Síntese e caracterização de ferritas de níquel dopadas com cobalto e efeito da substituição nas suas propriedades magnéticas

The ferrite composition Ni1 - xCoxFe2O4 (0 ≤ x ≤ 0.75) were obtained by the method of microwave assisted synthesis and had their structural and magnetic properties evaluated due to the effect of the substitution of Ni by Co. The compounds were prepared: according to the concept of chemical propellants and heated in the microwave oven with power 7000kw. The synthesized material was characterized by absorption spectroscopy in the infrared (FTIR), Xray diffraction (XRD) using the Rietveld refinement, specific surface area (BET) , scanning electron microscopy (SEM) with aid of energy dispersive analysis (EDS) and magnetic measurements (MAV). The results obtained from these techniques confirmed the feasibility of the method of synthesis employed to obtain the desired spinel structure, the ferrite, nickel ferrite as for nickel doped with cobalt. The results from XRD refinement ally showed the formation of secondary phases concerning stages α - Fe2O3, FeO, (FeCo)O e Ni0. On the other hand, there is an increase in crystallite size with the increase of cobalt in systems, resulting in an increased crystallinity. The results showed that the BET systems showed a reduction in specific surface area with the increase of cobalt and from the SEM, the formation of irregular porous blocks and that the concentration of cobalt decreased the agglomerative state of the system. The magnetic ferrites studied showed different characteristics according to the amount of dopant used, ranging from a very soft magnetic material (easy magnetization and demagnetization ) - for the system without cobalt - a magnetic material with a little stiffer behavior - for systems containing cobalt. The values of the coercive field increased with the increasing growth of cobalt, and the values of saturation magnetization and remanence increased up to x = 0,25 and then reduced. The different magnetic characteristics presented by the systems according to the amount of dopant used, allows the use of these materials as intermediates magnetic

Pharmaceutical applications of AC Biosusceptometry

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Síntese e caracterização de pós Ba(x)Sr(1-x)Co0,8Fe0,2O3- através do método de coprecipitação via oxalato

Ceramic powders based on oxides of perovskite-type structure is of fundamental interest nowadays, since they have important ionic-electronic conductivity in the use of materials with technological applications such as gas sensors, oxygen permeation membranes, catalysts and electrolytes for solid oxide fuel cells (SOFC). The main objective of the project is to develop nanostructured ceramic compounds quaternary-based oxide Barium (Br), Strontium (Sr), Cobalt (Co) and Iron (Fe). In this project were synthesized compounds BaxSr(1-x)Co0, 8Fe0,2O3- (x = 0.2, 0.5 and 0.8) through the oxalate co-precipitation method. The synthesized powders were characterized by thermogravimetric analysis and differential thermal analysis (TGADTA), X-ray diffraction (XRD) with the Rietveld refinement using the software MAUD and scanning electron microscopy (SEM). The results showed that the synthesis technique used was suitable for production of nanostructured ceramic solid solutions. The powders obtained had a crystalline phase with perovskite-type structure. The TGA-DTA results showed that the homogeneous phase of interest was obtained temperature above 1034°C. It was also observed that the heating rate of the calcination process did not affect the elimination of impurities present in the ceramic powder. The variation in the addition of barium dopant promoted changes in the average crystallite size in the nanometer range, the composition being BSCF(5582) obtained the lowest value (179.0nm). The results obtained by oxalate co-precipitation method were compared with those synthesis methods in solid state and EDTA-citrate method

Desenvolvimento de uma rota química alternativa de síntese de SrCo0,8Fe0,2O3- e LaNi0,3Co0,7O3- para aplicação na reação de oxidação do CO

