Synthesis and characterization of packed mesoporous tungsteno-silicates: application to the catalytic dehydrogenation of 2-propanol

The synthesis of highly ordered mesoporous tungsteno-silicas in which a high percentage of tungsten is introduced into a silica framework is reported hereafter. Powder XRD and TEM have been used to characterize the materials synthesized at room temperature. The materials are shown to be homogeneous as there is no evidence for any crystalline species other than the silica framework. The pore diameter and the surface area of the materials, evaluated from the nitrogen adsorption isotherms and unit cell parameter indicate a pore diameter of about 2 nm and a surface area of 1400 m(2) g(-1) for a content of 10% tungsten. Catalyzed dehydration of 2-propanol has been investigated and the activity of the materials synthesized is significant, even for low tungsten content W-MCM-41 materials. (C) 2003 Elsevier B.V. All rights reserved.

Catalisadores de vanádio (V) contendo ligante tris(pirazolil)borato : rotas de imobilização e avaliação em polimerização de etileno

As sínteses, caracterizações e estudos referentes a polimerização do etileno de uma série de complexos {TpMs*}V(NtBu)Cl2 (1), {TpMs*}V(O)Cl2 (2), {TpMePh]V(NtBu)Cl2 (3) e {Tp*}V(O)Cl2 (4) são descritas. A reação destes complexos com MAO geram espécies catalíticas ativas para a polimerização do etileno. Para as reações de polimerização realizadas em tolueno a 30°C, as atividades variaram entre 71 e 1.126 kg de PE/mol[V]·h·atm. A atividade mais alta foi obtida usando o precursor catalítico 1. As curvas de DSC mostraram a formação de polietileno de alta densidade com temperaturas de fusão entre 134 e 141ºC. Visando a obtenção de catalisadores suportados, o complexo 1 foi imobilizado através do método direto sobre os seguintes suportes inorgânicos: SiO2, SiO2 modificada com MAO, SiO2-Al2O3, MCM-41, MgO e MgCl2. O teor de metal imobilizado, determinado por XRF, permaneceu entre 0,22 e 0,50 % g V/g suporte (p/p %).Os maiores teores de metal foram encontrados para os suportes com maiores áreas superficiais (SiO2–Al2O3 e MCM-41). Todos os sistemas mostraram-se ativos na polimerização do etileno na presença de MAO ou TiBA/MAO (1:1) (Al/V = 1000). A atividade catalítica mostrou-se dependente da natureza do suporte, ficando esta entre 8 e 89 kg de PE/mol[V]·h·atm. Os melhores resultados foram obtidos para sílica. Suportes ácidos ou básicos forneceram sistemas catalíticos menos ativos. Os polietilenos apresentaram pesos moleculares médios (Mw) superiores a 2.000.000 g/mol, sugerindo a produção de polímeros com ultra-alto peso molecular. Baseado nos resultados referentes a imobilização de 1, o complexo 2 foi imobilizado sobre SiO2 e SiO2 modificada com MAO. As reações de polimerização deste catalisador suportado foram realizadas em tolueno a 30ºC, utilizando MAO ou TiBA/MAO (1:1) (Al/V = 1000). Os resultados de atividade variaram entre 7 e 236 kg de PE/mol[V]·h·atm, sendo a maior atividade encontrada para o sistema suportado 2/SiO2/MAO(4,0 % Al/SiO2) na presença da mistura de cocatalisadores TiBA/MAO (1:1). Os complexos 1 e 2 foram imobilizados “in situ” utilizando SiO2 e SiO2/MAO (4,0 % em peso de Al/SiO2) como suportes, empregando 0,02 % em peso de V/g suporte. Todos os sistemas estudados foram ativos nas reações de polimerização do etileno. Para o complexo 1, a maior atividade (1.903 kg de PE/mol[V]·h·atm) foi obtida utilizando o sistema 1/SiO2/MAO (4,0 % em peso de Al/SiO2) na presença do MAO. Cabe ressaltar que, para este sistema catalítico, o uso de TMA ao invés de MAO proporciona a formação de um sistema catalítico altamente ativo (1.342 kg de PE/mol[V]·h·atm). A maior atividade (1.882 kg de PE/mol[V]·h·atm) para o complexo 2 foi encontrada quando o mesmo foi suportado “in situ” sobre SiO2, utilizando MAO como cocatalisador. O catalisador de vanádio preparado “in situ” sobre o suporte na presença do MAO apresentou uma atividade catalítica de 22 kg de PE/mol[V]·h·atm) sendo a mesma inferior àquela obtida utilizando o sistema via imobilização do catalisador “in situ”. Várias rotas sintéticas (hidrolíticas e não-hidrolíticas) objetivando a preparação “in situ” do catalisador sobre sílicas-híbridas foram empregadas, entretanto todas as tentativas falharam devido à alta reatividade do grupo NCO com alguns reagentes empregados no processo de preparação das mesmas. Uma série de catalisadores híbridos foram preparados pela combinação e imobilização seqüencial de {TpMs*}V(NtBu)Cl2 (1) e [LFeCl2] (8) (L = 2,6-bis(imino)piridila) sobre SiO2/MAO (4,0% em peso de Al/SiO2) em diferentes proporções (1:1) e (1:3). Todos os sistemas foram ativos na polimerização do etileno na presença de MAO como cocatalisador. A atividade mostrou-se dependente da natureza do complexo e da ordem de imobilização. A maior atividade foi obtida para o sistema V/Fe/SMAO-4 (1:1) (117 kg de PE/mol[M]·h·atm). Baseado nas curvas de DSC, diferentes tipos de PE podem ser obtidos dependendo da natureza do complexo imobilizado e da ordem da adição dos catalisadores no suporte. Para os sistemas híbridos, a presença do Fe determina a formação de PE com dois picos de fusão.

