In vitro mechanical fatigue behavior of poly-ε-caprolactone macroporous scaffolds for cartilage tissue engineering: Influence of pore filling by a poly(vinyl alcohol) gel

Polymeric scaffolds used in regenerative therapies are implanted in the damaged tissue and subjected to repeated loading cycles. In the case of articular cartilage engineering, an implanted scaffold is typically subjected to long term dynamic compression. The evolution of the mechanical properties of the scaffold during bioresorption has been deeply studied in the past, but the possibility of failure due to mechanical fatigue has not been properly addressed. Nevertheless, the macroporous scaffold is susceptible to failure after repeated loading-unloading cycles. In this work fatigue studies of polycaprolactone scaffolds were carried by subjecting the scaffold to repeated compression cycles in conditions simulating the scaffold implanted in the articular cartilage. The behaviour of the polycaprolactone sponge with the pores filled with a poly(vinyl alcohol) gel simulating the new formed tissue within the pores was compared with that of the material immersed in water. Results were analyzed with Morrow’s criteria for failure and accurate fittings are obtained just up to 200 loading cycles. It is also shown that the presence of poly(vinyl alcohol) increases the elastic modulus of the scaffolds, the effect being more pronounced with increasing the number of freeze/thawing cycles.

Erratum: Influence of oxygen plasma treatment parameters on poly(vinylidene fluoride) electrospun fiber mats wettability

Electrospun poly(vinylidene fluoride) (PVDF) fiber mats find applications in an increasing number of areas, such as battery separators, filtration and detection membranes, due to their excellent properties. However, there are limitations due to the hydrophobic nature and low surface energy of PVDF. In this work, oxygen plasma treatment has been applied in order to modify the surface wettability of PVDF fiber mats and superhydrophilic PVDF electrospun membranes have been obtained. Further, plasma treatment does not significantly influences fiber average size (~400 ± 200 nm), morphology, electroactive -phase content (~80-85%) or the degree of crystallinity (Xc of 42 ± 2%), allowing to maintain the excellent physical-chemical characteristics of PVDF. Plasma treatment mainly induces surface chemistry modifications, such as the introduction of oxygen and release of fluorine atoms that significantly changes polymer membrane wettability by a reduction of the contact angle of the polymer fibers and an overall decrease of the surface tension of the membranes.

Development of a poly(L-Lactic acid) based drug release system

Dissertação de mestrado em Biofísica e Bionanossistemas

Disease-causing mutations improving the branch site and polypyrimidine tract: pseudoexon activation of LINE-2 and antisense Alu lacking the poly(T)-tail.

Cryptic exons or pseudoexons are typically activated by point mutations that create GT or AG dinucleotides of new 5' or 3' splice sites in introns, often in repetitive elements. Here we describe two cases of tetrahydrobiopterin deficiency caused by mutations improving the branch point sequence and polypyrimidine tracts of repeat-containing pseudoexons in the PTS gene. In the first case, we demonstrate a novel pathway of antisense Alu exonization, resulting from an intronic deletion that removed the poly(T)-tail of antisense AluSq. The deletion brought a favorable branch point sequence within proximity of the pseudoexon 3' splice site and removed an upstream AG dinucleotide required for the 3' splice site repression on normal alleles. New Alu exons can thus arise in the absence of poly(T)-tails that facilitated inclusion of most transposed elements in mRNAs by serving as polypyrimidine tracts, highlighting extraordinary flexibility of Alu repeats in shaping intron-exon structure. In the other case, a PTS pseudoexon was activated by an A>T substitution 9 nt upstream of its 3' splice site in a LINE-2 sequence, providing the first example of a disease-causing exonization of the most ancient interspersed repeat. These observations expand the spectrum of mutational mechanisms that introduce repetitive sequences in mature transcripts and illustrate the importance of intronic mutations in alternative splicing and phenotypic variability of hereditary disorders.

Involvement of the RNA-binding protein ARE/poly(U)-binding factor 1 (AUF1) in the cytotoxic effects of proinflammatory cytokines on pancreatic beta cells.

