Aging kinetics in the Cu-8 wt.% Al alloy with Ag additions

The influence of additions of 2, 4, 6, 8, 10 and 12 wt.% Ag in the isothermal aging kinetics of the Cu-8 wt.% Al alloy was studied using microhardness measurements, differential scanning calorimetry, optical and scanning electron microscopy and X-ray diffractometry. The results indicate that the presence of silver is responsible for the shift of the equilibrium concentration to higher Al contents, allowing the formation of the gamma(1) phase (Al4Cu9) in this alloy. For Ag additions up to 6% the dominant kinetic process is Ag precipitation and for additions from 8 to 12% Ag the nucleation of the perlitic phase dominates. (C) 2003 Elsevier B.V. B.V. All rights reserved.

Effect of Ag additions on the reverse martensitic transformation in the Cu-10 mass% Al alloy

The effect of Ag additions on the reverse martensitic transformation in the Cu-10 mass% Al alloy was studied using differential thermal analysis (DTA), optical (OM) and scanning electron microscopies (SEM) and X-ray diffractometry. The results indicated that Ag additions to the Cu-10 mass% Al alloy shift the equilibrium concentration to higher Al contents, allow to obtain both beta(1)' and beta' martensitic phases in equilibrium and that Ag precipitation is a process associated with the perlitic phase formation.

beta Phase transformations in the Cu-11mass%Al alloy with Ag additions

In the Cu-Al system, due to the sluggishness of the beta a dagger" (alpha + gamma(1)) eutectoid reaction, the beta phase can be retained metastably. During quenching, metastable beta alloys undergo a martensitic transformation to a beta' phase at Al low content. The ordering reaction beta a dagger" beta(1) precedes the martensitic transformation. The influence of Ag additions on the reactions containing the beta phase in the Cu-11mass%Al alloy was studied using differential scanning calorimetry and in situ X-ray diffractometry. The results indicated that, on cooling, two reactions are occurring in the same temperature range, the beta -> (alpha + gamma(1)) decomposition reaction and the beta -> beta(1) reaction, with different reaction mechanisms (diffusive for the former and ordering for the latter) and, consequently, with different reaction rates. For lower cooling rates, the dominant is the decomposition reaction and for higher cooling rates the ordering reaction prevails. on heating, the (alpha + gamma(1)) -> beta reverse eutectoid reaction occurs with a resulting beta phase saturated with alpha. The increase of Ag concentration retards the beta -> (alpha + gamma(1)) decomposition reaction and the beta -> beta(1) ordering reaction, which occurs in the same temperature range, becomes the predominant process.

Ag-rich phase formation in the Cu-6 wt% Al alloy with Ag additions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Pearlitic reaction in Cu-10wt%Al alloy with Ag additions

The pearlitic reaction in Cu-10wt%Al alloy with additions of 4, 6, 8, and 10wt%Ag was studied using scanning electron microscopy, energy dispersive X-ray microanalysis, in situ X-ray diffractometry, and microhardness measurements. The results indicated that the presence of Ag changes the pearlitic phase microstructure and its mechanical properties, because of the influence of Ag in the pearlitic phase growth mechanism. (C) 2008 International Centre for Diffraction Data.

Influence of Ag additions on the activation energy for the reverse eutectoid reaction in Cu-Al alloys

The eutectoid transformation may be defined as a solid-state diffusion-controlled decomposition process of a high-temperature phase into a two-phase lamellar aggregate behind a migrating boundary on cooling below the eutectoid temperature. In substitutional solid solutions, the eutectoid reaction involves diffusion of the solute atoms either through the matrix or along the boundaries or ledges. The effect of Ag on the non-isothermal kinetics of the reverse eutectoid reaction in the Cu-9 mass%Al, Cu-10 mass%Al, and Cu-11 mass%Al alloys were studied using differential scanning calorimetry (DSC), X-ray diffraction (XRD), and scanning electron microscopy (SEM). The activation energy for this reaction was obtained using the Kissinger and Ozawa methods. The results indicated that Ag additions to Cu-Al alloys interfere on the reverse eutectoid reaction, increasing the activation energy values for the Cu-9 mass%Al and Cu-10 mass%Al alloys and decreasing these values for the Cu-11 mass%Al alloy for additions up to 6 mass%Ag. The changes in the activation energy were attributed to changes in the reaction solute and in Ag solubility due to the increase in Al content.

Mass fractal characteristics of sonogels prepared from sonohydrolysis of tetraethoxysilane with additions of dimethylformamide

Wet silica gels with similar to 1.4 x 10(-3) mol SiO2/cm(3) and similar to 90 vol.% liquid phase were prepared from the sonohydrolysis of tetraethoxysilane (TEOS) with different additions of dimethylformamide (DMF). Aerogels were obtained by CO2 supercritical extraction. The samples were studied mainly by small-angle X-ray scattering (SAXS) and nitrogen adsorption. Wet gels exhibit a mass fractal structure with fractal dimension D increasing from 2.23 to 2.35 and characteristic length xi decreasing from similar to 9.4 nm to similar to 5.1 nm, as the DMF/TEOS molar ratio is increased from 0 to 4. The supercritical process apparently eliminates some porosity, shortening the fractality domain in the mesopore region and developing an apparent surface/mass fractal (with correlated mass fractal dimension D-m similar to 2.6 and surface fractal dimension D-s similar to 2.3) in the micropore region. The fundamental role of the DMF addition on the structure of the aerogels is to diminish the porosity and the pore mean size, without, however, modify substantially the specific surface area and the average size of the silica particle of the solid network. (c) 2006 Elsevier B.V. All rights reserved.

