Influência da absorção de umidade no comportamento mecânico nos compósitos poliméricos híbridos Kevlar/vidro quando imerso em água do mar e petróleo

The polymer matrix composite materials are being used on a large scale in the most different industrial fields such as aerospace, automotive, oil, among others, since the industrial perspectives is currently working with materials which have a good mechanical performance at high service life and cost / benefit. Thus, the determination of the mechanical properties is indispensable for the characterization of waste resulting in greater expansion of this type of material. Thus, this work will be obtained three plates laminated with tereftálica polymeric matrix reinforced by a bidirectional woven E-glass and kevlar both industrially made, where the plates are manufactured by manual lamination process (hand lay-up), all laminates have five enhancement layers, the first hybrid laminate will consist of bidirectional woven E-glass fiber, kevlar fiber interspersed with layers, is formed by the second bidirectional woven kevlar fiber at the ends of the laminate (two layers), and in the center the glass fiber fabric (three layers), the third plate is composed of only the bidirectional woven E-glass fiber. Then were prepared specimens (CP) by standard, to determine the mechanical properties of tensile and bending in three points. After fabrication of the specimens, they were immersed in oil and seawater. After that, there was a comparison of the mechanical properties for the test condition in the dry state. Showing that there was a considerable increase in the properties studied because the effect of hybridization in laminates.

Preparação e caracterização de biomateriais poliméricos para avaliação da viabilidade de uso como phantom biológico

The theoretical and experimental developments in the biomaterials area have been directly applied to different fields of Medicine (odontology, regenerative medicine and radiotherapy). These advances have focused both for diagnosing diseases such as for quantifying degrees of progression. From the perspective of these studies, biomaterials are being designed and manufactured for application in various areas of science, provided advances in diagnostic radiology, radiotherapy dosimetry and calibration of radiotherapy equipment. Develop a phantom from a biomaterial has become a great ally of medicine in the treat patients with oncological diseases, allowing better performance of the equipment in order to reduce damage to healthy tissue due to excessive exposure to radiation. This work used polymers: chitosan and gelatin, for making the polymeric structures and controlled for different types of production and processing, characterizing and evaluating the biopolymer by physical techniques (STL, SEM and DEI) and therefore analyze applicability as phantom mouse lung. It was possible to evaluate the morphology of biomaterials quantitatively by scanning electron microscopy associated with imaging technique. The relevance of this work focuses on developing a phantom from polymeric biomaterials that can act as phantom providing high image contrast when subjected to analysis. Thus, the choice of DEI technique is satisfactory since it is an imaging technique of X-ray high resolution. The images obtained by DEI have shown the details of the internal microstructure of the biomaterial produced which have ≈ 10 μm dimension. The phantoms had made density ranging from 0.08 a 0.13 g/cm3.

Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos

The present work has as objective the development of ceramic pigments based in iron oxides and cobalt through the polymeric precursor method, as well as study their characteristics and properties using methods of physical, chemical, morphological and optical characterizations.In this work was used iron nitrate, and cobalt citrate as precursor and nanometer silica as a matrix. The synthesis was based on dissolving the citric acid as complexing agent, addition of metal oxides, such as chromophores ions and polymerization with ethylene glycol. The powder obtained has undergone pre-ignition, breakdown and thermal treatments at different calcination temperatures (700 °C, 800 °C, 900 °C, 1000 °C and 1100 °C). Thermogravimetric analyzes were performed (BT) and Differential Thermal Analysis (DTA), in order to evaluate the term decomposition of samples, beyond characterization by techniques such as BET, which classified as microporous materials samples calcined at 700 ° C, 800 º C and 900 º C and non-porous when annealed at 1000 ° C and 1100 º C, X-ray diffraction (XRD), which identified the formation of two crystalline phases, the Cobalt Ferrite (CoFe2O4) and Cristobalite (SiO2), Scanning Electron Microscopy (SEM) revealed the formation of agglomerates of particles slightly rounded;and Analysis of Colorimetry, temperature of 700 °C, 800 °C and 900 °C showed a brown color and 1000 °C and 1100 °C violet

Comportamento reológico de materiais cimentícios para poços de petróleo contendo naftaleno condensado ou policarboxilato

