Growth rate of fractal copper electrodeposits: Potential and concentration effects

Experiments are reported on fractal copper electrodeposits. An electrochemical cell was designed in order to obtain a potentiostatic control on the quasi-two-dimensional electrodeposition process. The aim was focused on the analysis of the growth rate of the electrodeposited phase, in particular its dependence on the electrode potential and electrolyte concentration.

Influence of an inert electrolyte on the morphology of quasi-two-dimensional electrodeposits

The influence of an inert electrolyte (sodium sulfate) on quasi-two-dimensional copper electrodeposition from a nondeaerated aqueous copper sulfate solution has been analyzed. The different morphologies for a fixed concentration of CuSO4 have been classified in a diagram in terms of the applied potential and the inert electrolyte concentration. The main conclusion is the extension of the well-known Ohmic model for the homogeneous growth regime for copper sulfate solutions with small amounts of sodium sulfate. Moreover, we have observed the formation of fingerlike deposits at large applied potential and inert electrolyte concentration values, before hydrogen evolution becomes the main electrode reaction.

Effect of tartrate content on aging and deposition condition of copper-tin electrodeposits from a non-cyanide acid bath

The effect of the presence of tartrate additive on the chemical stability of a Cu-Sn acid bath was evaluated. It was observed that this additive hinders decomposition of the Cu/Sn deposition bath with storage time, since the decrease in electrochemical efficiency was attenuated. In addition, it was observed that optimal galvanostatic deposition with or without tartrate occurs at approximately 11 mA cm(-2). However, in the presence of tartrate the deposition charge was lower, leading to lower energy consumption. SEM analysis showed that the tartrate added to the plating bath caused a marked change in the morphology of the Cu/Sn films obtained gal vanostatic ally. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Electrodeposition of copper on titanium wires: Taguchi experimental design approach

Electrodeposition of thin copper layer was carried out on titanium wires in acidic sulphate bath. The influence of titanium surface preparation, cathodic current density, copper sulphate and sulphuric acid concentrations, electrical charge density and stirring of the solution on the adhesion of the electrodeposits was studied using the Taguchi statistical method. A L(16) orthogonal array with the six factors of control at two levels each and three interactions was employed. The analysis of variance of the mean adhesion response and signal-to-noise ratio showed the great influence of cathodic current density on adhesion. on the contrary, the other factors as well as the three investigated interactions revealed low or no significant effect. From this study optimized electrolysis conditions were defined. The copper electrocoating improved the electrical conductivity of the titanium wire. This shows that copper electrocoated titanium wires could be employed for both electrical purpose and mechanical reinforcement in superconducting magnets. (C) 2008 Elsevier B.V. All rights reserved.

Quasi-two-dimensional electrodeposition under forced fluid flow

Experimental quasi-two-dimensional Zn electrodeposits are grown under forced convection conditions. Large-scale effects, with preferential growth towards the impinging flow, together with small-scale roughness suppression effects are evidenced and separately analyzed by using two different radial cell configurations. Interpretations are given in terms of primary concepts concerning current and concentration distributions.

Further insights on dynamic morphological transitions in quasi-two-dimensional electrodeposition

Dynamic morphological transitions in thin-layer electrodeposits obtained from copper sulphate solutions have been studied. The chemical composition of the electrodeposits indicates that they appear as a consequence of the competition between copper and cuprous oxide formation. In addition, the Ohmic control of the process is verified at initial stages of the deposit growth. At higher deposit developments, gravity-induced convection currents play a role in the control of the whole process and affect the position of these transitions.

AVALIAÇÃO DE PROPRIEDADES FÍSICAS E QUÍMICAS DE ELETRODEPÓSITOS DE Ni-W-P OBTIDOS EM CÉLULA DE HULL

Ni–W–P electrodeposits were synthesized in a Hull cell in order to simulate the obtainment under industrial conditions. Complete coverage of panels was accomplished by applying total currents of 1.0 and 2.0 A. Panels obtained with a current of 1.0 A appeared brighter. The best compositional uniformities, as determined by Energy Dispersive Spectrometer (EDS) occurred in the current density ranges of 0.6 to 3.0 A dm−2 and 1.6 to 6.0 A dm−2 obtained with 1.0 and 2.0 A, respectively. However, the best morphological characteristics, as determined by Scanning Electro Microscope (SEM), were observed in those obtained with a total current of 1.0 A. Analysis of corrosion resistance by Electrochemical Impedance Spectroscopy (EIS) and Potentiodynamic Linear Polarization (PLP) in NaCl have shown significant variations in the amount of corrosion potential, polarization resistance, and even total impedance. The alloys exhibited amorphous character (XRD) and crystallized above 400 °C to Ni and Ni3P phases, and possibly Ni–W, with a subsequent increase in hardness. The results suggest that under industrial conditions, current density variations due to the large and complex geometric shapes of substrates lead to formation of distinct alloys. Furthermore, these materials are potential substitutes for chromium deposits in many applications.

