Influence of Surface Treatment on the Shear Bond Strength of Ceramics Fused to Cobalt-Chromium

Purpose: To evaluate the influence of surface treatment on the shear bond strength between a Co-Cr alloy and two ceramics.Materials and Methods: Forty-eight metal cylinders were made (thickness: 4 mm, height: 3.7 mm) according ISO TR 11405. The 48 metallic cylinders were divided into four groups (n = 12), according to the veneering ceramic (StarLight Ceram and Duceram Kiss) and surface treatments: air-particle abrasion with Al(2)O(3) or tungsten drill (W). Gr1: StarLight + Al(2)O(3); Gr2: StarLight + W; Gr3: Duceram + Al(2)O(3); and Gr4: Duceram + W. The specimens were aged using thermal cycling (3000 x, 5 to 55 degrees C, dwell time: 30 seconds, transfer time: 2 seconds). The shear test was performed with a universal testing machine, using a load cell of 100 kg (speed: 0.5 mm/min) and a specific device. The bond strength data were analyzed using ANOVA and Tukey's test (5%), and the failure modes were analyzed using an optical microscope (30x).Results: The means and standard deviations of the shear bond strengths were (MPa): G1 (57.97 +/- 11.34); G2 (40.62 +/- 12.96); G3 (47.09 +/- 13.19); and G4 (36.80 +/- 8.86). Ceramic (p = 0.03252) and surface treatment (p = 0.0002) significantly affected the mean bond strength values.Conclusions: Air-particle abrasion with Al(2)O(3) improved the shear bond strength between metal and ceramics used.

Surface degradation of glass ceramics after exposure to acidulated phosphate fluoride

Objective: This study evaluated the surface degradation effect of acidulated phosphate fluoride (APF) gel exposure on the glassy matrix ceramics as a function of time. Material and methods: Disc-shaped ceramic specimens (N = 120, 10/per ceramic material) were prepared in stainless steel molds (inner diameter: 5 mm, height: 2 mm) using 6 dental ceramics: 3 indicated for ceramic-fused-to-metal (Vita Omega 900, Carmen and Vita Titankeramik), 2 for all-ceramic (Vitadur Alpha and Finesse (R) Low Fusing) and 1 for both types of restorations (IPS d. SIGN). The specimens were wet ground finished, ultrasonically cleaned and auto-glazed. All specimens were subjected to calculation of percentage of mass loss, surface roughness analysis and topographical description by scanning electron microscopy (SEM) before (0 min) and after exposure to 1.23 % APF gel for 4 min and 60 min representing short-and long-term etching effect, respectively. The data were analyzed using two-way ANOVA with repeated measures and Tukey` s test (alpha=0.05). Results: Significant effect of the type of the ceramics (p=0.0000, p=0.0031) and exposure time (p=0.0000) was observed in both surface roughness and percentage of mass loss values, respectively. The interaction factor between both parameters was also significant for both parameters (p=0.0904, p=0.0258). Both 4 min (0.44 +/- 0.1-0.81 +/- 0.2 mu m) and 60 min (0.66 +/- 0.1 - 1.04 +/- 0.3 mu m) APF gel exposure created significantly more surface roughness for all groups when compared to the control groups (0.33 +/- 0.2-0.68 +/- 0.2 mu m) (p<0.05). There were no significant differences in percentage of mass loss between the ceramics at 4 min (p>0.05) but at 60 min exposure, IPS d. SIGN showed the highest percentage of mass loss (0.1151 +/- 0.11). The mean surface roughness for Vita Titankeramik (0.84 +/- 0.2 mu m) and Finesse (R) Low Fusing (0.74.+/- 0.2 mu m) was significantly higher than those of the other ceramics (0.59 +/- 0.1 mu m - 0.49 +/- 0.1 mu m) and Vita Titankeramik (p<0.05) regardless of the exposure time. A positive correlation was found between surface roughness and percentage of mass loss for all ceramic materials [(r=0.518 (Vitadur Alpha), r=0.405 (Vita Omega 900), r=0.580 (Carmen), r=0.687 (IPS d. SIGN), r=0.442 (Finesse (R) Low Fusing), r=0.572 (Vita Titankeramik), Pearson's correlation coefficient)]. The qualitative SEM analysis showed evidence of corrosive attack on all of ceramics at varying degrees. Conclusions: The ceramics indicated for either metal-ceramic or all-ceramic restorations were all vulnerable to surface texture changes and mass loss after short-term and long-term APF gel exposure.

