High-temperature heat capacity and heat content of CaCu3Ti4O12 (CCTO)

The isobaric heat capacity of CaCu3Ti4O12 (CCTO) was measured from 300 to 1100 K using differential scanning calorimetry (DSC). The results were verified using drop calorimetric measurement of enthalpy increment (H-T - H-298.15) at T= 973 and 1073 K. The samples were dropped from room temperature into a calorimeter maintained at high temperature. The results show small negative deviation from Neumann-Kopp rule. The enthalpy and entropy increments are computed as a function of temperature and compared with values available in the literature. The results obtained in this study are consistent with available information on enthalpy and Gibbs energy of formation of CCTO.

Wide Ranged La Modification in CCTO Ceramics Through Sol-Gel: Effect on Microstructure and Dielectric Properties

Sol-Gel method was employed to synthesize pure and wide ranged La-modified CaCu3Ti4O12 ceramics using mixed acetate-nitrate-alcoxide individual metal-ion precursors. SEM pictures revealed that grain size monotonously decreases with the extent of La incorporation. All the prepared ceramics manifested dielectric constant in the range similar to 10(3)-10(4). Dielectric loss was found to decrease with La incorporation and got optimized for 20% La3+ while retaining its high dielectric constant which may be industrially important. Room temperature Impedance spectroscopy suggested that decrease in grain resistance is responsible for reduction in dielectric loss according to Internal Barrier Layer Capacitor (IBLC) model.

Preparação e caracterização de materiais com constante dieléctrica colossal baseados em CCTO

A procura de materiais com elevada constante dieléctrica (E’) motivou nos últimos anos uma intensa pesquisa neste domínio. Entre as várias aplicações destes materiais destacam-se os dispositivos de memória baseados em componentes capacitivos, como as DRAM, em que o valor da constante dieléctrica estática (Es) determina o seu nível de miniaturização. Entre estes materiais, o CaCu3Ti4O12 (CCTO) tem sido apontado como sendo bastante interessante na perspectiva das aplicações tecnológicas e do ponto de vista científico. O CCTO tem a estrutura da perovsquite, apresentando valores elevados de E’ e uma grande estabilidade numa vasta gama de temperaturas (100 – 400 K) e frequências (100 Hz – 1 MHz). Contudo, as elevadas perdas dieléctricas (tan ) têm sido um entrave à sua aplicação tecnológica. Neste trabalho foram preparados materiais derivados do CCTO pelos métodos de reacção do estado sólido, sol-gel e fusão de zona com laser, com o principal objectivo de optimizar as amostras preparadas ao nível estrutural e morfológico, de modo a reduzir tan e aumentar a gama de frequências na qual se verifique E’colossal. Do ponto de vista da sua caracterização estrutural e morfológica usaram-se técnicas de difracção de raios X, microscopia electrónica de varrimento, espectroscopia de dispersão de raios X e espectroscopia de Raman. Para a caracterização eléctrica foram medidas a condutividade ac e dc, a impedância complexa e E’ em função da temperatura e frequência. As medidas dieléctricas mostraram a existência de mecanismos de relaxação, que foram ajustados usando o modelo de Cole-Cole. Discutiu-se a correlação entre os parâmetros de relaxação obtidos e os resultados estruturais das amostras. Atendendo a que o mecanismo de polarização que está na origem das propriedades incomuns do CCTO ainda permanece em discussão, foram produzidas amostras com uma grande diversidade morfológica, variando as condições de síntese. Foram ainda dopadas amostras de CCTO com os óxidos TeO2 e GeO2. Constatou-se que a resposta dieléctrica das amostras de CCTO policristalinas é muito dependente do tamanho de grão. Em regra, verificou-se o aumento de Es e a diminuição da resistência dos grãos e fronteiras de grão com o aumento do tamanho de grão.

