Estudo da sinterização de eletrólito sólido de céria dopada com gadolínia

Fuel cells are electrochemical devices that convert chemical energy in electrical energy by a reaction directly. The solid oxide fuel cell (SOFC) works in temperature between 900ºC up to 1000ºC, Nowadays the most material for ceramic electrolytes is yttria stabilized zirconium. However, the high operation temperature can produce problems as instability and incompatibility of materials, thermal degradation and high cost of the surround materials. These problems can be reduced with the development of intermediate temperature solid oxide fuel cell (IT-SOFC) that works at temperature range of 600ºC to 800ºC. Ceria doped gadolinium is one of the most promising materials for electrolytes IT-SOFC due high ionic conductivity and good compatibility with electrodes. The inhibition of grain growth has been investigated during the sintering to improve properties of electrolytes. Two-step sintering (TSS) is an interesting technical to inhibit this grain growth and consist at submit the sample at two stages of temperature. The first one stage aims to achieve the critical density in the initiating the sintering process, then the sample is submitted at the second stage where the temperature sufficient to continue the sintering without accelerate grain growth until to reach total densification. The goal of this work is to produce electrolytes of ceria doped gadolinium by two-step sintering. In this context were produced samples from micrometric and nanometric powders by two routes of two-step sintering. The samples were obtained with elevate relative density, higher than 90% using low energy that some works at the same area. The average grain size are at the range 0,37 μm up to 0,51 μm. The overall ionic conductivity is 1,8x10-2 S.cm and the activation energy is 0,76 eV. Results shown that is possible to obtain ceria-doped gadolinium samples by two-step sintering technique using modified routes with characteristics and properties necessary to apply as electrolytes of solid oxide fuel cell

Corrosão dos aços UNS S30400 e 31600 em meios simuladores de poros de concreto

Com o objetivo de investigar a influência que o molibdênio exerce nas propriedades das camadas passivas das armaduras de aços austeníticos, barras redondas dos aços UNS S30400 e 31600 foram submetidas à ação de soluções que simulam as que são encontradas nos poros de concreto. Para caracterizar o efeito do molibdênio na resistência daqueles aços à corrosão por pites, foram conduzidos ensaios de circuito aberto, polarização anódica, espectroscopia de impedância eletroquímica, análise de Mott-Schottky, tração em baixa taxa de deformação e análise das superfícies por microscopias óptica e eletrônica de varredura. Os resultados obtidos demonstram que, de uma forma geral, o aço UNS S30400 (sem molibdênio) apresentou maior resistência à corrosão localizada que o UNS S31600 (2% de Mo) nas soluções alcalinas cloretadas naturalmente aeradas, comportamento este inverso ao que se observa nos mesmos materiais quando submetidos a soluções cloretadas neutras ou ácidas.

Avaliação de aminoácidos como inibidores de corrosão para cobre em meio de água do mar artificial

