Reversible ferromagnetic switching in ZnO:(Co,Mn) powders

We report here on the magnetic properties of ZnO:Mn- and ZnO:Co-doped nanoparticles. We have found that the ferromagnetism of ZnO:Mn can be switched on and off by consecutive low-temperature annealings in O2 and N2, respectively, while the opposite phenomenology was observed for ZnO:Co. These results suggest that different defects (presumably n-type for ZnO:Co and p-type for ZnO:Mn) are required to induce a ferromagnetic coupling in each case. We will argue that ferromagnetism is likely to be restricted to a very thin, nanometric layer at the grain surface. These findings reveal and give insight into the dramatic relevance of surface effects to the occurrence of ferromagnetism in ZnO-doped oxides.

Finite size effects on the structural and magnetic properties of sol–gel synthesized NiFe2O4 powders

Nanoparticles of nickel ferrite have been synthesized by the sol–gel method and the effect of grain size on its structural and magnetic properties have been studied in detail. X-ray diffraction (XRD) studies revealed that all the samples are single phasic possessing the inverse spinel structure. Grain size of the sol–gel synthesized powders has been determined from the XRD data and the strain graph. A grain size of 9 nm was observed for the as prepared powders of NiFe2O4 obtained through the sol–gel method. It was also observed that strain was induced during the firing process. Magnetization measurements have been carried out on all the samples prepared in the present series. It was found that the specific magnetization of the nanosized NiFe2O4 powders was lower than that of the corresponding coarse-grained counterparts and decreased with a decrease in grain size. The coercivity of the sol–gel synthesized NiFe2O4 nanoparticles attained a maximum value when the grain size was 15nm and then decreased as the grain size was increased further.

Finite size effects on the electrical properties of sol–gel synthesized CoFe2O4 powders: deviation from Maxwell–Wagner theory and evidence of surface polarization effects

Fine particles of cobalt ferrite were synthesized by the sol–gel method. Subsequent heat treatment at different temperatures yielded cobalt ferrites having different grain sizes. X-ray diffraction studies were carried out to elucidate the structure of all the samples. Dielectric permittivity and ac conductivity of all the samples were evaluated as a function of frequency, temperature and grain size. The variation of permittivity and ac conductivity with frequency reveals that the dispersion is due to Maxwell–Wagner type interfacial polarization in general, with a noted variation from the expected behaviour for the cold synthesized samples. High permittivity and conductivity for small grains were explained on the basis of the correlated barrier-hopping model

Survival of freeze dried Lactobacillus plantarum in instant fruit powders and reconstituted fruit juices

The aim of this study was to investigate the survival of freeze dried Lactobacillus plantarum cells mixed with several freeze dried instant fruit powders (strawberry, pomegranate, blackcurrant and cranberry) during storage for 12 months as well as after reconstitution with water each month. Inulin and gum arabic were also added to the instant fruit powders at two levels (10% and 20% w/w of dry weight) to improve the cell survival and functional properties of the product. The best cell survival over the 12 months of storage was observed for the blackcurrant powder (almost no decrease) followed by strawberry (~ 0.3 log decrease), pomegranate (~ 0.9 log decrease), whereas the worst survival was obtained in cranberry powder (~ 4.5 logs). To explain these results multiple regression analysis was conducted with the log decrease [log10N0 month − log10N12 months] as the dependent variable and water activity, pH, citric acid, dietary fibre and total phenol as the independent variables. The results indicated that among all the examined factors, the [log10N0 month − log10N12 months] depended only on the water activity (P < 0.05). Inulin and gum arabic demonstrated a substantial protective effect on cell survival (1–1.5 log) in the case of cranberry, which was likely due to a physical interaction between the cells and the carbohydrates. After reconstituting the dried fruit powders at room temperature and measuring cell viability for up to 4 h, it was shown that in the case of strawberry juice there was no decrease, and very little in the case of pomegranate and blackcurrant juices (< 0.5 log). On the other hand, a significant decrease was observed for cranberry juice (P < 0.05), which increased as the storage time of the dried cranberry powder increased, indicating that the cells became more susceptible with prolonged storage. Multiple regression analysis indicated that the main factors influencing cell survival were water activity and pH, while citric acid, dietary fibre and total phenol did not have an effect. Furthermore, inulin and gum arabic addition did not have a significant (P > 0.05) effect upon reconstitution of the dried fruit powder. This study showed that instant juice powders are very good carriers of probiotic cells and constitute good alternatives to highly acidic fruit juices.

