Production and characterization of Tm3+/Yb3+ codoped waveguides based on PbO-GeO2 thin films

Fabrication and optical characterization of Tm3+/Yb3+ codoped PbO-GeO2 (PGO) pedestal-type waveguides are investigated in this work. It is important to mention that, to the best of authors' knowledge, the use of PGO pedestal-type waveguide has not been studied before. PGO thin films codoped with Tm3+ and Yb3+ were obtained through RF magnetron sputtering technique. The pedestal profile was obtained using conventional optical lithography procedures, followed by plasma etching and sputtering deposition. The profile of Tm3+/Yb3+ codoped PGO waveguides was observed by means of Scanning Electron Microscopy (SEM) measurements. Also the infrared and infrared-to-visible frequency upconversion luminescences of Tm3+ ions were measured exciting the samples with a cw 980 nm diode laser. Propagation losses around 11 dB/cm and 9 dB/cm were obtained at 630 and 1050 nm, respectively, for waveguides in the 20-100 μm width range. Single-mode propagation was observed for waveguides width up to 12 μm and 7 μm, at 1050 nm and 630 nm, respectively; larger waveguides width provided multi-mode propagation. The present results corroborate the possibility of using Tm3+/Yb3+ codoped PGO thin films as active waveguide for photonic applications. © 2013 Elsevier B.V. All rights reserved.

Laser stimulated light reflection for TeO2-WO 3-Bi2O3 thin films with incorporated Si nanoparticles

A novel method of preparation of the Si nanoparticles (NPs) incorporated in tellurite TeO2-WO3-Bi2O3 (TWB) thin films is proposed. This mew method applies RF magnetron sputtering technique at room temperature. The incorporation of Si NP was confirmed by transmission electron microscopy (TEM); isolated Si NPs with diameters of around 6 nm are observed. Energy dispersive X-ray spectroscopy (EDS) was performed during TEM analysis in order to confirm the presence of Si NP and also the other elements of the thin film. The thin films are explored with respect to the photoinduced changes of the reflectivity within the 400-65 nm spectra range using a 10 ns pulsed Nd:YAG with power densities varying up to 400 MW/cm2 and beam diameter within the 3-5 mm range. The observed processes are analyzed within a framework of trapping level conceptions for the Si NP. The possible application of the discovered materials as optical sensitive sensors is proposed. © 2013 Elsevier B.V.

Síntese e caracterização de filmes finos de óxido de zinco

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito do tratamento a plasma do politetrafluoroetileno (PTFE) nas suas propriedades eletrostáticas e superficiais

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Electrical and Mechanical Properties of Post-annealed SiC(x)N(y) Films

Amorphous SiC(x)N(y) films have been deposited on (100) Si substrates by RF magnetron sputtering of a SiC target in a variable nitrogen-argon atmosphere. The as-deposited films were submitted to thermal anneling in a furnace under argon atmosphere at 1000 degrees C for 1 hour. Composition and structure of unannealed and annealed samples were investigated by RBS and FTIR. To study the electrical characteristics of SiC(x)N(y) films, Metal-insulator-semiconductor (MIS) structures were fabricated. Elastic modulus and hardness of the films were determined by nanoindentation. The results of these studies showed that nitrogen content and thermal annealing affect the electrical, mechanical and structural properties of SiC(x)N(y) films.

Investigação das propriedades ópticas de ZnO e ZnO:Al

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Investigation into the impact of grain boundaries, film interface, and crystallographic orientation on the ionic conductivity of thin film gadolinium-doped ceria