Inibidores de corrosão são substâncias que quando adicionadas a um meio agressivo, diminuem ou previnem a reação de oxidação de um metal com este meio e/ou as reações de redução de espécies presentes no meio. Para a inibição da corrosão de cobre e suas ligas em meios ácidos ou neutros, o inibidor mais empregado é o benzotriazol (BTAH), o qual forma complexos com os íons Cu (I) e Cu (II) na superfície do metal, diminuindo o processo corrosivo. A preocupação com a preservação ambiental e a toxicidade de inibidores de corrosão vem sendo discutida na literatura. Vários estudos têm-se intensificado usando aminoácidos, como proposta para substituição ao BTAH, considerado tóxico. Entre os aminoácidos estudados, dois apresentavam enxofre em suas moléculas (cisteína e metionina) e um outro sem heteroátomo na cadeira lateral (glicina). As concentrações variaram entre 10-2 a 10-4 mol/L e pH da solução entre 7,2 e 8,4. Foram realizadas medidas gravimétricas (ensaios de imersão total) e técnicas eletroquímicas, tais como polarização potenciodinâmica e espectroscopia de impedância eletroquímica. A caracterização morfológica da superfície do substrato após os ensaios de imersão total (743 horas) foi feita por meio de microscopia eletrônica de varredura (MEV), espectroscopia de raios X por dispersão de energia (EDS ou EDX) e difração de raios X (DRX). Embora os resultados com aminoácidos tenham sido sempre muito inferiores àqueles obtidos na presença de BTAH, comportamentos semelhantes em função da concentração dos aminoácidos puderam ser observados pelos diagramas de Nyquist. Contudo, com exceção dos resultados verificados para o meio contendo cisteína 10-2 mol/L, todas as eficiências de inibição para os meios contendo aminoácidos, obtidas pelos ensaios de imersão total, foram negativas, mostrando que o tempo de exposição também pode ser relevante para o desempenho destes inibidores. Entre todos os aminoácidos testados, os meios contendo glicina apresentaram os piores desempenhos anticorrosivos, inclusive acelerando o processo de dissolução anódica do cobre. Esse resultado pode estar relacionado à faixa de pH das soluções testadas e à solubilidade dos complexos de cobre formados com os aminoácidos, mostrando que uma faixa ótima de pH também deve ser assegurada para aprimorar a ação destes aminoácidos como inibidores de corrosão

Modified electrodes with Keggin-type polyoxotungstates

O objectivo deste trabalho é a produção de novos eléctrodos modificados com polioxotungstatos (POMs) do tipo Keggin, incluindo POMs lacunares e substituídos por metais de transição. A preparação e caracterização dos polioxotungstatos encontram-se descritas no Capítulo 2. No Capítulo 3 descreve-se a produção de eléctrodos de carbono vítreo funcionalizados com sais híbridos de tetra-n-butilamónio de vários silicotungstatos pelo método de evaporação da gota. As propriedades electroquímicas dos polioxotungstatos imobilizados foram comparadas com as das espécies solúveis correspondentes. A morfologia dos depósitos foi avaliada por microscopia óptica e por microscopia electrónica de varrimento. No capítulo 4 descreve-se a preparação de novos eléctrodos compósitos de carbono e poli(hexilmetacrilato) com fosfotungstatos. Os estudos electroquímicos revelaram que as principais características dos POMs são mantidas e que os processos de redução são controlados por difusão, dependendo da difusão dos protões da solução. O Capítulo 5 descreve a construção de filmes em multicamadas ultrafinos contendo POMs e polietilenimina, preparados pelo método de auto-montagem camada-sobre-camada em eléctrodos de carbono vítreo. Os filmes em multicamada foram caracterizados por voltametria cíclica e por microscopia electrónica de varrimento e foi usada a espectroscopia de absorção de UV-Vis em placas de quartzo para monitorar o crescimento de filme. Os resultados voltamétricos revelaram que os processos de redução dos POM são confinados à superfície. Alguns destes eléctrodos modificados revelaram propriedades electrocatalíticas relativamente à redução dos aniões nitrito, bromato e/ou iodato. A espectroscopia de impedância electroquímica também foi usada na caracterização destes filmes e os resultados revelaram que a resistência à transferência de carga aumenta com o aumento do número de bicamadas para ambas as espécies redox, indicando que a espessura do filme tem um efeito importante sobre a cinética de reacções de transferência de carga. No capítulo 6 descreve-se a síntese de filmes híbridos orgânicos/inorgânicos compostos por poli(3,4-etilenodioxitiofeno) (PEDOT) e por silicotungstatos do tipo Keggin através da polimerização electroquímica, em condições aquosas, na superfície de electrodos de carbono vítreo. A voltametria cíclica revelou que as características principais dos POMs são mantidas nos filmes. Verificou-se que estes filmes são muito estáveis, possivelmente devido a fortes interacções electrostáticas entre os POMs aniónicos e o polímero positivamente carregado. A espectroscopia de impedância electroquímica foi também utilizada e os resultados mostraram que a resistência de transferência de carga aumenta com o aumento do pH e para valores de potenciais mais elevados. O capítulo 7 apresenta as conclusões finais e possíveis trabalhos futuros.

