Bond durability in erbium:yttrium-aluminum-garnet laser-irradiated enamel

This study sought to evaluate the influence of thermocycling and water storage on the microtensile bond strength of composite resin bonded to erbium:yttrium-aluminum-garnet (Er:YAG)-irradiated and bur-prepared enamel. Eighty bovine incisors were selected and sectioned. Specimens were ground to produce a flat enamel surface. Samples were randomly assigned according to cavity preparation device: (I) Er:YAG laser and (II) high-speed turbine, and were subsequently restored with composite resin. They were subdivided according to the duration of water storage (WS)/number of thermocycles (TCs): 24 h WS/no TCs; 7 days WS/500 TCs; 1 month WS/2,000 TCs; 6 months WS/12,000 TCs. The teeth were sectioned into 1.0 mm(2)-thick slabs and subjected to tensile stress in a universal testing machine. Data were submitted to two-way analysis of variance (ANOVA) and Tukey`s test at a 0.05 significance level. The different periods of water storage and thermocycling did not influence the microtensile bond strength (A mu TBS) values in the Er:YAG laser-prepared groups. In bur-prepared enamel, the group submitted to 12,000 TCs/6 months` WS (IID) showed a significant decrease in bond strength values when compared to the group stored in water for 24 h and not submitted to thermocycling (IIA), but values were statistically similar to those obtained in all Er:YAG laser groups and in the bur- prepared groups degraded with 500 TCs/1 week WS (IIB) or 2,000 TCs/1 month WS (IIC). It may be concluded that adhesion of an etch-and-rinse adhesive to Er:YAG laser-irradiated enamel was not affected by the methods used to simulate degradation of the adhesive interface and was similar to adhesion in the bur-prepared groups in all periods of water storage and thermocycling.

Influence of water flow rate on shear bond strength of resin composite to Er : YAG cavity preparation

Purpose: To evaluate in vitro the influence of water flow rate on shear bond strength of a resin composite to enamel and dentin after Er:YAG cavity preparation. Methods: Ten bovine incisors were selected and roots removed. Crowns were sectioned in four pieces, resulting in 40 samples that were individually embedded in polyester resin (n=10), and ground to plane the enamel and expose the dentin. The bonding site was delimited and samples were randomly assigned according to cavity preparation: (1) Er:YAG/1.0 mL/minute; (2) Er:YAG/1.5 mL/minute; (3) Er:YAG/2.0 mL/minute and (4) High speed handpiece/bur (control group). Samples were fixed to a metallic device, where composite resin cylinders were prepared. Subsequently, they were stored for 24 hours and subjected to a shear bond strength test (500N at 0.5 mm/minute). Results: Means (MPa) were: enamel: 1: 12.8; 2: 16.8; 3: 17.5; 4: 36.0 and Dentin: 1: 13.6; 2: 18.7; 3: 12.1; 4: 21.3. Data were submitted to ANOVA and Tukey`s test. Adhesion to enamel was more efficient than for dentin. The cavities prepared with conventional bur (control) presented higher statistically significant bond strength values (P<0.05) than for Er:YAG laser for both enamel and dentin. No significant differences were observed between water flow rates employed during enamel ablation. For dentin, the shear bond strength of 2.0 mL/minute water flow rate was lower than for 1.5 mL/minute and 1.0 mL/minute rates. The Er:YAG laser adversely affected shear bond strength of resin composite to both enamel and dentin, regardless of the water flow rate used.

