Flash-Sintering and Characterization of La0.8Sr0.2Ga0.8Mg0.2O3-δ Electrolytes for Solid Oxide Fuel Cells

La_0.8Sr_0.2Ga_0.8Mg_0.2O_3-δ (LSGM), a promising electrolyte material for intermediate temperature solid oxide fuel cells, can be sintered to a fully dense state by a flash-sintering technique. In this work, LSGM is sintered by the current-limiting flash-sintering process at 690°C under an electric field of 100 V cm^-1, in comparison with up to 1400°C or even higher temperature in conventional furnace sintering. The resultant LSGM samples are investigated by scanning electron microscopy, X-ray diffraction, and electrochemical impedance spectroscopy. The SEM images exhibit well-densified microstructures while XRD results show that the perovskite structure after flash-sintering does not changed. EIS results show that the conductivity of LSGM sintered by the current-limiting flash-sintering process increases with sintering current density value. The conductivity of samples sintered at 120 mA mm^-2 reaches 0.049 σ cm^-1 at 800°C, which is approximate to the value of conventional sintered LSGM samples at 1400°C. Additionally, the flash-sintering process is interpreted by Joule heating theory. Therefore, the current-limiting flash-sintering technique is proved to be an energy-efficient and eligible approach for the densification of LSGM and other materials requiring high sintering temperature.

Sinterização flash do condutor catiônico beta-alumina sintetizada pelo método dos precursores poliméricos.

A beta-alumina de sódio é uma cerâmica condutora de íons Na+ utilizada como eletrólito sólido em baterias de sódio para armazenamento de energias intermitentes como energia solar e eólica. Devido ao alto teor de sódio, esse material é instável a altas temperaturas, podendo sofrer variações de composição durante a etapa de sinterização convencional que utiliza altas temperaturas por longos períodos de tempo. A sinterização flash é uma técnica de sinterização ativada por corrente elétrica que proporciona a densificação de compactos cerâmicos em poucos segundos, a temperaturas notavelmente mais baixas que as convencionais. Uma vez obrigatória a passagem de corrente elétrica através da amostra, a sinterização flash de qualquer material condutor parece bastante razoável. Não obstante, até o presente momento a maioria dos trabalhos publicados sobre o assunto aborda apenas condutores de vacância de oxigênio ou semicondutores, materiais compatíveis com eletrodos de platina (Pt). Nesse trabalho a sinterização flash de um condutor catiônico foi estudada utilizando-se a beta-alumina como material modelo. A beta-alumina foi sintetizada pelo método dos precursores poliméricos, caracterizada e então submetida à sinterização flash. O material de eletrodo padrão (platina) provou ser um eletrodo bloqueador em contato com a beta-alumina. O sucesso da sinterização flash foi determinado pela troca do material de eletrodo por prata (Ag), o que possibilitou uma reação eletroquímica reversível nas interfaces eletrodo-cerâmica e possibilitou a obtenção de um material densificado com morfologia e composição química homogêneas. Devido à metaestabilidade da beta-alumina, a atmosfera dos experimentos precisou ser alterada para manter a integridade desse material rico em um metal alcalino (Na+). A sinterização flash de um condutor catiônico é apresentada pela primeira vez na literatura e ressalta a importância da reação de eletrodo, que é um fator limitante para o sucesso da sinterização flash e precisa ser estudada e adaptada para cada tipo de material.

Sintering of porous alumina obtained by biotemplate fibers for low thermal conductivity applications

In this research report, a sintering process of porous ceramic materials based on Al2O3 was employed using a method where a cation precursor solution is embedded in an organic fibrous cotton matrix. For porous green bodies, the precursor solution and cotton were annealed at temperatures in the range of 100-1600°C using scanning electron microscopy (SEM) and thermogravimetric (TG) analysis to obtain a porous body formation and disposal process containing organic fibers and precursor solution. In a structure consisting of open pores and interconnected nanometric grains, despite the low porosity of around 40% (calculated geometrically), nitrogen physisorption determined a specific surface area of 14m2/g, which shows much sintering of porous bodies. Energy dispersive X-ray (EDX) and X-ray diffraction (XRD) analytical methods revealed a predominant amount of α-Al2O3 in the sintered samples. Thermal properties of the sintered Al2O3 fibers were obtained by using the Laser Flash which resulted in the lower thermal conductivity obtained by α-Al2O3 and therefore improved its potential use as an insulating material. © 2012 Elsevier Ltd.

Densification and enhancement of the grain boundary conductivity of gadolinium-doped barium cerate by ultra fast flash grain welding

Doped barium cerate is a promising solid electrolyte for intermediate temperature fuel cells as a protonic conductor. However, it is difficult to sinter it to high density at a reasonable temperature. Moreover, it presents a high grain boundary resistivity at intermediate temperatures. Flash grain welding was applied to compacted samples, starting from a temperature of 910 degrees C and applying, for a short time, an ac electric polarization of 40 V, 1000 Hz. At that frequency, the resulting current flows through the grain boundaries promoting a welding via a local Joule heating. A large decrease of the grain boundary resistivity was observed by impedance spectroscopy. Scanning electron microscopy observations of polished and etched surfaces revealed highly sintered regions. Attempts were also made to combine flash grain welding with conventional sintering. (C) 2012 Elsevier Ltd. All rights reserved.

