Role of the triplet state in the green emission peak of polyfluorene films: A time evolution study

The blue emission of ethyl-hexyl substituted polyfluorene (PF2/6) films is accompanied by a low energy green emission peak around 500 nm in inert atmosphere. The intensity of this 500 nm peak is large in electroluminescence (EL) compared to photoluminescence (PL)measurements. Furthermore, the green emission intensity reduces dramatically in the presence of molecular oxygen. To understand this, we have modeled various nonradiative processes by time dependent quantum many body methods. These are (i) intersystem crossing to study conversion of excited singlets to triplets leading to a phosphorescence emission, (ii) electron-hole recombination (e-hR) process in the presence of a paramagnetic impurity to follow the yield of triplets in a polyene system doped with paramagnetic metal atom, and (iii) quenching of excited triplet states in the presence of oxygen molecules to understand the low intensity of EL emission in ambient atmosphere, when compared with that in nitrogen atmosphere. We have employed the Pariser-Parr-Pople Hamiltonian to model the molecules and have invoked electron-electron repulsions beyond zero differential approximation while treating interactions between the organic molecule and the rest of the system. Our time evolution methods show that there is a large cross section for triplet formation in the e-hR process in the presence of paramagnetic impurity with degenerate orbitals. The triplet yield through e-hR process far exceeds that in the intersystem crossing pathway, clearly pointing to the large intensity of the 500 nm peak in EL compared to PL measurements. We have also modeled the triplet quenching process by a paramagnetic oxygen molecule which shows a sizable quenching cross section especially for systems with large sizes. These studies show that the most probable origin of the experimentally observed low energy EL emission is the triplets.

Li2MnO3: a rare red-coloured manganese(IV) oxide exhibiting tunable red-yellow-green emission

An experimental assessment of Li2MnO3 has been conducted, in conjunction with related Mn(IV) oxides, to investigate its red colour and photoluminescence. Optical absorption spectra revealed strong band gap absorption, with a sharp edge at similar to 610 nm and a transparent region between similar to 610 and similar to 650 nm, giving rise to the red colour of this compound. Octahedral Mn(IV) ligand field transitions have been observed in the excitation spectra of Li2MnO3, corresponding both to Mn(IV) at ideal sites and displaced in Li sites in the rock salt-based layered structure of Li2MnO3. Optical excitation at ligand field transition energies produces tunable emission in the red-yellow-green region, rendering Li2MnO3 a unique Mn(IV) oxide. The honeycomb-ordered LiMn6] units in its structure are probably the origin of both the absorption and the photoluminescent properties of Li2MnO3.

Blue green emission from a Cu+-Doped transparent material prepared by sintering porous glass

A colorless transparent, blue green emission material was fabricated by sintering porous glass impregnated with copper ions. The emission spectral profile obtained from Cu+ -doped high silica glass (HSG) by 267-mn monochromatic light excitation matches that obtained by pumping with an 800-nm femtosecond laser, indicating that the emissions in both cases come from an identical origin. The upconversion emission excited by 800-nm femtosecond laser is considered to be a three-photon excitation process. A tentative scheme of upconverted emission from Cu+ -doped HSG was also proposed. The glass materials presented herein are expected to find application in lamps, high density optical storage, and three-dimensional color displays.

Pressure behaviour of the UV and green emission bands in ZnO micro-rods

The pressure behavior of the ultraviolet (UV) and green emission bands in ZnO tetrapod-like micro-rods has been investigated at 300 and 70 K, respectively. The pressure coefficient of the UV band at 300 K is 24.5 meV/GPa, consistent with that of the band gap of bulk ZnO. However, the pressure coefficient of the green band is 25 meV/GPa, far larger than previous literature reports. The green band in this work originates from Cu-related emission, as confirmed by the fine structure observed in the spectra at 10 K. The pressure coefficients of four phonon replicas of the free exciton emission (FX) at 70 K are 21.0, 20.2, 19.8, and 19.3 meV/GPa, respectively. The energy shift rate of the FX emission and the LO phonon energies is then determined to be 21.4 and 0.55 meV/GPa. The pressure coefficient of the neutral donor bound exciton ((DX)-X-0) transition is 20.5 meV/GPa, only 4% smaller than that of FX. This confirms that the (DX)-X-0 emission corresponds to excitons bound to neutral shallow donors. (C) 2007 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Temperature and pressure dependences of the copper-related green emission in ZnO microrods

We have investigated the temperature and pressure dependences of the copper-related green emission, which show fine structure at low temperature, from tetrapodlike ZnO microrods. The temperature dependence of the green emission energy follows the changes in the band gap from 10-200 K, but deviates from this behavior above 200 K. The pressure dependence of the copper-related green band (25 +/- 5 meV/GPa) is similar to that of the band gap of ZnO, and is larger than that reported previously for defect-related green emission in ZnO. (c) 2006 American Institute of Physics.