Enhancement of aged and denatured fingerprints using the cyanoacrylate fuming technique following dusting with amino acid-containing powders

We have carried out experiments to investigate the ageing of latent fingerprints deposited on black PVC over a period of 4-15 weeks. A thumbprint was used in each case and before deposition of the print the donor rubbed their thumb around their nose to add sebaceous deposits. We have studied the effect of heat, light and moisture and we find that moisture is the most significant factor in the degradation of the latent print. We have attempted to enhance these latent prints by dusting with valine powder or powders composed of valine mixed with gold or red fluorescent commercial fingerprint powders. In order to make a direct comparison between “treated” and “untreated” prints, the prints were cut in half with one half being “treated” and one not. Our studies show the best results being obtained when powders of valine and red fluorescent powders are applied prior to cyanoacrylate fuming.

Electronic structure and optical properties of BaMoO(4) powders

Barium molybdate (BaMoO(4)) powders were synthesized by the co-precipitation method and processed in microwave-hydrothermal at 140 degrees C for different times. These powders were characterized by X-ray diffraction (XRD), Fourier transform Raman (FT-Raman), Fourier transform infrared (FT-IR), ultraviolet-visible (UV-vis) absorption spectroscopies and photoluminescence (PL) measurements. XRD patterns and FT-Raman spectra showed that these powders present a scheelite-type tetragonal structure without the presence of deleterious phases. FT-IR spectra exhibited a large absorption band situated at around 850.4 cm(-1), which is associated to the Mo-O antisymmetric stretching vibrations into the [MoO(4)] clusters. UV-vis absorption spectra indicated a reduction in the intermediary energy levels within band gap with the processing time evolution. First-principles quantum mechanical calculations based on the density functional theory were employed in order to understand the electronic structure (band structure and density of states) of this material. The powders when excited with different wavelengths (350 nm and 488 nm) presented variations. This phenomenon was explained through a model based in the presence of intermediary energy levels (deep and shallow holes) within the band gap. (C) 2009 Elsevier B.V. All rights reserved.

A new processing method of CaZn(2)(OH)(6)center dot 2H(2)O powders: Photoluminescence and growth mechanism

In this communication, we report on the formation of calcium hexahydroxodizincate dehydrate, CaZn(2)(OH)(6)center dot 2H(2)O (CZO) powders under microwave-hydrothermal (MH) conditions. These powders were analyzed by X-ray diffraction (XRD), Field-emission gum scanning electron microscopy (FEG-SEM), ultraviolet-visible (UV-vis) absorption spectroscopy and photoluminescence (PL) measurements. XRD patterns confirmed that the pure CZO phase was obtained after MH processing performed at 130 degrees C for 2 h. FEG-SEM micrographs indicated that the morphological modifications as well as the growth of CZO microparticles are governed by Ostwald-ripening and coalescence mechanisms. UV-vis spectra showed that this material have an indirect optical band gap. The pure CZO powders exhibited an yellow PL emission when excited by 350 nm wavelength at room temperature. (C) 2009 Elsevier Masson SAS. All rights reserved.

Thermal and structural investigation of Er:YAl(3)(BO(3))(4) nanocrystalline powders

Pure Er:YAB (Er:YAl(3)(BO(3))(4)) nanometer-sized crystalline powder was produced from low cost chemical route, the polymeric precursor method. The initial homogeneous solutions were heat treated from 200 to 700A degrees C under oxygen atmosphere and the unique crystalline phase was synthesized at around 1150A degrees C. The thermal treatments and the initial stoichiometry play a very important role on the Er:YAB preparation. The thermal events of amorphous precursor resins and the crystallization process up to phase formation were investigated.

Intense violet-blue photoluminescence in BaZrO3 powders: A theoretical and experimental investigation of structural order-disorder

Intense violet-blue photoluminescence (PL) emission at room temperature was verified in BaZrO3 (BZO) powders with structural order-disorder. Ab-initio calculations, ultraviolet-visible absorption spectroscopy and PL were performed. Theoretical results showed that the local disorder in the network-formed Zr clusters present an important role in the formation of hole-electron pair. The experimental data and theoretical results are in agreement, indicating that the PL emission in BZO powders can be related to the structural order-disorder degree in the lattice. (C) 2008 Elsevier B.V. All rights reserved.

Structure and optical properties of [Ba(1-x)Y(2x/3)](Zr(0.25)Ti(0.75))O(3) powders

[Ba(1-x)Y(2x/3)](Zr(0.25)Ti(0.75))O(3) powders with different yttrium concentrations (x = 0, 0.025 and 0.05) were prepared by solid state reaction. These powders were analyzed by X-ray diffraction (XRD). Fourier transform Raman scattering (FT-RS), Fourier transform infrared (FT-IR) and X-ray absorption near-edge (XANES) spectroscopies. The optical properties were investigated by means of ultraviolet-visible (UV-vis) absorption spectroscopy and photoluminescence (PL) measurements. Even with the addition of yttrium, the XRD patterns revealed that all powders crystallize in a perovskite-type cubic structure. FT-RS and FT-IR spectra indicated that the presence of [YO(6)] clusters is able to change the interaction forces between the O-Ti-O and O-Zr-O bonds. XANES spectra were used to obtain information on the off-center Ti displacements or distortion effects on the [TiO(6)] clusters. The different optical band gap values estimated from UV-vis spectra suggested the existence of intermediary energy levels (shallow or deep holes) within the band gap. The PL measurements carried out with a 350 nm wavelength at room temperature showed that all powders present typical broad band emissions in the blue region. (C) 2010 Elsevier Masson SAS. All rights reserved.