Avaliação da resistência de união metalocerâmica em função de diferentes tempos de oxidação prévia

Avaliou-se a resistência de união metal/porcelana utilizando-se uma liga de Ni-Cr, submetida a diferentes tempos de oxidação prévia com o sistema cerâmico Vita-VMK, através do teste preconizado por CHIODI NETTO3. A análise dos resultados permitiu as seguintes conclusões: a ausência da oxidação prévia possibilitou os melhores resultados, sendo que a diferença foi estatisticamente significante; diferentes tempos de oxidação prévia provocaram redução acentuada nos valores obtidos e foram semelhantes entre si; o grupo submetido ao processo de jateamento após a oxidação prévia por cinco minutos mostrou resultados similares aos grupos que também passaram pelo processo de oxidação e não sofreram jateamento posterior.

Effect of surface treatments on the bond strength of a resin cement to commercially pure titanium

Investigation of the effectiveness of surface treatments that promote a strong bond strength of resin cements to metals can contribute significantly to the longevity of metal-ceramic restorations. This study evaluated the effect of surface treatments on the shear bond strength (SBS) of a resin cement to commercially pure titanium (CP Ti). Ninety cast CP Ti discs were divided into 3 groups (n=30), which received one of the following airborne-particle abrasion conditions: (1) 50 μm Al2O3 particles; (2) 30 μm silica-modified Al2O3 particles (Cojet Sand); (3) 110 μm silica-modified Al2O3 particles (Rocatec). For each airborne-particle abrasion condition, the following post-airborne-particle abrasion treatments were used (n=10): (1) none; (2) adhesive Adper Single Bond 2; (3) silane RelyX Ceramic Primer. RelyX ARC resin cement was bonded to CP Ti surfaces. All specimens were thermally cycled before being tested in shear mode. Failure mode was determined. The best association was Rocatec plus silane. All groups showed 100% adhesive failure. There were combinations that promote higher SBS than the protocol recommended by the manufacturer of RelyX ARC.

Association of fixed partial denture and gingival prosthesis as alternative approach to recover esthetics and function in anterior maxillary region

Tooth replacement in the maxillary anterior region is especially difficult when the loss includes significant amounts of the residual ridge and the soft tissue. Several techniques are available, such as dental implants or fixed partial denture, and bone and gingival grafts or gingival prostheses, respectively. This article showed a clinical case of an elderly who was treated with a collarless metal-ceramic fixed partial denture and acrylic removable gingival prosthesis to recover the esthetics in the maxillary anterior region. The association of a metal-ceramic fixed denture and gingival prosthesis was an excellent alternative in cases when surgical procedures are contraindicated. © 2012 Japan Prosthodontic Society.

Síntese, caracterização e propriedades da matriz sílica-carbono impregnada com níquel obtida pelo método dos precursores poliméricos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da resistência ao cisalhamento de sistemas para reparo em metalocerâmicas. Efeito do armazenamento em água

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da resistência ao cisalhamento de sistemas para reparo em metalocerâmicas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da influência da angulação dos implantes com diferentes tipos de conexão protética na distribuição de tensões: estudo pelo método dos elementos finitos tridimensionais

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influência da carga oclusal parafuncional em próteses implantossuportadas, variando-se a proporção coroa/implante e o sistema de conexão protética: estudo pelo método dos elementos finitos tridimensionais

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Adaptação marginal e resistência à fratura de coroas totais executadas em diferentes sistemas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Aplicação do processo sol-gel na produção de recobrimentos de hidroxiapatita sobre ligas a base de Ti empregadas em implantes odontológicos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Determinação do calor específico de ligas AlCu produzidas em um dispositivo de solidificação unidirecional vertical ascendente