This thesis focuses on the coprecipitation synthesis method for preparation of ceramic materials with perovskite structure, their characterization and application as catalytic material in the reaction of converting CO to CO2 developing a methodological alternative route of synthesis from the middle via oxalate coprecipitation material SrCo0,8Fe0,2O3-d. In order to check the influence of this method, it was also synthesized using a combined citrate - EDTA complexing method. The material was characterized by: X-ray diffraction (XRD), Rietveld refinement method, thermogravimetry and differential thermo analysis (TG / DTA), scanning (SEM) and transmission (TEM) electron microscopy, particle size distribution and surface analysis method BET. Both methods led to post-phase synthesis, with pH as a relevant parameter. The synthesis based on the method via oxalate coprecipitation among particles led to the crystalline phase as those obtained using a combined citrate - EDTA complexing method under the same conditions of heat treatment. The nature of the reagent used via oxalate coprecipitation method produced a material with approximately 80 % lower than the average size of crystallites. Moreover, the via oxalate coprecipitation method precursors obtained in the solid state at low temperature (~ 26 oC), shorter synthesis, greater thermal stability and a higher yield of around 90-95 %, maintaining the same order of magnitude the crystallite size that the combined citrate - EDTA complexing method. For purposes of comparing the catalytic properties of the material was also synthesized by the using a combined citrate - EDTA complexing method. The evaluation of catalytic materials SrCo0,8Fe0,2O3-d LaNi0,3Co0,7O3-d was accompanied on the oxidation of CO to CO2 using a stainless steel tubular reactor in the temperature range of 75-300 oC. The conversion CO gas was evaluated in both materials on the results shaved that the firm conversion was loves for the material LaNi0,3Co0,7O3-d

Barium strontium titanate powders prepared by spray pyrolysis

Ultasonic spray pyrolysis (SP) has been investigated for the production of the barium strontium titanate (BST) powders from the polymeric precursors. The processing parameters, such as flux of aerosol and temperature profile inside the furnace, were optimized to obtain single phase BST. The powders were characterized by the methods of X-ray diffraction analysis, SEM, EDS and TEM. The obtained powders were submicronic, consisting of spherical, polycrystalline particles, with internal nanocrystalline structure. Crystallite size of 10 nut, calculated using Rietveld refinement, is in a good agreement with results of HRTEM. (c) 2005 Elsevier B.V. All rights reserved.

X-ray diffraction and mossbauer spectra of nickel ferrite prepared by combustion reaction

Nickel ferrite powders with a nominal NiFe2O4 composition were synthesized by combustion reaction using urea as fuel. The powder was obtained using a vitreous silica basin heated directly on a hot plate at 480 degrees C until self-ignition occurred. After combustion, the powder was calcined at 700 degrees C for 2 h. The formation of the spinel phase and the distribution of cations in the tetrahedral and octahedral sites of the crystal structure were investigated by the Rietveld method, using synchrotron X-ray diffraction data and Mossbauer spectroscopy. The material presented a crystallite size of 120 nm and magnetic properties. The resulting stoichiometry after the Rietveld refinement was (Fe-0.989(2) Ni-0.011(2)) [Fe-1.012(2) Ni-0.989(2)] O-4.

Rietveld analysis of mechanically activated BaCO(3)-TiO(2) system

BaTiO(3) powders were prepared through mechanical activation chemistry and analyzed by Rietveld refinement with X-ray diffraction data. Raw BaCO(3) and TiO(2) powders were dry milled for 5 and 20 h and then calcinated for 2 and 4 h at 800 degrees C. The milling process was found to have broken up the BaCO(3) and TiO(2) crystals into smaller crystals and formed only small amounts ( 1.5 wt%) of BaTiO(3). Subsequence calcinations for 2 and 4 h at 800 degrees C successfully produced large amounts (>97.7 wt%) of BaTiO(3) crystals. The calcination process also generated microstrains and crystallite-size anisotropy in BaTiO(3). An increase in the calcination time from 2 to 4 h increased the BaTiO(3) weight percentage and the crystal lite-shape anisotropy, but decreased the tetragonal distortion anisotropic microstrains in BaTiO(3) crystals. (C) 2008 International Centre for Diffraction Data.

Influência do método de síntese na obtenção de pós de Na2TiSiO5

Este trabalho apresenta um estudo sistemático sobre a síntese e caracterização de pós de Na2TiSiO5. Foram estudadas as propriedades estruturais e morfológicas dos pós por intermédio de difração de raios X, espectroscopia Raman e microscopia eletrônica de varredura. As amostras foram produzidas por meio de duas rotas sintéticas distintas baseadas em métodos tipo Pechini e submetidas a diferentes tratamentos térmicos. Medidas de espectroscopia Raman nas resinas poliméricas foram feitas visando verificar a influência das diferentes rotas utilizadas na síntese dos pós. Com os dados de difração de raios X foi feito um estudo da evolução das fases cristalográficas. A estrutura cristalina das amostras foi analisada por meio de refinamento Rietveld. Por fim, a morfologia dos compostos de Na2TiSiO5 foi examinada por microscopia eletrônica de varredura. Os resultados obtidos mostraram que é possível melhorar a qualidade das amostras de Na2TiSiO5 alterando-se a rota sintética utlizada.

