In this work, we present an investigation on the thickness of the eroded enamel layer in tooth samples after exposure to citric and hydrochloric acid by using Scanning Electrochemical Microscopy (SECM). Approaching curves with typical negative feedback behavior were obtained in enamel samples for evaluation of topographic changes. In a control experiment, SECM images showed no significant difference in the current monitored during the scan, implying that enamel demineralization did not occur in mineral water medium. Topographic SECM images obtained after contact with citric and hydrochloric acid for different periods of time showed a significant increase in the current relative to a previously protected surface, indicating the structural loss of enamel. The thickness of the enamel layer eroded after contact with hydrochloric acid was significantly higher when compared to the one obtained with citric acid. Hence, our results showed that the enamel acid erosion is a relatively fast process, which is strongly dependent on parameters such as pH, time, acid strength and acid concentration.

Erosion-corrosion of mild steel in hot caustic. Part II: The effect of acid cleaning

Corrosion rates of 1020 steel in 2.75 M NaOH solution at a temperature of 160 degrees C and velocities of 0.32 and 2.5 m/s were studied. The focus was on the effect of the acid cleaning which was performed by using strong, inhibited sulphuric acid in between the exposures to caustic. In situ electrochemical methods were used to measure the corrosion rate such as the potentiodynamic sweep and the polarization resistance method. Also used were the weight-loss method and scanning electron microscopy (SEM). Eight electrodes/coupons were used to monitor the metal loss rate, four were placed at the low velocity section, while the other four were placed in the high velocity section of a high temperature flow. The first three coupons in each section were placed within the disturbed flow region, while the fourth was placed in a fully developed flow region. During the exposure of mild steel to the inhibited acid, following the first caustic period, the corrosion rate increased significantly to between 3 and 10mm/y with a few electrodes experiencing as high as 50 mm/y. The second caustic period following the acidic period typically started with very high corrosion rates (20-80 mm/y). The length of this corrosion period was typically 2-3 h with a few exceptions when the high corrosion period lasted 7-10 h. Following the very high corrosion rates experienced at the beginning of the second caustic period, the corrosion rates were reduced sharply (as the corrosion potential increased) to nearly the same levels as those observed during the passive part of the first caustic period. (c) 2005 Elsevier Ltd. All rights reserved.

The efficacy of a highly concentrated fluoride dentifrice on bovine enamel subjected to erosion and abrasion

Background. Researchers have proposed the use of fluoride for the prevention of enamel wear; however, only limited information is available about the impact of fluoridated dentifrices. Because tooth wear is a well-recognized dental problem, the authors conducted an in situ, ex vivo study to assess the efficacy of a highly concentrated fluoride dentifrice on bovine enamel subjected to erosion and abrasion. Methods. The authors conducted a double-blind, crossover in situ study consisting of three phases (seven days each). In each phase, the authors tested one of the dentifrices (5,000 parts per million fluoride [F]; 1,100 ppm F; no F). They performed erosive challenges with the use of cola drink (60 seconds, four times per day) and abrasive challenges via toothbrushing (30 seconds, four times per day). The authors determined the enamel loss via profilometry. Results. The authors tested the data by using two-way analysis of variance (P <.05). For the erosion-plus-abrasion condition, the study results showed that enamel wear was significantly higher than that with erosion alone. The findings showed no significant differences between the dentifrices regarding enamel wear. Conclusions. Within the in situ, ex vivo conditions of this study, the authors concluded that the highly concentrated fluoride dentifrice did not have a protective effect on enamel against erosion and erosion plus toothbrushing abrasion. Clinical Implications. Patients at risk of developing enamel erosion should benefit from preventive measures other than fluoride dentifrice, because even a highly concentrated fluoride dentifrice does not appear to prevent enamel erosion.

In vitro evaluation of the microhardness of bovine enamel exposed to acid solutions after bleaching

Acid erosion is a superficial loss of enamel caused by chemical processes that do not involve bacteria. Intrinsic and extrinsic factors, such as the presence of acid substances in the oral cavity, may cause a pH reduction, thus potentially increasing acid erosion. The aim of this study was to evaluate the microhardness of bleached and unbleached bovine enamel after immersion in a soda beverage, artificial powder juice and hydrochloric acid. The results obtained for the variables of exposure time, acid solution and substrate condition (bleached or unbleached enamel) were statistically analyzed by the ANOVA and Tukey tests. It was concluded that a decrease in microhardness renders dental structures more susceptible to erosion and mineral loss, and that teeth left unbleached show higher values of microhardness compared to bleached teeth.