AIMS/HYPOTHESIS: Chronic exposure of pancreatic beta cells to proinflammatory cytokines leads to impaired insulin secretion and apoptosis. ARE/poly(U)-binding factor 1 (AUF1) belongs to a protein family that controls mRNA stability and translation by associating with adenosine- and uridine-rich regions of target messengers. We investigated the involvement of AUF1 in cytokine-induced beta cell dysfunction. METHODS: Production and subcellular distribution of AUF1 isoforms were analysed by western blotting. To test for their role in the control of beta cell functions, each isoform was overproduced individually in insulin-secreting cells. The contribution to cytokine-mediated beta cell dysfunction was evaluated by preventing the production of AUF1 isoforms by RNA interference. The effect of AUF1 on the production of potential targets was assessed by western blotting. RESULTS: MIN6 cells and human pancreatic islets were found to produce four AUF1 isoforms (p42>p45>p37>p40). AUF1 isoforms were mainly localised in the nucleus but were partially translocated to the cytoplasm upon exposure of beta cells to cytokines and activation of the ERK pathway. Overproduction of AUF1 did not affect glucose-induced insulin secretion but promoted apoptosis. This effect was associated with a decrease in the production of the anti-apoptotic proteins, B cell leukaemia/lymphoma 2 (BCL2) and myeloid cell leukaemia sequence 1 (MCL1). Silencing of AUF1 isoforms restored the levels of the anti-apoptotic proteins, attenuated the activation of the nuclear factor-κB (NFκB) pathway, and protected the beta cells from cytokine-induced apoptosis. CONCLUSIONS/INTERPRETATION: Our findings point to a contribution of AUF1 to the deleterious effects of cytokines on beta cell functions and suggest a role for this RNA-binding protein in the early phases of type 1 diabetes.

A viscous bioerodible poly(ortho ester) as a new biomaterial for intraocular application.

The biocompatibility of a viscous, hydrophobic, bioerodible poly(ortho ester) (POE) intended for intraocular application was investigated. POE was evaluated as a blank carrier and as containing modulators of degradation. Each formulation was injected intracamerally and intravitreally in rabbit eyes, and clinical and histological examinations were performed postoperatively for 2 weeks. In the case of intracameral injections, polymer biocompatibility appeared to depend on the amount injected in the anterior chamber. When 50 microL was administered, the polymer degraded within 2 weeks, and clinical observations showed good biocompatibility of POE with no toxicity to the ocular tissues or increase in intraocular pressure. The injection of a larger volume, 100 microL, of POE, appeared inappropriate because of direct contact of polymeric material with the corneal endothelium, and triggered reversible edema and inflammation in the anterior chamber of the eye that regressed after a few days. After intravitreal administration, POE was well tolerated and no inflammatory reaction developed during the observation period. The polymer degraded slowly, appearing as a round whitish bubble in the vitreous cavity. The presence of modulators of degradation both improved POE biocompatibility and prolonged polymer lifetime in the eye. POE appears to be a promising biomaterial for clinical intraocular application.

Ocular biocompatibility of a poly(ortho ester) characterized by autocatalyzed degradation.

The biocompatibility of autocatalyzed poly(ortho ester) (POE(70)LA(30)), a viscous, hydrophobic, bioerodible polymer, was investigated. POE(70)LA(30) was synthesized, sterilized by gamma irradiation, and injected in rabbit eyes at adequate volumes through subconjunctival, intracameral, intravitreal, and suprachoroidal routes. Clinical examinations were performed postoperatively at regular time points for 6 mo, and histopathologic analysis was carried out to confirm tissular biocompatibility. After subconjunctival injection, the polymer was well tolerated and persisted in the subconjunctival space for about 5 weeks. In the case of intracameral injections, polymer biocompatibility was good; the POE(70)LA(30) bubble was still present in the anterior chamber for up to 6 mo after injection. No major histopathologic anomalies were detected, with the exception of a localized Descemet membrane thickening. After intravitreal administration, POE(70)LA(30) biocompatibility was excellent, and no inflammatory reaction could be detected during the observation period. The polymer was degraded in approximately 3 mo. Suprachoroidal injections of POE(70)LA(30) were reproducible and well tolerated. POE(70)LA(30) triggered a slight elevation of the retina and choroid upon clinical observation. The polymer was detectable in the suprachoroidal space for about 6 mo. No inflammatory reaction and no major retinal anomalies could be detected by histology. In conclusion, POE(70)LA(30) appears to be a promising biomaterial for intraocular application, potentially providing sustained drug delivery over an extended period of time, with a good tolerance.