Pastas a base de cimento Portland são utilizadas na cimentação de poços de petróleo. Elas consistem de uma mistura de partículas sólidas de cimento dispersas em água e aditivos. Atualmente, diversos materiais alternativos são utilizados como aditivos, objetivando a modificação e a melhoria das propriedades das pastas de cimento, especialmente no aumento da fluidez. Novos aditivos plastificantes são capazes de suportar as diversas condições de poços, promovendo propriedades no estado fluido compatíveis às condições exigidas para cimentação.Dispersantes são os componentes da pasta que garantem fluidez, além de proporcionar controle na água perdida por filtração na formação porosa, garantindo o sucesso da operação de bombeio. Em deter minados campos, além do efeito da profundidade, as condições geológicas das formações promovemvariações do gradiente de pressão e temperatura ao longo da profundidade vertical do poço. Recentemente, diversos aditivos químicos da indústria da construção civil tem sido estudados em condições de cimentação de poços de petróleo. Vários produtos testados tem apresentado desempenho superior aos produtos normalmente empregados pela indústria de petróleo com boa relação custo/benefício em função do volume de mercado da construção civil. Resultados promissores na seleção de aditivos com função dispersante da construção civil para operações de cimentação de poços de petróleo onshore foram obtidos para temperaturas até 80°C. O potencial de uso desses aditivos permite estabelecer novas soluções para problemas encontrados na cimentação de poços de petróleo HPHT, poços sujeitos à injeção de vapor, poços depletados e poços produtores de gás. Na construção civil, os superplastificantes permitem reduzir o fator água/cimento das argamassas proporcionando melhoria de propriedades como resistência mecânica e fluidez. Assim, o objetivo deste trabalho foi o estudo e a caracterização reológica de pastas constituídas de cimento Portland, água e aditivos do tipo plastificante, com função dispersante a base de naftaleno condensado e policarboxilato, na faixa de temperaturas de 58°C e 70ºC. As condições utilizadas para a avaliação dos aditivos alternativos foram baseadas em uma cimentação primária para um poço hipotético de 2200 m de profundidade e gradientes geotérmicos de 1,7°F/100 pés e 2,1°F/100 pés. Os resultados demonstraram a grande eficiência e o poder dispersivo do policarboxilato para as temperaturas estudadas. O aditivo promoveu alta fluidez, sem efeitos de sedimentação da pasta. O dispersante à base de naftaleno reduziutant o a viscosidade plástica como o limite de escoamento acimada concentração a partir de 0,13%. O modelo de Bingham descreveu bem o comportamento reológico das pastas com policarboxilato para todas as concentrações

Síntese e caracterização de ferrita ni-zn pelo método dos precursores poliméricos calcinada por energia de microondas

Magnetic ceramics have been widely investigated, especially with respect to intrinsic and extrinsic characteristics of these materials. Among the magnetic ceramic materials of technological interest, there are the ferrites. On the other hand, the thermal treatment of ceramic materials by microwave energy has offered various advantages such as: optimization of production processes, high heat control, low consumption of time and energy among others. In this work were synthesized powders of Ni-Zn ferrite with compositions Ni1- xZnxFe2O4 (0.25 ≤ x ≤ 0.75 mols) by the polymeric precursor route in two heat treatment conditions, conventional oven and microwave energy at 500, 650, 800 and 950°C and its structural, and morphological imaging. The materials were characterized by thermal analysis (TG/ DSC), X-ray diffraction (XRD), absorption spectroscopy in the infrared (FTIR), scanning electron microscopy (SEM), X-ray spectroscopy and energy dispersive (EDS) and vibrating sample magnetometry (VSM). The results of X-ray diffraction confirmed the formation of ferrite with spinel-type cubic structure. The extrinsic characteristics of the powders obtained by microwave calcination and influence significantly the magnetic behavior of ferrites, showing particles ferrimagnéticas characterized as soft magnetic materials (soft), is of great technological interest. The results obtained led the potential application of microwave energy for calcining powders of Ni-Zn ferrite

Compósitos poliméricos a base de fibras de licuri: efeitos da hibridização e do envelhecimento ambiental acelerado