Mesoestruturas porosas a partir de materiais naturais

The MCM-41 mesoporous synthesis was done using rice hulls ash and chrysotile as natural alternative silica sources. For the using of these sources, chemical and thermic treatments were done in both materials. After chemical and thermic treatments, these materials were employed on the MCM-41 mesoctructures synthesis. The natural materials treated and employed in the synthesis were characterized by several techniques such as X-ray diffraction, N2 adsorption and desorption, scanning electronic microscopy and thermogravimetric analysis. MCM-41 standart samples synthetized with aerosil 200 commercial sílica were used to evaluation. The formed material from rice hulls ash showed values from BET specific area about 468 m².g-1, N2 adsorption and desorption isotherms and loss mass similar to reference materials. The silica from chrysotile calcined and leached was employed to mesoporous materials synthesis. The BET specific area showed values about 700 m².g-1, N2 adsorption and desorption isotherms type IV and loss mass similar to mesoporous materials. The formed material from calcined and leached chrysotile, without calcination, applied to phenol remotion carried high performance liquid chromatography and evaluated with organophilic clays with different treatments. By the characterization techniques were proved that mesoporous materials with lesser order that reference samples. The material formed from rice hulls ash without the calcination step achieved better adsorption results than organophilic clays

Conversão térmica e termocatalítica à baixa temperatura do óleo de girassol para obtenção de bio-óleo