Deposition of selenium thin layers on gold surfaces from sulphuric acid media: Studies using electrochemical quartz crystal microbalance, cyclic voltammetry and AFM

In this paper we report here new considerations about the relationship between the mass and charge variations (m/z relationship) in underpotential deposition (UPD), bulk deposition and also in the H(2)Se formation reaction. Nanogravimetric experiments were able to show the adsorption of H(2)SeO(3) on the AuO surface prior to the voltammetric sweep and that, after the AuO reduction, 0.40 monolayer of H(2)SeO(3) remains adsorbed on the newly reduced Au surface, which was enough to gives rise to the UPD layer. The UPD results indicate that the maximum coverage with Se(ads) on polycrystalline gold surface corresponds to approximately 0.40 monolayer, in good agreement with charge density results. The cyclic voltammetry experiments demonstrated that the amount of bulk Se obtained during the potential scan to approximately 2 Se monolayers, which was further confirmed by electrochemical quartz crystal microbalance (EQCM) measurements that pointed out a mass variation corresponding of 3 monolayers of Se. In addition, the Se thin films were obtained by chronoamperometric experiments, where the Au electrode was polarized at +0.10V during different times in 1.0 M H(2)SO(4) + 1.0 mM SeO(2). The topologic aspects of the electrodeposits were observed in Atomic Force Microscope (AFM) measurements. Finally, in highly negative potential polarizations, the H(2)Se formation was analyzed by voltammetric and nanogravimetric measurements. These finding brings a new light on the selenium electrodeposition and point up to a proposed electrochemical model for molecule controlled surface engineering. (c) 2009 Elsevier Ltd. All rights reserved.

Electrodeposition of copper on titanium wires: Taguchi experimental design approach

Electrodeposition of thin copper layer was carried out on titanium wires in acidic sulphate bath. The influence of titanium surface preparation, cathodic current density, copper sulphate and sulphuric acid concentrations, electrical charge density and stirring of the solution on the adhesion of the electrodeposits was studied using the Taguchi statistical method. A L(16) orthogonal array with the six factors of control at two levels each and three interactions was employed. The analysis of variance of the mean adhesion response and signal-to-noise ratio showed the great influence of cathodic current density on adhesion. on the contrary, the other factors as well as the three investigated interactions revealed low or no significant effect. From this study optimized electrolysis conditions were defined. The copper electrocoating improved the electrical conductivity of the titanium wire. This shows that copper electrocoated titanium wires could be employed for both electrical purpose and mechanical reinforcement in superconducting magnets. (C) 2008 Elsevier B.V. All rights reserved.

Estudo do comportamento eletroquímico e da resistência a corrosão de eletrodepósitos de ligas ZnFe e ZnFeCo para proteção de aço

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo do comportamento eletroquímico e da resistência à corrosão de eletrodepósitos de zinco e ligas de zinco em solução de NaCL e na presença de oxi-ânions do grupo VIB

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Electrooxidation of Ethanol on Pt and PtRu Surfaces Investigated by ATR Surface-Enhanced Infrared Absorption Spectroscopy

Herein, it was investigated for the first time the electro-oxidation of ethanol on Pt and PtRu electrodeposits in acidic media by using in situ surface enhanced infrared absorption spectroscopy with attenuated total reflection (ATR-SEIRAS). The experimental setup circumvents the weak absorbance signals related to adsorbed species, usually observed for rough, electrodeposited surfaces, and allows a full description of the CO coverage with the potential for both catalysts. The dynamics of adsorption-oxidation of CO was accessed by ATR-SEIRAS experiments (involving four ethanol concentrations) and correlated with expressions derived from a simple kinetic model. Kinetic analysis suggests that the growing of the CO adsorbed layer is nor influenced by the presence of Ru neither by the concentration of ethanol. The results suggest that the C-C scission is not related to the presence of Ru and probably happens at Pt sites.

Electrodeposition of PVA-protected PtCo electrocatalysts for the oxygen reduction reaction in H2SO4

In this paper we report the electrosynthesis of PVA-protected PtCo films (PVA = poly(vinylalcohol)) and their activities towards the oxygen reduction reaction (ORR). PtCo electrodeposits were potentiostatically obtained in the presence and absence of PVA at distinct potentials. The film morphology and composition were characterized by scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX), which revealed that the use of PVA in the electrodeposition of PtCo films was decisive to achieve better film composition control. Cyclic voltammetry for PVA-protected PtCo films showed that the electrochemical surface area is dependent on the electrodeposition potentials and suggested different adsorption strengths of oxygen-containing species. Films produced in the presence of PVA presented the following activity order towards ORR as a function of the electrodeposition potential (vs. Ag/AgCl): -0.9 V> -0.8 V> -1.0 V> -0.7 V. In contrast, PtCo films electrodeposited in the absence of PVA displayed very similar activities regardless of the electrodeposition potential. The simplicity of the electrodeposition method combined with its effectiveness enabled the production of "model electrodes" for investigating the fundamental aspects of the reactions taking place in the fuel cell cathodes. (C) 2011 Elsevier B.V. All rights reserved.

Electrooxidation of ethanol on Pt and PtRu surfaces investigated by ATR surface-enhanced infrared absorption spectroscopy

Herein, it was investigated for the first time the electro-oxidation of ethanol on Pt and PtRu electrodeposits in acidic media by using in situ surface enhanced infrared absorption spectroscopy with attenuated total reflection (ATR-SEIRAS). The experimental setup circumvents the weak absorbance signals related to adsorbed species, usually observed for rough, electrodeposited surfaces, and allows a full description of the CO coverage with the potential for both catalysts. The dynamics of adsorption-oxidation of CO was accessed by ATR-SEIRAS experiments (involving four ethanol concentrations) and correlated with expressions derived from a simple kinetic model. Kinetic analysis suggests that the growing of the CO adsorbed layer is nor influenced by the presence of Ru neither by the concentration of ethanol. The results suggest that the C-C scission is not related to the presence of Ru and probably happens at Pt sites.