Influence of dentin cavity surface finishing on micro-tensile bond strength of adhesives

The current trend toward minimal-invasive dentistry has introduced innovative techniques for cavity preparation. Chemical vapor deposition (CVD) and laser-irradiation technology have been employed as an alternative to the common use of regular burs in high-speed turbines. Objectives. The purpose of this study was to assess the influence of alternative techniques for cavity preparation on the bonding effectiveness of different adhesives to dentin, and to evaluate the morphological characteristics of dentin prepared with those techniques. Methods. One etch&rinse adhesive (OptiBond FL, Kerr) and three self-etch systems (Adper Prompt L-Pop, 3M ESPE; Clearfil SE Bond, Kuraray; Clearfil S3 Bond, Kuraray) were applied on dentin prepared with a regular bur in a turbine, with a CVD bur in a turbine, with a CVD tip in ultrasound and with an ErCr:YSGG laser. The micro-tensile bond strength (mu TBS) was determined after storage in water for 24 h at 37 degrees C, and morphological evaluation was performed by means of field -emission -gun scanning electron microscopy (Feg-SEM). Results. Feg-SEM evaluation revealed different morphological features on the dentin surface after the usage of both the conventional and alternative techniques for cavity preparation, more specifically regarding smear-layer thickness and surface roughness. CVD bur-cut, CVD ultra-sonoabraded and laser-irradiated dentin resulted in lower mu TBSs than conventionally bur-cut dentin, irrespective of the adhesive employed. Significance. The techniques, such as CVD diamond-bur cutting, CVD diamond ultra-sonoabrasion and laser-irradiation, used for cavity preparation may affect the bonding effectiveness of adhesives to dentin, irrespective of their acidity or approach. (C) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Bond Strength of Dental Adhesive Systems Irradiated with Ionizing Radiation

Purpose: The aim of the present paper was to determine the effect of different types of ionizing radiation on the bond strength of three different dentin adhesive systems. Materials and Methods: One hundred twenty specimens of 60 human teeth (protocol number: 032/2007) sectioned mesiodistally were divided into 3 groups according to the adhesives systems used: SB (Adper Single Bond Plus), CB (Clearfil SE Bond) and AP (Adper Prompt Self-Etch). The adhesives were applied on dentin and photo-activated using LED (Lec 1000, MMoptics, 1000 mW/cm(2)). Customized elastomer molds (0.5 mm thickness) with three orifices of 1.2 mm diameter were placed onto the bonding areas and filled with composite resin (Filtek Z-250), which was photo-activated for 20 s. Each group was subdivided into 4 Subgroups for application of the different types of ionizing radiation: ultraviolet radiation (UV), diagnostic x-ray radiation (DX), therapeutic x-ray radiation (TX) and without irradiation (control group, CG). Microshear tests were carried out (Instron, model 4411), and afterwards the modes of failure were evaluated by optical and scanning electron microscope and classified using 5 scores: adhesive failure, mixed failures with 3 significance levels, and cohesive failure. The results of the shear bond strength test were submitted to ANOVA with Tukey`s test and Dunnett`s test, and the data from the failure pattern evaluation were analyzed with the Mann Whitney test (p = 0.05). Results: No change in bond strength of CB and AP was observed after application of the different radiation types, only SB showed increase in bond strength after UV (p = 0.0267) irradiation. The UV also changed the failure patterns of SB (p = 0.0001). Conclusion: The radio-induced changes did not cause degradation of the restorations, which means that they can be exposed to these types of ionizing radiation without weakening the bond strength.

Orthodontic brackets removal under shear and tensile bond strength resistance tests - a comparative test between light sources

We have investigated if a new LEDs system has enough efficient energy to promote efficient shear and tensile bonding strength resistance under standardized tests. LEDs 470 +/- 10 nm can be used to photocure composite during bracket fixation. Advantages considering resistance to tensile and shear bonding strength when these systems were used are necessary to justify their clinical use. Forty eight human extracted premolars teeth and two light sources were selected, one halogen lamp and a LEDs system. Brackets for premolar were bonded through composite resin. Samples were submitted to standardized tests. A comparison between used sources under shear bonding strength test, obtained similar results; however, tensile bonding test showed distinct results: a statistical difference at a level of 1% between exposure times (40 and 60 seconds) and even to an interaction between light source and exposure time. The best result was obtained with halogen lamp use by 60 seconds, even during re-bonding; however LEDs system can be used for bonding and re-bonding brackets if power density could be increased.