The research reported in this dissertation investigates the impact of grain boundaries, film interface, and crystallographic orientation on the ionic conductivity of thin film Gd-doped CeO2 (GDC). Chapter 2 of this work addresses claims in the literature that submicron grain boundaries have the potential to dramatically increase the ionic conductivity of GDC films. Unambiguous testing of this claim requires directly comparing the ionic conductivity of single-crystal GDC films to films that are identical except for the presence of submicron grain boundaries. In this work techniques have been developed to grow GDC films by RF magnetron sputtering from a GDC target on single crystal r plane sapphire substrates. These techniques allow the growth of films that are single crystals or polycrystalline with 80 nm diameter grains. The ionic conductivities of these films have been measured and the data shows that the ionic conductivity of single crystal GDC is greater than that of the polycrystalline films by more than a factor of 4 over the 400-700°C temperature range. Chapter 3 of this work investigates the ionic conductivity of surface and interface regions of thin film Gd-doped CeO2. In this study, single crystal GDC films have been grown to thicknesses varying from 20 to 500 nm and their conductivities have been measured in the 500-700°C temperature range. Decreasing conductivity with decreasing film thickness was observed. Analysis of the conductivity data is consistent with the presence of an approximately 50 nm layer of less conductive material in every film. This study concludes that the surface and interface regions of thin film GDC are less conductive than the bulk single crystal regions, rather than being highly conductive paths. Chapter 4 of this work investigates the ionic conductivity of thin film Gd-doped CeO2 (GDC) as a function of crystallographic orientation. A theoretical expression has been developed for the ionic conductivity of the [100] and [110] directions in single crystal GDC. This relationship is compared to experimental data collected from a single crystal GDC film. The film was grown to a thickness of _300 nm and its conductivity measured along the [100] and [110] orientations in the 500-700°C temperature range. The experimental data shows no statistically significant difference in the conductivities of the [100] and [110] directions in single crystal GDC. This result agrees with the theoretical model which predicts no difference between the conductivities of the two directions.

Electrical resistivity change in amorphous Ta42Si13N45 films by stress relaxation

In a first experiment, a reactively sputtered amorphous Ta₄₂Si₁₃N₄₅ film about 260 nm thick deposited on a flat and smooth alumina substrate was thermally annealed in air for 30 min and let cooled again repeatedly at successively higher temperatures from 200 to 500 °C. This treatment successively and irreversibly increases the room temperature resistivity of the film monotonically from its initial value of 670 μΩ cm to a maximum of 705 μΩ cm (+5.2 %). Subsequent heat treatments at temperatures below 500 °C and up to 6 h have no further effect on the room temperature resistivity. The new value remains unchanged after 3.8 years of storage at room temperature. In a second experiment, the evolution of the initially compressive stress of a film similarly deposited by reactive sputtering on a 2-inch silicon wafer was measured by tracking the wafer curvature during similar thermal annealing cycles. A similar pattern of irreversible and reversible changes of stress was observed as for the film resistivity. Transmission electron micrographs and secondary ion mass profiles of the film taken before and after thermal annealing in air establish that both the structure and the composition of the film scarcely change during the annealing cycles. We reason that the film stress is implicated in the resistivity change. In particular, to interpret the observations, a model is proposed where the interface between the film and the substrate is mechanically unyielding.

Characterization of HFO2 Capacitors

Hafnium oxide (HfOn) is a promising dielectric for future microelectronic applications. Hf02 thin films (10-75nm) were deposited on Pt/Si02/Si substrates by pulsed DC magnetron reactive sputtering. Top electrodes of Pt were formed by e-beam evapo- ration through an aperture mask on the samples to create MIM (Metal-Insulator-Metal) capacitors. Various processing conditions (Arloz ratio, DC power and deposition rate) and post-deposition annealing conditions (time and temperature) were investigated. The structure of the Hf02 films was characterized by X-ray diffraction (XRD) and the roughness was measured by a profilometer. The electrical properties were characterized in terms of their relative permittivity (E,(T) and ~,.(f)) and leakage behavior (I-V, I-T and I- time). The electrical measurements were performed over a temperature range from -5 to 200°C. For the samples with best experimental results, the relative permittivity of HfOa was found to be -- 27 after anneal and increased by 0.027%/"C with increasing temperature over the measured temperature range. At 25"C, leakage current density was below lop8 ~ l c m ' at 1 volt. The leakage current increased with temperature above a specific threshold temperature below which the leakage current didn't change much. The leakage current increased with voltage. At voltages below lvolt, it's ohmic; at higher voltages, it follows Schottky model. The breakdown field is - 1 . 8 2 ~ lo6 Vlcm. The optical bandgap was measured with samples deposited on quartz substrates to be 5.4eV after anneal.

Sputter optimization of AlN on diamond substrates for high frequency SAW resonators

The AlN/diamond structure is an attractive combination for SAW devices and its application at high frequencies. In this work, the synthesis of AlN thin films by reactive sputtering has been optimized on diamond substrates in order to process high frequency devices. Polished microcrystalline and as-grown nanocrystalline diamond substrates have been used to deposit AlN of different thickness under equal sputtering conditions. For the smoother substrates, the FWHM of the rocking curve of the (002) AlN peak varies from 3.8° to 2.7° with increasing power. SAW one port resonators have been fabricated on these films, whose electrical characterization (in terms of S11 parameters) is reported.