Convenient synthesis of heterobifunctional poly(ethylene glycol) suitable for the functionalization of iron oxide nanoparticles for biomedical applications.

A straightforward route is proposed for the multi-gram scale synthesis of heterobifunctional poly(ethylene glycol) (PEG) oligomers containing combination of triethyloxysilane extremity for surface modification of metal oxides and amino or azido active end groups for further functionalization. The suitability of these PEG derivatives to be conjugated to nanomaterials was shown by pegylation of ultrasmall superparamagnetic iron oxide (USPIO) nanoparticles (NPs), followed by functionalization with small peptide ligands for biomedical applications.

Enhanced antitumor activity of doxorubicin in breast cancer through the use of poly(butylcyanoacrylate) nanoparticles.

The use of doxorubicin (DOX), one of the most effective antitumor molecules in the treatment of metastatic breast cancer, is limited by its low tumor selectivity and its severe side effects. Colloidal carriers based on biodegradable poly(butylcyanoacrylate) nanoparticles (PBCA NPs) may enhance DOX antitumor activity against breast cancer cells, thus allowing a reduction of the effective dose required for antitumor activity and consequently the level of associated toxicity. DOX loading onto PBCA NPs was investigated in this work via both drug entrapment and surface adsorption. Cytotoxicity assays with DOX-loaded NPs were performed in vitro using breast tumor cell lines (MCF-7 human and E0771 mouse cancer cells), and in vivo evaluating antitumor activity in immunocompetent C57BL/6 mice. The entrapment method yielded greater drug loading values and a controlled drug release profile. Neither in vitro nor in vivo cytotoxicity was observed for blank NPs. The 50% inhibitory concentration (IC50) of DOX-loaded PBCA NPs was significantly lower for MCF-7 and E0771 cancer cells (4 and 15 times, respectively) compared with free DOX. Furthermore, DOX-loaded PBCA NPs produced a tumor growth inhibition that was 40% greater than that observed with free DOX, thus reducing DOX toxicity during treatment. These results suggest that DOX-loaded PBCA NPs have great potential for improving the efficacy of DOX therapy against advanced breast cancers.

Poly-N-Acetyl Glucosamine Fibers Induce Angiogenesis in ADP Inhibitor-Treated Diabetic Mice

Background: It has been previously demonstrated that short-fiber poly-N-acetyl-glucosamine (sNAG) nanofibers specifically interact with platelets, are hemostatic, and stimulate diabetic wound healing by activating angiogenesis, cell proliferation, and reepithelialization. Platelets play a significant physiologic role in wound healing. The influence of altered platelet function by treatment with the ADP inhibitor Clopidogrel (CL) on wound healing and the ability of sNAG to repair wounds in diabetic mice treated with CL were studied.Methods: Dorsal 1 cm2 skin wounds were excised on genetically diabetic 8-week to 12-week-old, Lep/r-db/db male mice, and wound healing kinetics were determined. Microscopic analysis was performed for angiogenesis (PECAM-1) and cell proliferation (Ki67). Mice were either treated with CL (P2Y12 ADP receptor antagonist, CL) or saline solution (NT). CL wounds were also treated with either a single application of topical sNAG (CL-sNAG) or were left untreated (CL-NT).Results: CL treatment did not alter wound healing kinetics, while sNAG induced faster wound closure in CL-treated mice compared with controls. CL treatment of diabetic mice caused an augmentation of cell proliferation and reduced angiogenesis compared with nontreated wounds. However, sNAG reversed the effects of CL on angiogenesis and partially reversed the effect on cell proliferation in the wound beds. The sNAG-treated wounds in CL-treated mice showed higher levels of cell proliferation and not did inhibit angiogenesis.Conclusions: CL treatment of diabetic mice decreased angiogenesis and increased cell proliferation in wounds but did not influence macroscopic wound healing kinetics. sNAG treatment did not inhibit angiogenesis in CL-treated mice and induced faster wound closure; sNAG technology is a promising strategy to facilitate the healing of complex bleeding wounds in CL-treated diabetic patients.