The gradual replacement of conventional materials by the ones called composite materials is becoming a concern about the response of these composites against adverse environmental conditions, such as ultraviolet radiation, high temperature and moist. Also the search for new composite using natural fibers or a blend of it with synthetic fibers as reinforcement has been studied. In this sense, this research begins with a thorough study of microstructural characterization of licuri fiber, as a proposal of alternative reinforcement to polymeric composites. Thus, a study about the development of two composite laminates was done. The first one, involving only the fiber of licuri and the second comprising a hybrid composite based of fiber glass E and the fiber of licuri, in order to know the performance of the fiber when of fiber across the hybridization process. The laminates were made in the form of plates using the tereftálica ortho-polyester resin as matrix. The composite laminate made only by licuri fiber had two reinforcing fabric layers of unidirectional licuri and the hybrid composite had two reinforcing layers of unidirectional licuri fabric and three layers of fiber short glass-E mat. Finally, both laminates was exposed to aging acceleration in order to study the influence of environmental degradation involving the mechanical properties and fracture characteristics thereof. Regarding the mechanical properties of composites, these were determined through uniaxial tensile tests, uniaxial compression and three bending points for both laminates in original state, and uniaxial tensile tests and three bending points after accelerated aging. As regards the study of structural degradation due to aging of the laminates, it was carried out based on microscopic analysis and microstructure, as well as measuring weight loss. The characteristics of the fracture was performed by macroscopic and microscopic (optical and SEM) analysis. In general, the laminated composites based on fiber licuri showed some advantages in their responses to environmental aging. These advantages are observed in the behavior related to stiffness as well as the microstructural degradation and photo-oxidation processes. However, the structural integrity of this laminate was more affected in case the action of uniaxial tensile loads, where it was noted a lower rate of withholding his last resistance property

Biocompósitos poliméricos obtidos a partir da fração lignocelulósica e amilácea do caroço de manga (mangifera indica), Tommy atkins

This employment has the function the utilization of mango seeds Tommy Atkins, like starch source to obtain biopolymers and fibers source and nanowhiskers cellulose also, that will be use like reinforcing fillers in micro and nanobiocomposites polymeric. The fibers in natura removed from tegument mango seed were characterized, as weel as the treated fibers and nanowhiskers of cellulose extracted from them. The starch extracted from seed s almond showed a good performance (32%) and a high purity. The chemicals analyzes, of crystallinity and morphological of the fibers in natura, treated fibers and nanowhiskers of cellulose confirmed the efficacy of the chemical treatement performed to remove amorphous constituents (hemicellulose and lignina). The thermoplastic starch (TPS) obtained from two sources, corn starch and starchy material mango, was produced in a twin screw extruder with compositon mass of 62,5% of starch, 9,4% of water and 28,1% of glycerol. The starch material mango was the main objective of this work for the production of biodegradable materials, and the starch corn was utilized during the production stage to evaluate the processability of the starch and use as parameter for comparison, according of being a conventional source for obtaining conventional comercial starch. The incorporation of fibers (6% in mass) and nanowhiskers cellulose (1% in mass) in matrix of TPS to obtain composite and nanocomposite, respectively, it was performed in single screw extruder. The biocomposites and bionanocomposites polymeric were obtained and the TPS from starchy material mango presented better results of thermal and mechanicals properties when compared to TPS corn starch. Concludes that the sediment generated of the agroindustrial processing mango used presents potencial to producing of biodegradables materials

Sinterização de matrizes cerâmicas à base de alumina reforçadas por carbetos a partir de precursores poliméricos

Ceramic composites produced with polymerics precursors have been studied for many years, due to the facility of obtaining a complex shape, at low temperature and reduces cost. The main objective of this work is to study the process of sintering of composites of ceramic base consisting of Al2O3 and silicates, reinforced for NbC, through the technique of processing AFCOP, as well as the influence of the addition of LZSA, ICZ and Al as materials infiltration in the physical and mechanical properties of the ceramic composite. Were produced ceramic matrix composites based SiCxOy e Al2O3 reinforced with NbC, by hidrosilylation reaction between D4Vi and D1107 mixtured with Al2O3 as inert filler, Nb and Al as reactive filler. The specimens produced were pyrolised at 1200, 1250 and 1400°C and infiltred with Al, ICZ and LZSA, respectively. Density, porosity, flexural mechanical strength and fracture surface by scanning electron microscopy were evaluated. The microstructure of the composites was investigated by X-ray diffraction to identify the presence of crystalline phases. The composites presented apparent porosity varying of 31 up to 49% and mechanical flexural strength of 14 up to 34 MPa. The infiltration process improviment of the densification and reduction of the porosity, as well as increased the values of mechanical flexural strength. The obtained phases had been identified as being Al3Nb, NbSi2, Nb5S3, Nb3Si and NbC. The samples that were submitted the infiltration process presented a layer next surface with reduced pores number in relation to the total volume

