Thermal and structural properties of commercial dental resins light-cured with blue emitting diodes (LEDs)

We have investigated the thermal and structural properties of different commercial dental resins: Filtek(TM) Z-350, Grandio(A (R)), Tetric Ceram(A (R)), and TPH Spectrum(A (R)). The purpose of the present study was to evaluate quantitatively the photo-polymerization behavior and the effect of filler contents on the kinetic cures of the dental resins by using Differential Scanning Calorimetry (DSC) and Fourier Transform Infrared Spectroscopy (FT-IR) techniques. We have successfully obtained the low and high glass transition T (g) values of the dental composite resins from DSC curves. It was also observed a good agreement between the both T (g) values, activation energies from thermal degradation, and the degree of conversion obtained for all samples. The results have shown that Tetric Ceram(A (R)) dental resin presented the higher T (g) values, activation energy of 215 +/- A 6 KJ mol(-1), and the higher degree of conversion (63%) when compared to the other resins studied herein.

Polymerization of photocurable commercial dental methacrylate-based composites - Photocalorimetry study

Due to their excellent aesthetics, photopolymers have been extensively used in several dentistry applications. However, several problems are reported, e.g. low mechanical and abrasion resistance, shrinkage during polymerization, etc. Properties of the final restorations are intrinsically related to the polymerization stage, which can be conveniently studied by photocalorimetry. In the present work the polymerization reaction and the filler content of different photocurable commercial dental methacrylate-based composites were studied by means of photocalorimetry and thermogravimetry, respectively. The results show that the values of curing rate, the heat of polymerization and the filler content vary significantly from one composite to another.

Thermal and structural properties of commercial dental resins light-cured with blue emitting diodes (LEDs)

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Long-term quantification of the release of monomers from dental resin composites and a resin-modified glass ionomer cement

This study quantified the release of monomers from polymerized specimens of four commercially available resin composites and one glass ionomer cement immersed in water:ethanol solutions. Individual standard curves were prepared from five monomers: (1) triethylene glycol dimethacrylate (TEGDMA), (2) 2-hydroxy-ethyl methacrylate (HEMA), (3) urethane dimethacrylate (UDMA), (4) bisphenol A glycidyl dimethacrylate (BISGMA), and (5) bisphenol A. The concentration of the monomers was determined at Days 1, 7, 30, and 90 with the use of electrospray ionization/mass spectrometry. Data were expressed in mean mumol per mm(2) surface area of specimen and analyzed with Scheffe's test (P < 0.05). The following monomers were found in water: monomers (1) and (2) from Delton sealant, monomer (5) from ScotchBond Multipurpose Adhesive and Delton sealant, monomer (3) from Definite and monomer (4) from Fuji II LC, ScotchBond Multipurpose Adhesive, Synergy and Definite. All these monomers increased in concentration over time, with the exception of monomer (1) from Delton sealant. Monomers (3) and (5) were found in extracts of materials despite their absence from the manufacturer's published composition. All monomers were released in significantly higher concentrations in water:ethanol solutions than in water. The greatest release of monomers occurred in the first day. The effect of the measured concentrations of monomers (1-5) on human genes, cells, or tissues needs to be considered with the use of a biological model. (C) 2002 Wiley Periodicals, Inc.

Finite Element Analysis of Shear Versus Torsion Adhesive Strength Tests for Dental Resin Composites

Stress distributions in torsion and wire-loop shear tests were compared using three-dimensional (3-D) linear-elastic finite element method, in an attempt to predict the ideal conditions for testing adhesive strength of dental resin composites to dentin. The torsion test presented lower variability in stress concentration at the adhesive interface with changes in the proportion adhesive thickness/resin composite diameter, as well as lower variability with changes in the resin composite elastic modulus. Moreover, the torsion test eliminated variability from changes in loading distance, and reduced the cohesive fracture tendency in the dentin. The torsion test seems to be more appropriate than wire-loop shear test for testing the resin composite-tooth interface strength. (c) Koninklijke Brill NV, Leiden, 2009

Effect of curing protocol on the polymerization of dual-cured resin cements

Objectives. The purpose of this study was to evaluate how curing protocol affects the extent of polymerization of dual-cured resin cements. Methods. Four commercial resin cements were used (DuoLink, Panavia F 2.0, Variolink II and Enforce). The extent of polymerization of the resin cements cured under different conditions was measured using a (1)H Stray-Field MRI method, which also enabled to probe molecular mobility in the kHz frequency range. Results. Resin cements show well distinct behaviours concerning chemical cure. Immediate photo-activation appears to be the best choice for higher filler loaded resin cements (Panavia F 2.0 and Variolink). A photo-activation delay (5 min) did not induce any significant difference in the extent of polymerization of all cements. Significance. The extent of polymerization of dual-cured resin cements considerably changed among products under various curing protocols. Clinicians should optimize the materials choice taking into account the curing characteristics of the cements. (C) 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Color change using HSB color system of dental resin composites immersed in different common Amazon region beverages