Poly-N-acetyl glucosamine fibers are synergistic with vacuum-assisted closure in augmenting the healing response of diabetic mice.

BACKGROUND: Vacuum-assisted closure (VAC) has become the preferred modality to treat many complex wounds but could be further improved by methods that minimize bleeding and facilitate wound epithelialization. Short fiber poly-N-acetyl glucosamine nanofibers (sNAG) are effective hemostatic agents that activate platelets and facilitate wound epithelialization. We hypothesized that sNAG used in combination with the VAC device could be synergistic in promoting wound healing while minimizing the risk of bleeding. METHODS: Membranes consisting entirely of sNAG nanofibers were applied immediately to dorsal excisional wounds of db/db mice followed by application of the VAC device. Wound healing kinetics, angiogenesis, and wound-related growth factor expression were measured. RESULTS: The application of sNAG membranes to wounds 24 hours before application of the VAC device was associated with a significant activation of wounds (expression of PDGF, TGFβ, EGF), superior granulation tissue formation rich in Collagen I as well as superior wound epithelialization (8.6% ± 0.3% vs. 1.8% ± 1.1% of initial wound size) and wound contraction. CONCLUSIONS: The application of sNAG fiber-containing membranes before the application of the polyurethane foam interface of VAC devices leads to superior healing in db/db mice and represents a promising wound healing adjunct that can also reduce the risk of bleeding complications.

Controlled delivery of 5-chlorouracil using poly(ortho esters) in filtering surgery for glaucoma.

PURPOSE: To evaluate the antimitotic and toxic effects of 5-chlorouracil (5-CU) and 5-fluorouracil (5-FU) and study their potential to delay filtering bleb closure in the rabbit eye when released by poly(ortho esters) (POE). METHODS: Rabbit Tenon fibroblasts and human conjunctival cells were incubated with various 5-CU and 5-FU concentrations. Antiproliferative effects and toxicity were evaluated at 24 and 72 hours by monotetrazolium, neutral red, and Hoechst tests and cell counting. Mechanisms of cell death were evaluated using TUNEL assay, annexin V binding, immunohistochemistry for anti-apoptosis-inducing factor (AIF) and LEI/L-DNase II. Trabeculectomy was performed in pigmented rabbits. Two hundred microliters of POE loaded with 1% wt/wt 5-FU or 5-CU was injected into the subconjunctival space after surgery. Intraocular pressure (IOP) and bleb persistence were monitored for 150 days. RESULTS: In vitro, 5-FU showed a higher antiproliferative effect and a more toxic effect than 5-CU. 5-FU induced cell necrosis, whereas 5-CU induced mostly apoptosis. The apoptosis induced by 5-CU was driven through a non-caspase-dependent pathway involving AIF and LEI/L-DNase II. In vivo, at 34 days after surgery, the mean IOP in the POE/5-CU-treated group was 83% of the baseline level and only 40% in the POE/5-FU-treated group. At 100 days after surgery, IOP was still decreased in the POE/5-CU group when compared with the controls and still inferior to the preoperative value. The mean long-term IOP, with all time points considered, was significantly (P < 0.0001) decreased in the POE/5-CU-treated group (6.0 +/- 2.4 mm Hg) when compared with both control groups, the trabeculectomy alone group (7.6 +/- 2.9 mm Hg), and the POE alone group (7.5 +/- 2.6 mm Hg). Histologic analysis showed evidence of functioning blebs in the POE-5-CU-treated eyes along with a preserved structure of the conjunctiva epithelium. CONCLUSIONS: The slow release of 5-CU from POE has a longstanding effect on the decrease of IOP after glaucoma-filtering surgery in the rabbit eye. Thus, the slow release of POE/5-CU may be beneficial for the prevention of bleb closure in patients who undergo complicated trabeculectomy.