Cation size effects-modified phase and PTCR development in Er3+ and Ca2+ co-doped BaTiO3 ceramics during sintering

Development of the positive temperature coefficient of resistivity (PTCR) in Er3+ and Ca2+ co-doped ferroelectric BaTiO3 was studied in this work, with Er3+ being used to act as a donor doping. Irrespective of all the materials showing high densities after sintering at 1200 to 1300 ºC, these revealed insulator at the lowest sintering temperature, changing to semiconducting and PTCR-type materials only when the sintering temperature was further increased. Observations from X-ray diffraction help correlating this effect with phase development in this formulated (Ba,Ca,Er)TiO3 system, considering the formation of initially two separated major (Ba,Ca)TiO3- and minor (Ca,Er)TiO3-based compounds, as a consequence of cation size-induced stress energy effects. Thus, appearance and enhancement here of the semiconducting and PTCR responses towards higher sintering temperatures particularly involve the incorporation of Er3+ into the major phase, rendering finally possible the generation and "percolative-like" migration of electrons throughout the whole material.

Mechanical properties of Y-TPZ ceramics obtained by liquid phase sintering using bioglass as additive

Yttria stabilized tetragonal zirconia (Y-TZP) ceramics were sintered by liquid phase sintering at low temperatures using bioglass as sintering additive. ZrO2-bioglass ceramics were prepared by mixing a ZrO2 stabilized with 3 Mol%Y2O3 and different amounts of bioglass based on 3CaO center dot P2O5-MgO-SiO2 system. Mixtures were compacted by uniaxial cold pressing and sintered in air, at 1200 and 1300 degrees C for 120 min. The influence of the bioglass content on the densification, tetragonal phase stability, bending strength, hardness and fracture toughness was investigated. The ceramics sintered at 1300 degrees C and prepared by addition of 3% of bioglass, exhibited the highest strength of 435 MPa, hardness of 1170 HV and fracture toughness of 6.3 MPa m(1/2). These results are related to the low monoclinic phase content, high relative density and the presence of the thermal residual stress generated between the ZrO2-matrix and bioglass grain boundary, contributing to the activation of the toughening mechanisms. (c) 2007 Elsevier B.V. All rights reserved.

Effect of bioglass additions on the sintering of Y-TZP bioceramics

The objective of this work was to evaluate the influence of bioglass additions on the sintering and mechanical properties of yttria-stabilized zirconia ceramics, Y-TZP Samples containing different bioglass additions, varying between 0 and 30 wt.%, were cold uniaxial pressed at 80 MPa and sintered in air at 1200 degrees C or 1300 degrees C for 120 min. Sintered samples were characterized by X-ray Diffractometry and Scanning Electron Microscopy. Hardness and fracture toughness were determined using Vickers indentation method. As a preliminary biological evaluation, in vitro cytotoxicity tests by Neutral Red Uptake method (using mouse connective tissue cells, NCTC clone L929 from ATCC bank) were realized to determine the cytotoxicity level of ZrO(2)-bioglass ceramics. The increasing of bioglass amount leads to the decreasing of relative density due to martensitic (tetragonal-monoclinic) transformation during cooling of the sintered samples. Y-TZP samples sintered at 1300 degrees C containing 5 wt.% of bioglass presented the best results. with high relative density, hardness and fracture toughness of 11.3 GPa and 6.1 MPa m(1/2), respectively. Furthermore, the un-cytotoxic behavior was observed in all sintering conditions and bioglass amounts used in this study. (C) 2009 Elsevier B.V. All rights reserved.

CALCINED SLUDGE SINTERING EVALUATION BY HEATING MICROSCOPY THERMAL ANALYSIS

Aiming the use of the sewage sludge produced in one of the largest Brazilian wastewater treatment stations as a raw material for the ceramic industry, the sintering process of the ashes produced from its calcination was evaluated by heating microscopy thermal analysis (HMTA). From the microprocessed images, a method was developed to obtain HMTA dimensional change curves as a function of temperature, equivalent to those usually obtained from dilatometers or by thermomechanical analysis (TMA). The final product after sintering at 1050 degrees C, characterized by X-ray fluorescence spectrometry, scanning electron microscopy and X-ray dispersive energy, indicates the presence of a vitreous phase containing phosphorus, which explains the good sintering properties of the studied calcined sludge, as shown from its HMTA dimensional change curve.