Fluorescence Decay Characteristics of the Green Emission From CaF2:Ho3+

Variations in the decay times of the characteristic green emissions at 522.7, 551.3, 549.6, 547.6, 542.2, 540.2, 535.9 and 533.5nm from CaF2 :H03+ with concentration are studied at RT and LNT. A pulsed N2 laser beam of power density 1.5 MW cm-2 is used for the excitation. Temperature dependent concentration quenching of the decay times are observed for all the emission bands. But an increase in the decay time due to the reabsorption process is also observed for a few of the above bands.

The role of triplet states in the emission mechanism of polymer light-emitting diodes

The blue emission of polyfluorene (PF)-based light-emitting diodes (LEDs) is known to degrade due to a low-energy green emission, which hitherto has been attributed to oxidative defects. By studying the electroluminescence (EL) from ethyl-hexyl substituted PF LEDs in the presence of oxygen and in an inert atmosphere, and by using trace quantities of paramagnetic impurities (PM) in the polymer, we show that the triplet states play a major role in the low-energy emission mechanism. Our time-dependent many-body studies show a large cross-section for the triplet formation in the EL process in the presence of PM, primarily due to electron-hole recombination processes.

Upconversion emission in Er3+ doped novel bismuthate glass

Novel Er3+-doped bismuth lead strontiam glass was fabricated and characterized, and the absorption spectrum and upconversion spectrum of the glass were studied. The Judd-Ofelt intensity parameters Omega(t)(t = 2, 4, 6) were found to be Omega(2) = 3.27 x 10(-20) cm(2), Omega(4) = 1.15 x 10(-20) cm(2), and Omega(6) = 0.38 x 10(-20) cm(2). The oscillator strength, the spontaneous transition probabilities, the fluorescence branching ratios, and excited state lifetimes were also measured and calculated. The upconversion emission intensity varies with the power of infrared excitation intensity. A plot of log I-up vs log I-IR yields a straight line with slope 1.86, 1.88 and 1.85, corresponding to 525, 546, and 657 nm emission bands, respectively, which indicates that a two-photon process for the red and green emission.

Full-color emission from In2S3 and ln(2)S(3): Eu3+ nanoparticles

New observations on the luminescence Of In2S3 and europium-doped In2S3 nanoparticles show a green (5 10 nm) emission from In2S3 and In1.8Eu0.2S3 nanoparticles while a blue (425 nm) emission is observed from ln(1.6)Eu(0.4)S(3) nanoparticles. Both the blue and green emissions have large Stokes shifts of 62 and 110 nm, respectively. Excitation with longer-wavelength photons causes the blue emission to shift to a longer wavelength while the green emission wavelength remains unchanged. The lifetimes of both the green and blue emissions are similar to reported values for excitonic recombination. When doped with Eu3+, in addition to the broad blue and green emissions, a red emission near 615 nm attributed to Eu3+ is observed. Temperature dependences on nanoparticle thin films indicate that with increasing temperature, the green emission wavelength remains constant, however, the blue emission shifts toward longer wavelengths. Based on these observations, the blue emission is attributed to exciton recombination and the green emission to Indium interstitial defects. These nanoparticles show full-color emission with high efficiency, fast lifetime decays, and good stability; they are also relatively simple to prepare, thus making them a new type of phosphor with potential applications in lighting, flat-panel displays, and communications.

Green-light-emitting ZnSe nanowires fabricated via vapor phase growth

Stoichiometric ZnSe nanowires have been synthesized through a vapor phase reaction of zinc and selenium powder on the (100) silicon substrate coated with a gold film of 2 nm in thickness. The microstructures and the chemical compositions of the as-grown nanowires have been investigated by means of electron microscopy, the energy dispersive spectroscopy, and Raman spectroscopy. The results reveal that the as-grown materials consist of ZnSe nanowires with diameters ranging from 5 to 50 nm. Photoluminescence of the sample demonstrates a strong green emission from room temperature down to 10 K. This is attributed to the recombination of electrons from conduction band to the medium deep Au acceptors. (C) 2003 American Institute of Physics.