The use of biofuels remotes to the eighteenth century, when Rudolf Diesel made the first trials using peanut oil as fuel in a compression ignition engine. Based on these trials, there was the need for some chemical change to vegetable oil. Among these chemical transformations, we can mention the cracking and transesterification. This work aims at conducting a study using the thermocatalytic and thermal cracking of sunflower oil, using the Al-MCM-41 catalyst. The material type mesoporous Al-MCM-41 was synthesized and characterized by Hydrothermical methods of X-ray diffraction, scanning electron microscopy, nitrogen adsorption, absorption spectroscopy in the infrared and thermal gravimetric analysis (TG / DTG).The study was conducted on the thermogravimetric behavior of sunflower oil on the mesoporous catalyst cited. Activation energy, conversion, and oil degradation as a function of temperature were estimated based on the integral curves of thermogravimetric analysis and the kinetic method of Vyazovkin. The mesoporous material Al-MCM-41 showed one-dimensional hexagonal formation. The study of the kinetic behavior of sunflower oil with the catalyst showed a lower activation energy against the activation energy of pure sunflower oil. Two liquid fractions of sunflower oil were obtained, both in thermal and thermocatalytic pyrolisis. The first fraction obtained was called bio-oil and the second fraction obtained was called acid fraction. The acid fraction collected, in thermal and thermocatalytic pyrolisis, showed very high level of acidity, which is why it was called acid fraction. The first fraction was collected bio-called because it presented results in the range similar to petroleum diesel

Pirólise térmica e catalítica de resíduos de vácuo gerados no refino de petróleo

In this study, was used a very promising technique called of pyrolysis, which can be used for obtaining products with higher added value. From oils and residues, since the contribution of heavier oils and residues has intensified to the world refining industry, due to the growing demand for fuel, for example, liquid hydrocarbons in the range of gasoline and diesel. The catalytic pyrolysis of vacuum residues was performed with the use of a mesoporous material belonging the M41S family, which was discovered in the early 90s by researchers Mobil Oil Corporation, allowing new perspectives in the field of catalysis. One of the most important members of this family is the MCM-41, which has a hexagonal arrangement of mesopores with pore diameters between 2 and 10 nm and a high specific surface area, making it very promising for use as a catalyst in petroleum refining for catalytic cracking, and their mesopores facilitate the access of large hydrocarbon molecules. The addition of aluminum in the structure of MCM-41 increases the acidity of the material, making it more positive for application in the petrochemical industry. The mesoporous material of the type Al-MCM41 (ratio Si / Al = 50) was synthesized by hydrothermal method starting from the silica gel, NaOH and distilled water added to the gel pseudobohemita synthesis. Driver was used as structural CTMABr. Removal of organic driver (CTMABr) was observed by TG / DTG and FTIR, but this material was characterized by XRD, which was observed the formation of the main peaks characteristic of mesoporous materials. The analysis of adsorption / desorption of nitrogen this material textural parameters were determined. The vacuum residues (VR's) that are products of the bottom of the vacuum distillation tower used in this study are different from oil fields (regions of Ceará and Rio de Janeiro). Previously characterized by various techniques such as FTIR, viscosity, density, SARA, elemental analysis and thermogravimetry, which was performed by thermal and catalytic degradation of vacuum residues. The effect of AlMCM-41 was satisfactory, since promoted a decrease in certain ranges of temperature required in the process of conversion of hydrocarbons, but also promoted a decrease in energy required in the process. Thus enabling lower costs related to energy expenditure from degradation during processing of the waste

Pirólise rápida catalítica do capim elefante utilizando materiais mesoporosos e óxidos metálicos para deoxigenação em bio-óleo

The fast pyrolysis of lignocellulosic biomass is a thermochemical conversion process for production energy which have been very atratactive due to energetic use of its products: gas (CO, CO2, H2, CH4, etc.), liquid (bio-oil) and charcoal. The bio-oil is the main product of fast pyrolysis, and its final composition and characteristics is intrinsically related to quality of biomass (ash disposal, moisture, content of cellulose, hemicellulose and lignin) and efficiency removal of oxygen compounds that cause undesirable features such as increased viscosity, instability, corrosiveness and low calorific value. The oxygenates are originated in the conventional process of biomass pyrolysis, where the use of solid catalysts allows minimization of these products by improving the bio-oil quality. The present study aims to evaluate the products of catalytic pyrolysis of elephant grass (Pennisetum purpureum Schum) using solid catalysts as tungsten oxides, supported or not in mesoporous materials like MCM-41, derived silica from rice husk ash, aimed to reduce oxygenates produced in pyrolysis. The biomasss treatment by washing with heated water (CEL) or washing with acid solution (CELix) and application of tungsten catalysts on vapors from the pyrolysis process was designed to improve the pyrolysis products quality. Conventional and catalytic pyrolysis of biomass was performed in a micro-pyrolyzer, Py-5200, coupled to GC/MS. The synthesized catalysts were characterized by X ray diffraction, infrared spectroscopy, X ray fluorescence, temperature programmed reduction and thermogravimetric analysis. Kinetic studies applying the Flynn and Wall model were performed in order to evaluate the apparent activation energy of holoceluloce thermal decomposition on samples elephant grass (CE, CEL and CELix). The results show the effectiveness of the treatment process, reducing the ash content, and were also observed decrease in the apparent activation energy of these samples. The catalytic pyrolysis process converted most of the oxygenate componds in aromatics such as benzene, toluene, ethylbenzene, etc