Correlation of reactivity with structural factors in a series of Fe(II) substituted cobalt ferrites

A series of powdered cobalt ferrites, CoxFe3-xO4 with 0.66 <= x< 1.00 containing different amounts of Fe-II, were synthesized by a mild procedure, and their Fe and Co site occupancies and structural characteristics were explored using X-ray anomalous scattering and the Rietveld refinement method. The dissolution kinetics, measured in 0.1 M oxalic acid aqueous solution at 70 degrees C, indicate in all cases the operation of a contracting volume rate law. The specific rates increased with the Fell content following approximately a second-order polynomial expression. This result suggests that the transfer of Fe-III controls the dissolution rate, and that the leaching of a first layer of ions Co-II and Fe-II leaves exposed a surface enriched in slower dissolving octahedral Fe-III ions. Within this model, inner vicinal lattice Fe-II accelerates the rate of Fe-III transfer via internal electron hopping. A chain mechanism, involving successive electron transfers, fits the data very well. (C) 2006 Elsevier B.V. All rights reserved.

Characterization of ZnO-degraded varistors used in high-tension devices

The effects of the degradation process on the structural, microstructural and electrical properties of ZnO-based varistors were analyzed. Rietveld refinement showed that the BiO2-x phase is affected by the degradation process. Besides the changes in the spinel phase, the degradation process also affects the lattice microstrain in the ZnO phase. Scanning electron microscopy analysis showed electrode-melting failure, while wavelength dispersive X-ray spectroscopy qualitative analysis showed deficiency of oxygen species at the grain boundaries in the degraded samples. Atomic force microscopy using electrostatic mode force illustrated a decrease in the charge density at the grain boundaries of the degraded sample. Transmission electron microscopy showed submicrometric spinel grains embedded in a ZnO matrix, but their average grain size is smaller in the degraded sample than in the standard one. Long pulses appeared to be more harmful for the varistors' properties than short ones, causing higher leakage current values. The electrical characteristics of the degraded sample are partially restored after heat treatment in an oxygen-rich atmosphere. (C) 2006 Elsevier Ltd. All rights reserved.

Composition and electronic structure of Zn7-xMxSb2O12 (M = Ni and Co) spinel compounds

The relation between the composition and electronic structure of the perfectly inverse spinel compound Zn7-xMxSb2O12 (M = Ni and Co) has been studied by powder X-ray diffraction and X-ray photoelectron spectroscopy. Changes in the site occupancy are associated with shifts in the core levels as observed in the core level spectral analyses. The configuration of the density of states in the valence band due to the Co and Ni states can be observed in the valence band spectra. (C) 2004 Elsevier B.V. All rights reserved.

Low-temperature synthesis of single-phase Co7Sb2O12

Polycrystalline Co7Sb2O12 compounds have been synthesized by a chemical route, which is based on a modified polymeric precursor method. In order to study the physical properties of the samples, X-ray diffraction (XRD), thermal analyses (TG and DSC), infrared spectroscopy (IR), specific surface area (BET), and magnetization measurements were performed on these materials. Characterization through XRD revealed that the samples are single-phase after a heat-treatment at 1100degreesC for 2h, while the X-ray patterns of the samples heat-treated at lower temperatures revealed the presence of additional Bragg reflections belonging to the Co6Sb2O6 phase. These data were analyzed by means of Rietveld refinement and further analyze showed that Co7Sb2O12 displays an inverse spinel crystalline structure. In this structure, the Co2+ ions occupy the eight tetrahedral positions, and the sixteen octahedral positions are randomly occupied by the Sb5+ and Co2+ ions. IR studies disclosed two strong absorption bands, v(1) and v(2), in the expected spectral range for a spinel-type binary oxide with space group Fd3m. Exploratory studies concerning the magnetic properties indicated that this sample presents a spin-glass transition at T-f similar to 64 K. (C) 2004 Elsevier B.V. All rights reserved.

Structural Refinement and Photoluminescence Properties of MnWO4 Nanorods Obtained by Microwave-Hydrothermal Synthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis, structural refinement and optical behavior of CaTiO3 powders: A comparative study of processing in different furnaces

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Structural refinement and photoluminescence properties of irregular cube-like (Ca-1_Cu-x(x))TiO3 microcrystals synthesized by the microwave-hydrothermal method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)