Synthesis and characterization of monodisperse spherical core-shell structured SiO2@Y3Al5O12 : Ce3+/Tb3+ phosphors for field emission displays

Nanocrystalline Y3Al5O12: Ce3+/Tb3+ ( average crystalline size 30 nm) phosphor layers were coated on non-aggregated, monodisperse and spherical SiO2 particles by the sol-gel method, resulting in the formation of core-shell structured SiO2@Y3Al5O12:Ce3+/Tb3+ particles. X-ray diffraction, Fourier transform infrared spectroscopy, transmission electron microscopy, photoluminescence, cathodoluminescence spectra, as well as lifetimes were utilized to characterize the core-shell structured SiO2@Y3Al5O12: Ce3+/Tb3+ phosphor particles. The obtained core-shell structured phosphors consist of well-dispersed submicron spherical particles with a narrow size distribution. The thickness of the Y3Al5O12:Ce3+/Tb3+ shells on the SiO2 cores ( average size about 500 nm, crystalline size about 30 nm) could be easily tailored by varying the number of deposition cycles (100 nm for four deposition cycles). Under the excitation of ultraviolet and low-voltage electron beams (1-3 kV), the core-shell SiO2@Y3Al5O12:Ce3+/ Tb3+ particles show strong yellow-green and green emission corresponding to the 5d-4f emission of Ce3+ and D-5(4)-F-7(J) ( J = 6, 5, 4, 3) emission of Tb3+, respectively.

Green light-emitting polyfluorenes with improved color purity incorporated with 4,7-diphenyl-2,1,3-benzothiadiazole moieties

By incorporating 4,7-diphenyl- 2,1,3 benzothiadiazole instead of 2,1,3-benzothiadiazole into the backbone of polyfluorene, we developed a novel series of green light- emitting polymers with much improved color purity. Compared with the state-of-the-art green light-emitting polymer, poly(fluorene-co-benzothiadiazole) (lambda max = 537 nm), the resulting polymers (lambda(max) = 521 nm) showed 10-20 nm blueshifted electroluminescence (EL) spectra and greatly improved color purity because the insertion of two phenylene units between the 2,1,3-benzothiadiazole unit and the fluorene unit reduced the effective conjugation length in the vicinity of the 2,1,3-benzothiadiazole unit. As a result, the resulting polymers emitted pure green light with CIE coordinates of (0.29, 0.63), which are very close to (0.26, 0.65) of standard green emission demanded by the National Television System Committee (NTSC). Moreover, the insertion of the phenylene unit did not affect the photoluminescence (PL) and EL efficiencies of the resulting polymers. PL quantum efficiency in solid films up to 0.82 was demonstrated. Single-layer devices (ITO/PEDOT/ polymer/Ca/Al) of these polymers exhibited a turn-on voltage of 4.2 V, luminous efficiency of 5.96 cd A(-1) and power efficiency of 2.21 lm W-1. High EL efficiencies and good color purities made these polymers very promising for display applications.

Bright green organic electroluminescent devices based on a novel thermally stable terbium complex

A navel thermally stable terbium carboxylate complex, Tb(MTP)(3)(phen) (MTP=monotetradecyl phthalate, phen=1,10-phehanthroline), was synthesized and characterized. The device structure of glass substrate/indium-tin-oxide/poly(p-phenylenevinylene) (PPV)/poly (N-vinycarbazole) (PVK):Tb(MTP)(3)(phen): 1,3,4-oxadizole derivative (PBD)/tris(8-hydroxyquinoline) (Alq(3))/aluminum (Al) was employed to study the electroluminescent properties of Tb(MTP)(3)(phen). A green emission with extremely sharp spectral band of less than 10 nm at 544 nm peak wavelength was observed. A maximum luminance of 152 cd/m(2) and an external quantum efficiency of 0.017% were achieved at a drive voltage of 24 V. A possible mechanism of energy transfer based on the polymer doped with lanthanide organic complex was also proposed.

Infrared to visible up-conversion in biocellulose yttrium vanadate nanoparticle composite membranes. Demonstration of chloroaluminum phthalocyanine light emission under up-converted light excitation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)