A kinetic model for the ultrasound catalyzed hydrolysis of solventless TEOS-water mixtures and the role of the initial additions of ethanol

The acid and ultrasound catalyzed hydrolysis of solventless TEOS-water mixtures are studied, as a function of the initial additions of ethanol to the mixtures, by means of flux calorimetry measurements. A device was specially designed for this purpose. Under acid conditions, our proposed method has been able to resolve hydrolysis from other condensation reactions, by detecting the exothermal hydrolysis reaction heat. The process has been explained by a dissolution and reaction mechanism. Ultrasound forces the dissolution process to start the reaction. The alcohol produced in the reaction helps the dissolution process to further enhance the hydrolysis. Initial amounts of pure ethanol added to the mixtures shorten the start time of the reaction, due to an additional effect of dissolution, and diminish the reaction rate, as a result of the solvent dilution effect. Our dissolution and reaction mechanism modeling describes the main points arising from the experimental data and yields k(H) = 0.24 M(-1) min(-1) for the second-order hydrolysis rate constant at 39 degrees C.

Influence of silver additions on the Cu-13 wt pct Al alloy hardness.

The influence of silver additions on the Cu-13 wt. pot. Al alloy hardness was studied for additions in the range 0 to 16 wt. pot Ag. The results indicated a pronounced hardness increase with the silver content and an influence of the quenching temperature. Data obtained from scanning electron microscopy indicated that the formation of silver-rich precipitates, wich change with the quenching temperature, seems to produce the changes on alloys hardness.

Influence of silver additions on the thermal behavior of the Cu-8 mass% Al alloy

The influence of additions of 2, 4, 6, 8, 10 and 12 mass% Ag on the thermal behavior of the Cu-8 mass% Al alloy was studied using differential scanning calorimetry (DSC), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and X-ray diffractometry (XRD). The results indicate that the presence of silver introduces new thermal events, due to the formation of a silver-rich phase and, for additions of 10 and 12 mass% Ag, it is possible to verify the formation of the gamma (1) phase (Cu9Al4) and the metastable transitions which are only observed in alloys with a minimum of 9 mass% Al.

Structural characteristics of silica sonogels prepared with additions of isopropyl alcohol

Wet silica gels with similar to 1.4 x 10(-3) mol SiO2/cm(3) and similar to 92 vol% liquid phase were obtained from sonohydrolysis of tetraethoxysilane (TEOS) with different additions of isopropyl alcohol ( IPA). The IPA/TEOS molar ratio R was changed from 0 to 4. Aerogels were obtained by supercritical CO2 extraction. The samples were analyzed by small-angle X-ray scattering (SAXS) and nitrogen adsorption. The wet gels exhibit mass fractal structure with fractal dimension increasing from D similar to 2.10 to D similar to 2.22, characteristic length xi decreasing from similar to 9.5 to similar to 6.9 nm, as R increases from 0 to 4, and an estimated characteristic length for the primary silica particles lower than similar to 0.3 nm. The supercritical process apparently eliminates a fraction of the porosity, increasing the mass fractal dimension and shortening the fractality domain in the mesopore region. The fundamental role of isopropyl alcohol on the structure of the resulting aerogels is to decrease the porosity and the pore mean size as R changes from pure TEOS to R = 4. A secondary structure appearing in the micropore region of the aerogels can be described as a mass/surface fractal structure, with correlated mass fractal dimension D-m similar to 2.7 and surface fractal dimension D-s similar to 2.3, as inferred from SAXS and nitrogen adsorption data.

Thermal behavior of the Cu-22.55 at.%Al alloy with small Ag additions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Ag-rich phase precipitation in the Cu-9 mass% Al alloy with Ag additions

The Ag-rich phase precipitation in the Cu-9 mass% Al was studied using differential scanning calorimetry (DSC), X-ray diffractometry (XRD) and scanning electron microscopy (SEM). The results indicated that Ag additions did not interfere on the metastable transitions sequence of the Cu-mass% Al alloy but Ag precipitation disturbs the beta phase formation reaction and the martensitic phase decomposition reaction.

Influence of silver additions on the structure and phase transformation of the Cu-13 wt % Al alloy

The influence of silver additions on the structure and phase transformation of the Cu-13 wt % Al alloy was studied by differential thermal analysis, X-ray diffraction, scanning electron microscopy and energy dispersive analysis of X-rays. The results indicate that the presence of silver modifies the phase-stability field, the transition temperature and the structure of the alloy. These effects are more pronounced for silver concentrations up to 8 wt %.