Oxygen plasma treatment of sisal fibers and polypropylene: Effects on mechanical properties of composites

Polypropylene powder and sisal fibers were oxygen plasma treated, and the mechanical properties of their composites were tested. Two main effects were investigated: the incorporation of oxygen polar groups in the polypropylene surface and the surface degradation and chain scission of both polypropylene and sisal fibers. Prior to these treatments, three reactor configurations were tested to investigate the best condition for both effects to occur in PP film. Results showed that polypropylene-cellulose adhesion forces are about an order of magnitude higher for PP film treatments at 13.56 MHz than at 40 kHz owing to much higher chain scission at lower frequencies, although it probably also occurs at high frequency and high power. Polypropylene powder treated with oxygen plasma in optimum conditions for polar group incorporation did not result in improvement in any composite mechanical property, probably owing to the polymer melting. Sisal fibers and PP powder treated In conditions of surface degradation did not improve flexural or tensile properties but resulted in higher impact resistance, comparable to the improvement obtained with the addition of compatibilizer.

Morphological, mechanical properties and biodegradability of biocomposite thermoplastic starch and polycaprolactone reinforced with sisal fibers

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Pineapple Leaf Fibers for Composites and Cellulose

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Charge density alterations in human hair fibers: An investigation using electrostatic force microscopy

A new method for high-resolution analyses of hair surface charge density under ambient conditions is presented in this paper. Electrostatic force microscopy (EFM) is used here to analyze changes in surface charge density in virgin hair, bleached hair, and hair treated with a cationic polymer. The atomic force microscopy technique is used concomitantly to analyze morphological changes in hair roughness and thickness. The EFM images depict exactly how the polymer is distributed on the surface of the hair fiber. The EFM's powerful analytical tools enabled us to evaluate the varying degrees of interaction between the hair fiber surface charge density and the cationic polymer. The surface charge density and the polymer's distribution in the hair fibers are presented in the light of EFM measurements. © 2006 Society of Cosmetic Scientists and the Socièété Française de Cosmétologie.

Analysis of mechanical behavior in bending of polymer composites using the finite elements method

The use of composite materials has increased in the recent decades, mainly in the aeronautics and automotives industries. In the present study is elaborated a computational simulation program of the bending test using the finite elements method, in the commercial software ANSYS. This simulation has the objective of analyze the mechanical behavior in bending of two composites with polymeric matrix reinforced with carbon fibers. Also are realized bending tests of the 3 points to obtain the resistances of the materials. Data from simulation and tests are used to make a comparison between two failures criteria, Tsai-Wu and Hashin criterion. Copyright © 2009 SAE International.

Production of an axial piston: Impacts resulting from the substitution of steel by a polymer-based material

The substitution of steel as a raw material in the production of axial pistons for pressure washers by polyphthalamide, polytetrafluoroethylene and glass fiber-based composite was studied. The new production process with composite consists of only two steps, while the production of the steel piston is to comprise of thirteen steps. This replacement would result in an estimated reduction of 80% of water consumption, 83% of electricity consumption, 73% of the total cost and 88% of the final mass. With regard to the main mechanical properties required for the end product, the composite was found to withstand the critical axial loads and it shows acceptable wear resistance in an environment without lubrication, an additional advantage of this replacement. © 2012 Elsevier Ltd. All rights reserved.

Strategies to improve the mechanical properties of starch-based materials: plasticization and natural fibers reinforcement

Biodegradable polymers are starting to be introduced as raw materials in the food-packaging market. Nevertheless, their price is very high. Starch, a fully biodegradable and bioderived polymer is a very interesting alternative due to its very low price. However, the use of starch as the polymer matrix for the production of rigid food packaging, such as trays, is limited due to its poor mechanical properties, high hidrophilicity and high density. This work presents two strategies to overcome the poor mechanical properties of starch. First, the plasticization of starch with several amounts of glycerol to produce thermoplastic starch (TPS) and second, the production of biocomposites by reinforcing TPS with promising fibers, such as barley straw and grape waste. The mechanical properties obtained are compared with the values predicted by models used in the field of composites; law of mixtures, Kerner-Nielsen and Halpin-Tsai. To evaluate if the materials developed are suitable for the production of food-packaging trays, the TPS-based materials with better mechanical properties were compared with commercial grades of oil-based polymers, polypropylene (PP) and polyethylene-terphthalate (PET), and a biodegradable polymer, polylactic acid (PLA).

