Fatigue strength: effect of welding type and joint design executed in Ti-6Al-4V structures

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Caracterização mecânica e microestrutural de juntas de alumínio 6013 T4 soldados a laser

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Estudo do comportamento mecânico e microestrutural de um aço maraging após soldagem a laser e tratamentos térmicos

Pós-graduação em Engenharia Mecânica - FEG

Aplicação do processo laser CO2 de soldagem em aço ARBL na fabricação de rotores para máquinas elétricas

Pós-graduação em Engenharia Mecânica - FEG

Application of pulsed Nd:YAG laser in thin foil microwelding

Experimental investigations were carried out using a Nd:YAG laser operating in pulsed mode for welding a lap joint between thin foil and thick sheet. The pulse energy was varied from 1.5 to 3.0 J at increments of 0.25 J with a 4 ms pulse duration. The base material used for this study was AISI 316L foils with 100 mu m thickness and sheet with 3.0 mm thickness. The welds were analysed by optical and electronic microscopy, tensile shear tests and micro hardness. The results indicate that pulse energy control is of considerable importance to join thin foil and thick sheet with good quality. The ultimate tensile strength of the welded joints increased at first and then decreased as the pulse energy increased. The process appeared to be very sensitive to the gap between couples. Large voids delimited by the molten zone boundary were observed in joints welded with high pulse energy.

Mechanical and microstructural characterization of laser-welded joints of 6013-T4 aluminum alloy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of laser soldering irradiation on covalent bonds of pure collagen

Laser tissue welding and soldering is being increasingly used in the clinical setting for defined surgical procedures. The exact induced changes responsible for tensile strength are not yet fully investigated. To further improve the strength of the bonding, a better understanding of the laser impact at the subcellular level is necessary. The goal of this study was to analyze whether the effect of laser irradiation on covalent bonding in pure collagen using irradiances typically applied for tissue soldering. Pure rabbit and equine type I collagen were subjected to laser irradiation. In the first part of the study, rabbit and equine collagen were compared using identical laser and irradiation settings. In the second part of the study, equine collagen was irradiated at increasing laser powers. Changes in covalent bonding were studied indirectly using the sodium dodecylsulfate polyacrylamide gel electrophoresis (SDS-PAGE) technique. Tensile strengths of soldered membranes were measured with a calibrated tensile force gauge. In the first experiment, no differences between the species-specific collagen bands were noted, and no changes in banding were found on SDS-PAGE after laser irradiation. In the second experiment, increasing laser irradiation power showed no effect on collagen banding in SDS-PAGE. Finally, the laser tissue soldering of pure collagen membranes showed virtually no determinable tensile strength. Laser irradiation of pure collagen at typical power settings and exposure times generally used in laser tissue soldering does not induce covalent bonding between collagen molecules. This is true for both rabbit and equine collagen proveniences. Furthermore, soldering of pure collagen membranes without additional cellular components does not achieve the typical tensile strength reported in native, cell-rich tissues. This study is a first step in a better understanding of laser impact at the molecular level and might prove useful in engineering of combined collagen-soldering matrix membranes for special laser soldering applications.

Characterisation of laser hybrid welded dissimilar joints

The investigation addresses the over-all performance of dissimilar joints of low carbon steel and stainless steel thin sheets achieved by laser hybrid welding. First, the technological de-velopment of dissimilar laser hybrid welding of thin sheets is briefly pre-sented. Joint characterisation by means of macro and microstructural examination and hardness tests is fur-ther described. Microhardness testing was used as an alternative and effi-cient mean of assessing the changes in mechanical properties of difficult to characterize areas, like HAZ and fu-sion zone of these thin sheets Laser-GMA dissimilar welded joints. The overall tensile performance of the joint is discussed together with the weld metal strength overmatching. The ten-sile tests results indicate that in case of transversally loaded joints, the po-sitive difference in yield strength between the weld metal and the base materials (overmatching welds) may reduce the weight of the structure, without diminishing its strength.