Ta2O5/SiO2 insulating acoustic mirrors for AlN-based X-band BAW resonators

This work describes the performance of AlN-based bulk acoustic wave resonators built on top of insulating acoustic reflectors and operating at around 8 GHz. The acoustic reflectors are composed of alternate layers of amorphous Ta2O5and SiO2 deposited at room temperature by pulsed-DC reactive sputtering in Ar/O2 atmospheres. SiO2 layers have a porous structure that provides a low acoustic impedance of only 9.5 MRayl. Ta2O5 films exhibit an acoustic impedance of around 39.5 MRayl that was assessed by the picoseconds acoustic technique These values allow to design acoustic mirrors with transmission coefficients in the centre of the band lower than -40 dB (99.998 % of reflectance) with only seven layers. The resonators were fabricated by depositing a very thin AlN film onto an iridium bottom electrode 180 nm-thick and by using Ir or Mo layers as top electrode. Resonators with effective electromechanical coupling factors of 5.7% and quality factors at the antiresonant frequency around 600 are achieved.

Growth of AlN oriented films on insulating substrates.

This work describes the structural and piezoelectric assessment of aluminum nitride (AlN) thin films deposited by pulsed-DC reactive sputtering on insulating substrates. We investigate the effect of different insulating seed layers on AlN properties (crystallinity, residual stress and piezoelectric activity). The seed layers investigated, silicon nitride (Si3N4), silicon dioxide (SiO2), amorphous tantalum oxide (Ta2O5), and amorphous or nano-crystalline titanium oxide (TiO2) are deposited on glass plates to a thickness lower than 100 nm. Before AlN films deposition, their surface is pre-treated with a soft ionic cleaning, either with argon or nitrogen ions. Only AlN films grown of TiO2 seed layers exhibit a significant piezoelectric activity to be used in acoustic device applications. Pure c-axis oriented films, with FWHM of rocking curve of 6º, stress below 500 MPa, and electromechanical coupling factors measured in SAW devices of 1.25% are obtained. The best AlN films are achieved on amorphous TiO2 seed layers deposited at high target power and low sputtering pressure. On the other hand, AlN films deposited on Si3N4, SiO2 and TaOx exhibit a mixed orientation, high stress and very low piezoelectric activity, which invalidate their use in acoustic devices.

