High-performance flexible hybrid field-effect transistors based on cellulose fiber paper

IEEE Electron Device Letters, VOL. 29, NO. 9,

Properties Of Bologna-type Sausages With Pork Back-fat Replaced With Pork Skin And Amorphous Cellulose.

Bologna-type sausages were produced with 50% of their pork back-fat content replaced with gels elaborated with different ratios of pork skin, water, and amorphous cellulose (1:1:0, 1:1:0.1, 1:1:0.2, 1:1:0.3, and 1:1:0.4). The impact of such replacement on the physico-chemical characteristics and the consumer sensory profiling was evaluated. The modified treatments had 42% less fat, 18% more protein, and 8% more moisture than the control group. Treatments with amorphous cellulose had a lower cooking loss and higher emulsion stability. High amorphous cellulose content (1:1:0.3 and 1:1:0.4) increased hardness, gumminess, and chewiness. The gel formulated with the ratio of 1:1:0.2 (pork skin: water: amorphous cellulose gel) provided a sensory sensation similar to that provided by fat and allowed products of good acceptance to be obtained. Therefore, a combination of pork skin and amorphous cellulose is useful in improving technological quality and producing healthier and sensory acceptable bologna-type sausages.

Synthesis and Characterization of Cellulose fiber-silica nanocomposites

Cellulose fiber-silica nanocomposites with novel mechanical, chemical and thermal properties have potential to be widely applied in different area. Monodispered silica nanoparticles play an important role in enhancing hybrids properties of hardness, strength, thermal stability etc. On the other hand, cellulose is one of the world’s most abundant and renewable polymers and possesses several unique properties required in many areas and biomedicine. The aim of this master thesis is to study if silica particles from reaction of sodium silicate and sulphuric acid can be adsorbed onto cellulose fiber surfaces via in situ growth. First, nanosilica particles were synthesized. Effect of pH and silica contents were tested. In theoretical part, introduction of silica, methods of preparation of nanosilica from sodium silicate, effect factors and additives were discussed. Then, cellulose fiber-silica nanocomposites were synthesis via route from sodium silicate and route silicic acid. In the experiment of route from sodium silicate, the effects of types of sodium silicate, pH and target ratio of silica to fiber were investigated. From another aspect, the effects of types of sodium silicate, fiber concentration in mixture solution and target ratio of silica to fiber were tested in the experiment of route from silicic acid. Samples were investigated via zeta potential measurement, particle size distribution, ash content measurement and Scanning Electron Microscopy (SEM). The Results of the experiment of preparing silica sol were that the particle size of silica sol was smaller prepared in pH 11.7 than that prepared in pH 9.3. Then in the experiment of synthesis of cellulose fiber-silica nanocomposites, it was concluded that the zeta potential of all the samples were around -16 mV and the highest ash content of all the samples was only 1.4%. The results of SEM images showed only a few of silica particles could be observed on the fiber surface, which corresponded to the value of ash content measurement.

Dietary fiber as fat substitute in emulsified and cooked meat model system

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Brazilian Natural Fiber (jute) As Raw Material For Activated Carbon Production.

Jute fiber is the second most common natural cellulose fiber worldwide, especially in recent years, due to its excellent physical, chemical and structural properties. The objective of this paper was to investigate: the thermal degradation of in natura jute fiber, and the production and characterization of the generated activated carbon. The production consisted of carbonization of the jute fiber and activation with steam. During the activation step the amorphous carbon produced in the initial carbonization step reacted with oxidizing gas, forming new pores and opening closed pores, which enhanced the adsorptive capacity of the activated carbon. N2 gas adsorption at 77K was used in order to evaluate the effect of the carbonization and activation steps. The results of the adsorption indicate the possibility of producing a porous material with a combination of microporous and mesoporous structure, depending on the parameters used in the processes, with resulting specific surface area around 470 m2.g-1. The thermal analysis indicates that above 600°C there is no significant mass loss.