Comissão parlamentar de inquérito : o fato determinado e os limites materiais como garantidores dos direitos fundamentais

Analisa a limitação dos poderes das comissões parlamentares de inquérito e do fato determinado como garantidores do exercício dos direitos fundamentais no âmbito dessas mesmas comissões, a partir da doutrina sobre o assunto e da jurisprudência do Supremo Tribunal Federal. O enorme espaço que as CPIs têm na sociedade, aliado ao "poder de investigação próprio de autoridades judiciais", conferido pela Constituição Federal, nem sempre é compreendido pela maioria dos seus membros, que, não hesitam em dar a ela poderes jurisdicionais, privativos do Judiciário, gerando, desta forma, a violência contra os direitos fundamentais das testemunhas e pessoas por ela investigadas.

Retificação dos autógrafos do projeto de lei n° 24, de 2012-CN, em função da identificação de erros materiais; faculdade prevista na vigente Lei de Diretrizes Orçamentárias para 2013 e na resolução n° 1, de 2006-CN

Consultoria de Orçamento e Fiscalização Financeira. Núcleo Poderes, Justiça, Relações Exteriores, Defesa e Despesa Pessoal

Influência de agentes clareadores na rugosidade de compósitos dentários

O clareamento dental é o meio disponível mais simples, comum e conservador para o cirurgião-dentista proporcionar aos pacientes o padrão de cor de seus dentes mais desejado. Em alguns casos, os dentes que vão ser clareados podem apresentar restaurações realizadas com compósitos dentais, que são mais suscetíveis a alterações químicas, quando comparados a outros materiais restauradores. Alguns estudos mostraram que diferentes concentrações de agentes clareadores levaram a um aumento significativo da rugosidade superficial e das porosidades em compósitos dentais. Este estudo avaliou o efeito de dois agentes clareadores (Whiteness HP Blue 20%, Whiteness HP Max) sobre a rugosidade superficial de dois compósitos dentais, um micro-híbrido (Esthet X, Denstply) e outro nanoparticulado (Z 350, 3M ESPE). Um total de oito corpos de prova (9 x 2 mm) foram confeccionados com auxílio de uma matriz de teflon, sendo divididos em 4 grupos (Esthet X + Whiteness HP Blue 20%; Esthet X + Whiteness HP Max; Z 350 + Whiteness HP Blue 20%; Z 350 + Whiteness HP Max), sendo n=2. Os corpos de prova foram armazenados em saliva artificial neutra e, após 24 horas, foram polidos com discos de óxido de Alumínio (Sof-lex, 3M ESPE). Após sete dias de imersão salivar, cada corpo de prova foi levado a um microscópio de força atômica para obtenção do valor inicial de rugosidade superficial (Ra em nm). Em seguida, sem remover o corpo de prova do microscópio, o agente clareador foi aplicado sobre a superfície do corpo de prova, segundo as instruções do fabricante, de modo que permitisse uma posterior observação da mesma área do corpo de prova observada inicialmente, para obtenção do valor final de rugosidade superficial. Imagens em duas e três dimensões foram obtidas de cada corpo de prova para observação de alterações da topografia. Os resultados foram tratados estatisticamente por ANOVA e pelo teste de contraste Student-Newman-Keuls (p < 0,05). Não houve alteração significativa na rugosidade superficial (Ra) dos corpos da prova de compósitos micro-híbrido e nanoparticulado, submetidos aos agentes clareadores Whiteness HP Blue 20% e Whiteness HP Maxx. No entanto, independente do agente clareador utilizado, foram observadas maiores alterações topográficas nas imagens de microscopia de força atômica da superfície do compósito micro-híbrido do que nas imagens do nanoparticulado.