Síntese e caracterização de materiais nanoporosos para pirólise catalítica de óleos pesados

The present work reports the study of nanoporous structures, aiming at their use in research directed to the current demand of the petroleum industry to value heavy oil. Initially, two ways were chosen for the synthesis of porous structures from the molecular sieves of type Si-MCM-41. In the first way, the structure MCM-41 is precursory for heteroatom substitutes of silicon, generating catalyst of the type Al-MCM-41 from two different methods of incorporation of the metal. This variation of the incorporation method of Aluminum in the structure of Si-MCM-41 was carried out through the conventional procedure, where the aluminum source was incorporated to the gel of synthesis, and the procedure post-synthesis, where the Aluminum source was incorporated in catalyst after the synthesis of Si-MCM-41. In the second way, the MCM-41 acts as a support for growth of nanocrystals of zeolite embedded in their mesoporous, resulting in hybrid MCM-41/ZSM-5 catalyst. A comparative analysis was carried through characterizations by XRD, FTIR, measures of acidity through n-butylamine adsorption for TGA, SEM-XRF and N2 adsorption. Also crystalline aluminosilicate with zeolitic structure MFI of type ZSM-5 was synthesized without using organic templates. Methodologies to the preparation of these materials are related by literature using conventionally reactants that supply oxides of necessary silicon and aluminum, as well as a template agent, and in some cases co-template. The search for new routes of preparation for the ZSM-5 aimed at, above all, the optimization of the same as for the time and the temperature of synthesis, and mainly the elimination of the use of organic templates, that are material of high cost and generally very toxic. The current study is based on the use of the H2O and Na+ cations playing the role of structural template and charge compensation in the structure. Characterizations by XRD, FTIR, SEM-XRF and N2 adsorption were also conducted for this material in order to compare the samples of ZSM-5 synthesized in the absence of template and those used industrially and synthesized using structuring

Carregadores de oxigênio a base de níquel suportado em materiais mesooros para aplicação na recirculação química com reforma (RQR)

Oxygen carriers are metal oxides which have the ability to oxidize and reduce easily by various cycles. Due to this property these materials are widely usedin Chemical-Looping Reforming processes to produce H2 and syngas. In this work supports based on MCM-41 and La-SiO2 were synthesized by hydrothermal method. After the synthesis step they were calcined at 550°C for 2 hours and characterized by TG, XRD, surface area using the BET method and FTIR spectroscopy. The deposition of active phase, in this case Nickel, took place in the proportions of 5, 10 and 20% by weight of metallic nickel, for use as oxygen carriers.The XRD showed that increasing in the content of Ni supported on MCM-41 resulted in a decrease in spatial structure and lattice parameter of the material. The adsorption and desorption curves of the MCM-41 samples exhibited variations with the increase of Ni deposited. Surface area, average pore diameter and wall density of silica showed significant changes , due to the increase of the active phase on the mesoporous material. By other hand, in the samples with La-SiO2 composition was not observed peaks characteristic of hexagonal structure, in the XRD diffractogram. The adsorption/desorption isotherms of nitrogen observed are type IV, characteristic of mesoporous materials. The catalytic test indicates that the supports have no influence in the process, but the nickel concentration is very important, because the results for minor concentration of nickel are not good. The ratio H2/O2 was close to 2, for all 15 cycles involving the test storage capacity of O2, indicating that the materials are effective for oxygen transport