Weathering resistance of thin plasma polymer films on pre-coated steel

O trabalho apresentado teve origem no projecto de investigação “Tailored Thin Plasma Polymers Films for Surface Engineering of Coil Coated Steel”, financiado pelo Programa Europeu ECSC Steel Research. Sistemas de aço galvanizado pré-pintado em banda à base de poliéster e poliuretano foram submetidos a um processo de polimerização por plasma onde um filme fino foi depositado de modo a modificar as propriedades de superfície. Foram usados reactores de cátodo oco, microondas e rádio frequência para a deposição do polímero fino. Os sistemas preparados foram analisados de modo a verificar a influência do processo de polimerização por plasma na alteração das propriedades barreira dos sistemas pré-pintados em banda. Foi estudado o efeito dos diferentes passos do processo de polimerização por plasma, bem como o efeito de diferentes variáveis operatórias. A mistura precursora foi variada de modo a modificar as propriedades da superfície de modo a poder vir a obter maior hidrofobicidade, maior resistência a marcas digitais, bem como maior facilidade de limpeza. Os testes foram conduzidos em solução de NaCl 0,5 M. Para o trabalho foram usadas técnicas de análise da morfologia da superfície como Microscopia de Força Atómica e Microscopia Electrónica de Varrimento. As propriedades electroquímicas dos sistemas foram estudadas por Espectroscopia de Impedância Electroquímica. A estrutura dos filmes gerados no processo de polimerização por plasma foi caracterizada por Microscopia de Transmissão Electrónica. A modificação das propriedades ópticas devido ao processo de polimerização por plasma foi também obtida.

Electromechanical properties of engineered lead free potassium sodium niobate based materials