Luminescence characteristics of YAP:Ce scintillator powders and composites

Cerium doped yttrium aluminate perovskite YAlO(3) (YAP) powders are pursued as interesting alternatives to bulk crystals for application in scintillating devices. The emissions of these materials in the near-UV and visible spectral regions originate from electric dipole transitions between 4f and 5d energy levels of Ce(3+) and largely depend on the environment occupied by the ion. In search for improved synthesis conditions that can lead to phase pure powders with optimized structural and spectroscopic characteristics, in this work we have employed the polymeric precursor (Pechini) method to prepare crystalline and amorphous YAP:Ce powders doped with 1-10 mol% Ce(3+). Interesting composite materials were also obtained by dispersing some of the YAP:Ce powders in silica xerogels. A comparative structural and spectroscopic study of all the samples was done by XRD, FT-IR, emission, excitation and excited state lifetime measurements. In agreement with previous reports, excitation at 296 nm results in intense emission in the range 315-425 nm with an average decay time of 30 ns. (c) 2010 Elsevier B.V. All rights reserved.

Total phenolic content and free radical scavenging activities of methanolic extract powders of tropical fruit residues

Methanolic extract powders of acerola, passion fruit and pineapple industrial residues, including pulp, seeds and peel, altogether (except for acerola) devoid of seeds, were screened for antioxidant capacity. The total phenolic contents (TPCs) of the extract powders were compared with their radical-scavenging activities (RSA) against both DPPH(center dot) and superoxide anion (O(2)(center dot-)) radicals, and their protective effect against liposome peroxidation, triggered by peroxyl radical. Lipid peroxidation was followed by the fluorescence decay of the probe, 4,4-difluoro-5-(4-phenyl-1,3-butadienyl)-4-bora-3a,4a-diaza-s-indacene-3-undecanoic acid (C(11)-BODIPY(581/591)). The TPCs of acerola, passion fruit and pineapple extract powders were (94.6 +/- 7.4); (41.2 +/- 4.2) and (9.1 +/- 1.3) mg of gallic acid equivalents g(-1) of dry extract, respectively. Acerola showed the best RSA-DPPH(center dot) scores, whereas passion fruit was more protective on the RSA-O(2)(center dot-) system. Together with the protective effects against lipid peroxidation (rate of BODIPY decay) which, were similar for acerola and passion fruit extracts, these data suggest that the methanolic extracts of acerola and passion fruit residues may be useful as antioxidant supplements, particularly the acerola extract, due to its high phenolic content. (C) 2008 Elsevier Ltd. All rights reserved

Morphological and Structural changes of CaxSr1-xTiO3 Powders Obtained by the Microwave-Assisted Hydrothermal Method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Different origins of green-light photoluminescence emission in structurally ordered and disordered powders of calcium molybdate

A strong greenish-light photoluminescence (PL) emission was measured at room temperature for disordered and ordered powders of CaMoO4 prepared by the polymeric precursor method. The structural evolution from disordered to ordered powders was accompanied by XRD. Raman spectroscopy, and TEM imagery. High-level quantum mechanical calculations in the density functional framework were used to interpret the formation of the structural defects of disorder powders in terms of band diagram and density of states. Complex cluster vacancies [MoO3 center dot V-O(z)] and [CaO7 center dot V-O(z)] (where V-O(z) = V-O(X), V-O(center dot), V-O(center dot center dot)) were suggested to be responsible to the appearance of new states shallow and deeply inserted in the band gap. These defects give rise to the PL in disordered powders. The natural PL emission of ordered CaMoO4 was attributed to an intrinsic slight distortion of the [MoO4] tetrahedral in the short range.

Experimental and theoretical correlation of very intense visible green photoluminescence in BaZrO3 powders

Very intense visible green photoluminescence (PL) was observed at room temperature in structurally ordered-disordered BaZrO3 powders. Ab initio calculations, ultraviolet-visible absorption spectroscopy, electron paramagnetic resonance, and PL were performed. Theoretical and experimental results showed that local defects in the cubic structure caused by [ZrO5 center dot V-O(z)] complex clusters, where V-O(z) = V-O(x), V-O(center dot), and V-O(center dot center dot), play an important role in the formation of hole-electron pairs, giving rise to a charge gradient in the structure which is responsible for PL emission. (c) 2008 American Institute of Physics.