Stability and properties of cellulose-sodium hydroxide solution systems

Since cellulose is a linear macromolecule it can be used as a material for regenerated cellulose fiber products e.g. in textile fibers or film manufacturing. Cellulose is not thermoformable, thus the manufacturing of these regenerated fibers is mainly possible through dissolution processes preceding the regeneration process. However, the dissolution of cellulose in common solvents is hindered due to inter- and intra-molecular hydrogen bonds in the cellulose chains, and relatively high crystallinity. Interestingly at subzero temperatures relatively dilute sodium hydroxide solutions can be used to dissolve cellulose to a certain extent. The objective of this work was to investigate the possible factors that govern the solubility of cellulose in aqueous NaOH and the solution stability. Cellulose-NaOH solutions have the tendency to form a gel over time and at elevated temperature, which creates challenges for further processing. The main target of this work was to achieve high solubility of cellulose in aqueous NaOH without excessively compromising the solution stability. In the literature survey an overview of the cellulose dissolution is given and possible factors contributing to the solubility and solution properties of cellulose in aqueous NaOH are reviewed. Furthermore, the concept of solution rheology is discussed. In the experimental part the focus was on the characterization of the used materials and properties of the prepared solutions mainly concentrating on cellulose solubility and solution stability.

Chitosan, sisal cellulose, and biocomposite chitosan/sisal cellulose films prepared from thiourea/NaOH aqueous solution

Environmentally friendly biocomposites were successfully prepared by dissolving chitosan and cellulose in a NaOH/thiourea solvent with subsequent heating and film casting. Under the considered conditions, NaOH/thiourea led to chain depolymerization of both biopolymers without a dramatic loss of film forming capacities. Compatibility of both biopolymers in the biocomposite was firstly assessed through scanning electron microscopy, revealing an intermediate organization between cellulose fiber network and smoothness of pure chitosan. DSC analyses led to exothermic peaks close to 285 and 315 degrees C for the biocomposite, compared to the exothermic peaks of chitosan (275 degrees C) and cellulose (265 and 305 degrees C), suggesting interactions between chitosan and cellulose. Contact angle analyses pointed out the deformation that can occur at the surface due to the high affinity of the;e materials with water. T(2) NMR relaxometry behavior of biocomposites appeared to be dominated by chitosan. Other properties of films, as crystallinity, water sorption isotherms, among others, are also discussed. (C) 2010 Published by Elsevier Ltd.

NOVEL CELLULOSE/NbOPO4 center dot nH(2)O HYBRID MATERIAL FROM SUGARCANE BAGASSE

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Novel cellulose/NbOPO 4.nH 2O hybrid material from sugarcane bagasse

In recent years studies concerning the applications of lignocellulosic/ inorganic couples have resulted in the development of an interesting class of functional materials. In this work a cellulose/NbOPO 4.nH 2O hybrid using cellulose from surgacane bagasse was prepared and characterized in order to test for adsorption applications. The preparation process was conducted by carrying out metallic niobium dilution in hydrofluoric acid in the presence of nitric acid, then adding boric acid to form the complex and, finally, the cellulose sugar cane bagasse was added. Concentrated phosphoric acid was also inserted to precipitate hydrous niobium phosphate particles in the cellulose fiber. This material was characterized by X-ray diffractometry (XRD), thermogravimetry (TG/DTG), and scanning electronic microscopy (SEM) connected to an energy dispersive spectrophotometer (EDS). Results by SEM/EDS show that NbOPO 4.nH 2O was present in structure of the cellulose. During the preparation of the material, using boric acid it was observed that the formation of precipitate occurred in a shorter time than the material prepared without boric acid.

Cellulosic Films Obtained from the Treatment of Sugarcane Bagasse Fibers with N-methylmorpholine-N-oxide (NMMO)

Ethanol/water organosolv pulping was used to obtain sugarcane bagasse pulp that was bleached with sodium chlorite. This bleached pulp was used to obtain cellulosic films that were further evaluated by Fourier transform infrared (FTIR) spectroscopy, thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). A good film formation was observed when temperature of 74 degrees C and baths of distilled water were used, which after FTIR, TGA, and SEM analysis indicated no significant difference between the reaction times. The results showed this to be an interesting and promising process, combining the prerequisites for a more efficient utilization of agro-industrial residues.