K0.5Na0.5NbO3 (KNN), is the most promising lead free material for substituting lead zirconate titanate (PZT) which is still the market leader used for sensors and actuators. To make KNN a real competitor, it is necessary to understand and to improve its properties. This goal is pursued in the present work via different approaches aiming to study KNN intrinsic properties and then to identify appropriate strategies like doping and texturing for designing better KNN materials for an intended application. Hence, polycrystalline KNN ceramics (undoped, non-stoichiometric; NST and doped), high-quality KNN single crystals and textured KNN based ceramics were successfully synthesized and characterized in this work. Polycrystalline undoped, non-stoichiometric (NST) and Mn doped KNN ceramics were prepared by conventional ceramic processing. Structure, microstructure and electrical properties were measured. It was observed that the window for mono-phasic compositions was very narrow for both NST ceramics and Mn doped ceramics. For NST ceramics the variation of A/B ratio influenced the polarization (P-E) hysteresis loop and better piezoelectric and dielectric responses could be found for small stoichiometry deviations (A/B = 0.97). Regarding Mn doping, as compared to undoped KNN which showed leaky polarization (P-E) hysteresis loops, B-site Mn doped ceramics showed a well saturated, less-leaky hysteresis loop and a significant properties improvement. Impedance spectroscopy was used to assess the role of Mn and a relation between charge transport – defects and ferroelectric response in K0.5Na0.5NbO3 (KNN) and Mn doped KNN ceramics could be established. At room temperature the conduction in KNN which is associated with holes transport is suppressed by Mn doping. Hence Mn addition increases the resistivity of the ceramic, which proved to be very helpful for improving the saturation of the P-E loop. At high temperatures the conduction is dominated by the motion of ionized oxygen vacancies whose concentration increases with Mn doping. Single crystals of potassium sodium niobate (KNN) were grown by a modified high temperature flux method. A boron-modified flux was used to obtain the crystals at a relatively low temperature. XRD, EDS and ICP analysis proved the chemical and crystallographic quality of the crystals. The grown KNN crystals exhibit higher dielectric permittivity (29,100) at the tetragonal-to-cubic phase transition temperature, higher remnant polarization (19.4 μC/cm2) and piezoelectric coefficient (160 pC/N) when compared with the standard KNN ceramics. KNN single crystals domain structure was characterized for the first time by piezoforce response microscopy. It could be observed that <001> - oriented potassium sodium niobate (KNN) single crystals reveal a long range ordered domain pattern of parallel 180° domains with zig-zag 90° domains. From the comparison of KNN Single crystals to ceramics, It is argued that the presence in KNN single crystal (and absence in KNN ceramics) of such a long range order specific domain pattern that is its fingerprint accounts for the improved properties of single crystals. These results have broad implications for the expanded use of KNN materials, by establishing a relation between the domain patterns and the dielectric and ferroelectric response of single crystals and ceramics and by indicating ways of achieving maximised properties in KNN materials. Polarized Raman analysis of ferroelectric potassium sodium niobate (K0.5Na0.5)NbO3 (KNN) single crystals was performed. For the first time, an evidence is provided that supports the assignment of KNN single crystals structure to the monoclinic symmetry at room temperature. Intensities of A′, A″ and mixed A′+A″ phonons have been theoretically calculated and compared with the experimental data in dependence of crystal rotation, which allowed the precise determination of the Raman tensor coefficients for (non-leaking) modes in monoclinic KNN. In relation to the previous literature, this study clarifies that assigning monoclinic phase is more suitable than the orthorhombic one. In addition, this study is the basis for non-destructive assessments of domain distribution by Raman spectroscopy in KNN-based lead-free ferroelectrics with complex structures. Searching a deeper understanding of the electrical behaviour of both KNN single crystal and polycrystalline materials for the sake of designing optimized KNN materials, a comparative study at the level of charge transport and point defects was carried out by impedance spectroscopy. KNN single crystals showed lower conductivity than polycrystals from room temperature up to 200 ºC, but above this temperature polycrystalline KNN displays lower conductivity. The low temperature (T < 200 ºC) behaviour reflects the different processing conditions of both ceramics and single crystals, which account for less defects prone to charge transport in the case of single crystals. As temperature increases (T > 200 ºC) single crystals become more conductive than polycrystalline samples, in which grain boundaries act as barriers to charge transport. For even higher temperatures the conductivity difference between both is increased due to the contribution of ionic conduction in single crystals. Indeed the values of activation energy calculated to the high temperature range (T > 300 ºC) were 1.60 and 0.97 eV, confirming the charge transport due to ionic conduction and ionized oxygen vacancies in single crystals and polycrystalline KNN, respectively. It is suggested that single crystals with low defects content and improved electromechanical properties could be a better choice for room temperature applications, though at high temperatures less conductive ceramics may be the choice, depending on the targeted use. Aiming at engineering the properties of KNN polycrystals towards the performance of single crystals, the preparation and properties study of (001) – oriented (K0.5Na0.5)0.98Li0.02NbO3 (KNNL) ceramics obtained by templated grain growth (TGG) using KNN single crystals as templates was undertaken. The choice of KNN single crystals templates is related with their better properties and to their unique domain structure which were envisaged as a tool for templating better properties in KNN ceramics too. X-ray diffraction analysis revealed for the templated ceramics a monoclinic structure at room temperature and a Lotgering factor (f) of 40% which confirmed texture development. These textured ceramics exhibit a long range ordered domain pattern consisting of 90º and 180º domains, similar to the one observed in the single crystals. Enhanced dielectric (13017 at TC), ferroelectric (2Pr = 42.8 μC/cm2) and piezoelectric (d33 = 280 pC/N) properties are observed for textured KNNL ceramics as compared to the randomly oriented ones. This behaviour is suggested to be due to the long range ordered domain patterns observed in the textured ceramics. The obtained results as compared with the data previously reported on texture KNN based ceramics confirm that superior properties were found due to ordered repeated domain pattern. This study provides an useful approach towards properties improvement of KNN-based piezoelectric ceramics. Overall, the present results bring a significant contribution to the pool of knowledge on the properties of sodium potassium niobate materials: a relation between the domain patterns and di-, ferro-, and piezo-electric response of single crystals and ceramics was demonstrated and ways of engineering maximised properties in KNN materials, for example by texturing were established. This contribution is envisaged to have broad implications for the expanded use of KNN over the alternative lead-based materials.