The purpose of this study is to evaluate in vitro the color stability of composite resins when exposed to beverages with high coloring contents from the Amazon region. 240 samples from four different composite brands (Natural Look, Z350, 4Seasons and Opallis) of hue A3 were fabricated using an acrylic matrix. The samples were stored in distilled water at 37ºC for 24 hours. The initial color (T0) was registered using a Canon EOS Rebel XTi 10 mp camera, and then the samples were divided into four groups (n=15): G1 (coffee), G2 (açaí juice), G3 (energetic guaraná) and G4 (control - distilled water). The samples were exposed to solutions of DES (6hs) and RE (18hs) and placed in a double boiler under constant agitation, at 37ºC for 30 days. The samples were immersed in the coloring solutions for 15 minutes daily. After 7, 15 and 30 days, new photographic registers were made (T1, T2 and T3). The images were analyzed using Corel PHOTO-PAINT 12 software to identify the colors through the HSB system. The Kruskal-Wallis and t tests (p<0.05) demonstrated significant differences in color (hue, saturation and brightness). The results revealed that none of the tested composites showed color stability when exposed to coloring solutions, and that the Amazon region beverages (açaí juice and energetic guaraná) showed to be less coloring than coffee.

Y-TZP ceramic processing from coprecipitated powders: A comparative study with three commercial dental ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Knoop hardness of dental resin cements: Effect of veneering material and light curing methods

This study evaluated the Knoop hardness of one resin cement (dual-cure mode or light-cure mode) when illuminated directly or through restorative materials-ceramic (HeraCeram) or composite (Artglass)-by two light curing units. Light curing was carried out using a conventional quartz tungsten halogen (QTH) light source (XL2500) for 40 s, and a light emitting diodes (LED) light source (Ultrablue Is) for 40 s. Bovine incisors had their buccal faces flattened and hybridised. on these surfaces, a mould was seated and filled with cement. A disc of the veneering material (1.5 mm thickness) was positioned over this set for light curing. After storage (24 h/37 degrees C), samples (n = 10) were sectioned for hardness (KHN) measurements. Data were submitted to ANOVA and to Tukey's test (alpha = 0.05). In general, light curing with LED resulted in higher hardness values than QTH. Distinct cement behaviour was observed with different veneering material in association with different light curing units (LCUs). (C) 2006 Elsevier Ltd. All rights reserved.

The effects of exposure time on the surface microhardness of three dual-cured dental resin cements

This study evaluated the exposure time of light-curing of the polymers used for cementation on microhardness test in different storage times. The polymers (specifically called resin cements) were RelyX ARC, RelyX U100, and SET. Five specimens of each group were prepared and photo-polymerized with exposure times of 20 s and 180 s, using a LED polymerization unit with wavelength of 440 ~ 480 nm and light output was consistently 1,500 mW/cm2. The Vickers hardness test was performed in a MMT-3 Microhardness Tester. Data were submitted to ANOVA and Tukey's test (α = 0.05). The values of RelyX ARC showed statistically significant difference to groups with light exposure when considering only chemical cure (p < 0.05). The groups with light exposure (20 s and 180 s) showed no significant difference between them (p > 0.05). The RelyX U100 cured only chemically showed statistically significant difference between 48 h and 7 days (p < 0.05). The SET resin cement showed no significant difference to groups without light exposure for all storage times (p > 0.05). The values of hardening of the dual-cured resin cements improved after setting by light and chemical activation demonstrating the importance of light curing. © 2011 by the authors.

Effect of random/aligned nylon-6/MWCNT fibers on dental resin composite reinforcement

