Defect-induced failure of optical coating filters

Optical filters composed of Ag, Al2O3, and ZnSe films were prepared on BK7 substrates by evaporation. By employing spectrophotometer, microscope, scanning electron microscope (SEM), and energy dispersive spectrum (EDS) analysis, the moisture-dependent stability of the samples was tested. The experimental results revealed that filter failure often occurs initially at defect sites. Small sputtering particles and pinhole are found to be two types of defects that induced the optical coating filter failure. The mechanisms of the defect-induced failure of the filters also are discussed in the article. (C) 2005 Elsevier Ltd. All rights reserved.

SiO2 coating of silver nanoparticles by photoinduced chemical vapor deposition.

Gas-phase silver nanoparticles were coated with silicon dioxide (SiO2) by photoinduced chemical vapor deposition (photo-CVD). Silver nanoparticles, produced by inert gas condensation, and a SiO2 precursor, tetraethylorthosilicate (TEOS), were exposed to vacuum ultraviolet (VUV) radiation at atmospheric pressure and varying temperatures. The VUV photons dissociate the TEOS precursor, initiating a chemical reaction that forms SiO2 coatings on the particle surfaces. Coating thicknesses were measured for a variety of operation parameters using tandem differential mobility analysis and transmission electron microscopy. The chemical composition of the particle coatings was analyzed using energy dispersive x-ray spectrometry and Fourier transform infrared spectroscopy. The highest purity films were produced at 300-400 degrees C with low flow rates of additional oxygen. The photo-CVD coating technique was shown to effectively coat nanoparticles and limit core particle agglomeration at concentrations up to 10(7) particles cm(-3).