Estudo de novas técnicas de caracterização da resposta eléctrica em (Bio)sensores (para detecção de componentes agrícolas)

Faculdade de Ciências e Tecnologia – Universidade Nova de Lisboa Departamento de Engenharia Electrotécnica Tese de mestrado

Estudo eletroquímico das interações do tartarato de sódio sobre superfícies zincadas para posterior eletrodeposição de polipirrol

Neste trabalho, foi estudada a síntese eletroquimica do pirrol sobre eletrodos de zinco e aço galvanizado em tartarato de sódio. De modo a avaliar a interação aço galvanizadoltartarato e zincoltartarato, foram empregadas as técnicas de voltametria cíclica, espectroscopia de impedância eletroquímica, Raman e análise morfológica. Através dos resultados verificou-se que há a formação de um filme de tartarato sobre as superficies galvanizadas que inibe a dissolução anódica do metal. Verificou-se que houve fonnação de polipirrol sobre substratos galvanizados em meio tartarato de sódio. No estudo da eletropolimerização do pirrol, a influência de parâmetros tais como concentrações do eletrólito, do tenso ativo e dos pigmentos e tempo e densidade de corrente na eletrodeposição foi investigada. Com o objetivo de melhorar as propriedades anticorrosivas dos filmes de polipirrol, foi estudada a incorporação de tensoativos e dos pigmentos de dióxido de titânio e fosfato de zinco comercial ZMP. Para avaliar os substratos metálicos e os filmes de polipirrol, foram empregadas as técnicas de voltametria ciclica e espectroscopia de impedância eletroquimica. A morfologia dos filmes poliméricos foi analisada por microscopia eletrônica de varredura. Os filmes de Ppy foram também caracterizados por espectros copia Raman. Os filmes de poliméricos em presença de moléculas tensoativos tornaram-se mais compactos e homogêneos. Com relação à incorporação de pigmentos nestes filmes, a adição destes tende a aumentar a resistência à corrosão.

Formação e caracterização de óxidos crescidos anodicamente sobre Ti e Ti6Al4V

Foi estudada a formação e a caracterização de filmes de óxidos passivantes sobre o titânio puro e a liga Ti-6Al-4V em solução 1 M de ácido sulfúrico e em solução tampão de fosfato utilizando os métodos eletroquímicos potenciostáticos e potenciodinâmicos. Os filmes formados foram analisados via Microscopia Eletrônica de Varredura (MEV), Espectroscopia de Energia Dispersiva (EDS), Espectroscopia Raman, Voltametria Cíclica e Espectroscopia de Impedância Eletroquímica (EIE). As análises de microscopia eletrônica de varredura mostraram que o óxido formado pode apresentar variações significativas quanto à textura e a porosidade do filme. As análises de EDS, embora não tenham mostrado a presença do oxigênio presente na composição dos óxidos, indicaram outros picos de elementos oriundos do eletrólito ou do processo de polimento e limpeza do material, além dos elementos de liga. A espectroscopia Raman não se mostrou muito adequada, para este caso, por apresentar pouca definição dos picos correspondentes aos óxidos. Os voltamogramas cíclicos, obtidos em meio ácido e em solução fosfática, apresentaram comportamentos similares onde a formação do óxido ocorre fundamentalmente durante o primeiro ciclo, enquanto que nos ciclos subseqüentes aparecem os picos catódicos de dissolução do óxido e o da reação de formação de H2, uma região de passivação e o pico anódico da reação de formação do O2. A presença de dois patamares de corrente durante o ciclo inicial sugere a formação de um filme do tipo bi-camada. Os ensaios de EIE mostraram que tanto o titânio puro como a liga de titânio tem um comportamento resistivo / capacitivo pela presença do filme de óxido na interface metal / solução, sendo que a resistência de polarização aumenta significativamente após o processo de anodização e, na maioria dos ensaios, sua ordem de grandeza foi maior que 104 kW.cm2 sugerindo que houve aumento proporcional da espessura e das características protetoras do filme formado.