Controlo de águas do processo e optimização da produção de papel

Na Fábrica de Papel da Ponte Redonda fabricam-se sacos de papel multi-folhas e papel reciclado do tipo Kraft. Tendo em consideração a primeira actividade, é de grande interesse optimizar o processo de fabrico de papel com vista a incorporara a máxima taxa de papel produzido internamente nas diferentes camadas dos sacos de papel. Os papéis de maior interesse são os do tipo Fluting e Liners, tendo sido produzidos em 2010 um total de 4,9 mil toneladas, ou seja 90% de todo o papel fabricado em 2010, correspondendo a a 4 mil toneladas de papéis do tipo Liners e 0,9 mil toneladas para os papéis do tipo Fluting. Nos papéis do tipo Liners incluem-se os papéis do tipo Test-Liner e Kraft-Liner, representando em termos produtivos valores idênticos. No âmbito deste trabalho, em que se pretendeu controlar as águas do processo e optimizar a produção de papel, foram introduzidos uma unidade de flutuação e um sistema que permitisse regular a consistência da suspensão fibrosa à entrada da máquina do papel, e foram ainda estudadas as possibilidades de adição de produtos químicos para melhorar as características da pasta assim como um tratamento microbiológico mais eficaz para todo o processo. Para se avaliar se as medidas implementadas teriam um impacto positivo na qualidade desses dois tipos de papéis, desenvolveu-se o trabalho em duas fases: a primeira envolve a introdução de um sistema de flutuação e de um sistema de controlo de consistência da pasta, assim como a selecção de produtos químicos a adicionar ao processo. A segunda fase consistiu na avaliação do efeito destas medidas nas características do papel fabricado. Para o efeito foram escolhidos dois tipos de papel e de diferentes gramagens, nomeadamente Test-Liner de 80 g/m2 e Fluting de 110 g/m2. Introduziu-se um flutuador com o objectivo de tratar parte das águas do processo de fabrico com vista a serem reutilizadas em determinadas aplicações possíveis para a qualidade da água obtida (lavagens e água do processo), de modo a conseguir-se uma poupança de água, assim como aproveitar-se as lamas resultantes, ricas em fibra de celulose, para utilizá-las como matéria-prima. Foi introduzido um regulador de consistência no processo da Ponte Redonda com o objectivo de alimentar de uma forma constante a consistência da pasta à entrada da máquina do papel proporcionando uma melhor formação da folha, devido à ligação entre fibras, na direcção máquina e direcção transversal. Esse sistema inovador é um Regulador de Consistência que vem proporcionar à máquina do papel uma alimentação em fibra mais constante. O fabrico de papel apenas a partir de fibras de celulose não permitirá obter um papel com as características desejadas para a sua utilização. Para corrigir estas deficiências, são adicionados produtos químicos para atribuir ou melhorar as propriedades dos papéis. Desta forma considerou-se interessante introduzir no processo um agente de retenção numa fase posterior à preparação da pasta e antes da chegada à máquina de papel, de forma a melhorar as características da suspensão fibrosa. Assim foi implementado um sistema cuja eficácia foi avaliada. Concluiu-se que com a sua implementação a máquina de papel apresentou melhores resultados na drenagem e na turbidez da água removida, significando uma água com menor teor de matéria suspensa e dissolvida, devido à melhor agregação das fibras dispersas na suspensão fibrosa, levando a um aumento da drenagem e consequentemente melhor eficiência das prensas e secaria. Foi também elaborado um estudo para introdução de um sistema de tratamento microbiológico em todo o processo de fabrico de papel, devido à existência de microorganismos prejudiciais ao seu fabrico. Concluiu-se que a água clarificada proveniente do flutuador apresentou qualidade aceitável para os objectivos pretendidos. No entanto, considerando a eficiência de 26,5% na remoção de sólidos suspensos será necessário mais algum tempo de utilização da água clarificada, cerca de um ano, para avaliar se esta terá algum efeito prejudicial nos equipamentos. Verificou-se que devido à existência de microrganismos em todo o processo de fabrico de papel será necessário efectuar lavagens aos tinões, tanques e circuitos com alguma regularidade, aproveitando-se as paragens do processo assim como implementar um sistema de tratamento microbiológico mais eficaz. Em resultado das medidas implementadas concluiu-se que os papéis produzidos apresentaram melhorias, tendo-se obtido melhores resultados em todos os ensaios de resistência. No papel do tipo Test-Liner destacam-se os bons resultados nos ensaios de superfície, Cobb60 e rebentamento. No caso do parâmetro do Cobb60, foi um resultado surpreendente visto que por norma este tipo de papéis reciclados não suportam este ensaio. Concluiu-se também que as medidas implementadas proporcionaram uma melhor agregação e ligação entre fibras, e melhor formação da folha na máquina do papel proporcionando aos papéis propriedades físico-mecânicas mais interessantes.

