Transport properties of YBa 2 Cu 3 O 7, PrBa 2 Cu 3 O 7-superlattices

The understanding of the coupling between superconducting YBa2Cu3O7 (YBCO) layers decoupled by non superconducting PrBa2Cu3O7 (PBCO) layers in c-axis oriented superlattices was the aim of this thesis. For this purpose two conceptually different kind of transport experiments have been performed. rnrnIn the first type of transport experiments the current is flowing parallel to the layers. Here the coupling is probed indirectly using magnetic vortex lines, which are penetrating the superlattice. Movement of the vortex segments in neighbouring YBCO layers is more or less coherent depending on the thickness of both the superconducting and non superconducting layers. This in-plane transport was measured either by sending an external current through bridges patterned in the superlattice or by an induced internal current. rnThe vortex-creep activation energy U was determined by analysis of the in-plane resistive transition in an external magnetic field B oriented along the c-axis. The activation energies for two series of superlattices were investigated. In one series the thickness of the YBCO layers was constant (nY=4 unit cells) and the number of the PBCO unit cells was varied, while in the other the number of PBCO layers was constant (nP=4) and nY varied. The correlation length of the vortex system was determined to be 80 nm along the c-axis direction. It was found that even a single PBCO unit cell in a superlattice effectively cuts the flux lines into shorter weakly coupled segments, and the coupling of the vortex systems in neighbouring layers is negligible already for a thickness of four unit cells of the PBCO layers. A characteristic variation of the activation energy for the two series of superlattices was found, where U0 is proportional to the YBCO thickness. A change in the variation of U0 with the current I in the specimen was observed, which can be explained in terms of a crossover in the vortex creep process, generated by the transport current. At low I values the dislocations mediated (plastic) vortex creep leads to thermally assisted flux-flow behaviour, whereas at high current the dc transport measurements are dominated by elastic (collective) creep.rnThe analysis of standard dc magnetization relaxation data obtained for a series superlattices revealed the occurrence of a crossover from elastic (collective) vortex creep at low temperature to plastic vortex creep at high T. The crossover is generated by the T dependent macroscopic currents induced in the sample. The existence of this creep crossover suggests that, compared with the well known Maley technique, the use of the normalized vortex creep activation energy is a better solution for the determination of vortex creep parameters.rnrnThe second type of transport experiments was to measure directly a possible Josephson coupling between superconducting CuO2 double planes in the superlattices by investigation of the transport properties perpendicular to the superconducting planes. Here three different experiments have been performed. The first one was to pattern mesa structures photolithographically as in previous works. The second used three-dimensional nanostructures cut by a focused ion beam. For the these two experiments insufficient patterning capabilities prevented an observation of the Josephson effect in the current voltage curves. rnA third experiment used a-axis and (110) oriented YBCO films, where in-plane patterning can in principle be sufficient to measure transport perpendicular to the superconducting planes. Therefore the deposition of films with this unusual growth orientation was optimized and investigated. The structural and microstructural evolution of c-axis to a-axis orientation was monitored using x-ray diffraction, scanning electron microscopy and magnetization measurements. Films with full a-axis alignment parallel to the substrate normal could be achieved on (100)SrTiO3. Due to the symmetry of the substrate the c-axis direction in-plane is twofold. Transferring the deposition conditions to films grown on (110)SrTiO3 allowed the growth of (110) oriented YBCO films with a unique in-plane c-axis orientation. While these films were of high quality by crystallographic and macroscopic visual inspection, electron microscopy revealed a coherent crack pattern on a nanoscale. Therefore the actual current path in the sample was not determined by the macroscopic patterning which prohibited investigations of the in-plane anisotropy in this case.rn

Thermoelektrische Eigenschaften dünner Schichten und Übergitterstrukturen von IV-VI- und V-VI-Verbundhalbleitern

Als ein vielversprechendes Konzept zur Erhöhung der thermoelektrischen Effizienz wird seit Anfang der 90er Jahre die Nutzung niederdimensionaler Systeme angesehen. Aus theoretischen Arbeiten von Hicks und Dresselhaus folgt, dass in ein- und zweidimensionalen Systemen eine Erhöhung der thermoelektrischen Effizienz möglich ist, die einen Durchbruch für die Anwendung thermoelektrischer Wandler zur Folge haben könnte. Die Realisierung solcher niederdimensionaler Systeme ist in geeigneten Mehrlagenstrukturen und durch Verwendung von Halbleiterverbindungen mit unterschiedlicher Energiebandlücke möglich. Ziel des Verbundprojektes Nitherma war es Mehrfachschichtsysteme mit 2-dimensionalem Transportverhalten aus thermoelektrischen Materialien (Pb1-xSrxTe, Bi2(SexTe1-x)3) herzustellen und auf die erwartete hohe thermoelektrische Effizienz zu untersuchen. Diese wurde messtechnischrndurch die Bestimmung der elektrischen Leitfähigkeit, des Seebeck-Koeffizienten und der Wärmeleitfähigkeit parallel zu den Schichtebenen (in-plane-Transporteigenschaft) ermittelt. Ziel dieser Arbeit war einerseits die Verbesserung der Präparations- und Messtechnik bei der Untersuchung der Wärmeleitfähigkeit von Schichten und Schichtsystemen sowie die Demonstration der Reproduzierbarkeit, andererseits die Interpretation der an niederdimensionalen Strukturen ermittelten Transportmessungen. Um den Einfluß der Niederdimensionalität auf die Wärmeleitfähigkeit zu ermitteln, wurden umfangreiche Messungen an unterschiedlich dimensionierten Übergitter- und Multi-Quantum-Well-Strukturen (MQW-Strukturen) durchgeführt. Die Verifizierung der von den Projektpartnern durchgeführten Transportmessungen wurde durch die Messung des Seebeck-Koeffizienten unterstützt.Neben der Charakterisierung durch Transportmessungen erfolgte die Bestimmung der thermoelektrischen Effizienz.