Comportamento eletroquímico do alumínio em misturas etilenoglicol-água : efeito da adição de agentes quelantes

Estudou-se o comportamento eletroquímico do alumínio em misturas de etilenoglicol (EG) e água, em presença e ausência de agentes quelantes (EDTA - ácido etilenodiaminotetraacético ou EDTPO - ácido etilenodiamino tetrametilenofosfônico), na faixa de pH entre 7 e 9, através de ensaios potenciodinâmicos, de espectroscopia de impedância eletroquímica e microscopia de força atômica. Em solução EG-água, a eficiência de inibição do EDTA na corrosão do Al depende da proporção de etilenoglicol e do pH do eletrólito, observando-se que o filme de óxido de alumínio é mais uniforme e estável quando o teor de EG na mistura é maior ou igual a 35 % v/v, mantido o pH em 7. Nestes casos, a adsorção do EDTA sobre o eletrodo é favorecida. Por outro lado, verificou-se que a dissolução do Al é acentuada com a adição de EDTA em eletrólitos com pH alcalino e com teores de água maiores. Nas mesmas condições experimentais, o EDTPO apresentou um efeito inibidor superior ao do EDTA, podendo ser empregado em uma faixa de pH mais ampla. Este comportamento é atribuído a uma adsorção mais forte do ácido fosfônico sobre a superfície do eletrodo, favorecendo a formação de um filme de óxido de elevada resistência, que se mantém por longos tempos de imersão. Verificou-se neste caso que a adsorção de EDTPO é favorecida em meio etilenoglicol-água, similarmente ao que ocorre com o EDTA. Observou-se ainda um efeito inibidor do EDTPO na corrosão do Al em solução aquosa com pH 9,2 contendo íon cloreto. Imagens da superfície do metal obtidas por microscopia de força atômica indicam que o filme de óxido apresenta um espessamento quando em presença dos agentes quelantes em concordância com os experimentos por espectroscopia de impedância.

Corrosão do aço induzida por íons cloreto : uma análise crítica das técnicas eletroquímicas aplicadas ao sistema aço-concreto com ou sem pozolana