Preparation and evaluation of the electrospun chitosan/PEO fibers for potential applications in cartilage tissue engineering

Fibrous materials have morphological similarities to natural cartilage extracellular matrix and have been considered as candidate for bone tissue engineering scaffolds. In this study, we have evaluated a novel electrospun chitosan mat composed of oriented sub-micron fibers for its tensile property and biocompatibility with chondrocytes (cell attachment, proliferation and viability). Scanning electronic microscope images showed the fibers in the electrospun chitosan mats were indeed aligned and there was a slight cross-linking between the parent fibers. The electrospun mats have significantly higher elastic modulus (2.25 MPa) than the cast films (1.19 MPa). Viability of cells on the electrospun mat was 69% of the cells on tissue-culture polystyrene (TCP control) after three days in culture, which was slightly higher than that on the cast films (63% of the TCP control). Cells on the electrospun mat grew slowly the first week but the growth rate increased after that. By day 10, cell number on the electrospun mat was almost 82% that of TCP control, which was higher than that of cast films (56% of TCP). The electrospun chitosan mats have a higher Young’s modulus (P <0.01) than cast films and provide good chondrocyte biocompatibility. The electrospun chitosan mats, thus, have the potential to be further processed into three-dimensional scaffolds for cartilage tissue repair.

Tannin-phenolic resins: Synthesis, characterization, and application as matrix in biobased composites reinforced with sisal fibers

A tannin-phenolic resin (40 wt% of tannin, characterized by H-1 nuclear magnetic resonance (NMR) and C-13 NMR, Fourier transform infrared, thermogravimetry, differential scanning calorimetry) was used to prepare composites reinforced with sisal fibers (30-70 wt%). Inverse gas chromatography results showed that the sisal fibers and the tannin-phenolic thermoset have close values of the dispersive component and also have predominance of acid sites (acid character) at the surface, confirming the favoring of interaction between the sisal fibers and the tannin-phenolic matrix at the interface. The Izod impact strength increased up to 50 wt% of sisal fibers. This composite also showed high storage modulus, and the lower loss modulus, confirming its good fiber/matrix interface, also observed by SEM images. A composite with good properties was prepared from high content of raw material obtained from renewable sources (40 wt% of tannin substituted the phenol in the preparation of the matrix and 50 wt% of matrix was replaced by sisal fibers). (C) 2012 Elsevier Ltd. All rights reserved.

Materials prepared from biopolyethylene and curaua fibers: Composites from biomass

Composites of high-density biopolyethylene (HDBPE) obtained from ethylene derived from sugarcane ethanol and curaua fibers were formed by first mixing in an internal mixer followed by thermopressing. Additionally, hydroxyl-terminated polybutadiene (LHPB), which is usually used as an impact modifier, was mainly used in this study as a compatibilizer agent. The fibers, HDBPE and LHPB were also compounded using an inter-meshing twin-screw extruder and, subsequently, injection molded. The presence of the curaua fibers enhanced some of the properties of the HDBPE, such as its flexural strength and storage modulus. SEM images showed that the addition of LHPB improved the adhesion of the fiber/matrix at the interface, which increased the impact strength of the composite. The higher shear experienced during processing probably led to a more homogeneous distribution of fibers, making the composite that was prepared through extruder/injection molding more resistant to impact than the composite processed by the internal mixer/thermopressing. (c) 2012 Elsevier Ltd. All rights reserved.

Novel Sealing Technique for Practical Liquid-Core Photonic Crystal Fibers

In this letter, we describe a simple and effective technique to prevent evaporation in liquid-core photonic crystal fibers (PCFs). The technique consists of using a micropipette to deploy a micro-droplet of an ultraviolet curable polymer adhesive in both core inputs. After it is cured, the adhesive creates sealing polymer plugs with quite satisfactory insertion loss (overall optical transmission of about 15%). Processed fibers remained liquid-filled for at least six weeks. From a practical point of view, we conducted a supercontinuum generation experiment in a water-core PCF to demonstrate a 120-minute spectral width stability and the ability to withstand at least 3-mW average power at the sealed fiber input. Similar experiments carried out with nonsealed fibers produced supercontinuum spectra lasting no longer than 10 minutes, with average powers kept below 0.5 mW to avoid thermally induced evaporation.