Effects of buffering properties and undissociated acid concentration on dissolution of dental enamel in relation to pH and acid type

To quantify the relationships between buffering properties and acid erosion and hence improve models of erosive potential of acidic drinks, a pH-stat was used to measure the rate of enamel dissolution in solutions of citric, malic and lactic acids, with pH 2.4-3.6 and with acid concentrations adjusted to give buffer capacities (β) of 2-40 (mmol·l(-1))·pH(-1) for each pH. The corresponding undissociated acid concentrations, [HA], and titratable acidity to pH 5.5 (TA5.5) were calculated. In relation to β, the dissolution rate and the strength of response to β varied with acid type (lactic > malic ≥ citric) and decreased as pH increased. The patterns of variation of the dissolution rate with TA5.5 were qualitatively similar to those for β, except that increasing pH above 2.8 had less effect on dissolution in citric and malic acids and none on dissolution in lactic acid. Variations of the dissolution rate with [HA] showed no systematic dependence on acid type but some dependence on pH. The results suggest that [HA], rather than buffering per se, is a major rate-controlling factor, probably owing to the importance of undissociated acid as a readily diffusible source of H(+) ions in maintaining near-surface dissolution within the softened layer of enamel. TA5.5 was more closely correlated with [HA] than was β, and seems to be the preferred practical measure of buffering. The relationship between [HA] and TA5.5 differs between mono- and polybasic acids, so a separate analysis of products according to predominant acid type could improve multivariate models of erosive potential.

Avaliação in vitro da microdureza superficial do esmalte bovino exposto a soluções ácidas, após receber ou não, clareamento com peróxido de hidrogênio a 35%

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Desenvolvimento de microssensores eletroquímicos e aplicações no estudo de processos dinâmicos interfaciais utilizando microscopia eletroquímica de varredura

O trabalho descrito nesta tese mostra de forma detalhada a fabricação e caracterização de diferentes microssensores eletroquímicos os quais têm sido recentemente utilizados como sondas em grupo de técnicas conhecida como Scanning Electrochemical Probe Microscopy (SEPM). Desta forma, a caracterização de superfícies pode ser feita explorando diferentes fenômenos interfaciais relevantes à Ciência. Neste sentido, as interfaces de materiais cristalinos como hidroxiapatita (materiais dentários) e calcita foram o foco de estudo neste trabalho. Assim, diferentes técnicas SEPM foram exploradas no sentido de se obter informações relevantes relacionadas aos processos dentários, como a erosão ácida e hipersensibilidade. Inicialmente, microeletrodos de platina foram desenvolvidos empregando uma metodologia convencional na qual são utilizados microfibras encapsuladas em capilares de vidro. Scanning Electrochemical Microscopy (SECM) no modo amperométrico foi utilizada para obtenção de informações com relação às alterações de topografia do esmalte dentário causadas pelo contato com substâncias ácidas. Adicionalmente, SECM foi empregada no estudo do transporte de espécies eletroativas em amostras de dentina e investigações relacionadas ao bloqueio dos túbulos empregando-se cremes dentais comerciais foram realizadas. A permeação de peróxido de hidrogênio pela dentina também foi estudada. Os resultados de SECM foram comparados com imagens SEM obtidas nas mesmas condições experimentais. Microeletrodos de membrana ionófora íon-seletiva (Ion Selective Microelectrodes-ISMEs) sensíveis a íons cálcio também foram desenvolvidos e caracterizados, com subsequente aplicação em SECM no modo potenciométrico. A dissolução ácida de esmalte bovino (erosão dentária) foi investigada em diferentes valores de pH (2,5; 4,5; 6,8). Além disso, o transporte de íons cálcio através de membranas porosas sintéticas foi avaliado a uma distância tip/substrato de 300µm. Alterações no fluxo de íons cálcio foram correlacionadas em experimentos realizados na presença e ausência de campos magnéticos gerados por nanopartículas de magnetita incorporadas à membrana porosa. Microcristais de calcita facilmente sintetizados pelo método de precipitação foram utilizados como superfície modelo para investigações interfaciais, cujos resultados podem ser correlacionados aos materiais dentários. Desta forma, nanopipetas de vidro preenchidas com eletrólito suporte foram fabricadas e utilizadas como sonda em Scanning Ion Conductance Microscopy (SICM). O mapeamento topográfico de alta resolução espacial da superfície de um microcristal de calcita foi obtido utilizando o modo de varredura hopping mode. Adicionalmente, sondas multifuncionais ISME-SICM também foram desenvolvidas e caracterizadas para investigações simultâneas com relação às alterações topográficas e quantificação de íons cálcio sobre a superfície de um microcristal de calcita. A adição de reagentes ácidos no canal SICM promoveu a dissolução da superfície do microcristal, sendo obtidos dados cinéticos de dissolução. Investigações em meio neutro também foram realizadas utilizando a sonda ISME-SICM. Os resultados experimentais obtidos também foram comparados com aqueles oriundos de simulação computacional.