O objetivo deste estudo foi investigar o processo de corrosão no aço embutido nos concretos com relação a/agl 0,40; a/agl 0,50 e a/agl 0,70, com substituição parcial do cimento por 30% de cinza da casca de arroz (CCA), 25% ou 50% de cinza volante (CV), expresso por massa de cimento, obtendo-se concretos convencionais com resistência mecânica variando entre 17 e 51 MPa, aos 28 dias de idade. O processo de corrosão foi induzido pelos íons cloreto, por exposição aos ciclos de imersão em solução com 3,5% NaCl e secagem ao ar, durante um longo período de exposição (5 anos). Foram apresentados os resultados obtidos das propriedades físicas (resistência mecânica à compressão axial, índice de vazios e absorção de água) e propriedades elétricas (queda ôhmica, resistência e capacitância do concreto e interfacial). Foram discutidas as técnicas eletroquímicas usadas para avaliar o processo de corrosão, tais como o monitoramento do potencial de corrosão (Ecorr), resistência de polarização (Rp), espectroscopia de impedância eletroquímica (EIS) e curvas de polarização. A técnica de interrupção de corrente foi usada para obter-se informações sobre a queda ôhmica no sistema. No presente estudo foram utilizados diferentes métodos de determinação da velocidade de corrosão (icorr), tais como Rp e EIS. Ambas as técnicas foram relativamente adequadas para a determinação do valor da icorr, quando o aço se encontrava no estado de corrosão ativa. O valor da icorr obtida pela extrapolação das retas de Tafel (retas tangentes às curvas de polarização) tendeu ser mais baixo. Observou-se que a técnica de Rp é relativamente simples, rápida e quantitativa, mas requer a determinação da compensação da queda ôhmica no sistema, o qual pode variar com o tempo de exposição, conteúdo de umidade, teor de íons cloreto e com o grau de hidratação. A técnica EIS pode fornecer informações precisas sobre a icorr, processo de difusão envolvido, heterogeneidade ou porosidade da matriz e interfaces do concreto. Todavia, pode criar um espectro de difícil interpretação, além de consumir muito tempo para a aquisição dos resultados. A dificuldade na técnica EIS ficou também relacionada com a obtenção direta da resistência de transferência de carga (Rt) no diagrama de Nyquist. A evolução do processo de corrosão pode ser mais bem avaliada pelo acompanhamento da diminuição da inclinação da curva log |Z| x log ƒ no diagrama de Bode, sendo esta diretamente proporcional à Rt. Para a análise dos dados de impedância, um circuito equivalente foi proposto, auxiliando na interpretação física do processo de corrosão acontecendo no sistema aço-concreto sem pozolana. Os resultados obtidos também demonstraram que os concretos com mais baixa relação a/agl estudada e com pozolana (30% CCA, 25% CV ou 50% CV, por massa de cimento) foram mais eficientes no controle da iniciação do processo de corrosão, induzida por íons cloreto, quando monitorado pela medida do Ecorr.

Comportamento elétrico a alta temperatura de termistor cerâmico alfa-Fe2O3 com coeficiente de temperatura negativo

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Obtenção e Caracterização Físico-Química do Sistema Compósito PEG-TiO2

Hybrid systems formed from polymers and transition metals have now their physical and chemical properties extensively investigated for use in electronic devices. In this work, Titanium Dioxide (TiO2) from the precursor of titanium tetrabutoxide and the composite system Poly(Ethylene Glycol)-Titanium Dioxide (TiO2-PEG) were synthesized by sol-gel method. The PEG as acquired and TiO2 and composites powders were analyzed by X-Ray Diffraction (XRD), Spectroscopy in the Infrared region with Fourier transform (IRFT), Thermogravimetric Analysis (TGA), Scanning Electron Microscopy (SEM) and Electrochemical Impedance Spectroscopy (EIS). In the XRD analysis were observed in the TiO2 crystal faces of one of its polymorphs - anatase phase, crystal planes in Poly (Ethylene Glycol) with considerable intensity and in the composite systems the mixture of crystal faces of their precursors isolated and reduction of crystallinity. The TG / DTG suggested increasing the thermal instability of PEG in the composite powders as TiO2 is incorporated into the system. Spectral analysis presented in the infrared overlapping bands for the polymer and metal oxide, reducing the intensity of symmetric stretching of ligand groups in the main chain polymer and angular deformations; were observed using SEM micrographs of the morphological changes suffered by composite systems with the variation of the oxide concentration. Analyses by impedance spectroscopy indicated that the increased conductivity in composite occurs in line with the addition of the metal oxide concentration in the composite system

Estudo da eficácia do tensoativo sorbitano tween 80 veiculado em nanoemulsão contendo óleo de soja, como inibidor de corrosão