Schottky-type grain boundaries in CCTO ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Crystallization and optical properties of CCTO thin films under pressure influence

CCTO thin films were deposited on Pt(111)/Ti/SiO 2/Si substrates using a chemical (polymeric precursor) and pressure method. The pressure effects on the CCTO thin films were evaluated by XRD, FEG-SEM and optical properties. Pressure films were found to be more homogeneous and dense than chemical deposition films. Pressure also leaded to an increase in the photoluminescence emission; it is suggested that the displacement of Ti in the titanate clusters, favors the charge transference from TiO 6 to [TiO 5V o z], TiO 5V o z] to [CaO 11V o z] and [TiO 5V o z] to [CuO 4] x. The low synthesis temperature used in the pressure method allows the deposition of films on less expensive substrates (i.e. glass, aluminum, polymer and others).

Red shift and higher photoluminescence emission of CCTO thin films undergoing pressure treatment

CCTO thin films were deposited on Pt(1 1 1)/Ti/SiO2/Si substrates using a chemical (polymeric precursor) and pressure method. Pressure effects on CCTO thin films were evaluated by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM) and optical properties which revealed that a pressure film (PF) is denser and more homogeneous than a chemical film (CF). Pressure also causes a decrease in the band gap and an increase in the photoluminescence (PL) emission of CCTO films which suggests that the pressure facilitates the displacement of Ti in the titanate clusters and the charge transference from TiO6 to [TiO5V0z], [TiO5V0z] to [CaO11V0z] and [TiO5V0z] to [CuO4]x. © 2013 Elsevier B.V. All rights reserved.

Influência dos defeitos cristalinos nas propriedades dielétricas e não-ôhmicas do 'CA' 'CU IND.3' 'TI IND.4' 'O IND.12'(CCTO)

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Composições varistoras à base de óxido misto de cálcio, cobre e titânio (CCTO) e titanato de cálcio (CaTiO3) e respectivo método de obtenção de blocos varistores

A presente invenção refere-se a composições varistoras à base de óxidos metálicos, mais particularmente à base de óxido misto de cálcio, cobre e titánio (CCTO), com a presença, ou não, de titanato de cálcio (CaTiO~ 3~), para conformação de blocos cerâmicos varistores (resistores não-lineares).

Synthesis of nanoparticles of the giant dielectric material, CaCu3Ti4O12 from a precursor route

A complex oxalate precursor, CaCu3(TiO)(4)(C2O4)(8)center dot 9H(2)O, (CCT-OX), was synthesized and the precipitate that obtained was confirmed to be monophasic by the wet chemical analyses, X-ray diffraction, FTIR absorption and TG/DTA analyses. The thermal decomposition of this oxalate precursor led to the formation of phase-pure calcium copper titanate, CaCu3Ti4O12, (CCTO) at a parts per thousand yen680A degrees C. The bright-field TEM micrographs revealed that the size of the as synthesized crystallites to be in the 30-80 nm range. The powders so obtained had excellent sinterability resulting in high density ceramics which exhibited giant dielectric constants upto 40000 (1 kHz) at 25A degrees C, accompanied by low dielectric losses.

In situ synthesis and characterization of polyaniline-CaCu3Ti4O12 nanocrystal composites

High dielectric constant (ca. 2.4 x 10(6) at 1 kHz) nanocomposite of polyaniline (PANI)/CaCu3Ti4O12 (CCTO) was synthesized using a simple procedure involving in situ polymerization of aniline in dil. HCl. The PANI and the composite were subjected to X-ray diffraction, Fourier transform infrared, thermo gravimetric, scanning electron microscopy and transmission electron microscopy analyses. The presence of the nanocrystallites of CCTO embedded in the nanofibers of PANI matrix was established by TEM. Frequency dependent characteristics of the dielectric constant. dielectric loss and AC conductivity were studied for the PANI and the composites. The dielectric constant increased as the CCTO content increased in PANI but decreased with increasing frequency (100 Hz-1 MHz) of measurement. The dielectric loss was two times less than the value obtained for pure PANI around 100 Hz. The AC conductivity increased slightly up to 2 kHz as the CCTO content increased in the PANI which was attributed to the polarization of the charge carriers.