Surface and subsurface erosion of primary enamel by acid beverages over time

This study evaluated the influence of a cola-type soft drink and a soy-based orange juice on the surface and subsurface erosion of primary enamel, as a function of the exposure time. Seventy-five primary incisors were divided for microhardness test (n=45) or scanning electron microscopy (SEM) analysis (n=30). The specimens were randomly assigned to 3 groups: 1 - artificial saliva (control); 2 - cola-type soft drink; and 3 - soy-based orange juice. Immersion cycles in the beverages were undertaken under agitation for 5 min, 3 times a day, during 60 days. Surface microhardness was measured at 7, 15, 30, 45 and 60 days. After 60 days, specimens were bisected and subsurface microhardness was measured at 30, 60, 90, 120, 150 and 200 µm from the surface exposed. Data were analyzed by ANOVA and Tukey’s test (a=0.05). Groups 2 and 3 presented similar decrease of surface microhardness. Regarding subsurface microhardness, group 2 presented the lowest values. SEM images revealed that after 60 days the surfaces clearly exhibited structural loss, unlike those immersed in artificial saliva. It may be concluded that erosion of the surfaces exposed to the cola-type soft drink was more accentuated and directly proportional to the exposure time.

Dental erosion patterns from intrinsic acid regurgitation and vomiting

Background: The distribution of lesions from dental erosion due to intrinsic acid regurgitation and vomiting may be different from patterns of dental erosion due to extrinsic acids. To date studies have failed to validate this assumption. This study described the sites and nature of lesions from dental erosion in cases of intrinsic acid regurgitation, and compared them with the distribution of lesions occurring in age and sex matched controls, whose lesions are due to extrinsic acids. Methods: The University of Queensland tooth wear clinic patients were screened to select 30 cases, 21 self-identified bulimics and nine medically diagnosed chronic gastric acid regurgitators, and 30 controls. Epoxy resin models of the subjects' dentition were examined under stereoscopic light microscope at magnification 16 to 40. The patterns and sites of tooth wear were recorded for teeth representative of 20 tooth sites in every subject. Results: While the incisal edges of maxillary and mandibular anterior teeth of acid regurgitators were more frequently affected by erosion, incisal attrition was more common on controls' teeth. Cervical lesions were more commonly found in association with incisal attrition in the controls, and in association with incisal erosion in the cases. In 10 per cent of sites in case subjects, cervical lesions associated with incisal erosion were found on the lingual aspects of their mandibular incisors, canines and premolars. These lesions were almost exclusive to the case subjects. Conclusions: These results validate that lingual cervical lesions associated with incisal erosion on the mandibular anterior teeth are strong discriminators between tooth wear in patients with bulimia nervosa or chronic gastro-oesophageal reflux and those whose dental erosion is due to extrinsic acids.