Capacidade de selamento de três materiais retrobturadores frente à infiltração microbiana por Enterococcus faecalis

O objetivo deste estudo foi comparar a capacidade de selamento apical de três materiais retrobturadores em dentes submetidos à infiltração microbiana por Enterococcus faecalis. Além de analisar a ocorrência da infiltração microbiana em relação à variável tempo. Para tal, foram utilizados 80 caninos superiores permanentes humanos extraídos, instrumentados com o sistema rotatório ProTaper Universal (MAILLEFER) e obturados pela técnica de compactação lateral, com dois tipos de cimento endodôntico: Endofill (DENTSPLY) e AH Plus (DENTSPLY). A apicetomia foi realizada com a remoção de 3mm do terço apical e o retropreparo confeccionado com pontas ultrasônicas. As amostras foram subdivididas, aleatoriamente, em 6 grupos com 10 dentes cada, e 2 grupos controles. Os materiais utilizados para a retrobturação foram MTA branco (ANGELUS), IBC BioAggregate (INNOVATIVE BIOCERAMIX INC.) e Acroseal (SEPTODONT). Foram confeccionados dispositivos para fixação dos dentes aos tubos Eppendorfs. As amostras foram inoculadas com cepas de E. faecalis e incubadas a 37C, por um período de 90 dias, para análise da presença de turvação do meio Enterococcosel. Para a realização da análise estatística foram utilizados os seguintes testes: Qui-quadrado com Prova Exata de Fisher e Kruskal-Wallis. Os resultados mostraram que todos os grupos nos quais foi realizada a obturação e a posterior retrobturação apresentaram infiltração. Comparando todos os grupos, não houve diferença significativa entre os materiais testados. Em relação apenas aos materiais retrobturadores, o Acroseal obteve a menor infiltração, seguido do MTA branco e do IBC BioAggregate. As amostras obturadas com o cimento Endofill não apresentaram diferença estatística em relação à variável tempo. Porém, nas amostras obturadas com o cimento AH Plus, houve maior ocorrência de infiltração nas amostras retrobturadas com o IBC BioAggregate e menor infiltração nas amostras retrobturadas com Acroseal, com diferença estatisticamente significante ao nível de 10%.

Materiais compósitos biocidas baseados em resinas reticuladas contendo nanopartículas de prata

Nesta dissertação, duas resinas reticuladas comerciais (denominadas, AmberliteGT73 e AmberliteIRC748) foram empregadas para suportar partículas de prata. Os grupos tiol da GT73 e ácido iminodiacético da IRC748 presentes nessas resinas foram empregados para a fixação de íons Ag+ a partir de solução aquosa. Posteriormente, os íons Ag+ foram reduzidos pelo emprego de três redutores diferentes em pH alcalino, denominados hidrazina, hidroxilamina e formaldeído (pH  12). A morfologia e a impregnação de prata dos materiais binários assim obtidos foram avaliadas por meio de microscópio eletrônico de varredura equipado com detector de elétrons retro-espalhados (SEM-BSE). O detector de espectrometria de energia dispersiva de raios-X (EDAX) acoplado ao SEM permitiu a observação de partículas de prata. Os espectros de raios-X revelaram a presença do metal nas superfícies interna e externa das microesferas dos compósitos. A quantidade de prata incorporada foi determinada pelo método titulométrico, empregando solução padrão de tiocianato de potássio. As características antibactericidas dos compósitos foram avaliadas em colunas contendo pérolas de resina por onde foram percoladas suspensões da bactéria Escherichia coli auxotrópica AB1157 (tipo selvagem) nas concentrações de 103 a 107 células/mL. A avaliação biocida mostrou que estes materiais foram completamente bactericidas, sendo efetivos na eliminação da bactéria em poucos minutos. Esta ação biocida foi atribuída à combinação da atuação da prata e dos grupos funcionais das resinas

Distribuição de tensões em próteses parciais fixas posteriores livres de metal com retentores intracoronários: análise em elementos finitos

