solution. The ordering alignment deteriorates significantly as the In content is increased to above 0.5. The 2D ordering can be described as a centered rectangular unit mesh with the two sides parallel to [0 1 (1) over bar] and [(2) over bar 3 3], respectively. Their relative arrangement seems to be determined by a combination of the strongly repulsive elastic interaction between the neighboring islands and the minimization of the strain energy of the whole system. The ordering also helps to improve the size homogeneity of the InGaAs islands. The photoluminescence (PL) result demonstrates that QDs grown on (3 1 1)B have the narrowest linewidth and the strongest integrated intensity, compared to those on (1 0 0) and other high-index planes under the same condition. (C) 1999 Elsevier Science B.V. All rights reserved.

In composition dependence of lateral ordering in InGaAs quantum dots grown on (311)B GaAs substrates

Self-assembled InxGa1-xAs quantum dots (QDs) on (311)A/B GaAs surfaces have been grown by molecular beam epitaxy (MBE). Spontaneously ordering alignment of InxGa1-xAs with lower In content around 0.3 have been observed. The direction of alignment orientation of the QDs formation differs from the direction of misorientation of the (311)B surface, and is strongly dependent upon the In content x. The ordering alignment become significantly deteriorated as the In content is increased to above 0.5 or as the QDs are formed on (100) or (311)A substrates. (C) 1999 Elsevier Science B.V. All rights reserved.

Indium composition dependence of the size uniformity of InGaAs quantum dots on (311)B GaAs grown by molecular beam epitaxy

The deposition of InxGa1-xAs (0.2 less than or equal to x less than or equal to 0.5) on (311)B GaAs surfaces using solid source molecular beam epitaxy (MBE) has been studied. Both AFM and photoluminescence emission showed that homogeneous quantum dots could be formed on (311)B GaAs surface when indium composition was around 0.4. Indium composition had a strong influence on the size uniformity and the lateral alignment of quantum dots. Compared with other surface orientation, (100) and (n11) A/B (n=1,2,3), photoluminescence measurement confirmed that (311)B surface is the most advantageous in fabricating uniform and dense quantum dots.

Photoluminescence investigation of GaInP/GaAs multiple quantum wells grown on (001) and (311) B GaAs surfaces by gas source molecular beam epitaxy

Photoluminescence (PL) investigation was carried out on GaInP/GaAs multiple quantum wells structures grown on (001) and (311) B surfaces of GaAs by gas source molecular beam epitaxy. Superlattice structures of GaAs/GaInP grown on (001) GaAs substrate were also studied in comparison. Deep-level luminescence was seen to dominate the PL spectra from the quantum wells and superlattice structures that were grown on (001) GaAs substrate. In contrast, superior optical properties were exhibited in the same structures grown on (311) B GaAs surfaces. The results suggested that GaAs/GaInP quantum well structures on (311) B oriented substrates could efficiently suppress the deep-level emissions, result in narrower PL peaks indicating smooth interfaces. (C) 1998 American Institute of Physics.

Optical characterization of InAs monolayer quantum structures grown on (311)A, (311)B, and (100)GaAs substrates

Low-temperature photoluminescence and excitation spectra from InAs monolayer quantum structures, grown on (311)A, (311)B, and (100) GaAs substrates, are investigated, The structures were grown simultaneously by conventional molecular-beam epitaxy (MBE), The experimental results show that the quality of InAs monolayer on (311)B GaAs substrate is obviously better in crystal quality than those on the two other oriented GaAs substrates. In addition, the transition peaks of the InAs layer grown on (311) GaAs substrates shift to higher energy with respect to that from the InAs layer grown on (100) GaAs substrate.

Two-dimensional ordering of self-assembled InAs quantum dots grown on (311)B InP substrate

Self-assembled InAs quantum dots (QDs) in InAlAs grown on (001) and (311)B InP substrates by molecular beam epitaxy (MBE) have been comparatively investigated. A correlated study of atomic force microscopy (AFM) and photoluminescence (PL) disclosed that InAs QDs grown on high-index InP substrates can lead to high density and uniformity. By introducing a lattice-matched InAlGaAs overlayer on InAlAs buffer, still more dense and uniform InAs QDs were obtained in comparison with InAs QDs formed with only InAlAs matrix. Moreover, two-dimensional well-ordered InAs dots with regular shape grown on (311)B InP substrates are reported for the first time. We explained this exceptional phenomenon from strain energy combined with kinetics point of view. (C) 2000 Elsevier Science B.V. All rights reserved.

Self-organized type-II In0.55Al0.45As/Al0.50Ga0.50As quantum dots realized on GaAs(311)A

Self-organized In0.55Al0.45As/Al0.50Ga0.50As quantum dots are grown by the Stranski-Krastanow growth mode using molecular beam epitaxy on the GaAs(311)A substrate. The optical properties of type-II InAlAs/AlGaAs quantum dots have been demonstrated by the excitation power and temperature dependence of photoluminescence spectra. A simple model accounting for the size-dependent band gap of quantum dots is given to qualitatively understand the formation of type-II In0.55Al0.45As/Al0.50Ga0.50As quantum dots driven by the quantum-confinement-induced Gamma --> X transition. The results provide new insights into the band structure of InAlAs/AlGaAs quantum dots. (C) 2000 American Institute of Physics. [S0003-6951(00)00725-7].