Insights into preventive measures for dental erosion

Dental erosion is defined as the loss of tooth substance by acid exposure not involving bacteria. The etiology of erosion is related to different behavioral, biological and chemical factors. Based on an overview of the current literature, this paper presents a summary of the preventive strategies relevant for patients suffering from dental erosion. Behavioral factors, such as special drinking habits, unhealthy lifestyle factors or occupational acid exposure, might modify the extent of dental erosion. Thus, preventive strategies have to include measures to reduce the frequency and duration of acid exposure as well as adequate oral hygiene measures, as it is known that eroded surfaces are more susceptible to abrasion. Biological factors, such as saliva or acquired pellicle, act protectively against erosive demineralization. Therefore, the production of saliva should be enhanced, especially in patients with hyposalivation or xerostomia. With regard to chemical factors, the modification of acidic solutions with ions, especially calcium, was shown to reduce the demineralization, but the efficacy depends on the other chemical factors, such as the type of acid. To enhance the remineralization of eroded surfaces and to prevent further progression of dental wear, high-concentrated fluoride applications are recommended. Currently, little information is available about the efficacy of other preventive strategies, such as calcium and laser application, as well as the use of matrix metalloproteinase inhibitors. Further studies considering these factors are required. In conclusion, preventive strategies for patients suffering from erosion are mainly obtained from in vitro and in situ studies and include dietary counseling, stimulation of salivary flow, optimization of fluoride regimens, modification of erosive beverages and adequate oral hygiene measures.

The influence of residual salivary fluoride from dentifrice on enamel erosion: an in situ study

The objective of this study was to assess the salivary residual effect of fluoride dentifrice on human enamel subjected to an erosive challenge. This crossover in situ study was performed in two phases (A and B), involving ten volunteers. In each phase, they wore acrylic palatal appliances, each containing 3 human enamel blocks, during 7 days. The blocks were subjected to erosion by immersion of the appliances in a cola drink for 5 minutes, 4 times a day. Dentifrice was used to brush the volunteers’ teeth, 4 times a day, during 1 minute, before the appliance was replaced into the mouth. In phases A and B the dentifrices used had the same formulation, except for the absence (PD) or presence (FD) of fluoride, respectively. Enamel alterations were determined using profilometry, microhardness (%SMHC), acid- and alkali-soluble F analysis. The data were tested using ANOVA (p < 0.05). The concentrations (mean ± SD) of alkali- and acid-soluble F (µgF/cm²) were, respectively, PD: 1.27ª ± 0.70/2.24A ± 0.36 and FD: 1.49ª ± 0.44/2.24A ± 0.67 (p > 0.05). The mean wear values (± SD, µm) were PD: 3.63ª ± 1.54 and FD: 3.54ª ± 0.90 (p > 0.05). The mean %SMHC values (± SD) were PD: 89.63ª ± 4.73 and FD: 87.28ª ± 4.01 (p > 0.05). Thus, we concluded that the residual fluoride from the fluoride-containing dentifrice did not protect enamel against erosion.

Effect of Nd:YAG Laser and Acidulated Phosphate Fluoride on Bovine and Human Enamel Submitted to Erosion/Abrasion or Erosion Only: An in Vitro Preliminary Study

Objective: The aim of the present in vitro study was to evaluate, using two different methodologies, the effectiveness of pulsed Nd:YAG laser irradiation associated with topical acidulated phosphate fluoride (APF) for preventing enamel erosion and structure loss under regimes of erosion and abrasion or erosion only. Background Data: An increased incidence of noncarious lesions (erosion and abrasion) has been observed, consequently new preventative therapies have been proposed. Materials and Methods: Two different methodologies were performed. For the first, 100 bovine crowns were submitted to four different treatments (n = 25): no treatment (control), 4 min application of APF, Nd:YAG laser irradiation (1 W, 100 mJ, 10 Hz, 141.5 J/cm(2)), and Nd:YAG laser irradiation+4 min of APF. After the specimens were exposed to citric acid (2% w/v; 30 min), they were submitted to 5000 brushing cycles. Specimen mass was measured before and after the treatments. For the second methodology, 20 human crowns were embedded in acrylic resin and cut surfaces were exposed and polished. The specimens were divided into four groups (n = 10): no treatment (control), APF for 4 min, Nd:YAG laser irradiation (1 W, 100 mJ, 10 Hz, 125 J/cm(2)), and Nd:YAG laser irradiation+APF. The samples were then immersed in citric acid (2% w/v; 90 min). Vickers hardness was obtained before and after the treatments. Results: The Nd:YAG laser irradiation+APF (bovine and human enamel) was more effective and yielded statistically significant results for surface microhardness and enamel wear. Conclusion: Nd:YAG laser irradiation associated with APF reduced bovine enamel wear and human enamel softening when samples were submitted to a regime of erosion and abrasion or erosion only in vitro.