Clay-containing block copolymer nanocomposites with aligned morphology prepared by extrusion

Clay-containing nanocomposites of polystyrene-b-poly(ethylene-co-butylene)-b-polystyrene (SEBS) copolymers having cylindrical domains were obtained by melt extrusion using a tape die. One type of sample (SEBS-MA) had maleic anhydride attached to the middle block. Two types of organoclays were added, namely Cloisite 20A and Cloisite 30B. Small angle X-ray scattering and transmission electron microscopy (TEM) analyses showed that the addition of 20A clay to SEBS and SEBS-MA resulted in nanocomposites with intercalated and partially exfoliated structures, respectively. The addition of 30B clay to SEBS and SEBS-MA promoted the formation of composites containing relatively large micron-sized and partially exfoliated clay particles, respectively. Our TEM analysis revealed that clay particles embedded in SEBS are preferably in contact with the polystyrene cylindrical domains, while in SEBS-MA they are in contact with the maleated matrix. The extrusion processing promoted alignment of the axes of the polystyrene cylinders along the extrusion direction in all samples, and the basal planes of the clay particles were mostly parallel to the main external surfaces of the extruded tapes. © 2013 Society of Chemical Industry.

Liquid crystal polymer brushes and their application as alignment layers in liquid crystal cells

Liquid Crystal Polymer Brushes and their Application as Alignment Layers in Liquid Crystal Cells Polymer brushes with liquid crystalline (LC) side chains were synthesized on planar glass substrates and their nematic textures were investigated. The LC polymers consist of an acrylate or a methacrylate main chain and a phenyl benzoate group as the mesogenic unit which is connected to the main chain via a flexible alkyl spacer composed of six CH2 units. The preparation of the LC polymer brushes was carried out according to the “grafting from” technique: polymerization is carried out from azo-initiators that have been previously self-assembled on the substrate. LC polymer brushes with a thickness from a few nm to 230 nm were synthesized by varying the monomer concentration and the polymerization time. The LC polymer brushes were thick enough to allow for direct observation of the nematic textures with a polarizing microscope. The LC polymer brushes grown on untreated glass substrates exhibited irregular textures (“polydomains”). The domain size is in the range of some micrometers and depends only weakly on the brush thickness. The investigations on the texture-temperature relationship of the LC brushes revealed that the brushes exhibit a surface memory effect, that is, the identical texture reappears after the LC brush sample has experienced a thermal isotropization or a solvent treatment, at which the nematic LC state has been completely destroyed. The surface memory effect is attributed to a strong anchoring of the orientation of the mesogenic units to heterogeneities at the substrate surface. The exact nature of the surface heterogeneities is unknown. The effect was observed for the LC brushes swollen with low molecular weight nematic molecules, as well. Rubbing the glass substrate with a piece of velvet cloth prior to the surface modification with the initiator and the brush growth gives rise to the formation of homogenous alignment of the mesogenic units in the LC polymer side chains. Monodomain textures were obtained for these LC brushes. The mechanism for the homogeneous alignment is based on the transfer of Nylon fibers during the rubbing process. A surfactant was mixed with the azo-initiator in modifying rubbed substrates for subsequent brush generation. Such brushes exhibited biaxial optical properties. Hybrid LC cells made from a substrate modified with biaxial brushes and a rubbed glass substrate show an orientation with a tilt angle of a = –15.6 . This work shows that LC brushes grown on rubbed surfaces fulfill the important criteria for alignment layers: the formation of macroscopic monodomains. First results indicate that by diluting the brush with molecules which are also covalently bound to the surface but induce a different orientation, a system is obtained in which the two conflicting alignment mechanisms can be used to generate a tilted alignment. In order to allow for an application of the alignment layers into a potential product, subsequent work should focus on the questions how easy and in which range the tilt angle can be controlled.

Polymer-liquid crystal interface: a molecular dynamics study

Liquid crystals (LCs) are an interesting class of soft condensed matter systems characterized by an unusual combination of fluidity and long-range order, mainly known for their applications in displays (LCDs). However, the interest in LC continues to grow pushed by their application in new technologies in medicine, optical imaging, micro and nano technologies etc. In LCDs uniaxial alignment of LCs is mainly achieved by a rubbing process. During this treatment, the surfaces of polymer coated display substrates are rubbed in one direction by a rotating cylinder covered with a rubbing cloth. Basically, LC alignment involves two possible aligning directions: uniaxial planar (homogeneous) and vertical (homeotropic) to the display substrate. An interesting unresolved question concerning LCs regards the origin of their alignment on rubbed surfaces, and in particular on the polymeric ones used in the display industry. Most studies have shown that LCs on the surface of the rubbed polymer film layer are lying parallel to the rubbing direction. In these systems, micrometric grooves are generated on the film surface along the rubbing direction and also the polymer chains are stretched in this direction. Both the parallel aligned microgrooves and the polymer chains at the film surface may play a role in the LC alignment and it is not easy to quantify the effect of each contribution. The work described in this thesis is an attempt to find new microscopic evidences on the origin of LC alignment on polymeric surfaces through molecular dynamics (MD) simulations, which allow the investigation of the phenomenon with atomic detail. The importance of the arrangement of the polymeric chains in LCs alignment was studied by performing MD simulations of a thin film of a typical nematic LC, 4-cyano-4’-pentylbiphenyl (5CB), in contact with two different polymers: poly(methyl methacrylate)(PMMA) and polystyrene (PS). At least four factors are believed to influence the LC alignment: 1. the interactions of LCs with the backbone vinyl chains; 2. the interactions of LCs with the oriented side groups; 3. the anisotropic interactions of LCs with nanometric grooves; 4. the presence of static surface charges. Here we exclude the effect of microgrooves and of static surface charges from our virtual experiment, by using flat and neutral polymer surfaces, with the aim of isolating the chemical driving factors influencing the alignment of LC phases on polymeric surfaces.