Surface assembly of poly(I:C) on PEGylated microspheres to shield from adverse interactions with fibroblasts.

By expressing an array of pattern recognition receptors (PRRs), fibroblasts play an important role in stimulating and modulating the response of the innate immune system. The TLR3 ligand polyriboinosinic acid-polyribocytidylic acid, poly(I:C), a mimic of viral dsRNA, is a vaccine adjuvant candidate to activate professional antigen presenting cells (APCs). However, owing to its ligation with extracellular TLR3 on fibroblasts, subcutaneously administered poly(I:C) bears danger towards autoimmunity. It is thus in the interest of its clinical safety to deliver poly(I:C) in such a way that its activation of professional APCs is as efficacious as possible, whereas its interference with non-immune cells such as fibroblasts is controlled or even avoided. Complementary to our previous work with monocyte-derived dendritic cells (MoDCs), here we sought to control the delivery of poly(I:C) surface-assembled on microspheres to human foreskin fibroblasts (HFFs). Negatively charged polystyrene (PS) microspheres were equipped with a poly(ethylene glycol) (PEG) corona through electrostatically driven coatings with a series of polycationic poly(L-lysine)-graft-poly(ethylene glycol) copolymers, PLL-g-PEG, of varying grafting ratios g from 2.2 up to 22.7. Stable surface assembly of poly(I:C) was achieved by incubation of polymer-coated microspheres with aqueous poly(I:C) solutions. Notably, recognition of both surface-assembled and free poly(I:C) by extracellular TLR3 on HFFs halted their phagocytic activity. Ligation of surface-assembled poly(I:C) with extracellular TLR3 on HFFs could be controlled by tuning the grafting ratio g and thus the chain density of the PEG corona. When assembled on PLL-5.7-PEG-coated microspheres, poly(I:C) was blocked from triggering class I MHC molecule expression on HFFs. Secretion of interleukin (IL)-6 by HFFs after exposure to surface-assembled poly(I:C) was distinctly lower as compared to free poly(I:C). Overall, surface assembly of poly(I:C) may have potential to contribute to the clinical safety of this vaccine adjuvant candidate.

A new poly(ortho ester)-based drug delivery system as an adjunct treatment in filtering surgery.

PURPOSE: Pharmacologic modulation of wound healing after glaucoma filtering surgery remains a major clinical challenge in ophthalmology. Poly(ortho ester) (POE) is a bioerodible and biocompatible viscous polymer potentially useful as a sustained drug delivery system that allows the frequency of intraocular injections to be reduced. The purpose of this study was to determine the efficacy of POE containing a precise amount of 5-fluorouracil (5-FU) in an experimental model of filtering surgery in the rabbit. METHODS: Trabeculectomy was performed in pigmented rabbit eyes. An ointmentlike formulation of POE containing 1% wt/wt 5-FU was injected subconjunctivally at the site of surgery, during the procedure. Intraocular pressure (IOP), bleb persistence, and ocular inflammatory reaction were monitored until postoperative day 30. Quantitative analysis of 5-FU was performed in the anterior chamber. Histologic analysis was used to assess the appearance of the filtering fistula and the polymer's biocompatibility. RESULTS: The decrease in IOP from baseline and the persistence of the filtering bleb were significantly more marked in the 5-FU-treated eyes during postoperative days 9 through 28. Corneal toxicity triggered by 5-FU was significantly lower in the group that received 5-FU in POE compared with a 5-FU tamponade. Histopathologic evaluation showed that POE was well tolerated, and no fibrosis occurred in eyes treated with POE containing 5-FU. CONCLUSIONS: In this rabbit model of trabeculectomy, the formulation based on POE and containing a precise amount of 5-FU reduced IOP and prolonged bleb persistence in a way similar to the conventional method of a 5-FU tamponade, while significantly reducing 5-FU toxicity.