Síntese e caracterização de zeólita beta hierarquizada e materiais híbridos micro-mesoporosos aplicados no craqueamento de PEAD

A catalyst of great interest to the scientific community tries to unite the structure of ordered pore diameter from mesoporous materials with the properties of stability and acid activity to microporous zeolites. Thus a large number of materials was developed in the past decades, which although being reported as zeolites intrinsically they fail to comply with some relevant characteristics to zeolites, and recently were named zeolitic materials of high accessibility. Among the various synthesis strategies employed, the present research approaches the synthesis methods of crystallization of silanized protozeolitic units and the method of protozeolitic units molded around surfactant micelles, in order for get materials defined as hierarchical zeolites and micro-mesoporous hybrid materials, respectively. As goal BEA/MCM-41 hybrid catalysts with bimodal pore structure formed by nuclei of zeolite Beta and cationic surfactant cetyltrimethylammonium were developed. As also was successfully synthesized the hierarchical Beta zeolite having a secondary porosity, in addition to the typical and uniform zeolite micropores. Both catalysts were applied in reactions of catalytic cracking of high density polyethylene (HDPE), to evaluate its properties in catalytic activity, aiming at the recycling of waste plastics to obtain high value-added raw materials and fuels. The BEA/MCM-41 hybrid materials with 0 days of pre-crystallization did not show enough properties for use in catalytic cracking reactions, but they showed superior catalytic properties compared to those ordered mesoporous materials of Al-MCM-41 type. The structure of Beta zeolite with hierarchical porosity leads the accessibility of HDPE bulky molecules to active centers, due to high external area. And provides higher conversion to hydrocarbons in the gasoline range, especially olefins which have great interest in the petrochemical industry

Síntese de catalisadores nanoporosos na ausência total e parcial de direcionadores orgânicos para pirólise catalítica de óleos pesados e intermediários

The processing of heavy oil produced in Brazil is an emergency action and a strategic plan to obtain self-sufficiency and economic surpluses. Seen in these terms, it is indispensable to invest in research to obtain new catalysts for obtaining light fraction of hydrocarbons from heavy fractions of petroleum. This dissertation for the degree of Doctor of Philosophy reports the materials preparation that combine the high catalytic activity of zeolites with the greater accessibility of the mesoporosity, more particularly the HZSM-5/MCM-41 hybrid, done by synthesis processes with less environmental impact than conventional ones. Innovative methodologies were developed for the synthesis of micro-mesoporous hybrid material by dual templating mechanism and from crystalline zeolitic aluminosilicate in the absence of organic template. The synthesis of hybrid with pore bimodal distribution took place from one-single organic directing agent aimed to eliminate the use of organic templates, acids of any kind or organic solvents like templating agent of crystalline zeolitic aluminosilicate together with temperature-programmed microwave-assisted, making the experimental procedures of preparation most practical and easy, with good reproducibility and low cost. The study about crystalline zeolitic aluminosilicate in the absence of organic template, especially MFI type, is based on use of H2O and Na+ cation playing a structural directing role in place of an organic template. Advanced characterization techniques such as X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), Scanning Electron Microscopy (SEM), Highresolution Transmission Electron Microscopy (HRTEM), Adsorption of N2 and CO2, kinetic studies by Thermogravimetric Analysis (TGA) and Pyrolysis coupled to Gas Chromatography/Mass Spectrometry (Pyrolysis-GC/MS) were employed in order to evaluate the synthesized materials. Achieve the proposed objectives, has made available a set of new methodologies for the synthesis of zeolite and hybrid micro-mesoporous material, these suitable for catalytic pyrolysis of heavy oils aimed at producing light fraction

Estudo de materiais mesoporosos funcionalizados com diferentes aminas para captura do dióxido de carbono através do processo de adsorção