Effect of the addition of B2O3 and BaO-B2O3-SiO2 glasses on the microstructure and dielectric properties of giant dielectric constant material CaCu3Ti4O12

The effect of the addition of glassy phases on the microstructure and dielectric properties of CaCu3Ti4O12 (CCTO) ceramics was investigated. Both single-component (B2O3) and multi-cornponent (30wt% BaO-60wt% B2O3-10wt% SiO2 (BBS)) glass systems were chosen to study their effect on the density, microstructure and dielectric properties of CCTO. Addition of an optimum amount of B2O3 glass facilitated grain growth and an increase in dielectric constant. However, further increase in the B2O3 content resulted in its segregation at the grain boundaries associated with a reduction in the grain size. In contrast, BBS glass addition resulted in well-faceted grains and increase in the dielectric constant and decrease in the dielectric loss. An internal barrier layer capacitance (IBLC) model was invoked to correlate the dielectric constant with the grain size in these samples. (c) 2007 Elsevier Inc. All rights reserved.

Influence of sintering conditions and doping on the dielectric relaxation originating from the surface layer effects in CaCu3Ti4O12 ceramics

Detailed investigations into the dielectric dispersion phenomenon in the giant dielectric constant material CaCu3Ti4O12 (CCTO) around room temperature revealed the existence of two successive dielectric relaxations. In the temperature domain, a new dielectric relaxation was clearly observed around 250K, in addition to the well-investigated dielectric relaxation close to 100K. The effect of sintering and doping (La3+) on the strength of these dielectric relaxations were studied in detail. The sintering temperature as well as its duration was found to have tremendous influence on the dielectric relaxation that was encountered around 250 K. This Maxwell-Wagner (M-W) type of relaxation was found to be originating from the surface layer containing the Cu-rich phase, which was ascribed to the difference in the oxygen content between the surface and the interior of the sample. Interestingly, this particular additional relaxation was not observed in La2/3Cu3Ti4O12, a low dielectric constant member of the CCTO family, in which the segregation of Cu-rich phase on the surface was absent. Indeed the correlation between the new relaxation and the presence of Cu-rich phase in CCTO ceramics was further corroborated by the absence of the same after removing the top and bottom layers. (C) 2007 Elsevier Ltd. All rights reserved.

Dielectric properties of Poly(vinylidene fluoride)/CaCu3Ti4O12 composites

The possibility of obtaining relatively high dielectric constant polymer-ceramic composite by incorporating the giant dielectric constant material, CaCu3Ti4O12 (CCTO) in a Poly(vinylidene fluoride) (PVDF) polymer matrix by melt mixing and hot pressing process was demonstrated. The structure, morphology and dielectric properties of the composites were characterized using X-ray diffraction, Thermal analysis. scanning electron microscope, and impedance analyzer. The effective dielectric constant a(epsilon(eff)) of the composite increased with increase in the volume fraction of CCTO at all the frequencies(100 Hz-1 MHz) under study. The dielectric loss did not show any variation up to 40% loading of CCTO, but showed an increasing trend beyond 40%. The room temperature dielectric constant as high as 95 at 100 Hz has been realized for the composite with 55 vol.% of CCTO, which has increased to about 190 at 150 degrees C. Theoretical models like Maxwell's, Clausius-Mossotti, Effective medium theory, logarithmic law and Yamada were employed to rationalize the dielectric behaviour of the composite and discussed. (C) 2010 Published by Elsevier Ltd.

Low Temperature Synthesis of Nano-Crystalline CaCu3Ti4O12 Through aFuel Mediated Auto-Combustion Pathway

A novel, cost effective,environment-friendly and energetically beneficial alternative method for the synthesis of giant dielectric pseudo-perovskite material CaCu3Ti4O12 (CCTO) is presented. The method involved auto-combustion of an aqueous precursor solution in oxygen atmosphere with the help of external fuels and is capable of producing high amount of CCTO at ultra-low temperature, in the combustion residue itself. The amount of phase generated was observed to be highly dependent on the combustion process i.e. on the nature and amount of external-fuels added for combustion. Two successful fuel combinations capable of producing reasonably higher amount of the desired compound were investigated. On a structural characterization grain size was observed to decrease drastically to nano-dimension compared to submicron-size that was obtained in a traditional sol-gel combustion and subsequent cacination method. Therefore, the method reported can produce nano-crystalline CaCu3Ti4O12 ceramic matrix at an ultra-low temperature and is expected to be applicable for other multifunctional perovskite oxide materials.