Photoreactions of n-alkyl-3-nitrophenyl ethers with aromatic amines in SDS micelles: A laser flash photolysis study

The quenching of the triplet state of three n-alkyl 3-nitrophenyl ethers: 3-nitroanisol (3-NA), n-butyl 3-nitrophenyl ether (3-NB) and n-decyl 3-nitrophenyl ether (3-ND) by four aniline derivatives: aniline (AN), N,N-dimethylaniline (DMA), 2,4,6-trimethylaniline (TMA), and 4-tetradecylaniline (TDA), was investigated in aqueous micellar SDS solutions by laser flash photolysis. The transient absorption spectra for 3-NA and 3-NB reveal the formation of long-lived intermediate species in the presence of all four quenchers. while for 3-ND no amine-induced intermediates are observed. Comparison of the transient absorption spectra of the probe 3-NA in the presence of DMA in aqueous and micellar solutions shows that the intermediate species are favored by the SDS micelles. With DMA and TMA as quenchers the intermediates are suggested to be the ion radicals generated by single electron transfer from the amine to the probe in the triplet excited state. For the quenchers AN and TDA, the intermediates may be a-complexes. The relative quenching efficiencies generally decrease as the affinity of the quencher for the micellar phase (AN < DMA < TMA < TDA) increases and the mobility of the excited probe (3-NA > 2-NB) decreases. (C) 2011 Elsevier B.V. All rights reserved.

Surface oxide and the role of magnesium during the sintering of aluminum

The effect of trace additions of magnesium on the sintering of aluminum and its alloys is examined. Magnesium, especially at low concentrations, has a disproportionate effect on sintering because it disrupts the passivating Al2O3 layer through the formation of a spinel phase. Magnesium penetrates the sintering compact by solid-state diffusion, and the oxide is reduced at the metal-oxide interface. This facilitates solid-state sintering, as well as wetting of the underlying metal by sintering liquids, when these are present. The optimum magnesium concentration is approximately 0.1 to 1.0 wt pet, but this is dependent on the volume of oxide and, hence, the particle size, as well as the sintering conditions. Small particle-size fractions require proportionally more magnesium than large-size fractions do.

The influence of the atmosphere on the sintering of aluminum

Alloys of Al, Al-0.15Mg, and Al-12Sn made using air atomized aluminum powder and pressed to green densities of 75 to 98 pet were sintered under argon or nitrogen. Sintering in argon is only effective at high green densities when magnesium is present. In contrast, highly porous aluminum can be sintered in nitrogen without the need for magnesium. The oxygen concentration in the gas is reduced by the aluminum through a self-gettering process. The outer layers of the porous powder compact serve as a getter for the inner layers such that the oxygen partial pressure is reduced deep within the pore network. Aluminum nitride then forms, either by direct reaction with the metal or by reduction of the oxide layer, and sintering follows.

Sintering kinetics of Mo-free cermets

Titanium carbonitride-based cermets are important materials for contemporary cutting tools. Ceramic powders of Ti(CN), TaC, WC were mixed, compacted and heat-treated at high temperatures to form (Ti, W, Ta)(C, N) solid solution, which was then ball-milled to fine powders before being mixed with metallic binder and compacted. Liquid-phase sintering of the samples was carried out in a nitrogen atmosphere at different sintering temperatures and holding times. The microhardness and porosity of the sintered cermets were studied. It is demonstrated that the microhardness increases with sintering temperature, but at the same time, the porosity level also goes up with temperature and time. At the beginning of sintering (zero holding time), the majority of the pores are small (0.1 similar to 1 mu m); during sintering, the larger ports grow at the expense of smaller pores and the resulting pores are all concentrated in the 10 similar to 100 mu m range. The number of larger pores increases with temperature and prolonged holding time, which results in deteriorated properties. (C) 1997 Elsevier Science S.A.

Effect of temperature and heating rate on the sintering of leucite-based dental porcelains

The aim of this work was to determine the effect of temperature and heating rate on the densification of four leucite-based dental porcelains: two low-fusion (Dentsply Ceramco and Ivoclar) and two high-fusion commercial porcelains (Dentsply Ceramco). Porcelain powders were characterized by differential thermal analysis (DTA), X-ray diffraction (XRD), particle size distribution, helium picnometry, and by scanning electron microscopy. Test specimens were sintered from 600 to 1050 degrees C, with heating rates of 55 degrees C/min and 10 degrees C/min. The bulk density of the specimens was measured by the Archimedes method in water, and microstructures of fracture surfaces were analyzed by scanning electron microscopy (SEM). The results showed that densification of specimens increased with the increase in temperature. The increase in the heating rate had no effect on the densification of the porcelains studied. Both high-fusion materials and one of the low-fusing porcelains reached the maximum densification at a temperature that was 50 degrees C lower than that recommended by the manufactures. (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Surgical planning for resection of an ameloblastoma and reconstruction of the mandible using a selective laser sintering 3D biomodel

Ameloblastoma is a benign locally aggressive infiltrative odontogenic lesion. It is characterized by slow growth and painless swelling. The treatment for ameloblastoma varies from curettage to en bloc resection, and the reported recurrence rates after treatment are high; the safety margin of resection is important to avoid recurrence. Advances in technology brought about great benefits in dentistry; a new generation of computed tomography scanners and 3-dimensional images enhance the surgical planning and management of maxillofacial tumors. The development of new prototyping systems provides accurate 3D biomodels on which surgery can be simulated, especially in cases of ameloblastoma, in which the safety margin is important for treatment success. A case of mandibular follicular ameloblastoma is reported where a 3D biomodel was used before and during surgery.