Intensive use of machinery and engines burning fuel dumps into the atmosphere huge amounts of carbon dioxide (CO2), causing the intensification of the greenhouse effect. Climate changes that are occurring in the world are directly related to emissions of greenhouse gases, mainly CO2, gases, mainly due to the excessive use of fossil fuels. The search for new technologies to minimize the environmental impacts of this phenomenon has been investigated. Sequestration of CO2 is one of the alternatives that can help minimize greenhouse gas emissions. The CO2 can be captured by the post-combustion technology, by adsorption using adsorbents selective for this purpose. With this objective, were synthesized by hydrothermal method at 100 °C, the type mesoporous materials MCM - 41 and SBA-15. After the synthesis, the materials were submitted to a calcination step and subsequently functionalized with different amines (APTES, MEA, DEA and PEI) through reflux method. The samples functionalized with amines were tested for adsorption of CO2 in order to evaluate their adsorption capacities as well, were subjected to various analyzes of characterization in order to assess the efficiency of the method used for functionalization with amines. The physic-chemical techniques were used: X- ray diffraction (XRD), nitrogen adsorption and desorption (BET/BJH), scanning electron microscopy (SEM), transmission electron microscopy (TEM), CNH Analysis, Thermogravimetry (TG/DTG) and photoelectron spectroscopy X-ray (XPS). The CO2 adsorption experiments were carried out under the following conditions: 100 mg of adsorbent, at 25 °C under a flow of 100 ml/min of CO2, atmospheric pressure and the adsorption variation in time 10-210 min. The X-ray diffraction with the transmission electron micrographs for the samples synthesized and functionalized, MCM-41 and SBA-15 showed characteristic peaks of hexagonal mesoporous structure formation, showing the structure thereof was obtained. The method used was efficient reflux according to XPS and elemental analysis, which showed the presence of amines in the starting materials. The functionalized SBA -15 samples were those that had potential as best adsorbent for CO2 capture when compared with samples of MCM-41, obtaining the maximum adsorption capacity for SBA-15-P sample

Detecção e quantificação eletroquímica de substâncias de interesse clínico, ambiental e forense utilizando eletrodo de pasta de grafite modificado com trisilanol poss ligado a suportes porosos e eletrodos impressos obtidos via screen-printed

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Inverse size exclusion chromatography (ISEC)

In this work, an improved protocol for inverse size-exclusion chromatography (ISEC) was established to assess important pore structural data of porous silicas as stationary phases in packed chromatographic columns. After the validity of the values generated by ISEC was checked by comparison with data obtained from traditional methods like nitrogen sorption at 77 K (Study A), the method could be successfully employed as valuable tool at the development of bonded poly(methacrylate)-coated silicas, while traditional methods generate partially incorrect pore structural information (Study B). Study A: Different mesoporous silicas were converted by a pseudomorphical transition into ordered MCM-41-type silica while maintaining the particle-size and -shape. The essential parameters like specific surface area, average pore diameter and specific pore volume, the pore connectivity from ISEC remained nearly the same which was reflected by the same course of the theoretical plate height vs. linear velocity curves. Study B: In the development of bonded poly(methacrylate)-coated silicas for the reversed phase separation of biopolymers, ISEC was the only method to generate valid pore structural information of the polymer-coated materials. Synthesis procedures were developed to obtain reproducibly covalently bonded poly(methacrylate) coatings with good thermal stability on different base materials, employing as well particulate and monolithic materials.