Tailoring molecular weight of the conjugated model polymer MEH-PPV and its structure-property relations

In der vorliegenden Arbeit wurden Struktur-Eigenschaftsbeziehungen des konjugierten Modell-Polymers MEH-PPV untersucht. Dazu wurde Fällungs-fraktionierung eingesetzt, um MEH-PPV mit unterschiedlichem Molekulargewicht (Mw) zu erhalten, insbesondere MEH-PPV mit niedrigem Mw, da dieses für optische Wellenleiterbauelemente optimal geeignet ist Wir konnten feststellen, dass die Präparation einer ausreichenden Menge von MEH-PPV mit niedrigem Mw und geringer Mw-Verteilung wesentlich von der geeigneten Wahl des Lösungsmittels und der Temperatur während der Zugabe des Fällungsmittels abhängt. Alternativ dazu wurden UV-induzierte Kettenspaltungseffekte untersucht. Wir folgern aus dem Vergleich beider Vorgehensweisen, dass die Fällungsfraktionierung verglichen mit der UV-Behandlung besser geeignet ist zur Herstellung von MEH-PPV mit spezifischem Mw, da das UV-Licht Kettendefekte längs des Polymerrückgrats erzeugt. 1H NMR and FTIR Spektroskopie wurden zur Untersuchung dieser Kettendefekte herangezogen. Wir konnten außerdem beobachten, dass die Wellenlängen der Absorptionsmaxima der MEH-PPV Fraktionen mit der Kettenlänge zunehmen bis die Zahl der Wiederholeinheiten n  110 erreicht ist. Dieser Wert ist signifikant größer als früher berichtet. rnOptische Eigenschaften von MEH-PPV Wellenleitern wurden untersucht und es konnte gezeigt werden, dass sich die optischen Konstanten ausgezeichnet reproduzieren lassen. Wir haben die Einflüsse der Lösungsmittel und Temperatur beim Spincoaten auf Schichtdicke, Oberflächenrauigkeit, Brechungsindex, Doppelbrechung und Wellenleiter-Dämpfungsverlust untersucht. Wir fanden, dass mit der Erhöhung der Siedetemperatur der Lösungsmittel die Schichtdicke und die Rauigkeit kleiner werden, während Brechungsindex, Doppelbrechung sowie Wellenleiter-Dämpfungsverluste zunahmen. Wir schließen daraus, dass hohe Siedetemperaturen der Lösungsmittel niedrige Verdampfungsraten erzeugen, was die Aggregatbildung während des Spincoatings begünstigt. Hingegen bewirkt eine erhöhte Temperatur während der Schichtpräparation eine Erhöhung von Schichtdicke und Rauhigkeit. Jedoch nehmen Brechungsindex und der Doppelbrechung dabei ab.rn Für die Schichtpräparation auf Glassubstraten und Quarzglas-Fasern kam das Dip-Coating Verfahren zum Einsatz. Die Schichtdicke der Filme hängt ab von Konzentration der Lösung, Transfergeschwindigkeit und Immersionszeit. Mit Tauchbeschichtung haben wir Schichten von MEH-PPV auf Flaschen-Mikroresonatoren aufgebracht zur Untersuchung von rein-optischen Schaltprozessen. Dieses Verfahren erweist sich insbesondere für MEH-PPV mit niedrigem Mw als vielversprechend für die rein-optische Signalverarbeitung mit großer Bandbreite.rn Zusätzlich wurde auch die Morphologie dünner Schichten aus anderen PPV-Derivaten mit Hilfe von FTIR Spektroskopie untersucht. Wir konnten herausfinden, dass der Alkyl-Substitutionsgrad einen starken Einfluss auf die mittlere Orientierung der Polymerrückgrate in dünnen Filmen hat.rn