Structural and optical properties of self-assembled InAs quantum dots grown on GaAs (311) A substrate

We report the structural and optical characteristics of InAs quantum dots (QDs) grown on GaAs (311)A substrates. Atomic force microscopic result shows that QDs on (311)A surface exhibit a nonconventional, faceted, arrowhead-like shapes aligned in the [233] direction. The photoluminescence (PL) intensity, peak position and the full width at half maxinum (FWHM) are all closely related to the measurement temperature. The fast redshift of PL energy and monotonous decrease of linewidth with increasing temperature were observed and explained by carriers being thermally activated to the barrier produced by the wetting layer and then being retrapped and recombined in energetically lower-lying QDs states. This model explains our results well.

Growth of GaAs/InAs vertical nanowires on GaAs (111)B by metalorganic chemical vapor deposition

The growth mechanism and properties of GaAs/InAs nanowires prepared by metalorganic chemical vapor deposition are investigated. Vertical InAs nanowires on GaAs (111)B substrates are successfully grown despite the large lattice mismatch (-7.2%). The crystallographic perfection of InAs nanowires is confirmed by hexagonal or triangular cross section. An interesting L-shaping of GaAs/InAs heterostructure nanowire which could be useful for novel device application is observed. © 2005 IEEE.

Atomic hydrogen induced step bunching and fabrication of quantum wire arrays on GaAs (311)A substrate by molecular beam epitaxy

Atomic hydrogen assisted molecular beam epitaxy (MBE) is a novel type of epitaxial growth of nanostructures. The GaAs (311)A surface naturally forms one-dimensional step arrays by step bunching along the direction of (-233) and the space period is around 40nm. The step arrays extend over several mum without displacement. The InGaAs quantum wire arrays are grown on the step arrays as the basis. Our results may prompt further development of more uniform quantum wire and quantum dot arrays.

InAs self-assembled quantum dots grown on an InP (311)B substrate by molecular beam epitaxy

Self-assembled InAs quantum dots (QDs) have been grown by solid-source molecular beam epitaxy on a (311)B InP substrate. Transmission electron microscopy clearly shows that a high density of smaller InAs islands can be obtained by using such a high index substrate. After introducing a lattice-matched underlying In0.52Al0.24Ga0.24As layer, the InAs QDs are much more uniform in size and form two-dimensional well ordered arrays. The photoluminescence (PL) spectra also confirm that the InAs QDs grown on underlying In0.52Al0.24Ga0.24As have a better quality than those grown in the In0.52Al0.48As matrix. A simple calculation indicates that the redshift of the PL peak energy mainly results from InAs QDs on underlying In0.52Al0.24Ga0.24As of large size. (C) 2001 American Institute of Physics.

Self-limiting MBE growth and characterization of three-dimensionally confined nanostructures on patterned GaAs(311)A substrates

The formation of triangular-shaped dot-like (TD) structures grown by molecular beam epitaxy on GaAs (311)A substrates patterned with square- and triangular-shaped holes is compared. On substrates patterned with square-shaped holes, TD structures are formed via the pinch-off of two symmetrically arranged {111} planes which develop freely in the regions between the holes on the original substrate surface, while the (111)A sidewalls of the as-etched holes develop a rough morphology during growth. The evolution of the rough ( 1 1 1)A sidewalls is eliminated on substrates patterned with triangular shaped holes resulting in similar TD structures with highly improved uniformity over the entire pattern. Spectrally and spatially resolved cathodoluminescence spectroscopy reveals the lateral variation of the quantum-well confinement energy in the TD structures generating distinct lateral energy barriers between the top portion and the nearby smooth regions with efficient radiative recombination. Formation of TD structures provides a new approach Do fabricate three-dimensionally confined nanostructures in a controlled manner.

GaAs（311）A衬底上自组装InAs量子点的结构和光学特性

于2010-11-23批量导入

Lateral ordered InGaAs self-organized quantum dots grown on (311) GaAs by conventional molecular beam epitaxy

Self-assembled InxGa1-xAs quantum dots (QDs) on (311) and (100) GaAs surfaces have been grown by conventional solid source molecular beam epitaxy. Spontaneously ordering alignment of InxGa1-xAs QDs with lower In content around 0.3 has been observed on As-terminated (B type) surfaces. The direction of alignment orientation of the QDs formation differs from the direction of misorientation of the (311) B surface, and is strongly dependent upon the In content x. The ordering alignment becomes significantly deteriorated as the In content is increased to above 0.5 or as the QDs are formed on (100) and (311) Ga-terminated (A type) substrates.