Hypersonic phonon propagation in mesoscopic systems by Brillouin spectroscopy

Phononic crystals, capable to block or direct the propagation of elastic/acoustic waves, have attracted increasing interdisciplinary interest across condensed matter physics and materials science. As of today, no generalized full description of elastic wave propagation in phononic structures is available, mainly due to the large number of variables determining the band diagram. Therefore, this thesis aims for a deeper understanding of the fundamental concepts governing wave propagation in mesoscopic structures by investigation of appropriate model systems. The phononic dispersion relation at hypersonic frequencies is directly investigated by the non-destructive technique of high-resolution spontaneous Brillouin light scattering (BLS) combined with computational methods. Due to the vector nature of the elastic wave propagation, we first studied the hypersonic band structure of hybrid superlattices. These 1D phononic crystals composed of alternating layers of hard and soft materials feature large Bragg gaps. BLS spectra are sensitive probes of the moduli, photo-elastic constants and structural parameters of the constituent components. Engineering of the band structure can be realized by introduction of defects. Here, cavity layers are employed to launch additional modes that modify the dispersion of the undisturbed superlattice, with extraordinary implications to the band gap region. Density of states calculations in conjunction with the associated deformation allow for unambiguous identication of surface and cavity modes, as well as their interaction with adjacent defects. Next, the role of local resonances in phononic systems is explored in 3D structures based on colloidal particles. In turbid media BLS records the particle vibration spectrum comprising resonant modes due to the spatial confinement of elastic energy. Here, the frequency and lineshapes of the particle eigenmodes are discussed as function of increased interaction and departure from spherical symmetry. The latter is realized by uniaxial stretching of polystyrene spheres, that can be aligned in an alternating electric field. The resulting spheroidal crystals clearly exhibit anisotropic phononic properties. Establishing reliable predictions of acoustic wave propagation, necessary to advance, e.g., optomechanics and phononic devices is the ultimate aim of this thesis.

Thermoelectric properties of TiNiSn and Zr 0.5 Hf 0.5 NiSn thin films and superlattices with reduced thermal conductivities

Durch steigende Energiekosten und erhöhte CO2 Emission ist die Forschung an thermoelektrischen (TE) Materialien in den Fokus gerückt. Die Eignung eines Materials für die Verwendung in einem TE Modul ist verknüpft mit der Gütezahl ZT und entspricht α2σTκ-1 (Seebeck Koeffizient α, Leitfähigkeit σ, Temperatur T und thermische Leitfähigkeit κ). Ohne den Leistungsfaktor α2σ zu verändern, soll ZT durch Senkung der thermischen Leitfähigkeit mittels Nanostrukturierung angehoben werden.rnBis heute sind die TE Eigenschaften von den makroskopischen halb-Heusler Materialen TiNiSn und Zr0.5Hf0.5NiSn ausgiebig erforscht worden. Mit Hilfe von dc Magnetron-Sputterdeposition wurden nun erstmals halbleitende TiNiSn und Zr0.5Hf0.5NiSn Schichten hergestellt. Auf MgO (100) Substraten sind stark texturierte polykristalline Schichten bei Substrattemperaturen von 450°C abgeschieden worden. Senkrecht zur Oberfläche haben sich Korngrößen von 55 nm feststellen lassen. Diese haben Halbwertsbreiten bei Rockingkurven von unter 1° aufgewiesen. Strukturanalysen sind mit Hilfe von Röntgenbeugungsexperimenten (XRD) durchgeführt worden. Durch Wachstumsraten von 1 nms 1 konnten in kürzester Zeit Filmdicken von mehr als einem µm hergestellt werden. TiNiSn zeigte den höchsten Leistungsfaktor von 0.4 mWK 2m 1 (550 K). Zusätzlich wurde bei Raumtemperatur mit Hilfe der differentiellen 3ω Methode eine thermische Leitfähigkeit von 2.8 Wm 1K 1 bestimmt. Es ist bekannt, dass die thermische Leitfähigkeit mit der Variation von Massen abnimmt. Weil zudem angenommen wird, dass sie durch Grenzflächenstreuung von Phononen ebenfalls reduziert wird, wurden Übergitter hergestellt. Dabei wurden TiNiSn und Zr0.5Hf0.5NiSn nacheinander abgeschieden. Die sehr hohe Kristallqualität der Übergitter mit ihren scharfen Grenzflächen konnte durch Satellitenpeaks und Transmissionsmikroskopie (STEM) nachgewiesen werden. Für ein Übergitter mit einer Periodizität von 21 nm (TiNiSn und Zr0.5Hf0.5NiSn jeweils 10.5 nm) ist bei einer Temperatur von 550 K ein Leistungsfaktor von 0.77 mWK 2m 1 nachgewiesen worden (α = 80 µVK 1; σ = 8.2 µΩm). Ein Übergitter mit der Periodizität von 8 nm hat senkrecht zu den Grenzflächen eine thermische Leitfähigkeit von 1 Wm 1K 1 aufgewiesen. Damit hat sich die Reduzierung der thermischen Leitfähigkeit durch die halb-Heusler Übergitter bestätigt. Durch die isoelektronischen Eigenschaften von Titan, Zirkonium und Hafnium wird angenommen, dass die elektrische Bandstruktur und damit der Leistungsfaktor senkrecht zu den Grenzflächen nur schwach beeinflusst wird.rn