Effect of light-curing units on push-out fiber post bond strength in root canal dentin

The purpose of this study was to evaluate the effectiveness of different light-curing units on the bond strength (push-out) of glass fiber posts in the different thirds of the root (cervical, middle and apical) with different adhesive luting resin systems (dual-cure total-etch; dual-cured and self-etch bonding system; and dual-cure self-adhesive cements), Disks of the samples (n = 144) were used, with approximately 1 mm of thickness of 48 bovine roots restored with glass fiber posts, that were luted with resin cements photo-activated by halogen LCU (QTH, Optilux 501) and blue LED (Ultraled), with power densities of 600 and 550 mW/cm(2), respectively. A universal testing machine (MTS 810 Material Test System) was used with a 1 mm diameter steel rod at cross-head speed of 0.5 mm/min until post extrusion, with load cell of 50 kg, for evaluation of the push-out strength in the different thirds of each sample. The push-out strength values in kgf were converted to MPa and analyzed through Analysis of Variance and Tukey`s test, at significance level of 5%. The results showed that there were no statistical differences between the QTH and LED LCUs. The self-adhesive resin cement had lower values of retention. The total-etch and self-adhesive system resin cements seem to be a possible alternative for glass fiber posts cementation into the radicular canal and the LED LCU can be applied as an alternative to halogen light on photo-activation of dual-cured resin cements.

Bond Strength and Etching Pattern of Adhesive Systems to Enamel: Effects of Conditioning Time and Enamel Preparation

Statement of the problem: The performance of self-etch systems on enamel is controversial and seems to be dependent on the application technique and the enamel preparation. Purpose of the Study: To examine the effects of conditioning time and enamel surface preparation on bond strength and etching pattern of adhesive systems to enamel. Materials and Methods: Ninety-six teeth were divided into 16 conditions (N = 6) in function of enamel preparation and conditioning time for bond strength test. The adhesive systems OptiBond FL (Kerr, Orange, CA, USA), OptiBond SOLO Plus (Kerr), Clearfil SE Bond (Kuraray, Osaka, Japan), and Adper Prompt L-Pop (3M ESPE, St. Paul, MN, USA) were applied on unground or ground enamel following the manufacturers` directions or doubling the conditioning time. Cylinders of Filtek Flow (0.5-mm height) were applied to each bonded enamel surface using a Tygon tube (0.7 mm in diameter; Saint-Gobain Corp., Aurora, OH, USA). After storage (24 h/37 degrees C), the specimens were subjected to shear force (0.5 mm/min). The data were treated by a three-way analysis of variance and Tukey`s test (alpha = 0.05). The failure modes of the debonded interfaces and the etching pattern of adhesives were observed using scanning electron microscopy. Results: Only the main factor ""adhesive"" was statistically significant (p < 0.001). The lowest bond strength value was observed for OptiBond FL. The most defined etching pattern was observed for 35% phosphoric acid and for Adper Prompt L-Pop. Mixed failures were observed for all adhesives, but OptiBond FL showed cohesive failures in resin predominantly. Conclusions: The increase in the conditioning time as well as the enamel pretreatment did not provide an increase in the resin-enamel bond strength values for the studied adhesives. CLINICAL SIGNIFICANCE The surface enamel preparation and the conditioning time do not affect the performance of self-etch systems to enamel. (J Esthet Restor Dent 20:322-336, 2008)

Effect of heat-treatment atmosphere on the bond strength of apatite layer on Ti substrate

Objectives
The purpose of this study was to investigate the bond strength of apatite layer on titanium (Ti) substrate coated by biomimetic method and to improve the bonding of apatite layer to Ti substrate by optimizing the alkali heat-treatment process.