O conhecimento das propriedades termofísicas é de fundamental importância para o estudo de ligas metálicas obtidas por solidificação,uma vez que esta se relaciona de forma direta com o coeficiente de transferência de calor na interface metal/molde. Assim, o Grupo de Pesquisa em Metalurgia e de Meio Ambiente – GAPEMM da Universidade Federal do Pará desenvolve uma linha de pesquisa que propõe um conjunto de técnicas e procedimentos que visa determiná-las. Por outro lado, sabe-se que existe uma correlação significativa entre processo, estrutura e propriedades de um material obtido por solidificação, visto que a distribuição de soluto em uma liga metálica ocorre de maneira não uniforme. A maneira como ocorre solidificação e a quantificação das variáveis envolvidas no processo têm influência fundamental nas propriedades do material. O presente trabalho utilizou ligas Al-Cu (Al-2%Cu, Al-5%Cu e Al-8%Cu) obtidas por solidificação unidirecional vertical ascendente, realizado através de um dispositivo projetado, construído e aferido pelo GAPEMM. Através destas, pretende-se fazer um estudo do calor específico à medida que a frente de solidificação se afasta da chapa molde bem como com o aumento do teor de soluto. Para isso, foi utilizada uma técnica conhecida na literatura como Lei de Resfriamento de Newton, a qual possibilita através das curvas de temperatura x tempo determinar as temperaturas necessárias para o cálculo do calor específico.

Influência da convecção termossolutal na transição colunar/equiaxial em ligas Al-Si sob condições unidirecionais e transitórias de extração de calor

A relação entre macroestrutura e propriedades mecânicas de um material tem sido objeto de intensa investigação pois o tamanho dos grãos, a orientação cristalina e a distribuição dos mesmos exercem influência direta no comportamento mecânico dos produtos acabados. Assim, o entendimento dos fatores que influenciam a formação das zonas estruturais coquilhada, colunar e equiaxial nos materiais fundidos como, por exemplo, o sistema de liga, composição da liga, temperatura de vazamento, temperatura do molde, material do molde, coeficientes de transferência de calor na interface metal/molde, taxa de resfriamento, gradientes térmicos, dimensão da peça, presença de convecção no líquido, transporte de soluto, etc é de fundamental importância para a melhoria da eficiência do processo de fundição envolvido. Com base no conhecimento dos princípios termofísicos em que essas zonas são formadas, é possível manipular de forma bastante razoável a estrutura dos produtos fundidos e, conseqüentemente, as propriedades mecânicas dos mesmos. Tendo como principal foco a análise da mudança da zona colunar para a equiaxial, este trabalho apresenta um estudo teórico-experimental sobre a transição colunar/equiaxial (TCE) das ligas hipoeutéticas Al- 3%Si, Al-7%Si Al-9%Si solidificadas unidirecionalmente em um dispositivo horizontal refrigerado a água sob condições transientes de fluxo de calor. A condição de contato térmico na superfície de extração de calor foi padronizada como sendo polida. Os perfis térmicos foram medidos em diferentes posições do lingote e os dados foram armazenados automaticamente. Um método numérico é utilizado na determinação de variáveis térmicas de solidificação como coeficientes de transferência de calor na interface metal/molde (h_i), velocidades das isotermas liquidus (V_L), gradientes térmicos (G_L) e taxas de resfriamento (T_R) que influenciam diretamente a referida transição estrutural. Os resultados teóricos e experimentais apresentaram boa concordância. Um estudo comparativo entre os resultados obtidos neste trabalho e valores propostos na literatura para analisar a TCE durante a solidificação unidirecional vertical ascendente sob condições transientes de extração de calor das ligas investigadas, também é apresentado.

Resistência á fratura de diferentes selamentos de orifício de acesso ao parafuso de fiação e da porcela de cobertura de restaurações metalo-cerâmicas parafusadas implantossuportadas

Pós-graduação em Reabilitação Oral - FOAR