Sviluppo dei materiali innovativi e studio della loro interazione con sistemi biologici e biomimetici

Nell’ambito della Chimica Sostenibile e dell’applicazione dei suoi principi per la salvaguardia dell’ambiente, il progetto di dottorato ha riguardato lo sviluppo di materiali innovativi e lo studio della loro interazione con sistemi biologici e biomimetici. In particolare l’attività si è focalizzata sulla sintesi di liquidi ionici ed indagini delle interazioni con membrane cellulari e sull’utilizzo ed isolamento di molecole da fonti rinnovabili. I liquidi ionici sono sali organici liquidi a temperature inferiori ai 100 °C; sono considerati promettenti solventi a ridotta tossicità, ma vanno chiarite a pieno le modalità di interazione con i sistemi biologici ed i meccanismi di tossicità. A questo scopo è stata impiegata una batteria di test bio-chimici, con saggi di fluorescenza e colorimetrici, che hanno permesso di discriminare le diverse tipologie di interazioni con varie strutture di membrana. Le informazioni raccolte sono servite per progettare sostanze meno dannose per le strutture cellulari, al fine di scegliere le funzionalità molecolari che consentano ai liquidi ionici di mantenere la loro attività ma di essere meno dannosi per l’ambiente. Per quanto riguarda l’utilizzo ed isolamento di molecole da fonte rinnovabili, si è utilizzata la tecnica della pirolisi per l’ottenimento di starting materials ed il loro impiego nella sintesi di chemicals in alternativa a composti derivanti da fonti fossili. La pirolisi tradizionale della cellulosa fornisce una molecola interessante, per semplicità denominata LAC, in quantità insufficienti ad un uso applicativo. Nell’ambito delle ricerche svolte è stato scoperto che la pirolisi condotta in presenza di catalizzatori meso-strutturati (MCM-41) drogati con metalli di transizione, fornisce buone quantità di LAC. LAC si è dimostrato promettente sia per la produzione di nuove molecole con possibili applicazioni nella chimica fine e farmaceutica, che come monomero per nuovi polimeri (copolimero ed omopolimero).

Sintesi e caratterizzazione di sistemi catalitici a base di pd-cu e loro utilizzo nella reazione di idrodeclorurazione di molecole clorofluorurate

Questo lavoro di tesi ha avuto come obiettivo quello di individuare e studiare diverse strategie di sintesi per la preparazione di catalizzatori a base di Pd-Cu supportati su materiali mesoporosi a basi di SiO2. Queste strategie sono state mirate a migliorare: -Distribuzione della fase metallica attiva e la sua accessibilità; -Formazione della fase mista Pd-Cu; -Dimensione delle specie metalliche sulla superficie; -Differenti caratteristiche morfologiche del supporto. I diversi catalizzatori preparati sono stati poi testati sulla reazione di idrodeclorurazione del 1,2-dicloro-1,1,2-trifluoro-2-(triflurometossi)etano (AM), svolta in fase gas con idrogeno a pressione atmosferica, con lo scopo di ottenere il composto insaturo corrispondente 1,1,2-trifluoro-2-(trifluorometossi)etene (MVE). Attualmente, il processo industriale per la produzione di MVE, è condotto con l’utilizzo di quantità stechiometriche di Zn in dimetilformammide; questo processo a causa delle quantità stechiometriche di ZnCl2 prodotto e dell'elevato consumo di solvente tossico risulta assai dispendioso dal punto di vista economico ed ambientale. La tipologia di materiali microporosi, già investigata, può limitare l'efficienza verso substrati ingombranti, è quindi interessante investigare catalizzatori con dimensione dei pori mesoporosi a base di silice; in particolare sono stati analizzati MCM-41 e silice amorfa GRACE® DAVICAT - 1401. In particolare, durante il lavoro di tesi sono stati sviluppati i seguenti argomenti: 1.Studio degli effetti della metodologia di sintesi e del contenuto metallico sui parametri chimico-fisici e catalitici dei sistemi a base di Pd-Cu supportati su MCM-41 e GRACE® DAVICAT - 1401; 2.Ottimizzazione del processo di sintesi dei supporti di MCM-41, ponendo attenzione alle quantità dei reagenti utilizzati, alla metodologia di eliminazione del templante e al tempo di trattamento idrotermale; 3.Ottimizzazione del processo di sintesi dei sistemi catalitici a base di Pd-Cu, al fine di ottenere una fase attiva costituita da particelle con dimensioni ridotte composte da una fase mista Pd-Cu.