Ultra high frequency thin film saw devices

Durante los últimos años el flujo de datos en la transmisión que tiene lugar en los sistemas de comunicación ha aumentado considerablemente de forma que día a día se requieren más aplicaciones trabajando en un rango de frecuencias muy alto (3-30 GHz). Muchos de estos sistemas de comunicación incluyen dispositivos de onda acústica superficial (SAW) y por tanto se hace necesario el aumento de frecuencia a la que éstos trabajan. Pero este incremento de frecuencia de los dispositivos SAW no sólo es utilizado en los sistemas de comunicación, varios tipos de sensores, por ejemplo, aumentan su sensibilidad cuando la frecuencia a la que trabajan también lo hace. Tradicionalmente los dispositivos SAW se han fabricado sobre cuarzo, LiNbO3 y LiTaO3 principalmente. Sin embargo la principal limitación de estos materiales es su velocidad SAW. Además, debido a la alta temperatura a la que se depositan no pueden ser integrados en la tecnología de fabricación CMOS. El uso de la tecnología de capa delgada, en la que un material piezoeléctrico es depositado sobre un substrato, se está utilizando en las últimas décadas para incrementar la velocidad SAW de la estructura y poder obtener dispositivos trabajando en el rango de frecuencias requerido en la actualidad. Por otra parte, esta tecnología podría ser integrada en el proceso de fabricación CMOS. Durante esta tesis nos hemos centrado en la fabricación de dispositivos SAW trabajando a muy alta frecuencia. Para ello, utilizando la tecnología de capa delgada, hemos utilizado la estructura nitruro de aluminio (AlN) sobre diamante que permite conseguir velocidades SAW del sustrato que no se pueden alcanzar con otros materiales. El depósito de AlN se realizó mediante sputtering reactivo. Durante esta tesis se han realizado diferentes experimentos para optimizar dicho depósito de forma que se han obtenido los parámetros óptimos para los cuales se pueden obtener capas de AlN de alta calidad sobre cualquier tipo de sustrato. Además todo el proceso se realizó a baja temperatura para que el procesado de estos dispositivos pueda ser compatible con la tecnología CMOS. Una vez optimizada la estructura AlN/diamante, mediante litografía por haz de electrones se fabricaron resonadores SAW de tamaño nanométrico que sumado a la alta velocidad resultante de la combinación AlN/diamante nos ha permitido obtener dispositivos trabajando en el rango de 10-28 GHz con un alto factor de calidad y rechazo fuera de la banda. Estás frecuencias y prestaciones no han sido alcanzadas por el momento en resonadores de este tipo. Por otra parte, se han utilizado estos dispositivos para fabricar sensores de presión de alta sensibilidad. Estos dispositivos son afectados altamente por los cambios de temperatura. Se realizó también un exhaustivo estudio de cómo se comportan en temperatura estos resonadores, entre -250ºC y 250ºC (rango de temperaturas no estudiado hasta el momento) diferenciándose dos regiones una a muy baja temperatura en la que el dispositivo muestra un coeficiente de retraso en frecuencia (TCF) relativamente bajo y otra a partir de los -100ºC en la que el TCF es similar al observado en la bibliografía. Por tanto, durante esta tesis se ha optimizado el depósito de AlN sobre diamante para que sea compatible con la tecnología CMOS y permita el procesado de dispositivos trabajando a muy alta frecuencia con altas prestaciones para comunicaciones y sensores. ABSTRACT The increasing volume of information in data transmission systems results in a growing demand of applications working in the super-high-frequency band (3–30 GHz). Most of these systems work with surface acoustic wave (SAW) devices and thus there is a necessity of increasing their resonance frequency. Moreover, sensor application includes this kind of devices. The sensitivity of them is proportional with its frequency. Traditionally, quartz, LiNbO3 and LiTaO3 have been used in the fabrication of SAW devices. These materials suffer from a variety of limitations and in particular they have low SAW velocity as well as being incompatible with the CMOS technology. In order to overcome these problems, thin film technology, where a piezoelectric material is deposited on top of a substrate, has been used during the last decades. The piezoelectric/substrate structure allows to reach the frequencies required nowadays and could be compatible with the mass electronic production CMOS technology. This thesis work focuses on the fabrication of SAW devices working in the super-high-frequency range. Thin film technology has been used in order to get it, especially aluminum nitride (AlN) deposited by reactive sputtering on diamond has been used to increase the SAW velocity. Different experiments were carried out to optimize the parameters for the deposit of high quality AlN on any kind of substrates. In addition, the system was optimized under low temperature and thus this process is CMOS compatible. Once the AlN/diamond was optimized, thanks to the used e-beam lithography, nanometric SAW resonators were fabricated. The combination of the structure and the size of the devices allow the fabrication of devices working in the range of 10-28 GHz with a high quality factor and out of band rejection. These high performances and frequencies have not been reached so far for this kind of devices. Moreover, these devices have been used as high sensitivity pressure sensors. They are affected by temperature changes and thus a wide temperature range (-250ºC to 250ºC) study was done. From this study two regions were observed. At very low temperature, the temperature coefficient of frequency (TCF) is low. From -100ºC upwards the TCF is similar to the one appearing in the literature. Therefore, during this thesis work, the sputtering of AlN on diamond substrates was optimized for the CMOS compatible fabrication of high frequency and high performance SAW devices for communication and sensor application.

Optimization of AlN thin layers on diamond substrates for high frequency SAW resonators

AlN/diamond heterostructures are very promising for high frequency surface acoustic wave (SAW) resonators. In their design, the thickness of the piezoelectric film is one of the key parameters. On the other hand, the film material quality and, hence, the device performance, also depend on that thickness. In this work, polished microcrystalline diamond substrates have been used to deposit AlN films by reactive sputtering, from 150 nm up to 3 μm thick. A high degree of the c-axis orientation has been obtained in all cases. SAW one port resonators at high frequency have been fabricated on these films with a proper combination of the film thickness and transducer size.

TEM study of the AlN grain orientation grown on NCD diamond substrate

Piezoelectric AlN layer grain orientation, grown by room temperature reactive sputtering, is analyzed by transmission electron microscopy (TEM).Two types of samples are studied: (i) AlN grown on well-polished NCD (nano-crystalline diamond) diamond, (ii) AlN grown on an up-side down NCD layer previously grown on a Si substrate, i.e. diamond surface as smooth as that of Si substrates. The second set of sample show a faster lignment of their AlN grain caxis attributed to it smoother diamond free surface. No grain orientation relationship between diamond substrate grain and the AlN ones is evidenced, which seems to indicate the preponderance role of the surface substrate state.