Para reabilitar a ausência de um elemento dentário posterior, as próteses parciais fixas (PPF) com retentores intracoronários são uma alternativa aos implantes osseointegrados. O objetivo deste estudo foi avaliar a distribuição de tensões nessas próteses com três combinações de materiais: cerâmica de zircônia parcialmente estabilizada por ítria (ZPEI) revestida por cerâmica de fluorapatita (α), cerâmica de dissilicato de lítio (β) ou compósito fibrorreforçado (γ). Na composição α, foram analisadas a presença ou ausência da cerâmica de revestimento na parede cervical das caixas proximais e três variações na área total da seção transversal dos conectores (4 mm de largura x 3,2, 4,2 ou 5,2 mm de altura). Em 8 modelos bidimensionais de elementos finitos, uma carga vertical de 500 N foi aplicada na fossa central do pôntico e as tensões principais máximas (tração) e mínimas (compressão) foram apontadas em MPa. Inicialmente foram avaliados os 6 modelos com PPF de ZPEI e suas variações. Os maiores valores das tensões de tração foram encontrados no terço cervical dos conectores. Quando presente nestas regiões, a cerâmica de revestimento recebeu tensões acima do limite de sua resistência à flexão. Na comparação entre os modelos sem cerâmica de revestimento na parede cervical das caixas proximais, mesmo aquele com conectores de 3,2 x 4 mm, cuja infraestrutura apresentava 2,5 x 3 mm, poderia ser recomendado para uso clínico. Altos valores de tensões de compressão foram registrados entre o terço oclusal e médio dos conectores, correspondente à união entre as cerâmicas, o que poderia ocasionar, devido à flexão, falhas adesivas. Posteriormente, o modelo de ZPEI com a cerâmica de fluorapatita ausente da parede cervical das caixas proximais e área total dos conectores de 4,2 x 4 mm foi comparado aos dois outros materiais com conectores de mesma área. Na PPF de dissilicato de lítio, os valores representaram uma provável violação do limite de sua resistência à flexão. A PPF de compósito fibrorreforçado apresentou tensões bem abaixo do limite de resistência à flexão de sua infraestrutura, mas, como no modelo de ZPEI, tensões compressivas se concentraram com alto valor entre o terço oclusal e médio dos conectores, local de união entre a resina composta e a infraestrutura de fibras. Os resultados mostraram que a cerâmica de dissilicato de lítio e a presença da cerâmica de fluorapatita na parede cervical das caixas proximais deveriam ser contraindicadas para a condição proposta. Parece viável uma área de conectores na infraestrutura de ZPEI com no mínimo 2,5 x 3 mm. A PPF de compósito fibrorreforçado apresenta resistência estrutural para a situação estudada, mas, como também aquelas compostas de ZPEI, aparenta ter como pontos fracos a adesão entre a infraestrutura e o material de cobertura e a própria resistência deste último.

Avaliação comparativa da alteração dimensional de diferentes materiais utilizados para a confecção de troquéis

Neste trabalho experimental, objetivou-se avaliar comparativamente a alteração dimensional de três diferentes materiais utilizados na confecção de troqueis: gesso tipo IV Fuji Rock (GC), resina epóxica industrial Sikadur 32 (Sika) e resina epóxica Tri-Epoxy Die Material (Tri-Dynamics). Foram confeccionados dois modelos-padrão em aço inoxidável. Um desses modelos foi confeccionado de modo a simular um preparo para coroa total em um pré-molar. O outro modelo foi confeccionado 2,0mm maior em todas as dimensões em relação ao primeiro de modo a proporcionar um alívio uniforme para a base leve do material de moldagem. Trinta troquéis foram obtidos a partir de moldes em silicona de adição (Aquasil Dentsply) utilizada com a técnica de dois passos. Os troqueis foram divididos em grupos de dez para cada material. As alterações foram mensuradas através das medições da altura e dos diâmetros da base e do topo dos troqueis obtidos, com o auxílio de um Projetor de Perfis Deltronic DV-114 com leitura em software. As medidas obtidas foram dispostas em tabelas e analisadas estatisticamente. Após avaliação pode-se concluir que houve diferença estatisticamente significante entre todos os grupos testados. Os troquéis de gesso tipo IV Fuji Rock (GC) contraíram nas medições da altura e do diâmetro do topo, e expandiram nas medições do diâmetro da base, apresentando diferença estatisticamente significativa em todas as comparações com o grupo controle (metal). Os troquéis de resina epóxica Tri-Epoxy (Tri-Dynamics) contraíram nas medições da altura e do diâmetro do topo, e expandiram nas medições diâmetro da base, apresentando diferença estatisticamente significante somente no diâmetro do topo nas comparações com o grupo controle (metal). Os troquéis de resina epóxica Sikadur 32 (Sika) contraíram nas medições da altura e do diâmetro do topo, e expandiram nas medições do diâmetro das base, apresentando diferença estatisticamente significante em todas as comparações com o grupo controle (metal).