Effect of a Single Application of TiF(4) and NaF Varnishes and Solutions Combined with Nd:YAG Laser Irradiation on Enamel Erosion in Vitro

Objective: This in vitro study aimed to analyze the influence of neodymium-doped yttrium aluminum garnet (Nd:YAG) laser irradiation on the efficacy of titanium tetrafluoride (TiF(4)) and sodium fluoride (NaF) varnishes and solutions to protect enamel against erosion. Background data: The effect of Nd:YAG laser irradiation on NaF and AmF was analyzed; however, there is no available data on the interaction between Nd:YAG laser irradiation and TiF(4). Methods: Bovine enamel specimens were pre-treated with NaF varnish, TiF(4) varnish, NaF solution, TiF(4) solution, placebo varnish, Nd:YAG (84.9 J/cm(2)), Nd:YAG prior to or through NaF varnish, Nd:YAG prior to or through TiF(4) varnish, Nd:YAG prior to or through NaF solution, Nd:YAG prior to or through TiF(4) solution, and Nd:YAG prior to or through placebo varnish. Controls remained untreated. Ten specimens in each group were then subjected to an erosive demineralization (Sprite Zero, 4x90 s/day) and remineralization (artificial saliva, between the erosive cycles) cycling for 5 days. Enamel loss was measured profilometrically (mu m). Additionally, treated but non-eroded specimens were additionally analyzed by scanning electron microscope (SEM) (each group n-2). The data were statistically analyzed by ANOVA and Tukey's post-hoc test (p < 0.05). Results: Only TiF(4) varnish (1.8 +/- 0.6 mu m), laser prior to TiF(4) varnish (1.7 +/- 0.3 mu m) and laser prior to TiF(4) solution (1.4 +/- 0.3 mu m) significantly reduced enamel erosion compared to the control (4.1 +/- 0.6 mu m). SEM pictures showed that specimens treated with TiF(4) varnish presented a surface coating. Conclusions: Nd:YAG laser irradiation was not effective against enamel erosion and it did not have any influence on the efficacy of F, except for TiF(4) solution. On the other hand, TiF(4) varnish protected against enamel erosion, without the influence of laser irradiation.

Effect of Titanium Tetrafluoride and Amine Fluoride Treatment Combined with Carbon Dioxide Laser Irradiation on Enamel and Dentin Erosion

Objective: This in vitro study aimed to analyze the influence of carbon dioxide (CO(2)) laser irradiation on the efficacy of titanium tetrafluoride (TiF(4)) and amine fluoride (AmF) in protecting enamel and dentin against erosion. Methods: Bovine enamel and dentin samples were pretreated with carbon dioxide (CO(2)) laser irradiation only (group I), TiF(4) only (1% F, group II), CO(2) laser irradiation before (group III) or through (group IV) TiF(4) application, AmF only (1% F, group V), or CO(2) laser irradiation before (group VI) or through (group VII) AmF application. Controls remained untreated. Ten samples of each group were then subjected to an erosive demineralization and remineralization cycling for 5 days. Enamel and dentin loss were measured profilometrically after pretreatment, 4 cycles (1 day), and 20 cycles (5 days) and statistically analyzed using analysis of variance and Scheffe's post hoc tests. Scanning electron microscopy (SEM) analysis was performed in pretreated but not cycled samples (two samples each group). Results: After 20 cycles, there was significantly less enamel loss in groups V and IV and significantly less dentin loss in group V only. All other groups were not significantly different from the controls. Lased surfaces (group I) appeared unchanged in the SEM images, although SEM images of enamel but not of dentin showed that CO(2) laser irradiation affected the formation of fluoride precipitates. Conclusion: AmF decreased enamel and dentin erosion, but CO(2) laser irradiation did not improve its efficacy. TiF(4) showed only a limited capacity to prevent erosion, but CO(2) laser irradiation significantly enhanced its ability to reduce enamel erosion.