The aims of this study were (1) to synthesize and characterize random and aligned nanocomposite fibers of multi-walled carbon nanotubes (MWCNT)/nylon-6 and (2) to determine their reinforcing effects on the flexural strength of a dental resin composite.Nylon-6 was dissolved in hexafluoropropanol (10 wt%), followed by the addition of MWCNT (hereafter referred to as nanotubes) at two distinct concentrations (i.e., 0.5 or 1.5 wt%). Neat nylon-6 fibers (without nanotubes) were also prepared. The solutions were electrospun using parameters under low- (120 rpm) or high-speed (6000 rpm) mandrel rotation to collect random and aligned fibers, respectively. The processed fiber mats were characterized by scanning (SEM) and transmission (TEM) electron microscopies, as well as by uni-axial tensile testing. To determine the reinforcing effects on the flexural strength of a dental resin composite, bar-shaped (20 x 2 x 2 mm(3)) resin composite specimens were prepared by first placing one increment of the composite, followed by one strip of the mat, and one last increment of composite. Non-reinforced composite specimens were used as the control. The specimens were then evaluated using flexural strength testing. SEM was done on the fractured surfaces. The data were analyzed using ANOVA and the Tukey's test (alpha=5%).Nanotubes were successfully incorporated into the nylon-6 fibers. Aligned and random fibers were obtained using high- and low-speed electrospinning, respectively, where the former were significantly (p<0.001) stronger than the latter, regardless of the nanotubes'presence. Indeed, the dental resin composite tested was significantly reinforced when combined with nylon-6 fibrous mats composed of aligned fibers (with or without nanotubes) or random fibers incorporated with nanotubes at 0.5 wt%. (C) 2015 Elsevier Ltd. All rights reserved.

Effects of age condition on the distribution and integrity of inorganic fillers in dental resin composites

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of experimental heat treatment on mechanical properties of resin composites

The aim of this study was to verify the influence of an experimental heat treatment (170ºC/10 min) using a casting furnace on the mechanical properties (hardness and flexural strength) of 2 commercial direct resin composites (TPH Spectrum and Filtek P60) compared to a commercial indirect resin system (BelleGlass). Heat treatment temperature was determined after thermal characterization by thermogravimetry (TG) and differential scanning calorimetry (DSC). Data was analyzed by ANOVA and Tukey's test at 5% significance level. There was statistical significance for the main factor heat treatment (p=0.03) and composite (p=0.02), for flexural strength. For Knoop hardness, only the main factor composite was statistically significant (p=0.00). P60 presented higher hardness than TPH. No statistically significant correlation between mechanical properties tested was detected. Based on these results, it was possible to conclude that heat treatment influenced flexural strength of direct composites, while it was not observed for hardness. The association of direct composites with a simple post-cure heat treatment may be an alternative for current indirect composite systems, although more studies are needed to verify other properties of the composites for this application.

Novos monômeros obtidos a partir do metacrilato de glicidila, bisfenol A e 4, 4 isopropilidenodicicloexanol : síntese, caracterização estrutural e propriedades de compósitos para utilização em resinas de restauração dental

Nowadays, composite resins are the direct restorative materials more important in dental clinical performance, due to their versatility and aesthetic excellence. Bis-GMA (2,2-bis[4(2-hydroxy-3-metacryloxypropoxy)phenil]propane) is the base monomer more frequently used in restorative composite resins. However, this monomer presents some disadvantages, such as high viscosity and two aromatic rings in its structure that can promote allergic reactions to the humans. In this work, the main purpose was to synthesize new monomers from glycidyl methacrylate to use in dental restorative materials. Structural characterization of the monomers was carried out through FTIR and NMR 1H, and eight composites were produced from the new monomers, by addition of silane-treated alumino silicate particles (inorganic filler) and a photocuring system (camphorquinone and ethyl 4-dimethylaminebenzoate). The composites were analyzed by environmental scanning electronic microscopy and the water sorption and solubility, compressive strength and elastic modulus were determined. A commercial composite resin [Z100 (3M)] was used to comparison effect. The new composites presented general characteristics similar to the commercial ones; however, they didn t present the properties expected. This behavior was attributed to the lower degree of monomer reaction and to the granulometry and size distribution of the mineral filler in the polymeric matrix

Kinetic parameters and monomeric conversion of different dental composites using standard and soft-start photoactivation modes

This paper evaluates the photopolymerization kinetics and degree of conversion of different commercial dental composites when photoactivated by a LED curing unit using two different modes (standard and soft-start mode). The investigation was performed on with RelyX ARC (dual-cured), Filtek Z-350 (Nanocomposite), Filtek Z-250 (Hybrid), and Filtek Z-350flow (Flowable) resin composites. The analysis used was attenuated total reflection with a Fourier transform infrared (ATR-FTIR). The RelyX ARC resin demonstrated the highest degree of conversion with both LED photoactivation modes. For this resin a 28% decrease in maximum rate was observed and the time to reach its highest rate was almost 2.3 times higher than when the soft-start photoactivation light curing was used. Z-350flow resin recorder a higher maximum rate using the soft-start mode rather than the standard mode. In contrast, the Z-250 showed a higher value using the standard mode. Although Z-250 and Z-350 showed a higher total degree of conversion effectiveness using the soft-start mode, RelyX and Z-350flow achieved a higher value using the standard mode.