Methods
Ti plates pre-treated with an alkali solution of 10 M sodium hydroxide (NaOH) were heat-treated at 600 °C for 1 h at different atmospheres: in air and in vacuum. A dense apatite layer formed on top of the sodium titanate layer after soaking the alkali and heat-treated Ti samples in simulated body fluid (SBF) for up to 3 weeks. The bond strengths of the sodium titanate layer on Ti substrate, and apatite layer on the sodium titanate layer, were measured, respectively, by applying a tensile load. The fracture sites were observed with a scanning electron microscope (SEM).

Results
The apatite layer on the substrate after alkali heat-treatment in air achieved higher bond strength than that on the substrate after alkali heat-treatment in vacuum. It was found that the interfacial structure between the sodium titanate and Ti substrate has a significant influence on the bond strength of the apatite layer.

Significance
It is advised that titanium implants can achieve better osseointegration under load-bearing conditions by depositing an apatite layer in vivo on a Ti surface subjected to alkali and heat-treated in air.

Influence of deformation-induced heating on the bond strength of rolled metal multilayers

The bond strength of various metal multilayers produced by cold rolling of metal foils with different thermal conductivity was investigated. Results indicated that the metallic multilayer system with low thermal conductivity exhibited relative high bond strength while high thermal conductivity metal system may fail to be roll-bonded together. The relationship between the deformation-induced localized heating and the bond strength were discussed.

Effects of deformation-induced heating on bond strength of rolled metal multilayer

The bond strength of various metal multilayers produced by cold rolling of metal foils with different thermal conductivity was investigated. Results indicated that under the same conditions of deformation and surface preparation, the metallic multilayer system with low thermal conductivity exhibited relative high bond strength while high thermal conductivity metal system may fail to be roll-bonded together. The relationship between the deformation-induced localized heating and the bond strength were discussed. The deformation-induced localized heating in the low thermal conductivity metal multilayer systems may provide opportunities for achieving a successful accumulative roll bonding or a “cold roll/heat treatment/cold roll” process to synthesize metallic multilayer materials.

Assessment of bond strength in CFRP retrofitted beams under marine environment

Carbon fibre reinforced polymer (CFRP) sheet has gained its popularity to retrofit civil structures which is bonded externally, typically on the soffit of a beam. In this study, the bond between carbon fibre reinforced polymer (CFRP) and concrete is improved by modifying the property of commercial epoxy and compared against normal epoxy. The deterioration in bond strength was produced by placing the beam into salt water under wet dry cycles. Also, a model is proposed to determine the bond strength from flexural test and compared against the available bond strength models which are typically obtained from pull out test. This proposed model shows promising results in terms of predicting the bond strength from flexural test. In addition, a strength reduction factor is introduced to incorporate the effect of wet dry cycles to predict the long term behaviour. It is found that the modified epoxy enhance the ductile property and bond strength.

Effect of monomer treatment and polymerisation methods on the bond strength of resin teeth to denture base material

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of methyl methacrylate monomer on bond strength of denture base resin to acrylic teeth

Bond failures at the acrylic teeth and denture base resin interface are still a common clinical problem in prosthodontics. The effect of methyl methacrylate (MMA) monomer on the bond strength of three types of denture base resins (Acron MC, Lucitone 550 and QC-20) to two types of acrylic teeth (Biotone and Trilux) was evaluated. Twenty specimens were produced for each denture base resin/acrylic tooth combination and were randomly divided into control (acrylic teeth received no surface treatment) and experimental groups (MMA was applied to the surface of the acrylic teeth for 180 s) and were submitted to shear tests (1 mm/mm). Data (MPa) were analyzed using three-way ANOVA/Student's test (alpha = 0.05). MMA increased the bond strength of Lucitone denture base resins and decreased the bond strength of QC-20. No difference was detected for the bond strength of Acron MC base resin after treatment with MMA. (C) 2008 Elsevier Ltd. All rights reserved.