Kalvosuodatusprosessin tehostaminen paperiteollisuuden sovelluksissa

Tässä diplomityössä tutkittiin kalvosuodatuksen esikäsittelymenetelmiä ja kalvonpesua. Työn kirjallisuusosassa käsitellään vuon alenemiseen vaikuttavia tekijöitä, esikäsittelymenetelmiä ja kalvonpesua. Kokeellisessa osassa tutkittiin kemiallisten esikäsittelyjen vaikutusta vuon alenemiseen paperitehtaan happaman kiertoveden kirkkaan suodoksen kalvosuodatuksessa. Esikäsittelykemikaalit olivat ympäristöystävällisiä ja paperinvalmistusprosessiin soveltuvia. Lisäksi tutkittiin kalvonpesuaineiden pesutehokkuuksia. Tutkitut esikäsittelyaineet olivat mikrokiteinen kitosaani, karboksimetyyliselluloosa, selluloosa- ja puukuitu sekä kaupallinen antiskalantti. Pesuaineista tutkittiin kolmea kaupallista kalvonpesuainetta, yhtä kalvopesun tehostusainetta sekä peretikkahappoa. Kokeet tehtiin kahdella laboratoriomittakaavaisella kalvosuodattimella. Kalvoina käytettiin kahta nanosuodatus- ja yhtä ultrasuodatuskalvoa. Vuon alenemista tutkittiin suodatuksen aikaisena alenemisena ja vesivuohon verrattavana alenemisena. Esikäsittelyjen vaikutusta erotustehokkuuteen tutkittiin ioni-, johtokyky-, orgaanisen hiilen kokonaispitoisuus-, sokeri-, sameus- ja ligniinireduktioilla. Lisäksi määritettiin kalvon likaantuminen suodatuksen aikana vesivuon määrityksillä ennen ja jälkeen suodatuksen. Pesutehokkuus määritettiin vesivuon määrityksillä suodatuksen jälkeen ja pesun jälkeen. Kitosaani- ja karboksimetyyliselluloosakäsittelyillä oli vuon alenemista estävä vaikutus hydrofiilisellä nanosuodatuskalvolla suodatettaessa. Kitosaanikäsittelyn 5 g/dm3:n ja karboksimetyyliselluloosakäsittelyn 2 g/ dm3:n annostuksella vuot alentuivat suodatuksen aikana 8 %-yksikköä vähemmän kuin ilman esikäsittelyä. Puukuitukäsittely stabiloi 0,1 g/dm3:n annostuksella saman kalvon vuota, kun kiintoainetta ei poistettu syötöstä. Hydrofobisen nanosuodatuskalvon vuon alenemista ehkäisivät puu- ja selluloosakuitukäsittelyt sekä karboksimetyyliselluloosakäsittely. Karboksimetyyliselluloosakäsittely vähensi vuon alenemista 25 %-yksikköä ja puukuitukäsittely 13 %-yksikköä. Hydrofiilisellä ultrasuodatuskalvolla vuon aleneminen oli pientä ilman esikäsittelyä. Reduktioihin esikäsittelyt vaikuttivat parhaiten ultrasuodatuskalvolla. Kitosaanikäsittely nosti 1 g/dm3:n annostuksella alumiinireduktion 50 %:sta 96 %:iin ja 5 g/dm3:n annostuksella rautareduktion 30 %:sta 55 %:iin. Karboksyylimetyyliselluloosakäsittelyt vaikuttivat parantavasti mangaanin, magnesiumin, raudan ja kalsiumin reduktioihin. Optimi karboksyylimetyyliselluloosa-annostus oli 2 g/dm3. Merkittävin reduktion nousu oli kalsiumilla, jonka reduktio nousi esikäsittelyllä 4 %:sta 57 %:iin. Reduktiota nostava mekanismi oli kalvon pinnalle muodostuva sekundaarikerros. Pesuaineista tehokkain oli entsyymiä sisältävä kalvonpesuaine. Suurin vaikutus sillä oli hydrofobisen nanosuodatuskalvon pesussa. Optimiannostuksella (0,5 %) kalvon vesivuo pesun jälkeen oli 114 % pesua edeltäneestä vesivuosta. Muut kaupalliset pesuaneet oli tehokkaita hydrofiilisille kalvoille. Peretikkahappo oli yksittäisenä pesuaineena heikkotehoinen.