Nowadays, the use of chemicals that satisfactorily meet the needs of different sectors of the chemical industry is linked to the consumption of biodegradable materials. In this context, this work contemplated biotechnological aspects with the objective of developing a more environmentally-friendly corrosion inhibitor. In order to achieve this goal, nanoemulsion-type systems (NE) were obtained by varying the amount of Tween 80 (9 to 85 ppm) a sortitan surfactant named polyoxyethylene (20) monooleate. This NE-system was analyzed using phase diagrams in which the percentage of the oil phase (commercial soybean oil, codenamed as OS) was kept constant. By changing the amount of Tween 80, several polar NE-OS derived systems (O/W-type nanoemulsion) were obtained and characterized through light scattering, conductivity and pH, and further subjected to electrochemical studies. The interfacial behavior of these NE-OS derived systems (codenamed NE-OS1, S2, S3, S4 and S5) as corrosion inhibitors on carbon steel AISI 1020 in saline media (NaCl 3.5%) were evaluated by measurement of Open Circuit Potential (OCP), Polarization Curves (Tafel extrapolation method) and Electrochemical Impedance Spectroscopy (EIS). The analyzed NE-OS1 and NE-OS2 systems were found to be mixed inhibitors with quantitative efficacy (98.6% - 99.7%) for concentrations of Tween 80 ranging between 9 and 85 ppm. According to the EIS technique, maximum corrosion efficiency was observed for some tested NE-OS samples. Additionaly to the electrochemical studies, Analysis of Variance (ANOVA) and Principal Component Analysis (PCA) were used, characterization of the nanoemulsion tested systems and adsorption studies, respectively, which confirmed the results observed in the experimental analyses using diluted NE-OS samples in lower concentrations of Tween 80 (0.5 1.75 ppm)

Obtenção e caracterização físico-química de blendas poliméricas, baseadas em POE e PMMA, dopadas com dióxido de titânio

The study of polymer blends has been an alternative method in the search field of new materials for obtaining materials with improved properties. In this work blends of poly(methyl methacrylate) (PMMA) and poly(ethylene oxide) (PEO) doped with titanium dioxide (TiO2) were studied. The PEO is a polymer semicrystalline structure varying between, 70 and 84% crystallinity, while the PMMA exhibits behavior amorphous in their structure. The use of TiO2 is related to corrosion-resistant of titanium as well as good heat transfer and other characteristics. The study of these polymer blends doped TiO2 gives the properties junction organic (polymer) and inorganic (oxide) which leads to modification of the properties of the resultant material. The blends were doped TiO2 (POE/PMMA/TiO2) in different proportions of the PMMA with the PEO and TiO2 fixed. The ratios were: 90/10/0,1; 85/15/0, 1; 80/20/0,1, 75/25/0,1 and 70/30/0,1. The resulting material was obtained in powder form and being characterized by Fourier Transformed Infrared (FTIR) Spectroscopy, Scanning Electron Microscopy (SEM), X-Ray Diffraction (XRD), Thermogravimetric Analysis (TGA) and Electrochemical Impedance Spectroscopy (EIS). The infrared spectra (IR) for the blends in different ratios showed a band at 1744 cm-1, characteristic of the C=O stretching, which increases in intensity with increasing PMMA composition, while in the spectrum of pure PEO this band is absent. This may suggest that the interaction is occurring between the polymers. In the micrographs of the blends also observed change in their surfaces with variation of the composition of PMMA, contributing to the change of the electrical properties of the material. The EIS data showed that the material exhibited conductivity of the order of 10-6 S.cm-1. The blend in the ratio B2(85/15/0, 1) showed better conductivity, σ = 1.56 x 10-6 S.cm-1. It was observed that the diffusion coefficient for the blends, B5(70/30/0, 1) was the largest, 1.07 x 10-6 m2.s-1. The XRD data showing that, with the variation in the composition of the PMMA blend crystallinity of the material is decreased reaching a minimum B3(80/20/0,1), and then increases again. Thermal analysis suggests that blends made from the material obtained can be applied at room temperature